CN110424186A - A kind of reuse paper diaper leftover pieces fiber prepares adsorption paper and preparation method thereof - Google Patents
A kind of reuse paper diaper leftover pieces fiber prepares adsorption paper and preparation method thereof Download PDFInfo
- Publication number
- CN110424186A CN110424186A CN201910626099.9A CN201910626099A CN110424186A CN 110424186 A CN110424186 A CN 110424186A CN 201910626099 A CN201910626099 A CN 201910626099A CN 110424186 A CN110424186 A CN 110424186A
- Authority
- CN
- China
- Prior art keywords
- paper
- leftover pieces
- paper diaper
- diaper leftover
- pieces fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses reuse paper diaper leftover pieces fibers to prepare adsorption paper, includes absorption paper substrate, and the tow sides for adsorbing paper substrate are equipped with enhancing coating.The adsorption paper absorption property is strong, while reuse paper diaper leftover pieces are to economize on resources.The adsorption paper the preparation method comprises the following steps: step 1, will paper diaper leftover pieces fiber crush after it is soluble in water, sequentially add aluminium polychloride, bentonite, zeolite powder, cellulose microsphere and be sufficiently stirred, discongest, obtain fibre stuff;Step 2, by fibre stuff, copy paper is carried out;Step 3, by sodium alginate, konjac glucomannan, collagen it is soluble in water mixed solution, mixed solution is placed in water-bath, modified sodium alginate sizing agent is obtained;Step 4, with sizing applicator by sizing agent in absorption paper substrate tow sides on;Step 5, paper is soaked in calcium chloride solution after being glued obtained by step 4, is impregnated, and is dried in taking-up feeding glazing drying machine, press polish processing.The preparation method is environment friendly and pollution-free.
Description
Technical field
The invention belongs to pulp and paper technology fields, and in particular to a kind of reuse paper diaper leftover pieces fiber preparation absorption
Paper;The invention further relates to the preparation methods that the reuse paper diaper leftover pieces fiber prepares adsorption paper.
Background technique
In recent years, as domestic economy maintains sustained and rapid growth, convenient, the baby of improvement, the life of people's living standard
Youngster and the elderly increase the usage amount of paper diaper year by year.During producing paper diaper, more leftover pieces and property can be generated
Waste that can not be up to standard, this some materials is directly discarded will to cause the great wasting of resources, while also cause centainly to environment
Pollution.
With the development of urbanization process, while water resources consumption increases, the pollution of water body becomes increasingly severe, especially
It is the industries bring colored dyes contaminated wastewater such as dyestuff, textile, paper and plastics.To with adsorption materials such as active carbons
Material is that the physical absorption paper of representative comes into being, but the raw material of adsorption paper is all with protophyte fiber or reclaimed waste paper at present
Or mixing synthetic fibers preparation absorption paper, it is had no by the adsorption paper of primary raw material and preparation method of paper diaper leftover pieces fiber
Report.It is primarily due to adulterate super absorbent resin SAP (the Super Absorbent of high level in paper diaper fiber
Polymer), and fiber sheet is as Time of Fluff Slurry, and intensity is very low, has essential distinction with plant fiber material, if reuse and making
Standby adsorption paper, needs to solve that super water absorbent resin obstacle, paper strength are extremely low and the problems such as assign adsorptivity, and technology of preparing is wanted
Ask higher, difficulty larger.And using protophyte fiber as the preparation of the adsorption paper of raw material need persistently to fall trees for production,
It needs to bleach slurry, this will cause energy consumption, chemical cost, will also result in more environmental pollutions;It is with recycled fiber
Raw material prepares adsorption paper there is also certain difficulty, because domestic waste recovery constitution is incomplete, leads to domestic waste paper resource
Deficiency, paper plant's wastepaper as raw material depends on import more, and waste paper requirements for sale is gradually increased in recent years, and imported waste paper is caused also to break
Layer, finally also influences the reuse of waste paper, and waste paper is again with needing by the processes such as deinking, sterilization, complex process;To synthesize fibre
Mixed plant fiber preparation absorption paper is tieed up, there is a problem of that material is difficult to degrade.
Summary of the invention
The object of the present invention is to provide a kind of reuse paper diaper leftover pieces fibers to prepare adsorption paper, utilizes paper diaper leftover pieces
Fiber makes it have absorption property by abolishing SAP obstacle in paper diaper leftover pieces fiber.
It is a further object of the present invention to provide the preparation method that the reuse paper diaper leftover pieces fiber prepares adsorption paper, the systems
Preparation Method is environment friendly and pollution-free.
The technical scheme adopted by the invention is that reuse paper diaper leftover pieces fiber prepares adsorption paper, it include adsorption paper
Base, the tow sides for adsorbing paper substrate are equipped with enhancing coating.
