CN110376862A - Fixing roller and preparation method thereof - Google Patents
Fixing roller and preparation method thereof Download PDFInfo
- Publication number
- CN110376862A CN110376862A CN201910640358.3A CN201910640358A CN110376862A CN 110376862 A CN110376862 A CN 110376862A CN 201910640358 A CN201910640358 A CN 201910640358A CN 110376862 A CN110376862 A CN 110376862A
- Authority
- CN
- China
- Prior art keywords
- roller
- heat
- priming coat
- preparation
- peripheral surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of fixing rollers and preparation method thereof.Wherein, the preparation method of fixing roller includes the following steps: that fluororesin-coated material forms priming coat on the substrate roller on the outer peripheral surface of substrate roller;Heat-shrinkable pipe is coated to the outer peripheral surface of the priming coat of the substrate roller;And the stage heating treatment of substrate roller to heat-shrinkable pipe and the priming coat is coated with, when the outer peripheral surface of the inner peripheral surface and the priming coat that are warming up to the heat-shrinkable pipe melts, cooling processing is to get fixing roller.Compared to the technique that traditional face applies, fixing roller preparation of the invention is to prepare fixing roller in such a way that thermoplastic pipe coats substrate roller, and preparation method is simple, and avoids the use of pollution chemical coating during conventional face applies, energy conservation and environmental protection.
Description
Technical field
The present invention relates to Field of Office Automation, more particularly to a kind of fixing roller and preparation method thereof.
Background technique
Fixing is the process unstable on copy paper, delible toner image fixation.Fixing process is duplicator, passes
One of important procedure of the imaging devices such as prototype, printer imaging, and the quality of fixing roller quality will have a direct impact on fixing
Effect.
The preparation method of traditional fixing roller is mostly that primary coat-face applies technique: spraying basecoat material on substrate roller and forms bottom
Coating, high temperature sintering, grinding, is cleaned, is pressed light, cleaning to obtain fixing roller again at face painting.The preparation method of traditional fixing roller is numerous
It is trivial, and the poor image quality that fixing roller obtained is formed in subsequent fixing.
Summary of the invention
Based on this, for the cumbersome problem of the preparation method of traditional fixing roller, a kind of preparation method is provided and is simply fixed
The preparation method and fixing roller of roller.
A kind of preparation method of fixing roller comprising following steps:
Fluororesin-coated material forms priming coat on the substrate roller on the outer peripheral surface of substrate roller;
Heat-shrinkable pipe is coated to the outer peripheral surface of the priming coat of the substrate roller;And
The stage heating treatment of substrate roller to heat-shrinkable pipe and the priming coat is coated with, is warming up to the heat
When the outer peripheral surface of the inner peripheral surface of contraction pipe and the priming coat melts, cooling processing is to get fixing roller.
The preparation method of above-mentioned fixing roller is simple, specifically, first forming priming coat on the outer peripheral surface of substrate roller, then
Substrate roller is coated with heat-shrinkable pipe, then to carry out stage heating treatment equal to the surface that priming coat is in contact with heat-shrinkable pipe
It melts, vulcanization reaction occurs in melting process between contact surface, forms close molecule between heat-shrinkable pipe and priming coat
Between active force.In addition, heat-shrinkable pipe itself can be shunk at high temperature, to further strengthen heat-shrinkable pipe and priming coat
Between binding force, cool down processing again later, so that it may obtain fixing roller.Technique is applied compared to traditional primary coat-face, it is above-mentioned fixed
The preparation process of shadow roller is to prepare fixing roller in such a way that thermoplastic pipe coats substrate roller, and preparation method is simple, and avoids
The use of pollution chemical coating, energy conservation and environmental protection during conventional face applies.
In one of the embodiments, in the step to the stage heating treatment of substrate roller for being coated with heat-shrinkable pipe
In rapid, the stage heating is first to be warming up to 200 DEG C -220 DEG C with the heating rate of 6 DEG C/min-6.5 DEG C/min, heat preservation
3min-8min;Then 320 DEG C -350 DEG C are warming up to the heating rate of 2 DEG C/min-2.5 DEG C/min, keep the temperature 10min-25min.
