CN1103880A - Color coating paste for building decoration - Google Patents
Color coating paste for building decoration Download PDFInfo
- Publication number
- CN1103880A CN1103880A CN 93115415 CN93115415A CN1103880A CN 1103880 A CN1103880 A CN 1103880A CN 93115415 CN93115415 CN 93115415 CN 93115415 A CN93115415 A CN 93115415A CN 1103880 A CN1103880 A CN 1103880A
- Authority
- CN
- China
- Prior art keywords
- paste
- weight part
- building decoration
- color coating
- coating paste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention provides a colour building decoration paste which contains benzene-propane emulsion, compound polyvinyl alcohol solution, 831 cellulose, silica gel, doublle superphosphate, and multifunctional powder as well as plasticizer, film-forming aid, activated double superphosphate and organic silicon emulsion. It has no toxin, no peculiar smell, no radioactivity, high adhesion, pollution-resistance, light-resistance, scrubbing-resistance. It is smooth and fine after film-forming, hgih in hardness, low cost, simple process and long service life.
Description
What the present invention relates to is a kind of decorating paste, particularly be a kind of coating paste for building decoration that the building inside and outside wall face is decorated that is used for.
Coating development both at home and abroad at present is very fast, and developing direction has been tending towards water-soluble and no dissolubility two big classes.The characteristics of these two big classes are nontoxic, nuisanceless, and water-soluble class is with the welcome that is subjected to the user with low cost.Water-soluble class coating at home the usage quantity maximum be that polyvinyl alcohol water glass is coating and coating on this basis.Low but the poor water resistance of polyvinyl alcohol coating valency.Next is quality polyester acid preferably ethene, benzene-acrylic emulsion, B-propyl emulsion coating.This its advantage of class coating is that price is low, is easy to construction, thus still have market preferably, but this class coating impression is coarse, scrubbing resistance number of times undesirable (in 1000 times).The emulsion paint water tolerance is better but cost is higher.
In view of above reason, the objective of the invention is for a kind of nontoxic, "dead" element is provided, cohesive force is strong, fast light, weathering resistance is good, scrubbing resistance, smooth surface exquisiteness, color and luster is various, uses few, the cheap color coating paste for building decoration of heat energy.
Benzene-acrylic emulsion is arranged among the present invention, the composite polyethylene alcoholic solution, 831 Mierocrystalline celluloses, silicon sol, coarse whiting, the multipotency powder, benzene-acrylic emulsion is by vinylbenzene and acrylic ester monomer, emulsifying agent, initiator forms by emulsion polymerization, has the high-light-fastness of esters of acrylic acid, weathering resistance, non-yellowing properties also has good alkaline-resisting, water-fast, wet scrub resistance, also has the outward appearance exquisiteness, beautiful in colour, texture is good, with characteristics such as cement material sticking power are good, but easily be clamminess in this acrylic ester monomer conjunctiva rear surface, softer, in order to solve this shortcoming, so added an amount of silicon sol, silicon sol is a colloid silica, it is filmed and is difficult for producing static, is difficult for the absorption dust, and stain resistance is good, it is strong to basic unit's penetrating power to film, and tack is good; Coarse whiting belongs to natural crystal, "dead" element, and super quality and competitive price, look pure white, adds a large amount of coarse whitings in decorating paste of the present invention, greatly reduces cost; In decorating paste of the present invention, add inexpensive 831 Mierocrystalline celluloses and composite polyethylene alcoholic solution and can solve the problem of base-material (binding agent) thickening; Add the multipotency powder, can solve water-fast, erasibility after the decorating paste film forming of the present invention, can in decorating paste, add color dye as required, can allot versicolor polychromy cream.
Also have 0.05～0.1(weight part in the above-mentioned decorating paste) plasticising cream, make plasticity-of the present invention big, plasticising cream can adopt the o-2 potassium acid dibutylester.
Also have 0.15～0.3(weight part in the above-mentioned decorating paste) film coalescence aid, help the formation of filming, can adopt phenylcarbinol to make the film forming auxiliary agent.
Also have 0.1～0.5(weight part in the above-mentioned decorating paste) neutralizing agent, can adjust ph value of emulsion to 7, can adopt ammoniacal liquor to make neutralizing agent.
Also have dispersion agent, defoamer in the above-mentioned decorating paste, frostproofer or sanitas, mould inhibitor, its component (weight part) is:
Dispersion agent 0.001～0.003
Defoamer 0.001～0.003
Frostproofer 0.001～0.003
Sanitas 0.001～0.003
Mould inhibitor 0.001～0.003
Can add dispersion agent when in building cream, adding pigment, defoamer, can adopt Sodium hexametaphosphate 99 to make dispersion agent, the phosphoric acid dibutylester is made defoamer, add sanitas or mould inhibitor, be applicable to the summer of humidity, sweltering heat, add the winter of the suitable cold of frostproofer, can adopt propylene glycol to do frostproofer and furthermore flow agent effect, adopt not only sterilization but also anticorrosion of fungicidal preservative BTG.
Also have wollastonite powder, talcum powder in the above-mentioned decorating paste, guarantee the decorating paste quality, be easy to construction.