It is of the invention to be further characterized in that,
Absorption paper substrate is made of following raw material:
Paper diaper leftover pieces fiber, aluminium polychloride, bentonite, zeolite powder, cellulose microsphere;
Proportion relation between above-mentioned raw materials is as follows:
The additive amount of aluminium polychloride is the 0.1%~0.7% of paper diaper leftover pieces fiber quality;
Bentonitic additive amount is the 5%~10% of paper diaper leftover pieces fiber quality;
The additive amount of zeolite powder is the 0.1%-0.3% of paper diaper leftover pieces fiber quality;
The additive amount of cellulose microsphere is the 20%-30% of paper diaper leftover pieces fiber quality;
The particle size of zeolite powder is -200 mesh of 100 mesh, and the partial size of cellulose microsphere is 2 μm -100 μm.
Glue application layer is made of following raw material:
Sodium alginate, konjac glucomannan, collagen, calcium chloride;
Proportion relation between above-mentioned raw materials is as follows:
The addition quality of konjac glucomannan is the 10%-30% of sodium alginate dosage;
The addition quality of collagen is the 2.5% of sodium alginate dosage;
The addition quality of calcium chloride is the 2% of sodium alginate dosage.
Another technical solution of the present invention is that reuse paper diaper leftover pieces fiber prepares the preparation side of adsorption paper
Method, the specific steps are as follows:
Step 1, soluble in water after paper diaper leftover pieces fiber being crushed, sequentially add aluminium polychloride, bentonite, boiling
Mountain flour, cellulose microsphere are sufficiently stirred, and are then discongested, and fibre stuff is obtained;
Step 2, the fibre stuff that will be obtained after step 1 processing, carries out copy paper, obtains absorption paper substrate;
Step 3, by sodium alginate, konjac glucomannan, collagen mixed solution soluble in water simultaneously, mixed solution is placed
It is uninterrupted to stir in 60~70 DEG C of water-baths, modified sodium alginate sizing agent is prepared;
Step 4, with sizing applicator by the resulting sizing agent of step 3 in the obtained absorption paper substrate positive and negative two of step 2
On face;
Step 5, paper is soaked in calcium chloride solution after being glued obtained by step 4, is impregnated after a certain period of time, in adsorption paper
Enhancing coating is obtained on base's tow sides, is dried in taking-up feeding glazing drying machine, press polish processing.
It is of the invention to be further characterized in that,
In step 1, the additive amount of aluminium polychloride is the 0.1%~0.7% of paper diaper leftover pieces fiber quality;Bentonite
Additive amount be paper diaper leftover pieces fiber quality 5%~10%;The additive amount of zeolite powder is paper diaper leftover pieces cellulosic
The 0.1%~0.3% of amount;The additive amount of cellulose microsphere is the 20%-30% of paper diaper leftover pieces fiber quality;
The particle size of zeolite powder is -200 mesh of 100 mesh, and the partial size of cellulose microsphere is 2 μm -100 μm.
In step 1, slurry is discongested with fluffer, revolving speed is 25000 turns.
Copied in step 2 using pattern take device by treated in step 1 fibre stuff copies that paper is made, specific implementation method
Are as follows: with blender, by step 1, treated that fibre stuff is stirring evenly and then adding into pattern copies and take in device first, adds water, makes slurry
Online concentration reaches 0.5%, discharges water, makes wet web, then squeezed manually with pressure roller, is finally putting into page drying
Device is dried 5 minutes with 105 DEG C of temperature under conditions of vacuum degree is 0.06MPa, after drying, puts vacuum, take paper, inhaled
Attached paper substrate.
In step 3, the time uninterruptedly stirred is 30 minutes;Sodium alginate in water mass concentration range be 2%~
3%, the addition quality of konjac glucomannan is the 10%-30% of sodium alginate dosage, and the addition quality of collagen is sodium alginate use
The 2.5% of amount.
It is 6g/m in the resin added of the obtained absorption paper substrate tow sides of step 2 in step 42。
In step 5, the concentration of calcium chloride solution is 0.5mol/L, and dip time is 30 minutes.
The beneficial effects of the present invention are:
(1) reuse paper diaper leftover pieces fiber of the present invention prepares adsorption paper, and final realize abolishes paper diaper leftover pieces fiber
Middle SAP obstacle obtains to economize on resources by a relatively large margin with absorption property and the good adsorption paper of strength character, saving energy
Source saves transport, reduces discharge and improve society and economic benefit, and effectively improving the value of paper diaper Time of Fluff Slurry paper reuse,
The technological gap that paper diaper leftover pieces reuse prepares adsorption paper is filled up, larger contribution can be made for pulping and paper-making industry.
(2) method that the present invention prepares adsorption paper using paper diaper leftover pieces fiber, firstly, using aluminium polychloride, swollen
Moisten soil, zeolite powder, cellulose microsphere and handle paper diaper leftover pieces fiber, wherein aluminium chloride and bentonite synergistic effect destroy
SAP gel state, and cross-linking, be adsorbed between fiber, it efficiently solves SAP and paper diaper leftover pieces fiber reuse is caused
Obstacle;Zeolite has rack-like structure, and in their crystal, molecule connects together as building a framework, and centre forms very much
Cavity has good suction-operated;Cellulose microsphere is porous structure, has preferable absorption property.Pass through each component
Synergistic effect, it is final to realize the reuse of paper diaper leftover pieces fiber and assign its adsorptivity.Secondly, with sodium alginate, konjac glucomannan, glue
Former albumen is sizing agent, can largely improve the strength character of adsorption paper.