In one of the embodiments, in the step of cooling down processing, cooling processing be with 2.5 DEG C/min-3 DEG C/
The cooling rate of min is cooled to 20 DEG C -30 DEG C.
In one of the embodiments, the step of heat-shrinkable pipe to be coated to the outer peripheral surface of priming coat of the substrate roller
In, the mode of the cladding is nesting.
The finish of the heat-shrinkable pipe is 0.1Ra-0.3Ra in one of the embodiments,.
In one of the embodiments, the heat-shrinkable pipe with a thickness of 10 μm -100 μm.
The material of the heat-shrinkable pipe is total selected from tetrafluoroethene perfluoroalkyl vinyl ether in one of the embodiments,
At least one of polymers and polytetrafluoroethylene (PTFE).
Fluororesin-coated material is formed on the substrate roller on the outer peripheral surface of substrate roller in one of the embodiments,
In the step of priming coat, the mode of the coating is spraying.
Fluororesin-coated material is formed on the substrate roller on the outer peripheral surface of substrate roller in one of the embodiments,
In the step of priming coat, the fluorine resin material is in tetrafluoroethene perfluoroalkyl vinyl ether copolymer and polytetrafluoroethylene (PTFE)
At least one.
The present invention also provides a kind of fixing rollers comprising:
Substrate roller;
Priming coat, set on the outer peripheral surface of the substrate roller;And
Heat-shrinkable pipe, set on the outer peripheral surface of the priming coat.
The surface smoothness of above-mentioned fixing roller is good, and the picture quality being fixed with this fixing roller is good, and distortion rate is low.
Detailed description of the invention
Fig. 1 is the sectional view of fixing roller in one embodiment of the invention.
Specific embodiment
In order to make the foregoing objectives, features and advantages of the present invention clearer and more comprehensible, with reference to the accompanying drawing to the present invention
Specific embodiment be described in detail.Many details are explained in the following description in order to fully understand this hair
It is bright.But the invention can be embodied in many other ways as described herein, those skilled in the art can be not
Similar improvement is done in the case where violating intension of the present invention, therefore the present invention is not limited by the specific embodiments disclosed below.
Unless otherwise defined, all technical and scientific terms used herein and belong to technical field of the invention
The normally understood meaning of technical staff is identical.Term as used herein in the specification of the present invention is intended merely to description tool
The purpose of the embodiment of body, it is not intended that in the limitation present invention.Term " and or " used herein includes one or more phases
Any and all combinations of the listed item of pass.
Referring to Fig. 1, a kind of preparation method of fixing roller is provided in one embodiment of the invention comprising following steps:
S1, on the outer peripheral surface of substrate roller 100 fluororesin-coated material to form priming coat on the substrate roller 100
110。
Wherein, substrate roller 100 is the basic skeleton structure of fixing roller, can select fixing metal roller or heat-resist
Resin fixing roller.Further, when selecting fixing metal roller, the preferably good aluminium alloy roller of thermal conductivity.Of course it is to be understood that
Other materials as metal tube can also be with, such as iron, nickel and their alloy, stainless steel etc..Further, when selection resin
When fixing roller, the preferred good polyimides roller of heat curing type.Other resin material rollers that heat curing type is good can certainly be selected.
It is appreciated that the so-called substrate roller 100 of the present invention is inside it also containing heating element necessary to production fixing roller.
It is also coated with Heat Conduction Material in the inner peripheral surface of substrate roller 100 in one of the embodiments, to be conducive to substrate
100 internal heating element of roller generates heat and conducts to surface.
In one of the embodiments, on the outer peripheral surface of substrate roller 100 fluororesin-coated material in the substrate roller
It is formed before priming coat 110 on 100, further includes that the pre-heat treatment first is carried out to improve priming coat 110 and substrate roller to substrate roller 100
Adhesiveness between 100, specifically, the temperature of the pre-heat treatment are 30 DEG C -50 DEG C, and the time of the pre-heat treatment is 8min-12min.
