CN110373131A - A kind of interior make fixed glue of the dedicated moss material of scape and preparation method thereof - Google Patents
A kind of interior make fixed glue of the dedicated moss material of scape and preparation method thereof Download PDFInfo
- Publication number
- CN110373131A CN110373131A CN201910749973.8A CN201910749973A CN110373131A CN 110373131 A CN110373131 A CN 110373131A CN 201910749973 A CN201910749973 A CN 201910749973A CN 110373131 A CN110373131 A CN 110373131A
- Authority
- CN
- China
- Prior art keywords
- parts
- scape
- dedicated
- glue
- interior
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to fixed glue technical fields, specifically provide a kind of interior and make fixed glue of the dedicated moss material of scape and preparation method thereof, which is made of the raw material of following parts by weight: 10-15 part of hydroxypropyl methyl cellulose, 5-8 parts of food-grade dextrin, 3-5 parts of polyvinyl alcohol, 1-2 parts of dehydroactic acid sodium, is concentrated lemon extract 1-2 parts and 1000-1500 parts of reverse osmose pure-water at 2-4 parts of polyacrylamide；Preparation method after raw material hydroxypropyl methyl cellulose, polyacrylamide, food-grade dextrin, polyvinyl alcohol, dehydroactic acid sodium, concentration lemon extract are uniformly mixed and are compounded with pure water through the processes such as 30-40 DEG C of heating, cooling by realizing.Fixed glue prepared by the present invention has the characteristics that high viscosity, strong associativity, the high grade of transparency, anticorrosive mildewproof, smell are pure and fresh；In addition, the preparation process of the fixation glue is simple, and it is low in cost, it is suitble to industrialized production.
Description
Technical field
The present invention relates to fixed glue technical field, more particularly to a kind of interior make the fixed glue of the dedicated moss material of scape and its
Preparation method.
Background technique
More and more occur in people's daily life with the improvement of people's life quality, scape is made in interior, moss
Interior is made scape and is also favored deeply by people, with moss indoor greening and the indoor development for making scape engineering, the processing work of moss material
The problem of skill and Construction Technology short slab are also increasingly prominent, and matched processing technology and standardized product lack is urgently to be resolved.?
, not yet there is the fixation glue for making the dedicated moss material of scape in interior, on the market for fixing moss in the fixed aspect of bryophyte material
The colloid of material mostly uses greatly the Shui nationality to make product that the fields such as scape, engineering construction generally use, such as quick-drying gelatin, white glue with vinyl etc.,
The use scope of this kind of colloid has limitation, and part colloid is there is also penetrating odor or contains poisonous and harmful element, cannot
Meet increasingly fining, innoxious interior and makes scape demand.
Summary of the invention
The purpose of the invention is to provide a kind of interior to make fixed glue of the dedicated moss material of scape and preparation method thereof, in order to
This technical problem is solved, the technical scheme adopted by the invention is that:
The fixed glue of the dedicated moss material of scape is made in a kind of interior, which is made of the raw material of following parts by weight: hydroxypropyl first
10-15 parts of base cellulose, 2-4 parts of polyacrylamide, 5-8 parts of food-grade dextrin, 3-5 parts of polyvinyl alcohol, dehydroactic acid sodium 1-2
Part, lemon extract 1-2 parts and 1000-1500 parts of reverse osmose pure-water of concentration.
Preferably, the fixed glue of the dedicated moss material of scape is made in a kind of interior, which is by the raw material system of following parts by weight
At: 12-14 parts of hydroxypropyl methyl cellulose, 3-4 parts of polyacrylamide, 6-7 parts of food-grade dextrin, 4-5 parts of polyvinyl alcohol, dehydrogenation
1-2 parts of sodium acetate, lemon extract 1-2 parts and 1200-1400 parts of reverse osmose pure-water of concentration.