Detailed description of the invention
Fig. 1 is cellulose microsphere scanning electron microscope (SEM) photograph (2000 times of amplification);
Fig. 2 is cellulose microsphere scanning electron microscope (SEM) photograph (10000 times of amplification);
Fig. 3 is the laser particle size result figure of cellulose microsphere;
Fig. 4 is the adsorption effect pictorial diagram of the adsorption paper different amounts that are prepared with the method for the present invention to methylene blue solution;
Fig. 5 be different amounts the method for the present invention preparation adsorption paper to the absorption of methylene blue solution after, methylene blue is molten
Liquid concentration variation diagram.
Specific embodiment
The following describes the present invention in detail with reference to the accompanying drawings and specific embodiments.
The present invention provides a kind of reuse paper diaper leftover pieces fiber and prepares adsorption paper, includes absorption paper substrate, adsorption paper
The tow sides of base are equipped with enhancing coating.
Absorption paper substrate is made of following raw material:
Paper diaper leftover pieces fiber, aluminium polychloride, bentonite, zeolite powder, cellulose microsphere;
Proportion relation between above-mentioned raw materials is as follows:
The additive amount of aluminium polychloride is the 0.1%~0.7% of paper diaper leftover pieces fiber quality;
Bentonitic additive amount is the 5%~10% of paper diaper leftover pieces fiber quality;
The additive amount of zeolite powder is the 0.1%-0.3% of paper diaper leftover pieces fiber quality;
The additive amount of cellulose microsphere is the 20%-30% of paper diaper leftover pieces fiber quality;
The particle size of zeolite powder is -200 mesh of 100 mesh, and the partial size of cellulose microsphere is 2 μm -100 μm.
Glue application layer is made of following raw material:
Sodium alginate, konjac glucomannan, collagen, calcium chloride;
Proportion relation between above-mentioned raw materials is as follows:
The addition quality of konjac glucomannan is the 10%-30% of sodium alginate dosage;
The addition quality of collagen is the 2.5% of sodium alginate dosage;
The addition quality of calcium chloride is the 2% of sodium alginate dosage.
The present invention also provides the preparation methods that above-mentioned reuse paper diaper leftover pieces fiber prepares adsorption paper, and specific steps are such as
Under:
Step 1, soluble in water after paper diaper leftover pieces fiber being crushed, sequentially add aluminium polychloride, bentonite, boiling
Mountain flour, cellulose microsphere are sufficiently stirred, and are then discongested, and fibre stuff is obtained;
In step 1, the additive amount of aluminium polychloride is the 0.1%~0.7% of paper diaper leftover pieces fiber quality;Bentonite
Additive amount be paper diaper leftover pieces fiber quality 5%~10%;The additive amount of zeolite powder is paper diaper leftover pieces cellulosic
The 0.1%~0.3% of amount;The additive amount of cellulose microsphere is the 20%-30% of paper diaper leftover pieces fiber quality;
The particle size of zeolite powder is -200 mesh of 100 mesh, and the partial size of cellulose microsphere is 2 μm -100 μm.
In step 1, slurry is discongested with fluffer, revolving speed is 25000 turns;
Step 2, the fibre stuff that will be obtained after step 1 processing, carries out copy paper, obtains absorption paper substrate;
Copied in step 2 using pattern take device by treated in step 1 fibre stuff copies that paper is made, specific implementation method
Are as follows: with blender, by step 1, treated that fibre stuff is stirring evenly and then adding into pattern copies and take in device first, adds water, makes slurry
Online concentration reaches 0.5%, discharges water, makes wet web, then squeezed manually with pressure roller, is finally putting into page drying
Device is dried 5 minutes with 105 DEG C of temperature under conditions of vacuum degree is 0.06MPa, after drying, puts vacuum, take paper, inhaled
Attached paper substrate;
Step 3, by sodium alginate, konjac glucomannan, collagen mixed solution soluble in water simultaneously, mixed solution is placed
In 60~70 DEG C of water-baths, modified sodium alginate sizing agent is prepared in uninterrupted stirring 30 minutes;
In step 3, mass concentration range is 2%~3% to sodium alginate in water, and the addition quality of konjac glucomannan is alginic acid
The 10%-30% of sodium dosage, the addition quality of collagen are the 2.5% of sodium alginate dosage;
Step 4, with sizing applicator by the resulting sizing agent of step 3 in the obtained absorption paper substrate positive and negative two of step 2
On face;
It is 6g/m in the resin added of the obtained absorption paper substrate tow sides of step 2 in step 42。
Step 5, paper is soaked in calcium chloride solution after being glued obtained by step 4, and dipping is after 30 minutes, in absorption paper base
Enhancing coating is obtained on layer tow sides, is dried in taking-up feeding glazing drying machine, press polish processing;
In step 5, the concentration of calcium chloride solution is 0.5mol/L.
