CN110373036A - A kind of seal rubber frame and preparation method and the quickly dismantled power distribution cabinet with it - Google Patents
A kind of seal rubber frame and preparation method and the quickly dismantled power distribution cabinet with it Download PDFInfo
- Publication number
- CN110373036A CN110373036A CN201910633156.6A CN201910633156A CN110373036A CN 110373036 A CN110373036 A CN 110373036A CN 201910633156 A CN201910633156 A CN 201910633156A CN 110373036 A CN110373036 A CN 110373036A
- Authority
- CN
- China
- Prior art keywords
- parts
- hole
- pedestal
- seal rubber
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to a kind of seal rubber frame and preparation method and with its quickly dismantled power distribution cabinet；Including pedestal, the rear surface of pedestal is equipped with back plate, and pedestal both ends are equipped with side plate, and wherein the side plate of one end is connected by hinge with cabinet door, and base bottom is surrounded by support damping device, and top plate is equipped at the top of back plate and side plate, is installed with seal rubber frame on the inside of cabinet door；Board ends, top and bottom are respectively equipped with several card columns afterwards；Several card slots are equidistantly offered on the inside of the both ends of pedestal and top plate, pedestal and top plate both ends offer the first through hole across card slot respectively；The first card hole of pedestal and top plate inside back；Side plate top and bottom are respectively equipped with fixture block, and fixture block side offers the second through-hole；Side plate interior sides rear portion is equipped with the second card hole；Have the advantages that simple structure and reasonable design, to can be realized good damping effect and sealing effect when being rapidly assembled and disassembled, using good and power distribution cabinet internal unit service life can be significantly improved.
Description
Technical field
The invention belongs to power distribution cabinet technical fields, and in particular to a kind of seal rubber frame and preparation method and with the fast of its
Fast reassembling type power distribution cabinet.
Background technique
Power distribution cabinet (case) sub-power power distribution cabinet (case) and light distribution cabinet (case), metering cabinet (case), are the ends of distribution system
Grade equipment；Power distribution cabinet is the general designation of motor control center, and power distribution cabinet is used in the occasion that load is more dispersed, circuit is less；
The occasion that motor control center concentrates for load, circuit is more.Their electric energy a certain circuit of upper level controller switching equipment
Nearest load is distributed to, this grade of equipment reply load provides protection, monitoring and control.
Existing power distribution cabinet is typically all the integral type being completed by various screws, when being transported, volume
Larger, transport is inconvenient, and very complicated when being mounted and dismounted, some can not even be dismantled, and comes to using with conveyer belt
Certain difficulty.
Summary of the invention
The object of the invention is that providing a kind of simple structure and reasonable design, Neng Goushi to solve the above-mentioned problems
Good damping effect and sealing effect good feature when being now rapidly assembled and disassembled, using can be significantly improved inside power distribution cabinet and set
The seal rubber frame and preparation method of standby service life and the quickly dismantled power distribution cabinet with it.
The present invention through the following technical solutions to achieve the above objectives:
(1) a kind of seal rubber frame, is made of the raw material of following parts by weight: waste plastic crushed particles 100-120
Part, 30-40 parts of ethylene propylene diene rubber, 8-10 parts of zinc oxide, 1.5-2 parts of citrate, 10-20 parts of mica powder, 1-6 parts of paraffin,
Calcium soap or 2-4 parts of zinc soap, 2-3 parts of sulphur, 26-34 parts of paraffin oil, 15-20 parts of calcium carbonate, 1-1.6 parts of sodium tripolyphosphate, fragrance
0.7-1.6 parts of amine, 1-4 parts of dibenzoyl peroxide, 4-6 parts of terpene resin, 15-30 parts of zinc borate, 10-15 parts of phosphate and a-
0.3-0.4 parts of tocopherol.
(2) a kind of seal rubber frame, is made of the raw material of following parts by weight: 105 parts of waste plastic crushed particles, three
40 parts of first EP rubbers, 9 parts of zinc oxide, 1.8 parts of citrate, 18 parts of mica powder, 1 part of paraffin, calcium soap or 3 parts of zinc soap, sulphur 3
Part, 28 parts of paraffin oil, 16 parts of calcium carbonate, 1.2 parts of sodium tripolyphosphate, 1 part of aromatic amine, 3 parts of dibenzoyl peroxide, terpene resin
4 parts, 16 parts of zinc borate, 11 parts of phosphate and 0.3 part of a- tocopherol.
(3) a kind of seal rubber frame, is made of the raw material of following parts by weight: 120 parts of waste plastic crushed particles, three
31 parts of first EP rubbers, 10 parts of zinc oxide, 2 parts of citrate, 12 parts of mica powder, 5 parts of paraffin, calcium soap or 2 parts of zinc soap, sulphur 2
Part, 33 parts of paraffin oil, 15 parts of calcium carbonate, 1.5 parts of sodium tripolyphosphate, 1.3 parts of aromatic amine, 2 parts of dibenzoyl peroxide, terpenes tree
6 parts of rouge, 26 parts of zinc borate, 15 parts of phosphate and 0.4 part of a- tocopherol.