S2, heat-shrinkable pipe 130 is coated the substrate roller 100 priming coat 110 outer peripheral surface, to be coated be heat-shrinked
Property pipe 130 and the priming coat 110 the first stage heating of the substrate roller 100, be warming up to the interior of the heat-shrinkable pipe 130
When the outer peripheral surface of circumferential surface and the priming coat 110 melts, then the processing that cools down is to get fixing roller.
Wherein, the stage heating is first progress first stage heating, i.e., with the heating speed of 6 DEG C/min-6.5 DEG C/min
Degree is warming up to 200 DEG C -220 DEG C, keeps the temperature 3min-8min.The main purpose of first stage heating is to exclude priming coat 110 and heat receipts
Bubble between contracting pipe 130.Then second stage heating is carried out, i.e., is heated up with the heating rate of 2 DEG C/min-2.5 DEG C/min
To 320 DEG C -350 DEG C, 10min-25min is kept the temperature.The main purpose of second stage heating is to make priming coat 110 and heat-shrinkable pipe
130 surfaces being in contact melt, that is to say, that the inner peripheral surface of the heat-shrinkable pipe 130 is outer with the priming coat 110
Circumferential surface melts.Sulphur occurs for the outer peripheral surface of the inner peripheral surface of heat-shrinkable pipe 130 and the priming coat 110 in melting process
Change reaction, forms close intermolecular force between heat-shrinkable pipe 130 and priming coat 110.In addition, heat-shrinkable pipe 130
Due to the heat shrinkable of itself, itself can shrink at high temperature, to further strengthen heat-shrinkable pipe and priming coat
Between binding force, cool down processing again later, so that it may obtain fixing roller.
In one of the embodiments, in the step of cooling down processing, cooling processing be with 2.5 DEG C/min-3 DEG C/
The cooling rate of min is cooled to 20 DEG C -30 DEG C.Fixing roller will be slow cooling under this cooling rate, avoid member inside fixing roller
Part generates deformation, or even rupture because of fast cooling.
Heat-shrinkable pipe 130 is being coated to the outer of the priming coat 110 of the substrate roller 100 in one of the embodiments,
It is on the outer peripheral surface for the priming coat 110 for being nested in the substrate roller 100 using heat-shrinkable pipe 130 in the step of circumferential surface.It is nested
Mode it is simple, it is easily operated.
The finish of the heat-shrinkable pipe 130 is 0.1Ra-0.3Ra in one of the embodiments,.Select this bright and clean
The benefit of the heat-shrinkable pipe 130 of degree is the fixing roller that is prepared in subsequent fixing, can reduce powder and paper because
The chance for rubbing and shifting, that is to say, that image distortion rate can be reduced.
In one of the embodiments, the heat-shrinkable pipe 130 with a thickness of 10 μm -100 μm.The thermal contraction of the application
Property pipe 130 thickness may be selected 100 μm, and traditional spray-coating surface applies the finishing coat finite thickness that the mode of material is formed, at most
It can only achieve 30 μm, such as overspray material again, there are the risks of material falls back, and can be too small because of thickness in fixing, pole
Easily loss is scrapped.
The material of the heat-shrinkable pipe 130 is selected from tetrafluoroethene perfluoroalkyl vinyl in one of the embodiments,
At least one of ether copolymer and polytetrafluoroethylene (PTFE).
In one of the embodiments, on the outer peripheral surface of substrate roller 100 fluororesin-coated material in the substrate roller
It is described applied to spraying in the step of forming priming coat 110 on 100.
In one of the embodiments, the fluorine resin material be selected from tetrafluoroethene perfluoroalkyl vinyl ether copolymer and
At least one of polytetrafluoroethylene (PTFE).
