CN110423582A - Interlabial pad individual labeling glue - Google Patents
Interlabial pad individual labeling glue Download PDFInfo
- Publication number
- CN110423582A CN110423582A CN201910754360.3A CN201910754360A CN110423582A CN 110423582 A CN110423582 A CN 110423582A CN 201910754360 A CN201910754360 A CN 201910754360A CN 110423582 A CN110423582 A CN 110423582A
- Authority
- CN
- China
- Prior art keywords
- thermoplastic elastomer
- tackifying resin
- parts
- analog thermoplastic
- styrene analog
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of interlabial pad individual labeling glue, the component including following parts by weight: 38-60 parts of styrene analog thermoplastic elastomer;30-45 parts of tackifying resin;10-15 parts of softening agent;1.5-2 parts of antioxidant.Pass through above-mentioned setting, there are unique two phase structures for styrene analog thermoplastic elastomer, no adhesion itself, wettability, cohesive force, peel strength and shear strength are improved by tackifying resin and softening agent, increase initial bonding strength and lasting adhesive strength, the stickup for enabling to labeling glue stable uses, and other components further improve whole performance, reaching can either have certain adhesion strength to be easy to remove in time in independent packaging use again, be easy to use.
Description
Technical field
The present invention relates to hygiene article sectors, in particular to interlabial pad individual labeling glue.
Background technique
Sanitary napkin is that women often uses one of amenities, and demand is big, and quality requirement is high, particularly, consumer for
The safety of the articles such as sanitary napkin and sanitation degree pay attention to day by day.Common sanitary towels packaging is mostly external whole big
Packaging, inside are equipped with a fairly large number of monolithic sanitary towels, and be in can be straight for all monolithic products after outer packaging is opened
The state used is connect, for the monolithic sanitary towels for failing to timely use, is tended to by pollution sources in external environment
Pollution, influence using.
Therefore, most products can also carry out independent packaging to every a piece of sanitary napkin in external big packaging currently on the market,
Thus ensured the normal use of monolithic product, and varied, the existing tearing mode that the opening ways of independent packaging are also the same
Also there is opening labeling type, opposite opening labeling type is more more environmentally-friendly, therefore applies more extensive.
Meanwhile the product of independent packaging is also more convenient to carry, and for the independent packaging of labeling type that is open, labeling
The adhesive property at place is then of crucial importance, and the adhesion strength of labeling and substrate can neither be too strong, to prevent from being difficult in time when opening
Raise, can not adhesion strength it is too weak, with prevent carry when cause edge warpage.
Summary of the invention
In view of the deficiencies of the prior art, the present invention intends to provide a kind of interlabial pad individual labeling use
Glue has the effect of that caking property is strong and is easily peeled off.
Above-mentioned technical purpose of the invention technical scheme is that, a kind of interlabial pad individual mark
Patch glue, the component including following parts by weight: 38-60 parts of styrene analog thermoplastic elastomer;30-45 parts of tackifying resin;It is soft
10-15 parts of agent;1.5-2 parts of antioxidant.
By using above-mentioned technical proposal, there are unique two phase structures for styrene analog thermoplastic elastomer, itself is without viscous
Knot property improves wettability, cohesive force, peel strength and shear strength by tackifying resin and softening agent, increases initial bonding strength and holds
Long adhesive strength, the stickup for enabling to labeling glue stable use, and other components further improve whole performance, reach both
There can be certain adhesion strength to be easy to remove in time in independent packaging use again, be easy to use.
The further setting of the present invention are as follows: the styrene analog thermoplastic elastomer is SBS, the styrene analog thermoplastic
The melt index (MI) of elastomer is less than 10g/10min.
The further setting of the present invention are as follows: the tackifying resin is to pass through hydrotreated C5/C9 Petropols.
By using above-mentioned technical proposal, tackifying resin is to hydrogenate complete C5/C9 Petropols, of light color and nontoxic,
Meet medical requirement, thus be applied to amenities be also completely can with, and hydrogenated resin molecular link after hydrotreating
Stable double bond is formed, is easily saturated, chemical property is stablized, therefore non-aging;Thermoplastic elastomer (TPE) has longer strand
It is intermolecular not easy to break so that finished product made of hot-fusible pressure-sensitive adhesive is easily peelable with good elasticity, and good elasticity makes
Residual is seldom had after must removing, and can smoothly be torn when independent packaging enables.
The further setting of the present invention are as follows: the softening agent is naphthenic oil, and the antioxidant is phenol antiager.