The reason of each raw material is selected in the present invention is as follows:
(1) the reason of adding aluminium polychloride, bentonite, zeolite powder, cellulose microsphere
Since addition aluminium polychloride can destroy the interfacial electric double layer of SAP gelatinous mass, inside and outside the two of the substance are improved
Phase density is poor, and interior phase is promoted to be easy to be precipitated, and bentonite adsorption promotes the thickness of gel to become larger in SAP gel surface, gel
The ratio between surface area relative gel volume becomes smaller, and with the formation of epidermis, builds up pressure in large quantities inside gel, causes in gel
External pressure difference becomes larger, and gel surface is promoted to be easily broken.The raising of two-phase density contrast, the enhancing of internal and external pressure difference inside and outside gel
Under synergistic effect, finally cause the destructurized of gel, swelling variation becomes irreversible.Make to make SAP lose water suction
With not re-forming gel form.
The crystal structure of zeolite is to be linked to be three-dimensional screen work by silicon (aluminium) oxygen tetrahedron, is had in screen work of all sizes
Hole and channel have very big opening.Cavity of different sizes present in lattice can be drawn and of different sizes lose suction
The SAP particle of water effect, meanwhile, it is given to the certain absorption property of paper.
Cellulose microsphere is porous surface, and the spherical structure (as shown in Figure 1 and Figure 2) of central hollow has suction-operated,
Paper absorption property can be improved into.
(2) using sodium alginate, konjac glucomannan, collagen as sizing agent the reason of
Sizing agent is made of sodium alginate, konjac glucomannan, collagen, environment friendly and pollution-free.Wherein, sodium alginate has fine
Film forming, the substrate as sizing agent;Konjac glucomannan is added later, plays thickening, bonding and stable effect, while can have
Effect improves the toughness of sodium alginate film forming;The strand of collagen is in three-dimensional spiral structure, contains firm peptide bond and crosslinking
Key, makes it have excellent mechanical performance, and collagen and water occur aquation, are swollen after water suction, has colloidal nature, add
Being added to is that can effectively improve the caking property of sizing agent in sizing agent, improves the mechanical performance of adsorption paper.
Paper diaper leftover pieces fiber used in of the invention and embodiment is paper diaper absorbed layer fluff pulp fibers;The present invention is implemented
Chemicals used in example includes the white aluminium polychloride that rich environmental protection company production is moistened in Zhengzhou City;The VF- of Wei Ke company, U.S. production
20 type bentonites;The experiment reagent artificial zeolite of Tianjin great Mao chemical reagent factory production is (after pulverizer crushes, by 100 mesh-
It is used after the sieve screening of 200 mesh);Make cellulose microsphere by oneself in laboratory;The analysis of Tianjin good fortune morning chemical reagent factory production is pure
Sodium alginate;The pure konjac glucomannan of analysis of Shandong You Suo Chemical Industry Science Co., Ltd production;Tianjin Ke Miou chemical reagent is limited
The pure calcium chloride of analysis of company's production;The ST-817 collagen of Hubei Hai Long industrial technology Co., Ltd production;
Wherein, make by oneself cellulose microsphere the preparation method comprises the following steps: weighs a certain amount of smashed bleaching needle-point leaf pulp plate, is put into
In beaker, according to wintercherry than the concentrated sulfuric acid that mass concentration is 61% is added for 10ml/g, 2~3min of stirring dissolves pulpboard, so
20min is reacted in the case where temperature is 45 DEG C of water bath condition afterwards, is persistently stirred using blender in reaction process, until reaction
At the end of, stop reaction with deionized water dilution, obtains white uniformity suspension.By this suspension centrifuge centrifugal water
It washes, outwells supernatant liquor every time, retain lower layer's decorating film and continue that water cleaning is added to be centrifuged, after eccentric cleaning 3~4 times, make final obtain
Stop centrifugation when the lotion pH arrived is between 4~5, this white emulsion is put into bag filter (molecular cut off 8000~14000)
In, it is constant to pH value with deionized water dialysis a couple of days.Suspension after dialysis handles 15min with supersonic oscillations, micro- to avoid
Crystalline cellulose is assembled because of overheat, and ultrasonic treatment carries out in 5 DEG C of low temperature water-baths.The microcrystalline cellulose water phase that will be ultrasonically treated
Suspension is dried, using spray dryer, inlet temperature be 160 DEG C under the conditions of by microcrystalline cellulose suspension liquid of aqueous phase
Drying is to get cellulose microsphere.(the same paper of method " influence of the drying means to acid hydrolyzed cellulose pattern and structure ", Shaanxi
University of Science and Technology's journal, 2018,36 (6): 25-29)
Embodiment 1
1) smashed paper diaper leftover pieces fiber is acquired as experiment raw material, this raw material sources is in paper diaper factory
Family.
2) sample after taking 2.6 grams of paper diaper leftover pieces fibers to crush is added in 500ml water, using AB L&W company, Sweden
260 type fluffers of production discongest slurry, discongest 25000 turns, add water to slurry concentration up to 0.5%, using German HG company
The BBS-3_D-45476 type pattern of production, which is copied, takes device to carry out copy paper, 105 DEG C of dryings, the scraps of paper is made, as blank sample.