(4) a kind of seal rubber frame, is made of the raw material of following parts by weight: 115 parts of waste plastic crushed particles, three
33 parts of first EP rubbers, 8 parts of zinc oxide, 1.5 parts of citrate, 14 parts of mica powder, 3 parts of paraffin, calcium soap or 4 parts of zinc soap, sulphur 2
Part, 30 parts of paraffin oil, 19 parts of calcium carbonate, 1 part of sodium tripolyphosphate, 0.8 part of aromatic amine, 3 parts of dibenzoyl peroxide, terpene resin
5 parts, 20 parts of zinc borate, 13 parts of phosphate and 0.36 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Calcium soap or zinc soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, boric acid
Zinc, phosphate and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
High-speed stirring is added in wax, calcium soap or zinc soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol
It mixes in device and mixes, stirred 30 minutes in the environment of 80 DEG C, obtain mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
The rear surface of a kind of quickly dismantled power distribution cabinet, including pedestal, the pedestal is equipped with back plate, and the both ends of pedestal are equipped with
Side plate, wherein the side plate of one end is connected by hinge with cabinet door, and the bottom of pedestal is surrounded by support damping device, back plate and side
The top of plate is equipped with top plate, is installed with above-mentioned (one)-(four) described in any item seal rubber frames on the inside of the cabinet door；It is described
Board ends, top and bottom are respectively equipped with several card columns afterwards；If equidistantly being offered on the inside of the both ends of the pedestal and top plate
The both ends of dry card slot, pedestal and top plate offer the first through hole across card slot respectively；The inside back of pedestal and top plate is set
There is the first card hole compatible with card column；The top and bottom of the side plate are respectively equipped with several cards compatible with card slot
Block, the side of several fixture blocks offer the second through-hole on position corresponding with first through hole；The rear portion of the side plate interior sides
Position corresponding with card column is equipped with the second card hole；Fixed mechanism is coated in the first through hole and the second through-hole.
Preferably, the support damping device includes that the top of fixed disk and the bottom of pedestal are fixedly linked, fixed disk
Bottom is connected with support column, and the lower part of support column is sleeved in support plate, between the bottom of support column and the interior bottom of support plate
Equipped with shock-absorbing spring.
It preferably, is welding between the top of the fixed disk and the bottom of pedestal, the bottom of fixed disk and support column
It is threaded connection between top.
Preferably, the fixed mechanism includes fixed column, and the both ends of fixed column offer threaded hole respectively, inside threaded hole
It is bolted with standing screw；The outboard end of standing screw is equipped with the disk of integral structure.
Preferably, the diameter of the fixed column is adapted with the diameter of first through hole and the second through-hole, first through hole and
The diameter of two through-holes is consistent, and the diameter of disk is greater than the diameter of first through hole and the second through-hole.
The present invention has simple structure and reasonable design, can be realized when being rapidly assembled and disassembled, using good damping effect and
Sealing effect is good and the advantages of capable of significantly improving power distribution cabinet internal unit service life.
Detailed description of the invention
Fig. 1 is the structural diagram of the present invention.
Fig. 2 is back plate structure schematic diagram of the invention.
Fig. 3 is schematic diagram of base structure of the invention.
Fig. 4 is lateral plate structure schematic diagram of the invention.
Fig. 5 is cabinet door structure schematic diagram of the invention.
Fig. 6 is support damping device structural schematic diagram of the invention.
Fig. 7 is fixed mechanism structural schematic diagram of the invention.
Specific embodiment
For a clearer understanding of the technical characteristics, objects and effects of the present invention, this hair of Detailed description of the invention is now compareed
Bright specific embodiment, identical label indicates identical component in the various figures.To make simplified form, in each figure only schematically
Ground indicates part relevant to invention, they do not represent its practical structures as product.
The present invention is a kind of seal rubber frame and preparation method and the quickly dismantled power distribution cabinet with it, wherein sealing rubber
Glue frame 8 includes:
(1) a kind of seal rubber frame, is made of the raw material of following parts by weight: waste plastic crushed particles 100-120
Part, 30-40 parts of ethylene propylene diene rubber, 8-10 parts of zinc oxide, 1.5-2 parts of citrate, 10-20 parts of mica powder, 1-6 parts of paraffin,
Calcium soap or 2-4 parts of zinc soap, 2-3 parts of sulphur, 26-34 parts of paraffin oil, 15-20 parts of calcium carbonate, 1-1.6 parts of sodium tripolyphosphate, fragrance
0.7-1.6 parts of amine, 1-4 parts of dibenzoyl peroxide, 4-6 parts of terpene resin, 15-30 parts of zinc borate, 10-15 parts of phosphate and a-
0.3-0.4 parts of tocopherol.
(2) a kind of seal rubber frame, is made of the raw material of following parts by weight: 105 parts of waste plastic crushed particles, three
40 parts of first EP rubbers, 9 parts of zinc oxide, 1.8 parts of citrate, 18 parts of mica powder, 1 part of paraffin, calcium soap or 3 parts of zinc soap, sulphur 3
Part, 28 parts of paraffin oil, 16 parts of calcium carbonate, 1.2 parts of sodium tripolyphosphate, 1 part of aromatic amine, 3 parts of dibenzoyl peroxide, terpene resin
4 parts, 16 parts of zinc borate, 11 parts of phosphate and 0.3 part of a- tocopherol.