Contain polyvinyl alcohol in the above-mentioned composite polyethylene alcoholic solution, oxalic dialdehyde, phosphoric acid, water, its component (weight part) is:
Polyvinyl alcohol 1～1.5
Ethylene glycol 0.5～1
Phosphoric acid 0.001～0.002
Water 100～120
Activate coarse whiting in the above-mentioned decorating paste in addition, the weight part of activation coarse whiting and the weight part ratio of coarse whiting are: 5: 100
Also have 1～1.8(weight part in the above-mentioned decorating paste) organic silicon emulsion, add an amount of water in the organic silicon emulsion, its weight part ratio is: organic silicon emulsion: water=1: (5～15) make decorate properties better.
The weight part ratio of added pigment and decorating paste is in the above-mentioned decorating paste: pigment: decorating paste=(0.02～0.05): 100.
Base-material of the present invention belongs to the compound base-material of emulsion-type, water-soluble type, the advantage of performance emulsion-type, water-soluble type and overcome mutual weakness.Given this, the present invention compares with existing coating, has following advantage:
1, nontoxic, the no three wastes, "dead", safety;
2, weathering resistance, photostabilization is strong;
3, drying and watering cycle, good air permeability;
4, surface hardness height, smooth exquisiteness (light such as glass surface);
5, construction adaptability is strong, integrates bottoming, facing, can construct in undried substrate, reduces construction cost, improves work efficiency;
6, starting material sources is abundant, inexpensively easily purchases;
7, to produce, construction technology is simple, required equipment is easily made;
8, decorative cover is effective, and color and luster is abundant, can reach kind more than 100;
9, applied widely, can do interior wall, decoration of exterior wall use.
Introduce embodiments of the invention (referring to table 1) below, but protection scope of the present invention is not limited only to the following examples:
Sanitas, mould inhibitor or frostproofer or dispersion agent, defoamer, neutralizing agent can add as required.
During preparation composite polyethylene alcoholic solution, in preparing device, add gauge water, when water temperature rises to 70 ℃, the polyvinyl alcohol micelle (1799) of adding 1% is down stirred in start, be warming up to 92 ℃ of continuation stirrings and got final product in 30 minutes, treat to add when solution is reduced to room temperature quantitative phosphoric acid, stirred 10 minutes, add quantitative oxalic dialdehyde again and stirred 5 minutes, filter standby.
In pigment: color coating paste for building decoration=(0.02～0.5): the ratio 100(weight part) adds required pigment as required and promptly gets required decorating paste in decorating paste.
Claims (10)
1, a kind of color coating paste for building decoration that contains benzene-acrylic emulsion is characterized in that also having the composite polyethylene alcoholic solution in the described decorating paste, 831 Mierocrystalline celluloses, and silicon sol, coarse whiting, the multipotency powder, its component (weight part) is:
Benzene-acrylic emulsion 10～20
Composite polyethylene alcoholic solution 100～120
831 Mierocrystalline celluloses 5～8
Silicon sol 3～4
Coarse whiting 240～300
Multipotency powder 5～8.
2, color coating paste for building decoration as claimed in claim 1 is characterized in that in the described decorating paste also having 0.05～0.1(weight part) softening agent.
3, color coating paste for building decoration as claimed in claim 1 is characterized in that in the described decorating paste also having 0.15～0.3(weight part) film coalescence aid.
4, color coating paste for building decoration as claimed in claim 1 is characterized in that in the described decorating paste also having 0.1～0.5(weight part) neutralizing agent.
5, color coating paste for building decoration as claimed in claim 1 is characterized in that also having dispersion agent in the described decorating paste, defoamer, frostproofer or sanitas, mould inhibitor, and its component (weight part) is:
Dispersion agent 0.001～0.003
Defoamer 0.001～0.003
Frostproofer 0.001～0.003
Sanitas 0.001～0.003
Mould inhibitor 0.001～0.003
6, color coating paste for building decoration as claimed in claim 1 is characterized in that also having wollastonite powder, talcum powder in the described decorating paste, and its component (weight part) is:
Wollastonite powder 0～6
Talcum powder 3～8
7, color coating paste for building decoration as claimed in claim 1, it is characterized in that containing in the described composite polyethylene alcoholic solution polyvinyl alcohol, oxalic dialdehyde, phosphoric acid, water, its component (weight part) is:
Polyvinyl alcohol 1～1.5
Oxalic dialdehyde 0.5～1
Phosphoric acid 0.001～0.002
Water 100～120
8, color coating paste for building decoration as claimed in claim 1 is characterized in that activating in addition in the described decorating paste coarse whiting, activation coarse whiting (weight part): coarse whiting (weight part)=5: 100.
9, color coating paste for building decoration as claimed in claim 1 is characterized in that also having 1～1.8(weight part in the described decorating paste) organic silicon emulsion, add an amount of water in the organic silicon emulsion, its weight part ratio is: organic silicon emulsion: water=1: (5～15).
10, color coating paste for building decoration as claimed in claim 1 is characterized in that the weight part ratio of added pigment and decorating paste is in the described decorating paste: pigment: decorating paste=(0.02～0.05): 100.