3) sample after taking 2.6 grams of paper diaper leftover pieces fibers to crush is added in 300ml water, then is weighed respectively relative to paper
The aluminium polychloride of urine pants leftover pieces fiber quality 0.1%, relative to paper diaper leftover pieces fiber quality 10% bentonite,
0.3% zeolite powder relative to paper diaper leftover pieces fiber quality, 20% relative to paper diaper leftover pieces fiber quality
Cellulose microsphere, and added in fibre stuff, add water constant volume to 500ml, stir evenly, then, using Sweden AB L&W
260 type fluffers of company's production discongest slurry, discongest 25000 turns, and German HG company production is put into after the completion of fiber is discongested
BBS-3_D-45476 type pattern copy and take device, add water, so that approach flow concentration is reached 0.5%, discharge water, make wet web,
It is squeezed manually with pressure roller again, is finally putting into page baker, under conditions of vacuum degree is 0.06MPa, with 105 DEG C of temperature
Degree drying 5 minutes, after drying, puts vacuum, the scraps of paper is made, to use pattern wait be glued.
0.4g sodium alginate is dissolved in 19.6ml water, is placed in beaker, mass concentration 2%, while adding konjaku
Glue, the additive amount of konjac glucomannan are the 25% of sodium alginate dosage, add collagen, and collagen additive amount is sodium alginate
The 2.5% of dosage.Beaker equipped with above-mentioned solution is put in 65 DEG C of water-baths, uninterrupted stirring 30 minutes, at this point, solution is in glue
Shape solution, to use sizing agent wait be glued.
It made is applied using the AUTO Sizer-01 type surface size press of Beijing Heng Chengyu Science and Technology Ltd. production by above-mentioned
Jelly is uniformly glued in the tow sides of pattern to be glued, and positive and negative resin added two-by-two is 6g/m2, pattern is then put into quality
Half an hour is impregnated in the 30ml calcium chloride solution that concentration is 0.5mol/L, places into rapid impregnation 10s in water, takes out and is sent into Xianyang
It is dried in the TD19-A type glazing drying machine of sensible light equipment Co., Ltd production, press polish processing, finally obtains reuse
Paper diaper leftover pieces fiber reproduces anti-bacteria paper.Referred to as 1# sample.
Embodiment 2
Sample after taking 2.6 grams of paper diaper to crush is added in 300ml water, then weighs respectively fine relative to paper diaper leftover pieces
Tie up quality 0.3% aluminium polychloride, relative to 6% bentonite of paper diaper leftover pieces fiber quality, relative to paper diaper
0.2% zeolite powder of leftover pieces fiber quality, relative to 25% cellulose microsphere of paper diaper leftover pieces fiber quality, and
It is added in fibre stuff, adds water constant volume to 500ml, stir evenly, then, using the 260 of the production of AB L&W company, Sweden
Type fluffer discongests slurry, discongests 25000 turns, and the BBS-3_D- of German HG company production is put into after the completion of fiber is discongested
45476 type patterns, which are copied, takes device, adds water, so that approach flow concentration is reached 0.5%, discharge water, and makes wet web, then with pressure roller into
Row squeezing manually, is finally putting into page baker, under conditions of vacuum degree is 0.06MPa, dries 5 points with 105 DEG C of temperature
Clock after drying, puts vacuum, the scraps of paper is made, to use pattern wait be glued.
0.4g sodium alginate is dissolved in 19.6ml water, is placed in beaker, mass concentration 2%, while adding konjaku
Glue, the additive amount of konjac glucomannan are the 10% of sodium alginate dosage, add collagen, and collagen additive amount is sodium alginate
The 2.5% of dosage.Beaker equipped with above-mentioned solution is put in 65 DEG C of water-baths, uninterrupted stirring 30 minutes, at this point, solution is in glue
Shape solution, to use sizing agent wait be glued.
It made is applied using the AUTO Sizer-01 type surface size press of Beijing Heng Chengyu Science and Technology Ltd. production by above-mentioned
Jelly is uniformly glued in the tow sides of pattern to be glued, and the resin added of tow sides is 6g/m2, pattern is then put into quality
Half an hour is impregnated in the 30ml calcium chloride solution that concentration is 0.5mol/L, places into rapid impregnation 10s in water, takes out and is sent into Xianyang
It is dried in the TD19-A type glazing drying machine of sensible light equipment Co., Ltd production, press polish processing, finally obtains reuse
Paper diaper leftover pieces fiber reproduces anti-bacteria paper.Referred to as 2# sample.