(3) a kind of seal rubber frame, is made of the raw material of following parts by weight: 120 parts of waste plastic crushed particles, three
31 parts of first EP rubbers, 10 parts of zinc oxide, 2 parts of citrate, 12 parts of mica powder, 5 parts of paraffin, calcium soap or 2 parts of zinc soap, sulphur 2
Part, 33 parts of paraffin oil, 15 parts of calcium carbonate, 1.5 parts of sodium tripolyphosphate, 1.3 parts of aromatic amine, 2 parts of dibenzoyl peroxide, terpenes tree
6 parts of rouge, 26 parts of zinc borate, 15 parts of phosphate and 0.4 part of a- tocopherol.
(4) a kind of seal rubber frame, is made of the raw material of following parts by weight: 115 parts of waste plastic crushed particles, three
33 parts of first EP rubbers, 8 parts of zinc oxide, 1.5 parts of citrate, 14 parts of mica powder, 3 parts of paraffin, calcium soap or 4 parts of zinc soap, sulphur 2
Part, 30 parts of paraffin oil, 19 parts of calcium carbonate, 1 part of sodium tripolyphosphate, 0.8 part of aromatic amine, 3 parts of dibenzoyl peroxide, terpene resin
5 parts, 20 parts of zinc borate, 13 parts of phosphate and 0.36 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Calcium soap or zinc soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, boric acid
Zinc, phosphate and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
High-speed stirring is added in wax, calcium soap or zinc soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol
It mixes in device and mixes, stirred 30 minutes in the environment of 80 DEG C, obtain mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
As shown in figs. 1-7, the rear surface of a kind of quickly dismantled power distribution cabinet, including pedestal 1, the pedestal 1 is equipped with back plate
15, the both ends of pedestal 1 are equipped with side plate 4, and wherein the side plate 4 of one end is connected by hinge 5 with cabinet door 6, and the bottom surrounding of pedestal 1 is set
Have and support damping device 3, the top of back plate 15 and side plate 4 is equipped with top plate 7, and the inside of the cabinet door 6 is installed with above-mentioned (one)-
(4) described in any item seal rubber frames 8；15 both ends of back plate, top and bottom are respectively equipped with several card columns 16；
Equidistantly offer several card slots 9 on the inside of the both ends of the pedestal 1 and top plate 7, the both ends of pedestal 1 and top plate 7 offer respectively
Across the first through hole 10 of card slot 9；The inside back of pedestal 1 and top plate 7 is equipped with first card hole 11 compatible with card column 16；Institute
The top and bottom for stating side plate 4 are respectively equipped with several fixture blocks 13 compatible with card slot 9, and the side of several fixture blocks 13 is opened
Position corresponding with first through hole 10 is equipped with the second through-hole 14；The rear portion of 4 inside of side plate is corresponding with card column 16
Position is equipped with the second card hole 12；Fixed mechanism 2 is coated in the first through hole 10 and the second through-hole 14.The support damping
Device 3 includes that the top of fixed disk 21 and the bottom of pedestal 1 are fixedly linked, and the bottom of fixed disk 21 is connected with support column 23, branch
The lower part of dagger 23 is sleeved in support plate 22, and shock-absorbing spring is equipped between the bottom of support column 23 and the interior bottom of support plate 22
17.Be welding between the top of the fixed disk 21 and the bottom of pedestal 1, the top of the bottom of fixed disk 21 and support column 23 it
Between for be threadedly coupled.The fixed mechanism 2 includes fixed column 18, and the both ends of fixed column 18 offer threaded hole 19, screw thread respectively
Standing screw 20 is bolted with inside hole 19；The outboard end of standing screw 20 is equipped with the disk 24 of integral structure.The fixed column
18 diameter is adapted with the diameter of first through hole 10 and the second through-hole 14, the diameter one of first through hole 10 and the second through-hole 14
It causes, the diameter of disk 24 is greater than the diameter of first through hole 10 and the second through-hole 14.