Preferably, the fixed glue of the dedicated moss material of scape is made in a kind of interior, which is by the raw material system of following parts by weight
At: 13 parts of hydroxypropyl methyl cellulose, 3 parts of polyacrylamide, 6 parts of food-grade dextrin, 4 parts of polyvinyl alcohol, dehydroactic acid sodium 1
Part, 1 part of lemon extract of concentration and 1200 parts of reverse osmose pure-water.
Preferably, the fixed glue of the dedicated moss material of scape is made in a kind of interior, which is by the raw material system of following parts by weight
At: 12 parts of hydroxypropyl methyl cellulose, 2 parts of polyacrylamide, 8 parts of food-grade dextrin, 3 parts of polyvinyl alcohol, dehydroactic acid sodium 2
Part, 2 parts of lemon extract of concentration and 1400 parts of reverse osmose pure-water.
Preferably, the fixed glue of the dedicated moss material of scape is made in a kind of interior, and wherein the unit of polyacrylamide is 15000.
Preferably, the fixed glue of the dedicated moss material of scape is made in a kind of interior, and wherein the granular size of polyvinyl alcohol is 100 mesh.
Wherein, polyvinyl alcohol is adhesive, it and hydrophilic fiber are known as good bonding force；Hydroxypropyl methyl fiber
Element and polyacrylamide are as thickener, and transparency is very high after dissolution, and thickening efficiency is high, especially to the thickening effect of water phase
It is good；Dextrin is as thickener, stabilizer；Dehydroactic acid sodium is as preservative；Lemon extract is concentrated as additive, adjusts gas
The characteristics of taste, above each ingredient, which combines, realizes fixation glue high viscosity, strong associativity, the high grade of transparency, the anticorrosive mildewproof, smell
The features such as pure and fresh, while the fixation glue is free of organic solvent, and each ingredient is cheap, it is safe and non-toxic, it is easy to use, to environment
It is harmless.
Make the preparation method of the fixed glue of the dedicated moss material of scape in above-mentioned interior: the following steps are included:
(1) by raw material hydroxypropyl methyl cellulose, polyacrylamide, food-grade dextrin, polyvinyl alcohol, dehydroactic acid sodium, concentration
Lemon extract is uniformly mixed, and obtains mixture A；
(2) to prepare a certain amount of reverse osmose pure-water with water purification machine spare；
(3) mixture A is added at one time in 30-40 DEG C of reverse osmose pure-water, is stirred well to mixture A and is completely dissolved；
(4) continue to stir, when solution becomes translucent paste, stop stirring, be cooled to room temperature and the fixation glue is made.
It should be understood that raw material hydroxypropyl methyl cellulose, polyacrylamide have been weighed, food-grade dextrin, polyethylene
After alcohol, dehydroactic acid sodium and concentration lemon extract, before compounding with water, have to guarantee that each raw material is sufficiently mixed uniformly；?
Each raw material can be replaced manually stirring with mechanical stirring during compounding with pure water；The reaction vessel for being used to prepare the fixation glue can
To be beaker or reaction kettle, prepared needed for depending on fixing the volume size of glue.
Compared with the prior art, the present invention has the following advantages: there is high viscosity, strong using the fixation glue of this method preparation
The features such as associativity, the high grade of transparency, anticorrosive mildewproof, pure and fresh smell, can be bonding to moss material, the fixation glue in the short time moment
Will not desiccation, can arbitrarily remove or bond again；In addition, the preparation process of the fixation glue is simple, and it is low in cost, it is suitble to industry
Metaplasia produces.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following embodiment is only used for more
Add and clearly demonstrate technical solution of the present invention, and not intended to limit the protection scope of the present invention.
The technical scheme adopted by the invention is that:
The fixed glue of the dedicated moss material of scape is made in a kind of interior, which is made of the raw material of following parts by weight: hydroxypropyl first
10-15 parts of base cellulose, 2-4 parts of polyacrylamide, 5-8 parts of food-grade dextrin, 3-5 parts of polyvinyl alcohol, dehydroactic acid sodium 1-2
Part, lemon extract 1-2 parts and 1000-1500 parts of reverse osmose pure-water of concentration.