Embodiment 3
Sample after taking 2.6 grams of paper diaper to crush is added in 300ml water, then weighs respectively fine relative to paper diaper leftover pieces
Tie up quality 0.5% aluminium polychloride, relative to 8% bentonite of paper diaper leftover pieces fiber quality, relative to paper diaper
0.1% zeolite powder of leftover pieces fiber quality, relative to 30% cellulose microsphere of paper diaper leftover pieces fiber quality, and
It is added in fibre stuff, adds water constant volume to 500ml, stir evenly, then, using the 260 of the production of AB L&W company, Sweden
Type fluffer discongests slurry, discongests 25000 turns, and the BBS-3_D- of German HG company production is put into after the completion of fiber is discongested
45476 type patterns, which are copied, takes device, adds water, so that approach flow concentration is reached 0.5%, discharge water, and makes wet web, then with pressure roller into
Row squeezing manually, is finally putting into page baker, under conditions of vacuum degree is 0.06MPa, dries 5 points with 105 DEG C of temperature
Clock after drying, puts vacuum, the scraps of paper is made, to use pattern wait be glued.
0.6g sodium alginate is dissolved in 19.4ml water, is placed in beaker, mass concentration 3%, while adding konjaku
Glue, the additive amount of konjac glucomannan are the 25% of sodium alginate dosage, add collagen, and collagen additive amount is sodium alginate
The 2.5% of dosage.Beaker equipped with above-mentioned solution is put in 70 DEG C of water-baths, uninterrupted stirring 30 minutes, at this point, solution is in glue
Shape solution, to use sizing agent wait be glued.
It made is applied using the AUTO Sizer-01 type surface size press of Beijing Heng Chengyu Science and Technology Ltd. production by above-mentioned
Jelly is uniformly glued in the tow sides of pattern to be glued, and the resin added of tow sides is 6g/m2, pattern is then put into quality
Half an hour is impregnated in the 30ml calcium chloride solution that concentration is 0.5mol/L, places into rapid impregnation 10s in water, takes out and is sent into Xianyang
It is dried in the TD19-A type glazing drying machine of sensible light equipment Co., Ltd production, press polish processing, finally obtains reuse
Paper diaper leftover pieces fiber reproduces anti-bacteria paper.Referred to as 3# sample.
Embodiment 4
Sample after taking 2.6 grams of paper diaper to crush is added in 300ml water, then weighs respectively fine relative to paper diaper leftover pieces
Tie up quality 0.7% aluminium polychloride, relative to 5% bentonite of paper diaper leftover pieces fiber quality, relative to paper diaper
0.3% zeolite powder of leftover pieces fiber quality, relative to 30% cellulose microsphere of paper diaper leftover pieces fiber quality, and
It is added in fibre stuff, adds water constant volume to 500ml, stir evenly, then, using the 260 of the production of AB L&W company, Sweden
Type fluffer discongests slurry, discongests 25000 turns, and the BBS-3_D- of German HG company production is put into after the completion of fiber is discongested
45476 type patterns, which are copied, takes device, adds water, so that approach flow concentration is reached 0.5%, discharge water, and makes wet web, then with pressure roller into
Row squeezing manually, is finally putting into page baker, under conditions of vacuum degree is 0.06MPa, dries 5 points with 105 DEG C of temperature
Clock after drying, puts vacuum, the scraps of paper is made, to use pattern wait be glued.
0.6g sodium alginate is dissolved in 19.4ml water, is placed in beaker, mass concentration 3%, while adding konjaku
Glue, the additive amount of konjac glucomannan are the 10% of sodium alginate dosage, add collagen, and collagen additive amount is sodium alginate
The 2.5% of dosage.Beaker equipped with above-mentioned solution is put in 70 DEG C of water-baths, uninterrupted stirring 30 minutes, at this point, solution is in glue
Shape solution, to use sizing agent wait be glued.
It made is applied using the AUTO Sizer-01 type surface size press of Beijing Heng Chengyu Science and Technology Ltd. production by above-mentioned
Jelly is uniformly glued in the tow sides of pattern to be glued, and the resin added of tow sides is 6g/m2, pattern is then put into quality
Half an hour is impregnated in the 30ml calcium chloride solution that concentration is 0.5mol/L, places into rapid impregnation 10s in water, takes out and is sent into Xianyang
It is dried in the TD19-A type glazing drying machine of sensible light equipment Co., Ltd production, press polish processing, finally obtains reuse
Paper diaper leftover pieces fiber reproduces anti-bacteria paper.Referred to as 4# sample.
Embodiment 5
Sample after taking 2.6 grams of paper diaper to crush is added in 300ml water, then weighs respectively fine relative to paper diaper leftover pieces
Tie up quality 0.4% aluminium polychloride, relative to 7% bentonite of paper diaper leftover pieces fiber quality, relative to paper diaper
0.2% zeolite powder of leftover pieces fiber quality, relative to 30% cellulose microsphere of paper diaper leftover pieces fiber quality, and
It is added in fibre stuff, adds water constant volume to 500ml, stir evenly, then, using the 260 of the production of AB L&W company, Sweden
Type fluffer discongests slurry, discongests 25000 turns, and the BBS-3_D- of German HG company production is put into after the completion of fiber is discongested
45476 type patterns, which are copied, takes device, adds water, so that approach flow concentration is reached 0.5%, discharge water, and makes wet web, then with pressure roller into
Row squeezing manually, is finally putting into page baker, under conditions of vacuum degree is 0.06MPa, dries 5 points with 105 DEG C of temperature
Clock after drying, puts vacuum, the scraps of paper is made, to use pattern wait be glued.