By using above-mentioned technical proposal, the addition of softening agent can make trademark adhesive be easy to construct in low temperature.Antioxidant
Addition can assign trademark adhesive good antioxygenic property, increase trademark adhesive the preservation time and paste after label gluing knot
Intensity is held time.
The further setting of the present invention is to be prepared using following steps:
Step 1: according to parts by weight, weighing 10-20 parts of styrene analog thermoplastic elastomer, 30-45 parts of tackifying resin, phenylethylene
15-20 parts of thermoplastic elastomer (TPE), 10-15 parts of softening agent, 1.5-2 parts of antioxidant;
Step 2: reaction vessel being heated to 135-140 DEG C, softening agent is added and is stirred heating;
Step 3: antioxidant, the tackifying resin of 20wt% and the styrene analog thermoplastic elastomer of 20wt%, control reaction is added
Vessel temp is 145-150 DEG C until tackifying resin and styrene analog thermoplastic elastomer melting are complete;
Step 4: control reaction vessel temperature is 165-170 DEG C, and styrene analog thermoplastic elastomer, antioxidant, remaining is added
Tackifying resin and remaining styrene analog thermoplastic elastomer are reacted, reaction to styrene analog thermoplastic elastomer, thickening
Resin and styrene analog thermoplastic elastomer melting completely, form first product;
Step 5: stop stirring, after first product is stablized, discharging;
Step 6: filtering, cooling, packaging.
By using above-mentioned technical proposal, main component is divided into front and back and is added twice, and is added for the first time on a small quantity, the
Secondary investment main component component, using this kind of seedage feeding mode, first is that a small amount of component is first allowed to have in the reaction vessel
There is a space for being sufficiently mixed and reacting, and keep being heated evenly that consistency is higher as far as possible, so as to steady promotion each component
Between reaction, then put into second of reacting dose again, incremental participation reaction reacts complete between guarantee each component as far as possible
It is complete abundant.
The further setting of the present invention are as follows: the melting of tackifying resin and styrene analog thermoplastic elastomer in the step 3
Shi Changwei 15-18min, styrene analog thermoplastic elastomer, tackifying resin and styrene analog thermoplastic elastomer in the step 4
Melting when a length of 38-45min.
By using above-mentioned technical proposal, each component reaction sufficiently, and makes the finished product glue being prepared after interacting
Body does not have penetrating odor, and colorless and transparent, while softening point can reach 70-80 DEG C, the tool in subsequent be applied on substrate
There is good mobility, it is higher for the applicability of substrate, it can be a variety of substrates such as non-woven fabrics, PE film or PVC base, just
Qualified labeling is obtained in coated and molded.
The further setting of the present invention are as follows: antioxidant, tackifying resin and styrene analog thermoplastic bullet is being added in the step 3
Property body after vacuumized again full of nitrogen, styrene analog thermoplastic elastomer, tackifying resin and phenylethylene is being added in the step 4
It is vacuumized again after thermoplastic elastomer (TPE) full of nitrogen;The vacuumize process make in reaction vessel air pressure be -0.1~-
0.5Mpa。
By using above-mentioned technical proposal, directly vacuumizing can cause still to have in reaction vessel because vacuum degree is inadequate
Vapor residual.And nitrogen is first full of in reaction vessel, make the vapor of nitrogen discharge reaction vessel, then vacuumized.
Remaining in reaction vessel at this time is nitrogen.And nitrogen is inert gas, compared to for vapor for product substantially without shadow
It rings.
The further setting of the present invention are as follows: when discharging in the S5, discharge port is heated, keeps discharge port temperature
Degree is 155 DEG C -162 DEG C, is forced into 0.1-0.15MPa, and step 6 is filtered using 120 mesh screens.
By using above-mentioned technical proposal, heating is carried out to discharge port and guarantees that colloid products smoothly flow out, and sieve
Setting can also timely be filtered out to complete constituent monomers are had neither part nor lot in, and promote the total quality of finished product pressure sensitive adhesive.
In conclusion the invention has the following advantages: can either have certain adhesion strength to be easy in independence again
Packaging is removed in time when using, and is easy to use;The environment-protecting and non-poisonous colorless and odorless of component used simultaneously, receiving degree are higher.
Detailed description of the invention
Fig. 1 is the process flow chart of embodiment 1.
Specific embodiment
Embodiment 1-5, a kind of interlabial pad individual labeling glue, the component contained and its corresponding content are as shown in table 1,
Middle styrene analog thermoplastic elastomer selects SBS, and tackifying resin is to pass through hydrotreated C5/C9 Petropols, and softening agent is
Naphthenic oil, antioxidant are phenol antiager.
