CN110403347A - A kind of wear-resisting environmental sanitation brush brush filament and its production method - Google Patents
A kind of wear-resisting environmental sanitation brush brush filament and its production method Download PDFInfo
- Publication number
- CN110403347A CN110403347A CN201910570160.2A CN201910570160A CN110403347A CN 110403347 A CN110403347 A CN 110403347A CN 201910570160 A CN201910570160 A CN 201910570160A CN 110403347 A CN110403347 A CN 110403347A
- Authority
- CN
- China
- Prior art keywords
- parts
- brush
- brush filament
- wear
- environmental sanitation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wear-resisting environmental sanitation brush brush filaments and its production method, including stainless steel wire, wrapping layer and wearing layer, the raw material of the following components by weight percent of wrapping layer: polymethyl methacrylate, high density polyethylene (HDPE), silicon oxide powder, carbon black, polysulfones, liquid crystal polymer, high-tenacity polyethylene fibre, Fypro, silicon carbide fibre, sticky agent.The present invention increases stainless steel wire on the basis of brush filament, increase the intensity of whole device, and abrasive rubber grain is also bonded in the outer surface of brush filament, further increase the wear-resisting property of brush filament, and in the material of brush filament ontology, polymethyl methacrylate, high density polyethylene (HDPE), silicon oxide powder, carbon black belongs to high-wearing feature substance, considerably increase the wear-resisting property of brush filament, conducive to the service life for promoting brush filament, polysulfones and liquid crystal polymer then promote the acid resistance of brush filament, avoid corrosion of the acidic materials to brush filament, rosin milk is then further such that the viscosity of brush filament raw material in production increases.
Description
Technical field
The present invention relates to the production related fields of environmental sanitation brush, specially a kind of wear-resisting environmental sanitation brush brush filament and its producer
Method.
Background technique
It is more more and more intense with people's environmental consciousness, The Surroundings in Cities health also increasingly by the attention of relevant departments,
Environmental sanitation cleaning needs to use sanitation cart, and main body cleaning structure is environmental sanitation brush, and environmental sanitation brush is on the PP disk of well cutting at one
Determine angular hole-boring, then with the flat wire or PP brush filament cut, go here and there after nylon yarn doubling insert made of brush.Environmental sanitation brush is generally seated in
Municipal sanitation truck is that most representative environmental sanitation brush is a kind of in the disc brush or steel wire class disc brush to clean Streets.Product has
Sweeper round brush, tabletting type roller combination sweep brush, roller type sweeping machine hairbrush, sweeper hairbrush, square sweep squeegee, circle branch is swept
Squeegee, sewage treatment hairbrush, floor-cleaning machine hairbrush, computer car washer hairbrush etc..
The brush filament of environmental sanitation brush belongs to the main structure of environmental sanitation brush, needs to contact road to realize and clean, if its wear-resisting property
Difference, then will affect the practical function of environmental sanitation brush, also will affect its service life, and then bring great inconvenience to environmental sanitation work,
In addition, the intensity and acid resistance of brush filament also influence its service life, so, it is badly in need of making a kind of wear-resisting environmental sanitation brush brush
Silk.
Summary of the invention
The purpose of the present invention is to provide a kind of wear-resisting environmental sanitation brush brush filaments and its production method, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the invention provides the following technical scheme:
A kind of wear-resisting environmental sanitation brush brush filament, including stainless steel wire, wrapping layer and wearing layer, the following components by weight percent of wrapping layer
Raw material: 10-20 parts of polymethyl methacrylate, 25-35 parts of high density polyethylene (HDPE), 3-7 parts of silicon oxide powder, 6-12 parts of carbon black,
3-7 parts of polysulfones, 6-11 parts of liquid crystal polymer, 3-5 parts of high-tenacity polyethylene fibre, 3-5 parts of Fypro, silicon carbide fibre 1-3
Part, 5-9 parts of sticky agent.
Preferably, the volume ratio of stainless steel wire, wrapping layer and abrasive rubber grain is 2:5:1.