0.4g sodium alginate is dissolved in 19.6ml water, is placed in beaker, mass concentration 2%, while adding konjaku
Glue, the additive amount of konjac glucomannan are the 30% of sodium alginate dosage, add collagen, and collagen additive amount is sodium alginate
The 2.5% of dosage.Beaker equipped with above-mentioned solution is put in 65 DEG C of water-baths, uninterrupted stirring 30 minutes, at this point, solution is in glue
Shape solution, to use sizing agent wait be glued.
It made is applied using the AUTO Sizer-01 type surface size press of Beijing Heng Chengyu Science and Technology Ltd. production by above-mentioned
Jelly is uniformly glued in the tow sides of pattern to be glued, and the resin added of tow sides is 6g/m2, pattern is then put into quality
Half an hour is impregnated in the 30ml calcium chloride solution that concentration is 0.5mol/L, places into rapid impregnation 10s in water, takes out and is sent into Xianyang
It is dried in the TD19-A type glazing drying machine of sensible light equipment Co., Ltd production, press polish processing, finally obtains reuse
Paper diaper leftover pieces fiber reproduces anti-bacteria paper.Referred to as 5# sample.
Using the surface of the VEGA 3SBH type scanning electron microscope characterization cellulose microsphere of company, TESCAN Czech production
Pattern, as shown in Figure 1 and Figure 2.By Fig. 1, Fig. 2 as it can be seen that cellulose microsphere surface is porous structure, as prepared by the present invention
One of ingredient of adsorption paper contributes the raising of the absorption property for adsorption paper.
Fiber is characterized using the A89994 type laser/image granularity particle shape analyzer of Dandong Bai Te Instrument Ltd. production
The partial size of plain microballoon, grain size distribution are shown in Fig. 3, and as seen from the figure, cellulose microsphere partial size is most of at 2 μm -100 μm, main to collect
In at 2 μm -10 μm.
The suction of adsorption paper is prepared using the UV, visible light light splitting photometry characterization present invention of Pa Jin Elmer Co., Ltd, U.S. production
Attached effect will converse methylene blue solution concentration value according to absorbance value, and finally calculate the removal rate of methylene blue.Fig. 4
Adsorption effect pictorial diagram after 30min is adsorbed to methylene blue solution for different adsorption paper dosages, is followed successively by Asia from left to right in figure
Methyl blue original solution, add 0.0754g adsorption paper absorption after methylene blue solution, add 0.1508g adsorption paper absorption after
Methylene blue solution, add 0.2262g adsorption paper absorption after methylene blue solution, add 0.3017g adsorption paper absorption after
Methylene blue solution.As seen from the figure, as adsorption paper additive amount increases, the color of methylene blue solution is more shallow, illustrates, with suction
Attached paper dosage increases, and adsorption effect is better.Meanwhile being also shown by table 1, with the increase of adsorption paper dosage, methylene blue is gone
Except rate is higher, when dosage is 0.3017g, methylene blue removal rate has reached up to 90.40%, if continuing addition absorption
Paper can obtain better adsorption effect, be also shown by Fig. 4, and the methylene blue solution blue of right end is close to colourless.Experimental result
It has been shown that, adsorption paper prepared by the present invention can effectively adsorb dyestuff, have good absorption property.
The different adsorption paper dosages of table 1 are to methylene blue adsorption number result
The tensile strength instrument of the model TH-1 produced using GB/T453-1989 method Sweden measures the anti-tensile of pattern
Index;Paper is measured using the PROTEAR tearability instrument that GB/T455.1-1989 method Thwing-Albert company, the U.S. produces
The tear index of sample, the results are shown in Table 2.
The intensity index statistical form of 2 pattern of table
As shown in Table 2, blank sample tensile index and tear index are lower.And pass through absorption prepared by method of the invention
Paper, tensile index are averagely increased to 49.2Nm/g from 6.3Nm/g, averagely improve 681%;Tear index is from 4.8mN
m2/ g is averagely increased to 11.1mNm2/ g, improves 131%.The result shows that the preparation method of the adsorption paper can significantly improve
The strength character of paper diaper leftover pieces fiber papermaking.
The present invention will in view of the deficiencies of the prior art, for the characteristic of paper diaper leftover pieces fiber, in conjunction with market to paper
Functional requirements have adsorption function paper using technical method preparation simple to operation using paper diaper leftover pieces as raw material, and
Its strength character is improved, the field technological gap is filled up, effective reuse of paper diaper leftover pieces fiber is realized, economizes on resources, keep away
Exempt to bleach energy consumption, chemical cost, reduce environmental pollution.Economic factor, reuse profit meeting are just fully considered from research and development are started
Constantly increase, from the point of view of saving material, energy saving, saving transport reduces discharge and improves application performance, effect highly significant,
Larger contribution can be made for pulping and paper-making industry.
