CN110408348A - A kind of electrician's route plastics pressure sensitive adhesive - Google Patents
A kind of electrician's route plastics pressure sensitive adhesive Download PDFInfo
- Publication number
- CN110408348A CN110408348A CN201810393628.0A CN201810393628A CN110408348A CN 110408348 A CN110408348 A CN 110408348A CN 201810393628 A CN201810393628 A CN 201810393628A CN 110408348 A CN110408348 A CN 110408348A
- Authority
- CN
- China
- Prior art keywords
- parts
- pressure sensitive
- sensitive adhesive
- antioxidant
- electrician
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of electrician's route plastics pressure sensitive adhesive, each component including following parts by weight are prepared: 80-160 parts of natural rubber, 50-100 parts of butadiene-styrene rubber, 20-60 parts of terpene resin, 10-18 parts of antioxidant D, 5-16 parts of rosin ester, 8-19 parts of glycerol, gasoline -5-16 parts of toluene Mixed Solvent, 5-15 parts of plasticizer, 5-9 parts of antioxidant.Pressure sensitive adhesive produced by the present invention has the characteristics that high solids content, peel resistance are strong, water resistance is strong, and coating speed is fast, coating temperature is low and coating efficiency is high when use；Gained pressure sensitive adhesive of the invention has excellent viscosity and duration, while convenient for removing, integrality is good after removing, and uvioresistant effect is good.
Description
Technical field
The present invention relates to a kind of component of pressure sensitive adhesive, specifically a kind of electrician's route plastics pressure sensitive adhesive belongs to pressure sensitive adhesive
Technical field.
Background technique
The abbreviation of pressure sensitive adhesive pressure sensitive adhesive pressure-sensitive adhesive.Be it is a kind of have have to pressure
The adhesive of sensibility.Mainly for the preparation of pressure sensitive adhesive tape.(adhesive tape glues the peeling force of general pressure sensitive adhesive with by maxxaedium pressurization
The peeling force showed after patch) < adhesive cohesive force (active force between pressure-sensitive xanthan molecule) < adhesive base adhesion force (glue
Adhesive force between stick and substrate).
Hot-fusible pressure-sensitive adhesive is very widely used at home, thermotropic pressure sensitive glue relatively before solution and emulsion pressure-sensitive,
Thermotropic pressure sensitive glue is solvent-free, is more advantageous to environmental protection and safety in production, high production efficiency, production cost is relatively low, so at present
The positive Devoting Major Efforts To Developing thermotropic pressure sensitive glue in countries in the world.The resin binder of current thermotropic pressure sensitive glue be mainly SIS, SBS,
These four thermoplastic elastomer (TPE)s of SEBS, SEPS.The thermotropic pressure sensitive glue of these four base-materials is since molecule polarity itself is small, only
It is relatively good to the lesser material caking property of some polarity, bonding well, which cannot be played, in the big Material Field of many polarity makees
With.
Come this year to pursue environment-friendly materials due to people, protection environmental consciousness improves, pollution-free, environmentally friendly, preparation process letter
It is singly rapidly developed and is widely used in people's lives, such as adhesive tape, label, medical pressure sensitive adhesive and aluminium alloy door's door and window
Factory protection etc..However, water soluble acrylic acid pressure sensitive adhesive solid content in the market is low, peeling force is in 800 grams or less, poor water resistance etc.
Defect restricts always its application.
Summary of the invention
The purpose of the present invention is in view of the above shortcomings of the prior art, providing a kind of electrician's route plastics pressure sensitive adhesive, this
Inventing pressure sensitive adhesive obtained has the characteristics that high solids content, peel resistance are strong, water resistance is strong, and coating speed is fast, is coated with when use
Temperature is low and coating efficiency is high；Gained pressure sensitive adhesive of the invention has excellent viscosity and duration, while convenient for removing, stripping
It is good from rear integrality.