Preferably, the raw material of the following components by weight percent of wrapping layer: 15 parts of polymethyl methacrylate, high density polyethylene (HDPE) 30
Part, 5 parts of silicon oxide powder, 9 parts of carbon black, 5 parts of polysulfones, 8.5 parts of liquid crystal polymer, 4 parts of high-tenacity polyethylene fibre, Fypro
4 parts, 2 parts of silicon carbide fibre, 7 parts of sticky agent.
Preferably, sticky agent is rosin milk.
A kind of production method of wear-resisting environmental sanitation brush brush filament, including following production method:
The production of wrapping layer: prepare polymethyl methacrylate, high density polyethylene (HDPE), silica according to above-mentioned parts by weight
Powder, carbon black, polysulfones, liquid crystal polymer, high-tenacity polyethylene fibre, Fypro, silicon carbide fibre and sticky agent, will be above-mentioned
Substance is once added in mixing device, and heating is uniformly mixed after a certain period of time, and mixture is carried out the to wire drawing machine everywhere while hot
Wire drawing;
The installation of steel wire: it for above-mentioned just wire drawing of molding first time, draws in stainless steel wire to first time wire drawing
Portion, then the first time wire drawing for being equipped with stainless steel wire is subjected to wire drawing again, wire drawing to defined size, to its cooling;
The bonding of rubber granule: abrasive rubber grain is placed in flush coater, is cooperated strong bonding agent, is uniformly sprayed in brush filament
Outer surface, formed wearing layer, whole device form brush filament main body;
Quality inspection storage: specification cutting is carried out to above-mentioned brush filament main body, its quality is detected after cutting, after detection passes through
It is mounted on PP disk, is stored being put in storage after finished product packing, waiting is sold.
Preferably, in the step of production of wrapping layer, heating temperature is 200-300 DEG C, mixing time 40-60min.
Preferably, in the step of installation of steel wire, cooling temperature be 2-10 DEG C, cooling time 3-5h.
Compared with prior art, the beneficial effects of the present invention are:
The present invention increases stainless steel wire on the basis of brush filament, increases the intensity of whole device, and in the appearance of brush filament
Face also bonds abrasive rubber grain, further increases the wear-resisting property of brush filament, and in the material of brush filament ontology, poly-methyl methacrylate
Ester, high density polyethylene (HDPE), silicon oxide powder, carbon black belong to high-wearing feature substance, considerably increase the wear-resisting property of brush filament, benefit
In the service life for promoting brush filament, polysulfones and liquid crystal polymer then promote the acid resistance of brush filament, avoid acidic materials to brush filament
Corrosion, and high-tenacity polyethylene fibre, Fypro and silicon carbide fibre then further increase the toughness of brush filament, rosin milk
Then further such that the viscosity of brush filament raw material in production increases, it is conducive to integrally formed.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment one
The present invention provides one kind wear-resisting environmental sanitation brush brush filament, including stainless steel wire, wrapping layer and wearing layer, wrapping layer are as follows
The raw material of components by weight percent: 10-20 parts of polymethyl methacrylate, 25-35 parts of high density polyethylene (HDPE), 3-7 parts of silicon oxide powder, charcoal
6-12 parts black, 3-7 parts of polysulfones, 6-11 parts of liquid crystal polymer, 3-5 parts of high-tenacity polyethylene fibre, 3-5 parts of Fypro, carbonization
1-3 parts of silica fibre, 5-9 parts of sticky agent.
In the above-described embodiments, the volume ratio of stainless steel wire, wrapping layer and abrasive rubber grain is 2:5:1.
In the above-described embodiments, the raw material of the following components by weight percent of wrapping layer: 10 parts of polymethyl methacrylate, high density are poly-
25 parts of ethylene, 3 parts of silicon oxide powder, 6 parts of carbon black, 3 parts of polysulfones, 6 parts of liquid crystal polymer, 3 parts of high-tenacity polyethylene fibre, polyamide
3 parts of fiber, 1 part of silicon carbide fibre, 5 parts of sticky agent.