Claims (10)
1. reuse paper diaper leftover pieces fiber prepares adsorption paper, which is characterized in that include absorption paper substrate, adsorb paper substrate
Tow sides are equipped with enhancing coating.
2. reuse paper diaper leftover pieces fiber according to claim 1 prepares adsorption paper, which is characterized in that the adsorption paper
Base is made of following raw material:
Paper diaper leftover pieces fiber, aluminium polychloride, bentonite, zeolite powder, cellulose microsphere;
Proportion relation between above-mentioned raw materials is as follows:
The additive amount of aluminium polychloride is the 0.1%~0.7% of paper diaper leftover pieces fiber quality;
Bentonitic additive amount is the 5%~10% of paper diaper leftover pieces fiber quality;
The additive amount of zeolite powder is the 0.1%-0.3% of paper diaper leftover pieces fiber quality;
The additive amount of cellulose microsphere is the 20%-30% of paper diaper leftover pieces fiber quality;
The particle size of the zeolite powder is -200 mesh of 100 mesh, and the partial size of the cellulose microsphere is 2 μm -100 μm.
3. reuse paper diaper leftover pieces fiber according to claim 1 prepares adsorption paper, which is characterized in that the glue application layer
It is made of following raw material:
Sodium alginate, konjac glucomannan, collagen, calcium chloride;
Proportion relation between above-mentioned raw materials is as follows:
The addition quality of konjac glucomannan is the 10%-30% of sodium alginate dosage;
The addition quality of collagen is the 2.5% of sodium alginate dosage;
The addition quality of calcium chloride is the 2% of sodium alginate dosage.
4. the preparation method that reuse paper diaper leftover pieces fiber prepares adsorption paper, which is characterized in that specific step is as follows:
Step 1, soluble in water after paper diaper leftover pieces fiber being crushed, sequentially add aluminium polychloride, bentonite, zeolite
Powder, cellulose microsphere are sufficiently stirred, and are then discongested, and fibre stuff is obtained;
Step 2, the fibre stuff that will be obtained after step 1 processing, carries out copy paper, obtains absorption paper substrate;
Step 3, by sodium alginate, konjac glucomannan, collagen mixed solution soluble in water simultaneously, mixed solution is placed in 60
It is uninterrupted to stir in~70 DEG C of water-baths, modified sodium alginate sizing agent is prepared;
Step 4, with sizing applicator by the resulting sizing agent of step 3 on the obtained absorption paper substrate tow sides of step 2;
Step 5, paper is soaked in calcium chloride solution after being glued obtained by step 4, and dipping after a certain period of time, is adsorbing paper substrate
Enhancing coating is obtained on tow sides, is dried in taking-up feeding glazing drying machine, press polish processing.
5. the preparation method that reuse paper diaper leftover pieces fiber according to claim 4 prepares adsorption paper, which is characterized in that
In step 1, the additive amount of aluminium polychloride is the 0.1%~0.7% of paper diaper leftover pieces fiber quality;Bentonitic additive amount
It is the 5%~10% of paper diaper leftover pieces fiber quality;The additive amount of zeolite powder is the 0.1% of paper diaper leftover pieces fiber quality
~0.3%;The additive amount of cellulose microsphere is the 20%-30% of paper diaper leftover pieces fiber quality;
The particle size of the zeolite powder is -200 mesh of 100 mesh, and the partial size of the cellulose microsphere is 2 μm -100 μm.
6. the preparation method that reuse paper diaper leftover pieces fiber according to claim 4 prepares adsorption paper, which is characterized in that
In step 1, slurry is discongested with fluffer, revolving speed is 25000 turns.
7. the preparation method that reuse paper diaper leftover pieces fiber according to claim 4 prepares adsorption paper, which is characterized in that
Copied in step 2 using pattern take device by treated in step 1 fibre stuff copies that paper is made, specific implementation method are as follows: use first
Treated that fibre stuff is stirring evenly and then adding into pattern copies and take in device by step 1 for blender, adds water, reaches approach flow concentration
It to 0.5%, discharges water, makes wet web, then squeezed manually with pressure roller, page baker is finally putting into, in vacuum degree
It under conditions of 0.06MPa, is dried 5 minutes with 105 DEG C of temperature, after drying, puts vacuum, take paper, obtain absorption paper substrate.
8. the preparation method that reuse paper diaper leftover pieces fiber according to claim 4 prepares adsorption paper, which is characterized in that
In step 3, the time uninterruptedly stirred is 30 minutes;Mass concentration range is 2%~3% to sodium alginate in water, konjac glucomannan
Addition quality be sodium alginate dosage 10%-30%, the addition quality of collagen is the 2.5% of sodium alginate dosage.
9. the preparation method that reuse paper diaper leftover pieces fiber according to claim 4 prepares adsorption paper, which is characterized in that
It is 6g/m in the resin added of the obtained absorption paper substrate tow sides of step 2 in step 42。
10. reuse paper diaper leftover pieces fiber according to claim 4 prepares the preparation method of adsorption paper, feature exists
In in step 5, the concentration of the calcium chloride solution is 0.5mol/L, and dip time is 30 minutes.