The melt index (MI) of styrene analog thermoplastic elastomer is 5g/min simultaneously.When preparation, as shown in Figure 1, according to following
Step preparation:
Step 1: according to the component of each group in embodiment 3, weighing styrene analog thermoplastic elastomer, tackifying resin, softening respectively
Agent, viscosity modifier and antioxidant;
Step 2: reaction kettle being heated to 135 DEG C, softening agent is added and is stirred heating;
Step 3: antioxidant, the tackifying resin of 20wt% and the styrene analog thermoplastic elastomer of 20wt%, control reaction is added
Kettle temperature degree is 145-150 DEG C until tackifying resin and styrene analog thermoplastic elastomer melt complete, tackifying resin and styrene
A length of 15min when the melting of analog thermoplastic elastomer;
Step 4: control temperature of reaction kettle is 165-170 DEG C, and viscosity modifier, antioxidant, remaining tackifying resin is added and remains
Remaining styrene analog thermoplastic elastomer is reacted, and reaction to styrene analog thermoplastic elastomer, tackifying resin melting are complete,
Form first product, styrene analog thermoplastic elastomer, tackifying resin melting when a length of 38min;
Step 5: stopping stirring, after first product is stablized, discharging when discharging, heats discharge port, keeps discharge port temperature
It is 155 DEG C -162 DEG C, is forced into 0.1-0.15MPa;
Step 6: using 120 mesh net filtrations, cooling, packaging.
And step 3 is full of nitrogen after all components such as antioxidant, tackifying resin and styrene analog thermoplastic elastomer are added
Gas vacuumizes again, and step 4 is taken out very after all components such as styrene analog thermoplastic elastomer, tackifying resin are added full of nitrogen again
It is empty;Vacuumize process makes air pressure in reaction vessel be maintained -0.1~-0.5Mpa twice.
Each component and its correspondence content table (g) in 1 embodiment 1-5 of table
Embodiment 6, a kind of interlabial pad individual labeling glue are with the difference for implementing 3, and following step is included when preparation
It is rapid:
Step 1: according to the component of each group in embodiment 3, weighing styrene analog thermoplastic elastomer, tackifying resin, softening respectively
Agent, viscosity modifier and antioxidant;
Step 2: reaction kettle being heated to 140 DEG C, softening agent is added and is stirred heating;
Step 3: antioxidant, the tackifying resin of 20wt% and the styrene analog thermoplastic elastomer of 20wt%, control reaction is added
Kettle temperature degree is 145-150 DEG C until tackifying resin and styrene analog thermoplastic elastomer melt complete, tackifying resin and styrene
A length of 18min when the melting of analog thermoplastic elastomer;
Step 4: control temperature of reaction kettle is 165-170 DEG C, and viscosity modifier, antioxidant, remaining tackifying resin is added and remains
Remaining styrene analog thermoplastic elastomer is reacted, and reaction to styrene analog thermoplastic elastomer, tackifying resin melting are complete,
Form first product, styrene analog thermoplastic elastomer, tackifying resin melting when a length of 45min;
Step 5: stopping stirring, after first product is stablized, discharging when discharging, heats discharge port, keeps discharge port temperature
It is 155 DEG C -162 DEG C, is forced into 0.1-0.15MPa;
Step 6: using 120 mesh net filtrations, cooling, packaging.
And step 3 is full of nitrogen after all components such as antioxidant, tackifying resin and styrene analog thermoplastic elastomer are added
Gas vacuumizes again, and step 4 is taken out very after all components such as styrene analog thermoplastic elastomer, tackifying resin are added full of nitrogen again
It is empty;Vacuumize process makes air pressure in reaction vessel be maintained -0.1~-0.5Mpa twice.
Embodiment 7, a kind of interlabial pad individual labeling glue are with the difference for implementing 3, further include 4-8 parts of weight
The viscosity modifier of number, viscosity modifier include paraffin and microwax, and the content ratio of paraffin and microwax is 1:1-2, and soft
Changing point is 90 DEG C.
