CN110373049A - A kind of production method of cable screen material conductive black - Google Patents
A kind of production method of cable screen material conductive black Download PDFInfo
- Publication number
- CN110373049A CN110373049A CN201910746767.1A CN201910746767A CN110373049A CN 110373049 A CN110373049 A CN 110373049A CN 201910746767 A CN201910746767 A CN 201910746767A CN 110373049 A CN110373049 A CN 110373049A
- Authority
- CN
- China
- Prior art keywords
- carbon black
- screen material
- anionic surfactant
- dispersing agent
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to carbon black production technology field, especially a kind of production method of cable screen material conductive black.A kind of production method of cable screen material conductive black of the invention, existing conventional method of producing black pigment is improved, in chilled water (chw) to introducing anionic surfactant and cation dispersing agent in high temperature carbon black smoke temperature-fall period, so that anionic surfactant coats the particle of powdered carbon black, it is evenly affixed to carbon blacksurface, cation dispersing agent is dispersed between powdered carbon black particle, improve dispersion of the carbon black in EVA, viscosity stability when carbon black and EVA mixing is improved simultaneously, increase the crosslinking of carbon black and EVA, improve the heat-resisting Stability of Resistivity of cable screen material;This method is suitable for the process that Audit For Process, steam stove method and channel process mix gas production carbon black;The carbon black of production is environmentally friendly, safe and pollution-free.
Description
Technical field
The present invention relates to carbon black production technology field, especially a kind of production method of cable screen material conductive black.
Background technique
Carbon black is a kind of amorphous carbon.Gently, pine and superfine black powder, surface area are very big, range is from 10-
3000m2/ g, be carbonaceous material (coal, natural gas, heavy oil, fuel oil etc.) under conditions of lack of air through imperfect combustion or
Product obtained by being thermally decomposed.
Conventional manufacturing technologies of carbon black includes a variety of, such as: fuel oil is pumped to fuel oil heater through fuel oil, heating
Reacting furnace combustion chamber is axially sprayed into after to 120 DEG C, is existed with air that is being provided for blower and being preheating to 850 DEG C through air preheater
The mixing of reacting furnace burning zone, burning, generate about 1970 DEG C of hot combustion gas stream;Feedstock oil is pumped to online original through feedstock oil
Expect oil preheater, be preheating to after 180 DEG C and radially spray into reacting furnace trunnion section, mixed with hot combustion gas stream, crack rapidly, generates
Carbon black.At reacting furnace rear portion, directly chilled water (chw) is sprayed into high temperature carbon black smoke, reduces rapidly its temperature, it is anti-to terminate carbon black
It answers, carbon black tail gas is sent by blower to boiler combustion, and powdered carbon black is sent to burgy tank, it is granulated by airtight valve, auger to pelletizer,
It is dried to obtain dry carbon black particle, product storage tank is delivered to by elevator, is packaged to be finished product.
Carbon black Shortcomings, cable shield in the use process of cable screen material as made from conventional production method
Material conductive black is all very high to the purity of carbon black, surface-active, dispersibility requirement, and the carbon black purity passed through at present can reach
To requirement, but carbon blacksurface is very smooth, and surface functional group is few, when carbon black being added in cable shield, carbon black and ethyl vinyl acetate
Ethylene copolymer (EVA) is crosslinked in kneading machine, the degree of crosslinking and the activity of carbon blacksurface and carbon black dispersion sexual intercourse
Closely, the surface-active of carbon black is low, and carbon black dispersion is bad, directly affects the quality of cable screen material, and high pressure and extra-high voltage
Requirement of the cable to shielding material is very high.
Therefore it provides a kind of production method of cable screen material conductive black, makes dedicated conductive black obtained in height
Pressure and extra-high-tension cable shield the dispersed phase in expecting and surface and can improve, and improve the quality of cable.
Summary of the invention
The purpose of the present invention is to provide a kind of production methods of cable screen material conductive black, overcome aforementioned existing skill
The deficiency that the carbon blacksurface of art manufacture is very smooth, surface functional group is few, surface-active is low and carbon black dispersion is bad.