Technical scheme is as follows: a kind of electrician's route plastics pressure sensitive adhesive, characterized in that including following parts by weight
Each component be prepared: 80-160 parts of natural rubber, 50-100 parts of butadiene-styrene rubber, 20-60 parts of terpene resin, antioxidant D 10-
18 parts, 5-16 parts of rosin ester, 8-19 parts of glycerol, gasoline -5-16 parts of toluene Mixed Solvent, 5-15 parts of plasticizer, antioxidant 5-9
Part.
The plasticizer is the one or two of dibutyl phthalate, lanolin, naphthenic oil and atoleine.
The antioxidant is antioxidant 1010 or 2,6 one di-tert-butyl p-cresol.
Pressure sensitive adhesive provided by the invention has excellent properties, has excellent viscosity and duration, while just
Integrality is good after removing, removing；Pressure sensitive adhesive service performance demand is met, and improves the water resistance of pressure sensitive adhesive, is solved
It has determined caducous phenomenon.
Pressure sensitive adhesive produced by the present invention has the characteristics that high solids content, peel resistance are strong, water resistance is strong, coating speed when use
Degree is fast, coating temperature is low and coating efficiency is high；Gained pressure sensitive adhesive of the invention has excellent viscosity and duration, while just
Integrality is good after removing, removing, and uvioresistant effect is good.
Specific embodiment
Embodiment 1
A kind of electrician's route plastics pressure sensitive adhesive, characterized in that each component including following parts by weight is prepared: natural rubber
80-160 parts, 50-100 parts of butadiene-styrene rubber, 20-60 parts of terpene resin, 10-18 parts of antioxidant D, 5-16 parts of rosin ester, glycerol 8-
19 parts, gasoline -5-16 parts of toluene Mixed Solvent, 5-15 parts of plasticizer, 5-9 parts of antioxidant.
The plasticizer is the one or two of dibutyl phthalate, lanolin, naphthenic oil and atoleine.
The antioxidant is antioxidant 1010 or 2,6 one di-tert-butyl p-cresol.
Embodiment 2
A kind of electrician's route plastics pressure sensitive adhesive, characterized in that each component including following parts by weight is prepared: natural rubber
80 parts, 50 parts of butadiene-styrene rubber, 20 parts of terpene resin, 10 parts of antioxidant D, 5 parts of rosin ester, 8 parts of glycerol, the mixing of gasoline-toluene it is molten
5 parts of agent, 5 parts of plasticizer, 5 parts of antioxidant.
The plasticizer is the one or two of dibutyl phthalate, lanolin, naphthenic oil and atoleine.
The antioxidant is antioxidant 1010 or 2,6 one di-tert-butyl p-cresol.
Embodiment 3
A kind of electrician's route plastics pressure sensitive adhesive, characterized in that each component including following parts by weight is prepared: natural rubber
160 parts, 100 parts of butadiene-styrene rubber, 60 parts of terpene resin, 18 parts of antioxidant D, 16 parts of rosin ester, 19 parts of glycerol, gasoline-toluene it is mixed
16 parts of bonding solvent, 15 parts of plasticizer, 9 parts of antioxidant.
The plasticizer is the one or two of dibutyl phthalate, lanolin, naphthenic oil and atoleine.
The antioxidant is antioxidant 1010 or 2,6 one di-tert-butyl p-cresol.
Claims (3)
1. a kind of electrician's route plastics pressure sensitive adhesive, characterized in that each component including following parts by weight is prepared: natural rubber
80-160 parts of glue, 50-100 parts of butadiene-styrene rubber, 20-60 parts of terpene resin, 10-18 parts of antioxidant D, 5-16 parts of rosin ester, glycerol
8-19 parts, gasoline -5-16 parts of toluene Mixed Solvent, 5-15 parts of plasticizer, 5-9 parts of antioxidant.
2. a kind of electrician's route plastics pressure sensitive adhesive according to claim 1, characterized in that the plasticizer is adjacent benzene two
The one or two of formic acid dibutyl ester, lanolin, naphthenic oil and atoleine.
3. a kind of electrician's route plastics pressure sensitive adhesive according to claim 1, characterized in that the antioxidant is antioxidant
1010 or 2,6 one di-tert-butyl p-cresol.