The preparation method of above-mentioned fixing roller is simple, specifically, first forming priming coat on the outer peripheral surface of substrate roller, then
Substrate roller is coated with heat-shrinkable pipe, then to carry out stage heating treatment equal to the surface that priming coat is in contact with heat-shrinkable pipe
It melts, vulcanization reaction occurs in melting process between contact surface, forms close molecule between heat-shrinkable pipe and priming coat
Between active force.In addition, heat-shrinkable pipe itself can be shunk at high temperature, to further strengthen heat-shrinkable pipe and priming coat
Between binding force, cool down processing again later, so that it may obtain fixing roller.Technique is applied compared to traditional primary coat-face, it is above-mentioned fixed
The preparation process of shadow roller is to prepare fixing roller in such a way that thermoplastic pipe coats substrate roller, and preparation method is simple, and avoids
The use of pollution chemical coating, energy conservation and environmental protection during conventional face applies.
Refering to fig. 1, the present invention also provides a kind of fixing rollers comprising:
Substrate roller 100;
Priming coat 110, set on the outer peripheral surface of the substrate roller 100;And
Heat-shrinkable pipe 130, set on the outer peripheral surface of the priming coat 110.
The surface smoothness of above-mentioned fixing roller is good, and the picture quality being fixed with this fixing roller is good, and distortion rate is low.
In order to which objects and advantages of the present invention are more clearly understood, the present invention is carried out with reference to embodiments further
It is described in detail.It should be appreciated that described herein, specific examples are only used to explain the present invention, is not intended to limit the present invention.
Embodiment 1
A kind of preparation method of fixing roller comprising following steps:
(1) axis direction length 250mm is taken, the aluminium alloy roller with a thickness of 30 μm of inside containing heating element is put into later
The pre-heat treatment in preheating furnace, the temperature of the pre-heat treatment are 50 DEG C, preheat 10min.
(2) on the outer peripheral surface of aluminium alloy roller ptfe coating perfluoroalkyl vinyl ether copolymer (PFA) in institute
State the priming coat that 5 μ m-thicks are formed on substrate roller.
(3) respectively by the outer peripheral surface of the priming coat of the nested substrate roller of 15 μm, 30 μm and 100 μm of heat-shrinkable pipe,
Wherein, heat-shrinkable pipe is that tetrafluoroethene perfluoroalkyl vinyl ether is copolymerized property management (PFA pipe).
(4) first stage heating treatment is placed in sintering furnace to the substrate roller for being nested with heat-shrinkable pipe, then cooled down
Processing, cutting, purged and packed obtain the fixing roller finished product of different-thickness.Wherein, the condition of stage heating is: first stage liter
Temperature is warming up to 220 DEG C with 6 DEG C of heating rate, keep the temperature 5min.Then second stage heating is carried out, i.e., with the liter of 2 DEG C/min
Warm speed is warming up to 320 DEG C, keeps the temperature 15min.The condition of cooling processing is: being cooled to 20 DEG C with the cooling rate of 2.5 DEG C/min.
Embodiment 2
A kind of preparation method of fixing roller comprising following steps:
(1) axis direction length 250mm is taken, the aluminium alloy roller with a thickness of 30 μm of inside containing heating element is put into later
The pre-heat treatment in preheating furnace, the temperature of the pre-heat treatment are 50 DEG C, preheat 10min.
(2) on the outer peripheral surface of aluminium alloy roller ptfe coating perfluoroalkyl vinyl ether copolymer (PFA) in institute
State the priming coat that 5 μ m-thicks are formed on substrate roller.
(3) respectively by the outer peripheral surface of the priming coat of the nested substrate roller of 15 μm, 30 μm and 100 μm of heat-shrinkable pipe,
Wherein, heat-shrinkable pipe is polyfluortetraethylene pipe (PTFE tube).
(4) first stage heating treatment is placed in sintering furnace to the substrate roller for being nested with heat-shrinkable pipe, then cooled down
Processing, cutting, purged and packed obtain the fixing roller finished product of different-thickness.Wherein, the condition of stage heating is: first stage liter
Temperature is warming up to 220 DEG C with 6 DEG C of heating rate, keep the temperature 5min.Then second stage heating is carried out, i.e., with the liter of 2 DEG C/min
Warm speed is warming up to 320 DEG C, keeps the temperature 15min.The condition of cooling processing is: being cooled to 20 DEG C with the cooling rate of 2.5 DEG C/min.