The technical scheme adopted by the invention to solve the technical problem is that:
A kind of production method of cable screen material conductive black, comprising the following steps:
(1) anionic surfactant is put into batch tank, adds water, be passed through compressed air and be stirred to mixing
It is even, aqueous solution of anionic surfactant is obtained, it is spare;
(2) cation dispersing agent is put into another batch tank, added with solvent, is stirred with stirring rod to being uniformly mixed,
Cation dispersing agent organic solution is obtained, it is spare;
(3) use metering pump by aqueous solution of anionic surfactant and cation dispersing agent organic solution respectively with 10-
The flow velocity of 40L/h and 10-100L/h is added in mixer and is mixed with chilled water (chw);
(4) aqueous solution of anionic surfactant, cation dispersing agent organic solution and chilled water (chw) are mixed by mixer
After closing uniformly, mixed solution is atomized by atomizer, and the mixed solution drop after atomization sprays into the charcoal black smoke containing hydrocarbon black powder
It in gas, comes into full contact with, heat in the mixed solution drop absorption carbon black smoke after atomization, steams with the carbon black smoke containing hydrocarbon black powder
Enter in carbon black smoke after hair, so that anionic surfactant coats the particle surface of powdered carbon black, uniformly adheres to
In the particle surface of powdered carbon black, cation dispersing agent is dispersed between the particle of powdered carbon black;
(5) by case filter, by step (4), treated that powdered carbon black is isolated from carbon black smoke, the powdery isolated
Carbon black is sent to burgy tank, is granulated by airtight valve, auger to pelletizer, wet carbon black particle is made, remaining tail gas is sent by blower
To boiler combustion;
(6) wet carbon black particle exchanges heat in drying machine with dry gas, obtains dry carbon black particle, passes through elevator
It is delivered to product storage tank, is packaged to be finished product.
Preferably, the chilled water (chw) is two chilled water (chw)s, and two chilled water (chw)s occur after fuel oil preheating device to before case filter, this
Not more than 300 DEG C of Duan Wendu.
Preferably, the batch tank in the step (1) and step (2) is the batch tank of 1000L.
Preferably, anionic surfactant is fluoride ion surfactant in the step (1).
The weight ratio of anionic surfactant and water is 1-10:80 in the preferred step (1).
Preferably, cation dispersing agent is 141 macromolecule dispersing agent of synde in the step (2), or opens up and receive for Holland
FD400, or be perfluorinated cation surfactant FC-911, the organic solvent is kerosene;The cation dispersing agent with have
The weight ratio of solvent is 1-10:64.
Preferably, the mixing time of the step (1) and step (2) is 8-15min.
The beneficial effects of the present invention are: compared with prior art, a kind of cable screen material conductive black of the invention
Production method improves existing conventional method of producing black pigment, in chilled water (chw) in high temperature carbon black smoke temperature-fall period
Anionic surfactant and cation dispersing agent are introduced, so that anionic surfactant coats powdered carbon black,
The even particle surface for being attached to powdered carbon black, cation dispersing agent are dispersed between the particle of powdered carbon black, improve carbon black
Dispersion in EVA, while viscosity stability when carbon black and EVA mixing is improved, increase the crosslinking of carbon black and EVA, improves electricity
The heat-resisting Stability of Resistivity of cable shielding material;This method is suitable for the process that Audit For Process, steam stove method and channel process mix gas production carbon black;
The carbon black of production is environmentally friendly, safe and pollution-free.