The present invention, which can be realized, to be rapidly assembled and disassembled, and can be easy to use and be transported, and when installing the present invention, will be propped up
Dagger 23 is threadably secured with the bottom of fixed disk 21 and connect, and shock-absorbing spring 17 is equipped between support column 23 and support plate 22,
Preferably, support plate 22 is the tube structure of top and bottom opening, and the lower part of support column 23 is sleeved in the tube structure of top,
The bottom opening of support plate 22 is bolted with closure plate, and closure plate can adjust the height of support plate 22, while its top can be vibration damping
Spring 17 provides limit；The bottom of support column 23 is equipped with convex portion, and it is top that the diameter of convex portion, which is greater than support plate 22,
The diameter of opening, to achieve the purpose that limit.Above structure can not only play cushioning effect for power distribution cabinet, and conveniently tear open
Dress；When supporting damping device 3 after the installation is completed, the card column 16 of 15 bottom of back plate is installed on to first card hole 11 at 1 top of pedestal
Interior, the card column 16 at 15 both ends of back plate is installed on respectively in the second card hole 12 of corresponding side plate 4, then by 4 bottom of two sides side plate
Fixture block 13 be connected in the card slot 9 of pedestal 1, fixture block in the first through hole 10 in the card slot 9 of pedestal 1 and the side plate 4 at this time
The second through-hole 14 in 13 is overlapped, and is installed on first through hole 10 by fixed mechanism 2 and the second through-hole 14 is fixed；When after
Plate 15 and the side plate of two sides 4 install top plate 7 after fixing with pedestal 1, and the card column 16 on 15 top of back plate is installed on
In first card hole 11 of 7 lower surface inside back of top plate, and the fixture block 13 on 4 top of the side plate of two sides is connected to 7 both ends of top plate
In the card slot 9 of inside, the second through-hole 14 in the first through hole 10 in the card slot 9 of top plate 7 and the side plate 4 in fixture block 13 at this time
It is overlapped, and first through hole 10 is installed on and the second through-hole 14 is fixed by fixed mechanism 2；Fixed mechanism 2 includes fixed column
18, the outer diameter of fixed column 18 is adapted with the internal diameter of first through hole 10, the internal diameter phase of the first through hole 10 and the second through-hole 14
Together, fixed column 18 is inserted into the inside of first through hole 10 and the second through-hole 14, and standing screw 20 is screwed onto 18 liang of fixed column respectively
In the threaded hole 19 at end, the outboard end of standing screw 20 is equipped with the disk 24 of integral structure, and the outer diameter of disk 24 is greater than first
The internal diameter of through-hole 10, when standing screw 20 screws the outside that rear disk 24 is fitted in above-mentioned first through hole 10, to reach to matching
The assembly of electric cabinet；When disassembly is desired, firstly, it is necessary to by disk 24 by standing screw 20 by back-outing in threaded hole 19, and will
Fixed column 18 is extracted out by first through hole 10 and the second through-hole 14, secondly, can successively dismantle by manually after hours when above-mentioned
Top plate 7, side plate 4 and back plate 15, above-mentioned disassembly process are to extract card column 16 by corresponding card hole；Finally, can
According to the actual situation by support column 23 by the bottom of fixed disk 21 carry out disassembly can (disassembly is to rotate support column 23, by
The bottom of fixed disk 21 screws out)；Can be realized being rapidly assembled and disassembled for power distribution cabinet by above structure, be readily transported with
And it uses.It can be avoided the equipment in power distribution cabinet because vibration was influenced using the longevity by the way that stabilized equipment support damping device 3 is arranged
Life；Seal rubber frame 8 is also used in the present invention, since seal rubber frame 8 has good hardness, tensile strength and fracture to stretch
The correlated performances such as long rate can effectively prevent rainwater and dust to enter, so that the overall sealing performance of power distribution cabinet is improved, into
It can be improved to one step the service life of each component in power distribution cabinet.
In order to more clearly explain the present invention, it is further described now in conjunction with specific embodiment.It is specific real
Under applying for example:
Embodiment one
A kind of seal rubber frame, is made of the raw material of following parts by weight: 100 parts of waste plastic crushed particles, ternary second
Third 30 parts of rubber, 8 parts of zinc oxide, 1.5 parts of citrate, 10 parts of mica powder, 1 part of paraffin, 2 parts of calcium soap, 2 parts of sulphur, paraffin oil
26 parts, 15 parts of calcium carbonate, 1 part of sodium tripolyphosphate, 0.7 part of aromatic amine, 1 part of dibenzoyl peroxide, 4 parts of terpene resin, boric acid
15 parts of zinc, 10 parts of phosphate and 0.3 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Calcium soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, zinc borate, phosphoric acid
Ester and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
Wax, calcium soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol are added in high speed agitator
Mixing, stirs 30 minutes in the environment of 80 DEG C, obtains mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
A kind of quickly dismantled power distribution cabinet, including pedestal 1, the rear surface of the pedestal 1 are equipped with back plate 15, and the two of pedestal 1
End is equipped with side plate 4, and wherein the side plate 4 of one end is connected by hinge 5 with cabinet door 6, and the bottom of pedestal 1 is surrounded by support damping dress
Set 3, the top of back plate 15 and side plate 4 is equipped with top plate 7, and the inside of the cabinet door 6 is installed with above-mentioned seal rubber frame 8；After described
15 both ends of plate, top and bottom are respectively equipped with several card columns 16；It is equidistantly opened up on the inside of the both ends of the pedestal 1 and top plate 7
There are several card slots 9, the both ends of pedestal 1 and top plate 7 offer the first through hole 10 across card slot 9 respectively；Pedestal 1 and top plate 7
Inside back be equipped with first card hole 11 compatible with card column 16；The top and bottom of the side plate 4 are respectively equipped with and block
Several the compatible fixture blocks 13 of slot 9, the side of several fixture blocks 13 open position corresponding with first through hole 10 and are equipped with the
Two through-holes 14；The rear portion position corresponding with card column 16 of 4 inside of side plate is equipped with the second card hole 12；The first through hole
10 and second are coated with fixed mechanism 2 in through-hole 14.The support damping device 3 includes top and the pedestal 1 of fixed disk 21
Bottom is fixedly linked, and the bottom of fixed disk 21 is connected with support column 23, and the lower part of support column 23 is sleeved in support plate 22, support
Shock-absorbing spring 17 is equipped between the bottom of column 23 and the interior bottom of support plate 22.The top of the fixed disk 21 and the bottom of pedestal 1
It is welding between portion, is threadedly coupled between the bottom and the top of support column 23 of fixed disk 21.The fixed mechanism 2 includes solid
Fixed column 18, the both ends of fixed column 18 offer threaded hole 19 respectively, standing screw 20 are bolted with inside threaded hole 19；Standing screw
20 outboard end is equipped with the disk 24 of integral structure.The diameter of the fixed column 18 and first through hole 10 and the second through-hole 14
Diameter is adapted, and first through hole 10 is consistent with the diameter of the second through-hole 14, and the diameter of disk 24 is greater than first through hole 10 and second
The diameter of through-hole 14.