Embodiment 3
A kind of preparation method of fixing roller comprising following steps:
(1) axis direction length 250mm is taken, the aluminium alloy roller with a thickness of 30 μm of inside containing heating element is put into later
The pre-heat treatment in preheating furnace, the temperature of the pre-heat treatment are 50 DEG C, preheat 10min.
(2) polytetrafluoroethylene (PTFE) (PTFE) is sprayed on the outer peripheral surface of aluminium alloy roller to form 5 μ m-thicks on the substrate roller
Priming coat.
(3) respectively by the outer peripheral surface of the priming coat of 15 μm, the 30 μm substrate rollers nested with 100 μm of heat-shrinkable pipes,
In, heat-shrinkable pipe is polyfluortetraethylene pipe (PTFE tube).
(4) first stage heating treatment is placed in sintering furnace to the substrate roller for being nested with heat-shrinkable pipe, then cooled down
Processing, cutting, purged and packed obtain the fixing roller finished product of different-thickness.Wherein, the condition of stage heating is: first stage liter
Temperature is warming up to 220 DEG C with 6.5 DEG C of heating rate, keep the temperature 8min.Then second stage heating is carried out, i.e., with 2.5 DEG C/min
Heating rate be warming up to 350 DEG C, keep the temperature 25min.The condition of cooling processing is: being cooled to the cooling rate of 2.5 DEG C/min
20℃。
Comparative example 1
A kind of preparation method of fixing roller comprising following steps:
(1) axis direction length 250mm is taken, the aluminium alloy roller with a thickness of 30 μm of inside containing heating element is put into later
The pre-heat treatment in preheating furnace, the temperature of the pre-heat treatment are 50 DEG C, preheat 10min.
(2) polytetrafluoroethylene (PTFE) (PTFE) is sprayed on the outer peripheral surface of aluminium alloy roller to form 5 μ m-thicks on the substrate roller
Priming coat.
(3) finishing coat that polytetrafluoroethylene (PTFE) (PTFE) is respectively formed 15 μm, 30 μm is sprayed on the outer peripheral surface of priming coat, it
It is placed in sintering furnace and 15min is sintered with 380 DEG C of temperature, grinding, cleaning, press polish, cutting, purged and packed obtain different-thickness
Fixing roller finished product.
Comparative example 2
A kind of preparation method of fixing roller comprising following steps:
(1) axis direction length 250mm is taken, the aluminium alloy roller with a thickness of 30 μm of inside containing heating element is put into later
The pre-heat treatment in preheating furnace, the temperature of the pre-heat treatment are 50 DEG C, preheat 10min.
(2) on the outer peripheral surface of aluminium alloy roller ptfe coating perfluoroalkyl vinyl ether copolymer (PFA) in institute
State 5 μm of priming coats of formation on substrate roller.
(3) ptfe coating perfluoroalkyl vinyl ether copolymer (PFA) is respectively formed on the outer peripheral surface of priming coat
15 μm, 30 μm of finishing coat, be placed in sintering furnace 15min be sintered with 380 DEG C of temperature, grinding, cleaning, press polish, cutting,
Purged and packed obtains the fixing roller finished product of different-thickness.
Effect test
Fixing roller made from each embodiment and comparative example is tested for the property respectively, test index includes contact angle, light
Cleanliness, yields and picture quality.
Contact angle evaluation: contact angle measures contact angle by tangential method using contact angle instrument, and contact angle is bigger, takes off
It is better to imitate fruit.
Image quality evaluation: black white image is printed using obtained fixing roller, and is evaluated.Surface when printing
Temperature is 150 DEG C.Irregular colour and rough surface situation are checked by visual observations, test result is shown in Table 1.