Specific embodiment
Embodiment 1
A kind of production method of cable screen material conductive black, comprising the following steps:
(1) by anionic surfactant 90kg investment 1000L batch tank in, add 800L water, be passed through compressed air into
Row stirring 10min, is uniformly mixed, obtains aqueous solution of anionic surfactant, spare;
(2) cation dispersing agent 10kg is put into the batch tank of another 1000L, added with 800L kerosene, is stirred with stirring rod
10min is mixed, is uniformly mixed, obtains cation dispersing agent organic solution, it is spare;
(3) use metering pump by aqueous solution of anionic surfactant and cation dispersing agent organic solution respectively with 10L/
The flow velocity of h and 20L/h is added in mixer and is mixed with chilled water (chw);
(4) aqueous solution of anionic surfactant, cation dispersing agent organic solution and chilled water (chw) are mixed by mixer
After closing uniformly, mixed solution is atomized by atomizer, and the mixed solution drop after atomization sprays into the charcoal black smoke containing hydrocarbon black powder
It in gas, comes into full contact with, heat in the mixed solution drop absorption carbon black smoke after atomization, steams with the carbon black smoke containing hydrocarbon black powder
Enter in carbon black smoke after hair, so that anionic surfactant coats the particle surface of powdered carbon black, uniformly adheres to
In the particle surface of powdered carbon black, cation dispersing agent is dispersed between the particle of powdered carbon black;
(5) by case filter, by step (4), treated that powdered carbon black is isolated from carbon black smoke, the powdery isolated
Carbon black is sent to burgy tank, is granulated by airtight valve, auger to pelletizer, wet carbon black particle is made, remaining tail gas is sent by blower
To boiler combustion;
(6) wet carbon black particle exchanges heat in drying machine with dry gas, obtains dry carbon black particle, passes through elevator
It is delivered to product storage tank, is packaged to be finished product.
Anionic surfactant is the fluorocarbon surfactant of DuPont Corporation's manufacture, model in the step (1)
Are as follows: Zonyl FS-610, specification are as follows: containing 22% fluorinated surfactant, 78% water, performance are as follows: improve product viscosity and stablize
Property.
Cation dispersing agent is the height that Zhuhai elder generation moral new material science and technology limited Company is manufactured in the step (2)
Dispersal agent molecule, model are as follows: synde 141, specification are as follows: active constituent content 98%, moisture content 2%, performance are as follows: accelerate
Carbon black dispersion.
The chilled water (chw) is two chilled water (chw)s.
This method is the improvement on conventional base in the background technology.
Embodiment 2
A kind of production method of cable screen material conductive black, comprising the following steps:
(1) by anionic surfactant 10kg investment 1000L batch tank in, add 800L water, be passed through compressed air into
Row stirring 10min, is uniformly mixed, obtains aqueous solution of anionic surfactant, spare;
(2) cation dispersing agent 90kg is put into the batch tank of another 1000L, added with 800L kerosene, is stirred with stirring rod
10min is mixed, is uniformly mixed, obtains cation dispersing agent organic solution, it is spare;
(3) use metering pump by aqueous solution of anionic surfactant and cation dispersing agent organic solution respectively with 20L/
The flow velocity of h and 40L/h is added in mixer and is mixed with chilled water (chw);
(4) aqueous solution of anionic surfactant, cation dispersing agent organic solution and chilled water (chw) are mixed by mixer
After closing uniformly, mixed solution is atomized by atomizer, and the mixed solution drop after atomization sprays into the charcoal black smoke containing hydrocarbon black powder
It in gas, comes into full contact with, heat in the mixed solution drop absorption carbon black smoke after atomization, steams with the carbon black smoke containing hydrocarbon black powder
Enter in carbon black smoke after hair, so that anionic surfactant coats the particle surface of powdered carbon black, uniformly adheres to
In the particle surface of powdered carbon black, cation dispersing agent is dispersed between the particle of powdered carbon black;
(5) by case filter, by step (4), treated that powdered carbon black is isolated from carbon black smoke, the powdery isolated
Carbon black is sent to burgy tank, is granulated by airtight valve, auger to pelletizer, wet carbon black particle is made, remaining tail gas is sent by blower
To boiler combustion;
(6) wet carbon black particle exchanges heat in drying machine with dry gas, obtains dry carbon black particle, passes through elevator
It is delivered to product storage tank, is packaged to be finished product.
Anionic surfactant is the fluorocarbon surfactant of DuPont Corporation's manufacture, model in the step (1)
Are as follows: Zonyl 9361, specification are as follows: containing 22% fluorinated surfactant, 78% water, performance are as follows: improve product viscosity stability.
Cation dispersing agent is the height that Zhuhai elder generation moral new material science and technology limited Company is manufactured in the step (2)
Dispersal agent molecule, model are as follows: synde 141, specification are as follows: active constituent content 98%, moisture content 2%, performance are as follows: accelerate
Carbon black dispersion.