Embodiment two
A kind of seal rubber frame, is made of the raw material of following parts by weight: 120 parts of waste plastic crushed particles, ternary second
Third 40 parts of rubber, 10 parts of zinc oxide, 2 parts of citrate, 20 parts of mica powder, 6 parts of paraffin, 4 parts of zinc soap, 3 parts of sulphur, paraffin oil 34
Part, 20 parts of calcium carbonate, 1.6 parts of sodium tripolyphosphate, 1.6 parts of aromatic amine, 4 parts of dibenzoyl peroxide, 6 parts of terpene resin, boric acid
30 parts of zinc, 15 parts of phosphate and 0.4 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Zinc soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, zinc borate, phosphoric acid
Ester and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
Wax, zinc soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol are added in high speed agitator
Mixing, stirs 30 minutes in the environment of 80 DEG C, obtains mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
A kind of quickly dismantled power distribution cabinet, structure are consistent with the distribution cabinet in embodiment one.
Embodiment three
A kind of seal rubber frame, is made of the raw material of following parts by weight: 110 parts of waste plastic crushed particles, ternary second
Third 35 parts of rubber, 9 parts of zinc oxide, 1.75 parts of citrate, 15 parts of mica powder, 3.5 parts of paraffin, 3 parts of calcium soap, 2.5 parts of sulphur, stone
30 parts of wax oil, 17.5 parts of calcium carbonate, 1.3 parts of sodium tripolyphosphate, 1.15 parts of aromatic amine, 2.5 parts of dibenzoyl peroxide, terpenes tree
5 parts of rouge, 22.5 parts of zinc borate, 12.5 parts of phosphate and 0.35 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Calcium soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, zinc borate, phosphoric acid
Ester and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
Wax, calcium soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol are added in high speed agitator
Mixing, stirs 30 minutes in the environment of 80 DEG C, obtains mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
A kind of quickly dismantled power distribution cabinet, structure are consistent with the distribution cabinet in embodiment one.
Example IV
A kind of seal rubber frame, is made of the raw material of following parts by weight: 105 parts of waste plastic crushed particles, ternary second
Third 40 parts of rubber, 9 parts of zinc oxide, 1.8 parts of citrate, 18 parts of mica powder, 1 part of paraffin, 3 parts of zinc soap, 3 parts of sulphur, paraffin oil
28 parts, 16 parts of calcium carbonate, 1.2 parts of sodium tripolyphosphate, 1 part of aromatic amine, 3 parts of dibenzoyl peroxide, 4 parts of terpene resin, boric acid
16 parts of zinc, 11 parts of phosphate and 0.3 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Zinc soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, zinc borate, phosphoric acid
Ester and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
Wax, zinc soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol are added in high speed agitator
Mixing, stirs 30 minutes in the environment of 80 DEG C, obtains mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
A kind of quickly dismantled power distribution cabinet, including pedestal 1, the rear surface of the pedestal 1 are equipped with back plate 15, and the two of pedestal 1
End is equipped with side plate 4, and wherein the side plate 4 of one end is connected by hinge 5 with cabinet door 6, and the bottom of pedestal 1 is surrounded by support damping dress
Set 3, the top of back plate 15 and side plate 4 is equipped with top plate 7, and the inside of the cabinet door 6 is installed with above-mentioned seal rubber frame 8；After described
15 both ends of plate, top and bottom are respectively equipped with several card columns 16；It is equidistantly opened up on the inside of the both ends of the pedestal 1 and top plate 7
There are several card slots 9, the both ends of pedestal 1 and top plate 7 offer the first through hole 10 across card slot 9 respectively；Pedestal 1 and top plate 7
Inside back be equipped with first card hole 11 compatible with card column 16；The top and bottom of the side plate 4 are respectively equipped with and block
Several the compatible fixture blocks 13 of slot 9, the side of several fixture blocks 13 open position corresponding with first through hole 10 and are equipped with the
Two through-holes 14；The rear portion position corresponding with card column 16 of 4 inside of side plate is equipped with the second card hole 12；The first through hole
10 and second are coated with fixed mechanism 2 in through-hole 14.The support damping device 3 includes top and the pedestal 1 of fixed disk 21
Bottom is fixedly linked, and the bottom of fixed disk 21 is connected with support column 23, and the lower part of support column 23 is sleeved in support plate 22, support
Shock-absorbing spring 17 is equipped between the bottom of column 23 and the interior bottom of support plate 22.The top of the fixed disk 21 and the bottom of pedestal 1
It is welding between portion, is threadedly coupled between the bottom and the top of support column 23 of fixed disk 21.The fixed mechanism 2 includes solid
Fixed column 18, the both ends of fixed column 18 offer threaded hole 19 respectively, standing screw 20 are bolted with inside threaded hole 19；Standing screw
20 outboard end is equipped with the disk 24 of integral structure.The diameter of the fixed column 18 and first through hole 10 and the second through-hole 14
Diameter is adapted, and first through hole 10 is consistent with the diameter of the second through-hole 14, and the diameter of disk 24 is greater than first through hole 10 and second
The diameter of through-hole 14.