In the above-described embodiments, sticky agent is rosin milk.
Embodiment two
The present invention provides one kind wear-resisting environmental sanitation brush brush filament, including stainless steel wire, wrapping layer and wearing layer, wrapping layer are as follows
The raw material of components by weight percent: 10-20 parts of polymethyl methacrylate, 25-35 parts of high density polyethylene (HDPE), 3-7 parts of silicon oxide powder, charcoal
6-12 parts black, 3-7 parts of polysulfones, 6-11 parts of liquid crystal polymer, 3-5 parts of high-tenacity polyethylene fibre, 3-5 parts of Fypro, carbonization
1-3 parts of silica fibre, 5-9 parts of sticky agent.
In the above-described embodiments, the volume ratio of stainless steel wire, wrapping layer and abrasive rubber grain is 2:5:1.
In the above-described embodiments, the raw material of the following components by weight percent of wrapping layer: 20 parts of polymethyl methacrylate, high density are poly-
35 parts of ethylene, 7 parts of silicon oxide powder, 12 parts of carbon black, 7 parts of polysulfones, 11 parts of liquid crystal polymer, 5 parts of high-tenacity polyethylene fibre, polyamides
5 parts of amine fiber, 3 parts of silicon carbide fibre, 9 parts of sticky agent.
In the above-described embodiments, sticky agent is rosin milk.
Embodiment three
The present invention provides one kind wear-resisting environmental sanitation brush brush filament, including stainless steel wire, wrapping layer and wearing layer, wrapping layer are as follows
The raw material of components by weight percent: 10-20 parts of polymethyl methacrylate, 25-35 parts of high density polyethylene (HDPE), 3-7 parts of silicon oxide powder, charcoal
6-12 parts black, 3-7 parts of polysulfones, 6-11 parts of liquid crystal polymer, 3-5 parts of high-tenacity polyethylene fibre, 3-5 parts of Fypro, carbonization
1-3 parts of silica fibre, 5-9 parts of sticky agent.
In the above-described embodiments, the volume ratio of stainless steel wire, wrapping layer and abrasive rubber grain is 2:5:1.
In the above-described embodiments, the raw material of the following components by weight percent of wrapping layer: 15 parts of polymethyl methacrylate, high density are poly-
30 parts of ethylene, 5 parts of silicon oxide powder, 9 parts of carbon black, 5 parts of polysulfones, 8.5 parts of liquid crystal polymer, 4 parts of high-tenacity polyethylene fibre, polyamides
4 parts of amine fiber, 2 parts of silicon carbide fibre, 7 parts of sticky agent.
In the above-described embodiments, sticky agent is rosin milk.
Principle steps, including following production method:
The production of wrapping layer: prepare polymethyl methacrylate, high density polyethylene (HDPE), silica according to above-mentioned parts by weight
Powder, carbon black, polysulfones, liquid crystal polymer, high-tenacity polyethylene fibre, Fypro, silicon carbide fibre and sticky agent, will be above-mentioned
Substance is once added in mixing device, and heating is uniformly mixed after a certain period of time, and mixture is carried out the to wire drawing machine everywhere while hot
Wire drawing;
The installation of steel wire: it for above-mentioned just wire drawing of molding first time, draws in stainless steel wire to first time wire drawing
Portion, then the first time wire drawing for being equipped with stainless steel wire is subjected to wire drawing again, wire drawing to defined size, to its cooling;
The bonding of rubber granule: abrasive rubber grain is placed in flush coater, is cooperated strong bonding agent, is uniformly sprayed in brush filament
Outer surface, formed wearing layer, whole device form brush filament main body;
Quality inspection storage: specification cutting is carried out to above-mentioned brush filament main body, its quality is detected after cutting, after detection passes through
It is mounted on PP disk, is stored being put in storage after finished product packing, waiting is sold.
Further, in the step of production of wrapping layer, heating temperature is 200-300 DEG C, mixing time 40-60min.
Further, in the step of installation of steel wire, cooling temperature be 2-10 DEG C, cooling time 3-5h.