The chilled water (chw) is two chilled water (chw)s.
This method is the improvement on conventional base in the background technology.
Embodiment 3
A kind of production method of cable screen material conductive black, comprising the following steps:
(1) by anionic surfactant 30kg investment 1000L batch tank in, add 800L water, be passed through compressed air into
Row stirring 10min, is uniformly mixed, obtains aqueous solution of anionic surfactant, spare;
(2) cation dispersing agent 70kg is put into the batch tank of another 1000L, added with 800L kerosene, is stirred with stirring rod
10min is mixed, is uniformly mixed, obtains cation dispersing agent organic solution, it is spare;
(3) use metering pump by aqueous solution of anionic surfactant and cation dispersing agent organic solution respectively with 30L/
The flow velocity of h and 60L/h is added in mixer and is mixed with chilled water (chw);
(4) aqueous solution of anionic surfactant, cation dispersing agent organic solution and chilled water (chw) are mixed by mixer
After closing uniformly, mixed solution is atomized by atomizer, and the mixed solution drop after atomization sprays into the charcoal black smoke containing hydrocarbon black powder
It in gas, comes into full contact with, heat in the mixed solution drop absorption carbon black smoke after atomization, steams with the carbon black smoke containing hydrocarbon black powder
Enter in carbon black smoke after hair, so that anionic surfactant coats the particle surface of powdered carbon black, uniformly adheres to
In the particle surface of powdered carbon black, cation dispersing agent is dispersed between the particle of powdered carbon black;
(5) by case filter, by step (4), treated that powdered carbon black is isolated from carbon black smoke, the powdery isolated
Carbon black is sent to burgy tank, is granulated by airtight valve, auger to pelletizer, wet carbon black particle is made, remaining tail gas is sent by blower
To boiler combustion;
(6) wet carbon black particle exchanges heat in drying machine with dry gas, obtains dry carbon black particle, passes through elevator
It is delivered to product storage tank, is packaged to be finished product.
Anionic surfactant is the fluorocarbon surfactant of DuPont Corporation's manufacture, model in the step (1)
Are as follows: Zonyl 9361, specification are as follows: containing 22% fluorinated surfactant, 78% water, performance are as follows: improve product viscosity stability.
Cation dispersing agent is the model that Dutch chemicals Tuo Na chemical company, enterprise manufactures in the step (2)
The dispersing agent of FD400, specification are as follows: active constituent content 99.5%, moisture content 0.5%, performance are as follows: accelerate carbon black dispersion.
The chilled water (chw) is two chilled water (chw)s.
This method is the improvement on conventional base in the background technology.
Embodiment 4
A kind of production method of cable screen material conductive black, comprising the following steps:
(1) by anionic surfactant 70kg investment 1000L batch tank in, add 800L water, be passed through compressed air into
Row stirring 10min, is uniformly mixed, obtains aqueous solution of anionic surfactant, spare;
(2) cation dispersing agent 30kg is put into the batch tank of another 1000L, added with 800L kerosene, is stirred with stirring rod
10min is mixed, is uniformly mixed, obtains cation dispersing agent organic solution, it is spare;
(3) use metering pump by aqueous solution of anionic surfactant and cation dispersing agent organic solution respectively with 40L/
The flow velocity of h and 80L/h is added in mixer and is mixed with chilled water (chw);
(4) aqueous solution of anionic surfactant, cation dispersing agent organic solution and chilled water (chw) are mixed by mixer
After closing uniformly, mixed solution is atomized by atomizer, and the mixed solution drop after atomization sprays into the charcoal black smoke containing hydrocarbon black powder
It in gas, comes into full contact with, heat in the mixed solution drop absorption carbon black smoke after atomization, steams with the carbon black smoke containing hydrocarbon black powder
Enter in carbon black smoke after hair, so that anionic surfactant coats the particle surface of powdered carbon black, uniformly adheres to
In the particle surface of powdered carbon black, cation dispersing agent is dispersed between the particle of powdered carbon black;
(5) by case filter, by step (4), treated that powdered carbon black is isolated from carbon black smoke, the powdery isolated
Carbon black is sent to burgy tank, is granulated by airtight valve, auger to pelletizer, wet carbon black particle is made, remaining tail gas is sent by blower
To boiler combustion;
(6) wet carbon black particle exchanges heat in drying machine with dry gas, obtains dry carbon black particle, passes through elevator
It is delivered to product storage tank, is packaged to be finished product.