Make the preparation method of the fixed glue of the dedicated moss material of scape in above-mentioned interior: the following steps are included:
(1) by raw material hydroxypropyl methyl cellulose, polyacrylamide, food-grade dextrin, polyvinyl alcohol, dehydroactic acid sodium, concentration
Lemon extract is uniformly mixed, and obtains mixture A；
(2) to prepare a certain amount of reverse osmose pure-water with water purification machine spare；
(3) mixture A is added at one time in 30-40 DEG C of reverse osmose pure-water, is stirred well to mixture A and is completely dissolved；
(4) continue to stir, when solution becomes translucent paste, stop stirring, be cooled to room temperature and the fixation glue is made.
The technical solution uses the relatively stronger polyvinyl alcohol of bonding force for adhesive；The very high hydroxypropyl of transparency after dissolution
Ylmethyl cellulose and polyacrylamide are as thickener；Dextrin is as thickener, stabilizer；Dehydroactic acid sodium is as anti-corrosion
Agent；Lemon extract is concentrated as flavoring agent, realizes fixation glue high viscosity, strong associativity, the high grade of transparency, the anticorrosive mildewproof, gas
The features such as taste is pure and fresh.
Embodiment 1
Fixed glue of the dedicated moss material of scape and preparation method thereof is made in a kind of interior, which includes following each component: 15g hydroxypropyl
Ylmethyl cellulose, 15000 unit polyacrylamide of 4g, 8g food-grade dextrin, 100 mesh polyvinyl alcohol of 5g, 2g dehydroactic acid
The reverse osmose pure-water of lemon extract, 1000 ml is concentrated in sodium, 1g.The preparation method of the fixation glue the following steps are included:
(1) by raw material hydroxypropyl methyl cellulose, polyacrylamide, food-grade dextrin, polyvinyl alcohol, dehydroactic acid sodium, concentration
Lemon extract is uniformly mixed, and obtains mixture A；
(2) to prepare a certain amount of reverse osmose pure-water with water purification machine spare；
(3) mixture A is added at one time into 30 DEG C of reverse osmose pure-water, is stirred well to mixture A and is completely dissolved；
(4) continue to stir, when solution becomes translucent paste, stop stirring, be cooled to room temperature and the fixation glue is made.
Embodiment 2
Fixed glue of the dedicated moss material of scape and preparation method thereof is made in a kind of interior, which includes following each component: 13g hydroxypropyl
Ylmethyl cellulose, 15000 unit polyacrylamide of 3g, 6g food-grade dextrin, 100 mesh polyvinyl alcohol of 4g, 1g dehydroactic acid
Lemon extract, 1200 ml reverse osmose pure-waters is concentrated in sodium, 1g.
The preparation method of the fixation glue the following steps are included:
(1) by raw material hydroxypropyl methyl cellulose, polyacrylamide, food-grade dextrin, polyvinyl alcohol, dehydroactic acid sodium, concentration
Lemon extract is uniformly mixed, and obtains mixture A；
(2) to prepare a certain amount of reverse osmose pure-water with water purification machine spare；
(3) mixture A is added at one time into 40 DEG C of reverse osmose pure-water, is stirred well to mixture A and is completely dissolved；
(4) continue to stir, when solution becomes translucent paste, stop stirring, be cooled to room temperature and the fixation glue is made.
Embodiment 3
Fixed glue of the dedicated moss material of scape and preparation method thereof is made in a kind of interior, which includes following each component: 12g hydroxypropyl
Ylmethyl cellulose, 15000 unit polyacrylamide of 2g, 8g food-grade dextrin, 100 mesh polyvinyl alcohol of 3g, 2g dehydroactic acid
Lemon extract, 1400 ml reverse osmose pure-waters is concentrated in sodium, 2g.
The preparation method of the present embodiment is same as Example 1.