By using above-mentioned technical proposal, wax essentially consists in the synthesis of two aspects for improving the property of hot-fusible pressure-sensitive adhesive
It influences, is on the one hand weaker boundary layer can be formed, to reduce the bonding of colloid since wax has lower surface tension
Intensity;On the other hand, the viscoplasticity of colloid can be improved in wax, to improve the adhesion strength of colloid.Since wax is elastomer
The expanding material of body and tackifying resin is introduced into hot-fusible pressure-sensitive adhesive and the compatibility of elastomer and tackifying resin can be improved,
It migrates the elastomer molecules being scattered in tackifying resin originally and tackifying resin molecule to elastomer phase, increases with viscoelastic
Volume fraction of the elastomer phase of property in entire adhesive causes the stripping of adhesive to improve the viscoplasticity of adhesive
It is improved from intensity, i.e., while meeting reduces label patch and the adhesion strength of substrate, also strengthens label patch and base
The peel strength of material is easy to use so that label patch and the adhesion strength of substrate be made to be in the range being suitble to.
Comparative example 1-4, a kind of interlabial pad individual labeling glue, the difference with embodiment 3 be containing component and
Its corresponding content is as shown in table 2, and wherein styrene analog thermoplastic elastomer selects SBS, and tackifying resin is by hydrogenation treatment
C5/C9 Petropols, softening agent is naphthenic oil, and antioxidant is phenol antiager.While styrene analog thermoplastic elastomer
Melt index (MI) is 5g/min.
Each component and its correspondence content table (g) in 2 comparative example 1-4 of table
Component | Comparative example 1 | Comparative example 2 | Comparative example 3 | Comparative example 4 |
Softening agent | 15 | 15 | 15 | 0 |
C5/C9 hydrogenated resin | 53 | 97 | 45 | 60 |
Antioxidant | 1.8 | 1.8 | 0 | 0 |
SBS | 52 | 0 | 52 | 52 |
Test portion
1) cohesive force is tested
Subjects: Example 1-5 and component in comparative example 1-4 or preparation method obtain specimen sample, amount to 9 groups.
Content carries out 180 ° of peel strength tests to the cloth after placing 6 hours in 7122-1996, and every group takes 5 experiments
As a result average value.Test method: taking the attachment substrate of same material (non-woven fabrics) and size (25mm*200mm), according to
GB/T
Test result: it measures cohesive force testing experiment result and is recorded into table 3.
3 cohesive force testing experiment result record sheet (N/mm) of table
Experimental group | Cohesive force | Experimental group | Cohesive force | Experimental group | Cohesive force |
Embodiment 1 | 11.3 | Embodiment 4 | 11.5 | Comparative example 2 | 12.1 |
Embodiment 2 | 11.5 | Embodiment 5 | 11.4 | Comparative example 3 | 11.5 |
Embodiment 3 | 11.7 | Comparative example 1 | 10.2 | Comparative example 4 | 10.1 |
2) inoxidizability is tested
Subjects: Example 1-5 and component in comparative example 1-4 or preparation method obtain specimen sample, amount to 9 groups.
Test method: taking the coating of 9 groups of subjects and (non-woven fabrics) on identical substrate, measures first day, second day, the
Five days and the tenth day cohesive forces.
Test result: using first day cohesive force as standard value x, cohesive force y that subsequent node measures and standard value x's
Difference is denoted as z, then by the change rate w=(z/x) * 100% of cohesive force, and cohesive force change rate is recorded into table 4.
4 cohesive force change rate record sheet (%) of table
Subjects | Second day | 5th day | Tenth day | Subjects | Second day | 5th day | Tenth day |
Embodiment 1 | 4.3 | 5.8 | 7.6 | Comparative example 1 | 4.5 | 6.1 | 7.8 |
Embodiment 2 | 4.4 | 5.3 | 6.8 | Comparative example 2 | 4.8 | 6.5 | 8.4 |
Embodiment 3 | 4.4 | 5.5 | 7.2 | Comparative example 3 | 4.3 | 5.2 | 6.5 |
Embodiment 4 | 4.3 | 5.2 | 6.7 | Comparative example 4 | 4.0 | 4.8 | 5.2 |
Embodiment 5 | 4.5 | 5.6 | 7.1 |
3) high-low temperature resistant is tested
Step 1: at room temperature at -10 DEG C, the glue of embodiment 2-4 and comparative example 1-4 are uniformly coated on to 7 pieces of areas respectively is
3cm*3cm and material be above the label of BOPP control glue with a thickness of 1mm, then take 7 pieces of lengths be respectively 5cm, 5cm,
1cm and material are polyacrylic plastic plate, and the label for being coated with glue pastes plastic sheet surface;
Step 2: 7 pieces of plastic plates for being pasted with label that step 1 is obtained are stored under -10 DEG C of environment to be taken out afterwards for 24 hours, observation mark
Whether label occur loosening or falling off;
Step 3: 7 pieces of plastic plates for being pasted with label that step 1 is obtained are stored under 60 DEG C of environment and take out afterwards for 24 hours, observation mark
Whether label occur loosening or falling off;
Step 4: being repeated 4 times step 1, step 2 and step 3, the number for loosening or falling off occurs in record label;
Step 5: at room temperature at 60 DEG C, the glue of embodiment 2-4 and comparative example 1-4 are uniformly coated on to 7 pieces of areas respectively is
3cm*3cm and material be above the label of BOPP control glue with a thickness of 1mm, then take 7 pieces of lengths be respectively 5cm, 5cm,
1cm and material are polyacrylic plastic plate, and the label for being coated with glue pastes plastic sheet surface;
Step 6: 7 pieces of plastic plates for being pasted with label that step 5 is obtained are stored under 60 DEG C of environment and take out afterwards for 24 hours, observation mark
Whether label occur loosening or falling off;
Step 7: 7 pieces of plastic plates for being pasted with label that step 5 is obtained are stored under -10 DEG C of environment to be taken out afterwards for 24 hours, observation mark
Whether label occur loosening or falling off;
Step 8: being repeated 4 times step 5, step 6 and step 7, record label the number for loosening or falling off occurs and is recorded in table 5
In.