Anionic surfactant is the fluorocarbon surfactant of DuPont Corporation's manufacture, model in the step (1)
Are as follows: Zonyl FS-610, specification are as follows: containing 22% fluorinated surfactant, 78% water, performance are as follows: improve product viscosity and stablize
Property.
Cation dispersing agent is the model that Dutch chemicals Tuo Na chemical company, enterprise manufactures in the step (2)
The dispersing agent of FD400, specification are as follows: active constituent content 99.5%, moisture content 0.5%, performance are as follows: accelerate carbon black dispersion.
The chilled water (chw) is two chilled water (chw)s.
This method is the improvement on conventional base in the background technology.
Embodiment 5
A kind of production method of cable screen material conductive black, comprising the following steps:
(1) by anionic surfactant 50kg investment 1000L batch tank in, add 800L water, be passed through compressed air into
Row stirring 10min, is uniformly mixed, obtains aqueous solution of anionic surfactant, spare;
(2) cation dispersing agent 50kg is put into the batch tank of another 1000L, added with 800L kerosene, is stirred with stirring rod
10min is mixed, is uniformly mixed, obtains cation dispersing agent organic solution, it is spare;
(3) use metering pump by aqueous solution of anionic surfactant and cation dispersing agent organic solution respectively with 30L/
The flow velocity of h and 60L/h is added in mixer and is mixed with chilled water (chw);
(4) aqueous solution of anionic surfactant, cation dispersing agent organic solution and chilled water (chw) are mixed by mixer
After closing uniformly, mixed solution is atomized by atomizer, and the mixed solution drop after atomization sprays into the charcoal black smoke containing hydrocarbon black powder
It in gas, comes into full contact with, heat in the mixed solution drop absorption carbon black smoke after atomization, steams with the carbon black smoke containing hydrocarbon black powder
Enter in carbon black smoke after hair, so that anionic surfactant coats the particle surface of powdered carbon black, uniformly adheres to
In the particle surface of powdered carbon black, cation dispersing agent is dispersed between the particle of powdered carbon black;
(5) by case filter, by step (4), treated that powdered carbon black is isolated from carbon black smoke, the powdery isolated
Carbon black is sent to burgy tank, is granulated by airtight valve, auger to pelletizer, wet carbon black particle is made, remaining tail gas is sent by blower
To boiler combustion;
(6) wet carbon black particle exchanges heat in drying machine with dry gas, obtains dry carbon black particle, passes through elevator
It is delivered to product storage tank, is packaged to be finished product.
Anionic surfactant is the fluorocarbon surfactant of DuPont Corporation's manufacture, model in the step (1)
Are as follows: Zonyl FS-610, specification are as follows: containing 22% fluorinated surfactant, 78% water, performance are as follows: improve product viscosity and stablize
Property.
Cation dispersing agent is the perfluorinated cation table that ancient cooking vessel High Seience Technology Co., Ltd. in Wuhan manufactures in the step (2)
Face activating agent, model are as follows: FC-911, specification are as follows: active constituent content 99%, moisture content 1%, performance are as follows: accelerate carbon black
Dispersion.
The chilled water (chw) is two chilled water (chw)s.
This method is the improvement on conventional base in the background technology.
Experimental example 1
The powdery of aqueous solution of anionic surfactant Yu cation dispersing agent organic solution is not added in Example 1-5
Carbon black sample analyzes volatile content.
Dry carbon black particle, analyzes pH value, toluene light transmittance and the fugitive constituent of carbon black particle, root in Example 1-5
The surface functional group of carbon black, surface Residual oil and surface-active size are judged according to the data of analysis.
Carbon black pH value reaction be carbon blacksurface quantity containing acidic-group number, acidic-group include-OH ,-
COOH ,-SO3,-NO3Deng;The substance that the carbon blacksurface of fugitive constituent numerical response can volatilize, including anion surface active
Agent, cation dispersing agent;The reaction of toluene transmittance values is the complete Residual oil quantity of carbon blacksurface unreacted.