Table 1
Annotation:
In image quality evaluation, irregular colour and rough surface is not observed in 1 representative;2 representatives are barely perceivable face
Color unevenness and rough surface;Irregular colour and rough surface are observed in 3 representatives, but all within the acceptable range.
As shown in Table 1, the finish of the fixing roller in embodiment is smaller than the finish numerical value of the fixing roller in comparative example,
Finish is more preferable, can reduce the chance that powder and paper shift by friction, reduces image distortion rate.In addition, passing through sight
It examines, irregular colour and rough surface situation is not observed in the picture quality printed in embodiment 1 and embodiment 2, figure
As high-quality.Furthermore as the fixing roller that finishing coat is greater than 50 μ m-thicks in such a way that primary coat-face applies, can not be made.
Each technical characteristic of embodiment described above can be combined arbitrarily, for simplicity of description, not to above-mentioned reality
It applies all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, all should be considered as described in this specification.
The embodiments described above only express several embodiments of the present invention, and the description thereof is more specific and detailed, but simultaneously
It cannot therefore be construed as limiting the scope of the patent.It should be pointed out that coming for those of ordinary skill in the art
It says, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to protection of the invention
Range.Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.
Claims (10)
1. a kind of fixing roller characterized by comprising
Substrate roller;
Priming coat, set on the outer peripheral surface of the substrate roller;And
Heat-shrinkable pipe, set on the outer peripheral surface of the priming coat.
2. a kind of preparation method of fixing roller, which comprises the steps of:
Fluororesin-coated material forms priming coat on the substrate roller on the outer peripheral surface of substrate roller;
Heat-shrinkable pipe is coated to the outer peripheral surface of the priming coat of the substrate roller;And
The stage heating treatment of substrate roller to heat-shrinkable pipe and the priming coat is coated with, is warming up to the thermal contraction
Property pipe inner peripheral surface and the outer peripheral surface of priming coat when melting, cooling is handled to get fixing roller.
3. the preparation method of fixing roller according to claim 2, which is characterized in that the institute for being coated with heat-shrinkable pipe
In the step of stating the stage heating treatment of substrate roller, the stage heating is the first heating speed with 6 DEG C/min-6.5 DEG C/min
Degree is warming up to 200 DEG C -220 DEG C, keeps the temperature 3min-8min;Then 320 are warming up to the heating rate of 2 DEG C/min-2.5 DEG C/min
DEG C -350 DEG C, keep the temperature 10min-25min.
4. the preparation method of fixing roller according to claim 2, which is characterized in that described in the step of cooling down processing
Cooling processing is to be cooled to 20 DEG C -30 DEG C with the cooling rate of 2.5 DEG C/min-3 DEG C/min.
5. according to the preparation method of the described in any item fixing rollers of claim 2-4, which is characterized in that by heat-shrinkable pipe packet
In the step of covering the outer peripheral surface of the priming coat of the substrate roller, the mode of the cladding is nesting.
6. according to the preparation method of the described in any item fixing rollers of claim 2-4, which is characterized in that the heat-shrinkable pipe
Finish is 0.1Ra-0.3Ra.
7. according to the preparation method of the described in any item fixing rollers of claim 2-4, which is characterized in that the heat-shrinkable pipe
With a thickness of 10 μm -100 μm.
8. according to the preparation method of the described in any item fixing rollers of claim 2-4, which is characterized in that the heat-shrinkable pipe
Material is selected from least one of tetrafluoroethene perfluoroalkyl vinyl ether copolymer and polytetrafluoroethylene (PTFE).
9. according to the preparation method of the described in any item fixing rollers of claim 2-4, which is characterized in that in the outer peripheral surface of substrate roller
For upper fluororesin-coated material in the step of forming priming coat on the substrate roller, the mode of the coating is spraying.
10. according to the preparation method of the described in any item fixing rollers of claim 2-4, which is characterized in that in the periphery of substrate roller
For fluororesin-coated material in the step of forming priming coat on the substrate roller, the fluorine resin material is selected from tetrafluoroethene on face
At least one of perfluoroalkyl vinyl ether copolymer and polytetrafluoroethylene (PTFE).