Embodiment five
A kind of seal rubber frame, is made of the raw material of following parts by weight: 105 parts of waste plastic crushed particles, ternary second
Third 40 parts of rubber, 9 parts of zinc oxide, 1.8 parts of citrate, 18 parts of mica powder, 1 part of paraffin, 3 parts of calcium soap, 3 parts of sulphur, paraffin oil
28 parts, 16 parts of calcium carbonate, 1.2 parts of sodium tripolyphosphate, 1 part of aromatic amine, 3 parts of dibenzoyl peroxide, 4 parts of terpene resin, boric acid
16 parts of zinc, 11 parts of phosphate and 0.3 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Calcium soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, zinc borate, phosphoric acid
Ester and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
Wax, calcium soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol are added in high speed agitator
Mixing, stirs 30 minutes in the environment of 80 DEG C, obtains mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
A kind of quickly dismantled power distribution cabinet, including pedestal 1, the rear surface of the pedestal 1 are equipped with back plate 15, and the two of pedestal 1
End is equipped with side plate 4, and wherein the side plate 4 of one end is connected by hinge 5 with cabinet door 6, and the bottom of pedestal 1 is surrounded by support damping dress
Set 3, the top of back plate 15 and side plate 4 is equipped with top plate 7, and the inside of the cabinet door 6 is installed with above-mentioned seal rubber frame 8；After described
15 both ends of plate, top and bottom are respectively equipped with several card columns 16；It is equidistantly opened up on the inside of the both ends of the pedestal 1 and top plate 7
There are several card slots 9, the both ends of pedestal 1 and top plate 7 offer the first through hole 10 across card slot 9 respectively；Pedestal 1 and top plate 7
Inside back be equipped with first card hole 11 compatible with card column 16；The top and bottom of the side plate 4 are respectively equipped with and block
Several the compatible fixture blocks 13 of slot 9, the side of several fixture blocks 13 open position corresponding with first through hole 10 and are equipped with the
Two through-holes 14；The rear portion position corresponding with card column 16 of 4 inside of side plate is equipped with the second card hole 12；The first through hole
10 and second are coated with fixed mechanism 2 in through-hole 14.The support damping device 3 includes top and the pedestal 1 of fixed disk 21
Bottom is fixedly linked, and the bottom of fixed disk 21 is connected with support column 23, and the lower part of support column 23 is sleeved in support plate 22, support
Shock-absorbing spring 17 is equipped between the bottom of column 23 and the interior bottom of support plate 22.The top of the fixed disk 21 and the bottom of pedestal 1
It is welding between portion, is threadedly coupled between the bottom and the top of support column 23 of fixed disk 21.The fixed mechanism 2 includes solid
Fixed column 18, the both ends of fixed column 18 offer threaded hole 19 respectively, standing screw 20 are bolted with inside threaded hole 19；Standing screw
20 outboard end is equipped with the disk 24 of integral structure.The diameter of the fixed column 18 and first through hole 10 and the second through-hole 14
Diameter is adapted, and first through hole 10 is consistent with the diameter of the second through-hole 14, and the diameter of disk 24 is greater than first through hole 10 and second
The diameter of through-hole 14.