Wherein, powder sample fugitive constituent and grain sample fugitive constituent are detected according to GB/T 7047-2006, and grain sample pH is according to GB/
T3780.7-2006 is detected, and grain sample toluene light transmittance is detected according to GB/T 3780.15-2006.
Carbon black particle obtained in embodiment 1 is prepared into cable screen material, and the CABLE MATERIALS of cable screen material is dispersed
90 DEG C of degree ratio, 0 DEG C of resistivity of CABLE MATERIALS and CABLE MATERIALS resistivity are tested.
Above-mentioned cable screen material the preparation method comprises the following steps: weighing following material: ethylene-vinyl acetate copolymer 73 by mass parts
Part, 23 parts of carbon black obtained, 0.6 part of 4,4'- thiobis (6- tert-butyl -3- methylphenol), stearoylketene amine 1.4 in embodiment 1
Part, 2 parts of dual-tert-butyl dicumyl peroxide;Above-mentioned raw materials are transported to reciprocating single spiral shell by automatic weight-loss metering system
Bar is kneaded by flexibility and carries out melting mixing to material, realizes the uniform mixing of material;80 DEG C of feeding section, 130 DEG C of melt zone,
140 DEG C of fluxing zone, 160 DEG C of extruding zone, screw speed is in 200rpm/min;Uniformly mixed material is passed through into filtration, purification system
System, makes material in the molten state, 500 mesh filter screen impurity screenings;Filtered material is entered into the melt pump housing by die melt
It squeezes out, carries out underwater cutpellet;155 DEG C of head temperature, melt pressure 7-7.5MPa, 40 DEG C of underwater cutpellet temperature;By water circulating pump
Pelletizing pellet is transported to centrifugal dehydrator vibrating screen to dehydrate;Pellet passes through certainly after 50 DEG C of dry 40min will be dried
Weight formula Weighing system enters rear absorption plant, and crosslinking agent is uniformly mixed with atomizing type injection with pellet, protects subsequently into absorbing
Warm feed bin ensures the complete osmotic absorption of crosslinking agent;70 DEG C of crosslinking agent atomizations spray into, and heat preservation ensures that crosslinking agent permeates completely for 24 hours
Absorb to get.
Cable screen material dispersion degree ratio (%) is in standard GB/T/T 6030-2006 1-10 grade judgment criteria
Dispersion degree, is changed to the evaluation method of 1%-100% by the optimization of progress by 1-10 grades of evaluation side's preliminary operation, increase visual and
The precision of classification, be evaluated as in GB/T 6030-2006 dispersion grade 9-10 (dispersion quality is horizontal: rank very well) point
In the range of divergence 90%-100%, 0 DEG C of resistivity Ω of cable screen material-1With 90 DEG C of resistivity Ω of cable screen material-1According to
GB/T 12706-2002 is detected.
Experimental result is as shown in table 1:
Table 1
Project | Embodiment one | Embodiment two | Embodiment three | Example IV | Embodiment five |
Powder sample fugitive constituent % | 3.9 | 3.6 | 4.1 | 4.0 | 3.5 |
Grain sample fugitive constituent % | 3.6 | 3.2 | 3.8 | 3.7 | 3.3 |
Grain sample pH value | 7.5 | 7.2 | 6.8 | 6.5 | 7.0 |
Grain sample toluene light transmittance % | 99.5 | 99.6 | 99.4 | 99.7 | 99.8 |
Cable screen material dispersion degree ratio % | 92.43 | 96.5 | 94.21 | 97.36 | 99.92 |
0 DEG C of resistivity Ω of cable screen material-1 | 62 | 65 | 73 | 78 | 50 |
90 DEG C of resistivity Ω of cable screen material-1 | 188 | 195 | 169 | 147 | 120 |
As can be seen from Table 1, pass through a kind of production method of cable screen material conductive black of the application, charcoal obtained
Black powder sample fugitive constituent and grain sample fugitive constituent are between 3-4%, and for grain sample pH value between 6.5-7.5, grain sample toluene light transmittance is equal
> 99% adds the equal > 92% of dispersion degree ratio of cable screen material made of carbon black particle obtained in the embodiment of the present application 1,
Equal 80 Ω of < of 0 DEG C of resistivity-1, equal 200 Ω of < of 90 DEG C of resistivity-1。
A kind of production method of cable screen material conductive black of the invention changes conventional manufacturing technologies of carbon black
It makes, is generally applicable to the process that Audit For Process, steam stove method and channel process mix gas production carbon black.