The present invention increases stainless steel wire on the basis of brush filament, increases the intensity of whole device, and in the appearance of brush filament
Face also bonds abrasive rubber grain, further increases the wear-resisting property of brush filament, and in the material of brush filament ontology, poly-methyl methacrylate
Ester, high density polyethylene (HDPE), silicon oxide powder, carbon black belong to high-wearing feature substance, considerably increase the wear-resisting property of brush filament, benefit
In the service life for promoting brush filament, polysulfones and liquid crystal polymer then promote the acid resistance of brush filament, avoid acidic materials to brush filament
Corrosion, and high-tenacity polyethylene fibre, Fypro and silicon carbide fibre then further increase the toughness of brush filament, rosin milk
Then further such that the viscosity of brush filament raw material in production increases, it is conducive to integrally formed.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of wear-resisting environmental sanitation brush brush filament, it is characterised in that: including stainless steel wire, wrapping layer and wearing layer, wrapping layer is as follows
The raw material of components by weight percent: 10-20 parts of polymethyl methacrylate, 25-35 parts of high density polyethylene (HDPE), 3-7 parts of silicon oxide powder, charcoal
6-12 parts black, 3-7 parts of polysulfones, 6-11 parts of liquid crystal polymer, 3-5 parts of high-tenacity polyethylene fibre, 3-5 parts of Fypro, carbonization
1-3 parts of silica fibre, 5-9 parts of sticky agent.
2. the wear-resisting environmental sanitation brush brush filament of one kind according to claim 1, it is characterised in that: stainless steel wire, wrapping layer and resistance to
The volume ratio of rubber milling grain is 2:5:1.
3. the wear-resisting environmental sanitation brush brush filament of one kind according to claim 1, it is characterised in that: the following components by weight percent of wrapping layer
Raw material: 15 parts of polymethyl methacrylate, 30 parts of high density polyethylene (HDPE), 5 parts of silicon oxide powder, 9 parts of carbon black, 5 parts of polysulfones, liquid crystal
8.5 parts of polymer, 4 parts of high-tenacity polyethylene fibre, 4 parts of Fypro, 2 parts of silicon carbide fibre, 7 parts of sticky agent.
4. the wear-resisting environmental sanitation brush brush filament of one kind according to claim 1, it is characterised in that: sticky agent is rosin milk.
5. the production method of the wear-resisting environmental sanitation brush brush filament of one kind according to claim 1 to 4, it is characterised in that: including
Following production method:
The production of wrapping layer: prepare polymethyl methacrylate, high density polyethylene (HDPE), silica powder according to above-mentioned parts by weight
End, carbon black, polysulfones, liquid crystal polymer, high-tenacity polyethylene fibre, Fypro, silicon carbide fibre and sticky agent, by above-mentioned object
Matter is once added in mixing device, and heating is uniformly mixed after a certain period of time, and mixture is carried out first to wire drawing machine everywhere while hot
Secondary wire drawing;
The installation of steel wire: for above-mentioned just wire drawing of molding first time, drawing stainless steel wire to the inside of first time wire drawing, then
The first time wire drawing for being equipped with stainless steel wire is subjected to wire drawing again, wire drawing to defined size, to its cooling;
The bonding of rubber granule: abrasive rubber grain is placed in flush coater, cooperates strong bonding agent, is uniformly sprayed in the outer of brush filament
Surface, forms wearing layer, and whole device forms brush filament main body;
Quality inspection storage: carrying out specification cutting to above-mentioned brush filament main body, detect after cutting to its quality, detects it after passing through
It on installation to PP disk, is stored being put in storage after finished product packing, waiting is sold.
6. the production method of the wear-resisting environmental sanitation brush brush filament of one kind according to claim 5, it is characterised in that: the system of wrapping layer
In the step of making, heating temperature is 200-300 DEG C, mixing time 40-60min.
7. the production method of the wear-resisting environmental sanitation brush brush filament of one kind according to claim 5, it is characterised in that: the installation of steel wire
The step of in, cooling temperature be 2-10 DEG C, cooling time 3-5h.