5 high-low temperature resistant test data of table collects table
Illustrate: component manufacturer used is as shown in the table in above-described embodiment and comparative example.
Ingredient names | Production firm |
Softening agent | Nanjing Hong Han petrochemical industry Co., Ltd |
Tackifying resin | American exxon |
Antioxidant | German Yang Ying group |
Styrene analog thermoplastic elastomer | Japan goes out light |
Claims (8)
1. a kind of interlabial pad individual labeling glue, which is characterized in that the component including following parts by weight: phenylethylene heat
38-60 parts of thermoplastic elastic;30-45 parts of tackifying resin;10-15 parts of softening agent;1.5-2 parts of antioxidant.
2. interlabial pad individual labeling glue according to claim 1, it is characterised in that: the styrene analog thermoplastic
Elastomer is SBS, and the melt index (MI) of the styrene analog thermoplastic elastomer is less than 10g/10min.
3. interlabial pad individual labeling glue according to claim 1, it is characterised in that: the tackifying resin is to pass through
Hydrotreated C5/C9 Petropols.
4. interlabial pad individual labeling glue according to claim 1, it is characterised in that: the softening agent is cycloalkanes
Oil, the antioxidant are phenol antiager.
5. interlabial pad individual labeling glue according to claim 1, which is characterized in that be prepared into using following steps
It arrives:
Step 1: according to parts by weight, weighing 38-60 parts of styrene analog thermoplastic elastomer, 30-45 parts of tackifying resin, softening agent
10-15 parts, 1.5-2 parts of antioxidant;
Step 2: reaction vessel being heated to 135-140 DEG C, softening agent is added and is stirred heating;
Step 3: antioxidant, the tackifying resin of 20wt% and the styrene analog thermoplastic elastomer of 20wt% is added, control reaction is held
Device temperature is 145-150 DEG C until tackifying resin and styrene analog thermoplastic elastomer melting are complete;
Step 4: control reaction vessel temperature is 165-170 DEG C, and antioxidant, remaining tackifying resin and remaining styrene is added
Analog thermoplastic elastomer is reacted, and reaction to styrene analog thermoplastic elastomer, tackifying resin melting completely, form first product;
Step 5: stop stirring, after first product is stablized, discharging;
Step 6: filtering, cooling, packaging.
6. interlabial pad individual labeling glue according to claim 5, it is characterised in that: viscosify tree in the step 3
A length of 15-18min when the melting of rouge and styrene analog thermoplastic elastomer, styrene analog thermoplastic elastomer in the step 4,
A length of 38-45min when the melting of tackifying resin.
7. interlabial pad individual labeling glue according to claim 6, it is characterised in that: the step 3 is anti-in addition
It is vacuumized again after oxygen agent, tackifying resin and styrene analog thermoplastic elastomer full of nitrogen, phenylethylene is being added in the step 4
It is vacuumized again after thermoplastic elastomer (TPE), tackifying resin full of nitrogen;The vacuumize process make in reaction vessel air pressure be-
0.1~-0.5Mpa。
8. interlabial pad individual labeling glue according to claim 7, it is characterised in that: right when discharging in the S5
Discharge port is heated, and keeping discharge port temperature is 155 DEG C -162 DEG C, is forced into 0.1-0.15MPa, and step 6 uses 120
Mesh screen is filtered.