Embodiment six
A kind of seal rubber frame, is made of the raw material of following parts by weight: 120 parts of waste plastic crushed particles, ternary second
Third 31 parts of rubber, 10 parts of zinc oxide, 2 parts of citrate, 12 parts of mica powder, 5 parts of paraffin, 2 parts of zinc soap, 2 parts of sulphur, paraffin oil 33
Part, 15 parts of calcium carbonate, 1.5 parts of sodium tripolyphosphate, 1.3 parts of aromatic amine, 2 parts of dibenzoyl peroxide, 6 parts of terpene resin, boric acid
26 parts of zinc, 15 parts of phosphate and 0.4 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Zinc soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, zinc borate, phosphoric acid
Ester and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
Wax, zinc soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol are added in high speed agitator
Mixing, stirs 30 minutes in the environment of 80 DEG C, obtains mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
A kind of quickly dismantled power distribution cabinet, including pedestal 1, the rear surface of the pedestal 1 are equipped with back plate 15, and the two of pedestal 1
End is equipped with side plate 4, and wherein the side plate 4 of one end is connected by hinge 5 with cabinet door 6, and the bottom of pedestal 1 is surrounded by support damping dress
Set 3, the top of back plate 15 and side plate 4 is equipped with top plate 7, and the inside of the cabinet door 6 is installed with above-mentioned seal rubber frame 8；After described
15 both ends of plate, top and bottom are respectively equipped with several card columns 16；It is equidistantly opened up on the inside of the both ends of the pedestal 1 and top plate 7
There are several card slots 9, the both ends of pedestal 1 and top plate 7 offer the first through hole 10 across card slot 9 respectively；Pedestal 1 and top plate 7
Inside back be equipped with first card hole 11 compatible with card column 16；The top and bottom of the side plate 4 are respectively equipped with and block
Several the compatible fixture blocks 13 of slot 9, the side of several fixture blocks 13 open position corresponding with first through hole 10 and are equipped with the
Two through-holes 14；The rear portion position corresponding with card column 16 of 4 inside of side plate is equipped with the second card hole 12；The first through hole
10 and second are coated with fixed mechanism 2 in through-hole 14.The support damping device 3 includes top and the pedestal 1 of fixed disk 21
Bottom is fixedly linked, and the bottom of fixed disk 21 is connected with support column 23, and the lower part of support column 23 is sleeved in support plate 22, support
Shock-absorbing spring 17 is equipped between the bottom of column 23 and the interior bottom of support plate 22.The top of the fixed disk 21 and the bottom of pedestal 1
It is welding between portion, is threadedly coupled between the bottom and the top of support column 23 of fixed disk 21.The fixed mechanism 2 includes solid
Fixed column 18, the both ends of fixed column 18 offer threaded hole 19 respectively, standing screw 20 are bolted with inside threaded hole 19；Standing screw
20 outboard end is equipped with the disk 24 of integral structure.The diameter of the fixed column 18 and first through hole 10 and the second through-hole 14
Diameter is adapted, and first through hole 10 is consistent with the diameter of the second through-hole 14, and the diameter of disk 24 is greater than first through hole 10 and second
The diameter of through-hole 14.
Embodiment seven
A kind of seal rubber frame, is made of the raw material of following parts by weight: 120 parts of waste plastic crushed particles, ternary second
Third 31 parts of rubber, 10 parts of zinc oxide, 2 parts of citrate, 12 parts of mica powder, 5 parts of paraffin, 2 parts of calcium soap, 2 parts of sulphur, paraffin oil 33
Part, 15 parts of calcium carbonate, 1.5 parts of sodium tripolyphosphate, 1.3 parts of aromatic amine, 2 parts of dibenzoyl peroxide, 6 parts of terpene resin, boric acid
26 parts of zinc, 15 parts of phosphate and 0.4 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Calcium soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, zinc borate, phosphoric acid
Ester and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
Wax, calcium soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol are added in high speed agitator
Mixing, stirs 30 minutes in the environment of 80 DEG C, obtains mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
A kind of quickly dismantled power distribution cabinet, including pedestal 1, the rear surface of the pedestal 1 are equipped with back plate 15, and the two of pedestal 1
End is equipped with side plate 4, and wherein the side plate 4 of one end is connected by hinge 5 with cabinet door 6, and the bottom of pedestal 1 is surrounded by support damping dress
Set 3, the top of back plate 15 and side plate 4 is equipped with top plate 7, and the inside of the cabinet door 6 is installed with above-mentioned seal rubber frame 8；After described
15 both ends of plate, top and bottom are respectively equipped with several card columns 16；It is equidistantly opened up on the inside of the both ends of the pedestal 1 and top plate 7
There are several card slots 9, the both ends of pedestal 1 and top plate 7 offer the first through hole 10 across card slot 9 respectively；Pedestal 1 and top plate 7
Inside back be equipped with first card hole 11 compatible with card column 16；The top and bottom of the side plate 4 are respectively equipped with and block
Several the compatible fixture blocks 13 of slot 9, the side of several fixture blocks 13 open position corresponding with first through hole 10 and are equipped with the
Two through-holes 14；The rear portion position corresponding with card column 16 of 4 inside of side plate is equipped with the second card hole 12；The first through hole
10 and second are coated with fixed mechanism 2 in through-hole 14.The support damping device 3 includes top and the pedestal 1 of fixed disk 21
Bottom is fixedly linked, and the bottom of fixed disk 21 is connected with support column 23, and the lower part of support column 23 is sleeved in support plate 22, support
Shock-absorbing spring 17 is equipped between the bottom of column 23 and the interior bottom of support plate 22.The top of the fixed disk 21 and the bottom of pedestal 1
It is welding between portion, is threadedly coupled between the bottom and the top of support column 23 of fixed disk 21.The fixed mechanism 2 includes solid
Fixed column 18, the both ends of fixed column 18 offer threaded hole 19 respectively, standing screw 20 are bolted with inside threaded hole 19；Standing screw
20 outboard end is equipped with the disk 24 of integral structure.The diameter of the fixed column 18 and first through hole 10 and the second through-hole 14
Diameter is adapted, and first through hole 10 is consistent with the diameter of the second through-hole 14, and the diameter of disk 24 is greater than first through hole 10 and second
The diameter of through-hole 14.