Embodiment 4
Fixed glue of the dedicated moss material of scape and preparation method thereof is made in a kind of interior, which includes following each component: 10g hydroxypropyl
Ylmethyl cellulose, 15000 unit polyacrylamide of 4g, 5g food-grade dextrin, 100 mesh polyvinyl alcohol of 4g, 2g dehydroactic acid
Lemon extract, 1500 ml reverse osmose pure-waters is concentrated in sodium, 1g.
The preparation method of the present embodiment is same as Example 2.
Embodiment 5
Fixed glue of the dedicated moss material of scape and preparation method thereof is made in a kind of interior, which includes following each component: 14g hydroxypropyl
Ylmethyl cellulose, 15000 unit polyacrylamide of 2g, 7g food-grade dextrin, 100 mesh polyvinyl alcohol of 3g, 1g dehydroactic acid
Lemon extract, 1500 ml reverse osmose pure-waters is concentrated in sodium, 2g.
The preparation method of the present embodiment is same as Example 1.
Claims (7)
1. the fixed glue of the dedicated moss material of scape is made in a kind of interior, it is characterised in that: the fixation glue is by the raw material of following parts by weight
Be made: 10-15 parts of hydroxypropyl methyl cellulose, 5-8 parts of food-grade dextrin, 3-5 parts of polyvinyl alcohol, takes off 2-4 parts of polyacrylamide
1-2 parts of hydroacetic acid sodium, lemon extract 1-2 parts and 1000-1500 parts of reverse osmose pure-water of concentration.
2. the fixed glue of the dedicated moss material of scape is made in a kind of interior as described in claim 1, it is characterised in that: the fixation glue be by
The raw material of following parts by weight is made: 12-14 parts of hydroxypropyl methyl cellulose, 3-4 parts of polyacrylamide, 6-7 parts of food-grade dextrin,
4-5 parts of polyvinyl alcohol, 1-2 parts of dehydroactic acid sodium, lemon extract 1-2 parts and 1200-1400 parts of reverse osmose pure-water of concentration.
3. the fixed glue of the dedicated moss material of scape is made in a kind of interior as claimed in claim 2, it is characterised in that: the fixation glue be by
The raw material of following parts by weight is made: 13 parts of hydroxypropyl methyl cellulose, 3 parts of polyacrylamide, 6 parts of food-grade dextrin, polyethylene
4 parts of alcohol, 1 part of dehydroactic acid sodium, 1 part of lemon extract of concentration and 1200 parts of reverse osmose pure-water.
4. the fixed glue of the dedicated moss material of scape is made in a kind of interior as described in claim 1, it is characterised in that: the fixation glue be by
The raw material of following parts by weight is made: 12 parts of hydroxypropyl methyl cellulose, 2 parts of polyacrylamide, 8 parts of food-grade dextrin, polyethylene
3 parts of alcohol, 2 parts of dehydroactic acid sodium, 2 parts of lemon extract of concentration and 1400 parts of reverse osmose pure-water.
5. a kind of interior as described in any one of claim 1,2,3,4 claim is made the dedicated moss material of scape and is fixed
Glue, it is characterised in that: the unit of the polyacrylamide is 15000.
6. the fixed glue of the dedicated moss material of scape is made in a kind of interior as described in any one of claim 1,2,3,4 right,
Be characterized in that: the granular size of the polyvinyl alcohol is 100 mesh.
7. the system that the fixed glue of the dedicated moss material of scape is made in a kind of interior as described in any one of claim 1,2,3,4 right
Preparation Method, it is characterised in that: the following steps are included:
(1) by raw material hydroxypropyl methyl cellulose, polyacrylamide, food-grade dextrin, polyvinyl alcohol, dehydroactic acid sodium, concentration
Lemon extract is uniformly mixed, and obtains mixture A；
(2) to prepare a certain amount of reverse osmose pure-water with water purification machine spare；
(3) mixture A is added at one time in 30-40 DEG C of reverse osmose pure-water, is stirred well to mixture A and is completely dissolved；
(4) continue to stir, when solution becomes translucent paste, stop stirring, be cooled to room temperature and the fixation glue is made.