Above-mentioned specific embodiment is only specific case of the invention, and scope of patent protection of the invention includes but is not limited to
The product form and style of above-mentioned specific embodiment, any claims of the present invention and any technical field of meeting
The appropriate changes or modifications that those of ordinary skill does it, all shall fall within the protection scope of the present invention.
Claims (9)
1. a kind of production method of cable screen material conductive black, it is characterised in that: the following steps are included:
(1) anionic surfactant is put into batch tank, adds water, be passed through compressed air and be stirred to being uniformly mixed, obtain
Aqueous solution of anionic surfactant, it is spare;
(2) cation dispersing agent is put into another batch tank, added with solvent, is stirred with stirring rod to being uniformly mixed, obtained positive
Ionic dispersants organic solution, it is spare;
(3) use metering pump by aqueous solution of anionic surfactant and cation dispersing agent organic solution respectively with 10-40L/h
It is added in mixer with the flow velocity of 10-100L/h and is mixed with chilled water (chw);
(4) aqueous solution of anionic surfactant, cation dispersing agent organic solution and chilled water (chw) are mixed by mixer equal
After even, mixed solution is atomized by atomizer, and the mixed solution drop after atomization sprays into the carbon black smoke containing hydrocarbon black powder,
It is come into full contact with the carbon black smoke containing hydrocarbon black powder, heat in the mixed solution drop absorption carbon black smoke after atomization, after evaporation
Into in carbon black smoke, so that anionic surfactant coats the particle surface of powdered carbon black, it is evenly affixed to powder
The particle surface of shape carbon black, cation dispersing agent are dispersed between the particle of powdered carbon black;
(5) by case filter, by step (4), treated that powdered carbon black is isolated from carbon black smoke, the powdered carbon black isolated
It send to burgy tank, is granulated by airtight valve, auger to pelletizer, wet carbon black particle is made, remaining tail gas is sent by blower to pot
Furnace burning;
(6) wet carbon black particle exchanges heat in drying machine with dry gas, obtains dry carbon black particle, is conveyed by elevator
To product storage tank, it is packaged to be finished product.
2. a kind of production method of cable screen material conductive black according to claim 1, it is characterised in that: the urgency
Cold water is two chilled water (chw)s.
3. a kind of production method of cable screen material conductive black according to claim 1, it is characterised in that: the step
Suddenly the batch tank in (1) and step (2) is the batch tank of 1000L.
4. a kind of production method of cable screen material conductive black according to claim 1, it is characterised in that: the step
Suddenly anionic surfactant is fluoride ion surfactant in (1).
5. a kind of production method of cable screen material conductive black according to claim 1, it is characterised in that: the step
Suddenly the weight ratio of anionic surfactant and water is (1-10) in (1): 80.
6. a kind of production method of cable screen material conductive black according to claim 1, it is characterised in that: described to have
Solvent is kerosene;The weight ratio of the cation dispersing agent and organic solvent is (1-10): 64.
7. a kind of production method of cable screen material conductive black according to claim 1, it is characterised in that: the step
Suddenly the mixing time of (1) and step (2) is 8-15min.
8. a kind of production method of cable screen material conductive black according to claim 1, it is characterised in that: the yin
Ionic surface active agent is fluoride ion surfactant.
9. a kind of production method of cable screen material conductive black according to claim 1, it is characterised in that: the sun
The macromolecule point that ionic dispersants are the model synde 141 that Zhuhai elder generation moral new material science and technology limited Company is manufactured
Powder, or the dispersing agent of the model FD400 for the manufacturing of Dutch Tuo Na chemical company, chemicals enterprise, or it is high for Wuhan ancient cooking vessel
The perfluorinated cation surfactant for the model FC-911 that Science and Technology Ltd. manufactures.