Embodiment eight
A kind of seal rubber frame, is made of the raw material of following parts by weight: 115 parts of waste plastic crushed particles, ternary second
Third 33 parts of rubber, 8 parts of zinc oxide, 1.5 parts of citrate, 14 parts of mica powder, 3 parts of paraffin, 4 parts of calcium soap, 2 parts of sulphur, paraffin oil
30 parts, 19 parts of calcium carbonate, 1 part of sodium tripolyphosphate, 0.8 part of aromatic amine, 3 parts of dibenzoyl peroxide, 5 parts of terpene resin, boric acid
20 parts of zinc, 13 parts of phosphate and 0.36 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Calcium soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, zinc borate, phosphoric acid
Ester and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
Wax, calcium soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol are added in high speed agitator
Mixing, stirs 30 minutes in the environment of 80 DEG C, obtains mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
A kind of quickly dismantled power distribution cabinet, including pedestal 1, the rear surface of the pedestal 1 are equipped with back plate 15, and the two of pedestal 1
End is equipped with side plate 4, and wherein the side plate 4 of one end is connected by hinge 5 with cabinet door 6, and the bottom of pedestal 1 is surrounded by support damping dress
Set 3, the top of back plate 15 and side plate 4 is equipped with top plate 7, and the inside of the cabinet door 6 is installed with above-mentioned seal rubber frame 8；After described
15 both ends of plate, top and bottom are respectively equipped with several card columns 16；It is equidistantly opened up on the inside of the both ends of the pedestal 1 and top plate 7
There are several card slots 9, the both ends of pedestal 1 and top plate 7 offer the first through hole 10 across card slot 9 respectively；Pedestal 1 and top plate 7
Inside back be equipped with first card hole 11 compatible with card column 16；The top and bottom of the side plate 4 are respectively equipped with and block
Several the compatible fixture blocks 13 of slot 9, the side of several fixture blocks 13 open position corresponding with first through hole 10 and are equipped with the
Two through-holes 14；The rear portion position corresponding with card column 16 of 4 inside of side plate is equipped with the second card hole 12；The first through hole
10 and second are coated with fixed mechanism 2 in through-hole 14.The support damping device 3 includes top and the pedestal 1 of fixed disk 21
Bottom is fixedly linked, and the bottom of fixed disk 21 is connected with support column 23, and the lower part of support column 23 is sleeved in support plate 22, support
Shock-absorbing spring 17 is equipped between the bottom of column 23 and the interior bottom of support plate 22.The top of the fixed disk 21 and the bottom of pedestal 1
It is welding between portion, is threadedly coupled between the bottom and the top of support column 23 of fixed disk 21.The fixed mechanism 2 includes solid
Fixed column 18, the both ends of fixed column 18 offer threaded hole 19 respectively, standing screw 20 are bolted with inside threaded hole 19；Standing screw
20 outboard end is equipped with the disk 24 of integral structure.The diameter of the fixed column 18 and first through hole 10 and the second through-hole 14
Diameter is adapted, and first through hole 10 is consistent with the diameter of the second through-hole 14, and the diameter of disk 24 is greater than first through hole 10 and second
The diameter of through-hole 14.
Embodiment nine
A kind of seal rubber frame, is made of the raw material of following parts by weight: 115 parts of waste plastic crushed particles, ternary second
Third 33 parts of rubber, 8 parts of zinc oxide, 1.5 parts of citrate, 14 parts of mica powder, 3 parts of paraffin, 4 parts of zinc soap, 2 parts of sulphur, paraffin oil
30 parts, 19 parts of calcium carbonate, 1 part of sodium tripolyphosphate, 0.8 part of aromatic amine, 3 parts of dibenzoyl peroxide, 5 parts of terpene resin, boric acid
20 parts of zinc, 13 parts of phosphate and 0.36 part of a- tocopherol.
A kind of preparation method of seal rubber frame, includes the following steps:
Step 1: weigh waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin,
Zinc soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, zinc borate, phosphoric acid
Ester and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, stone
High-speed stirring is added in wax, calcium soap or zinc soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol
It mixes in device and mixes, stirred 30 minutes in the environment of 80 DEG C, obtain mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, is stirred in the environment of 70 DEG C
It mixes 10 minutes, obtains mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3, stirs 15 in the environment of 75 DEG C
Minute, obtain mixture C；
Step 5: by the step 4 mixture C be sent into double screw extruder on extruding pelletization, 135 DEG C of extrusion temperature,
Obtain sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine, i.e.,
It can.
A kind of quickly dismantled power distribution cabinet, including pedestal 1, the rear surface of the pedestal 1 are equipped with back plate 15, and the two of pedestal 1
End is equipped with side plate 4, and wherein the side plate 4 of one end is connected by hinge 5 with cabinet door 6, and the bottom of pedestal 1 is surrounded by support damping dress
Set 3, the top of back plate 15 and side plate 4 is equipped with top plate 7, and the inside of the cabinet door 6 is installed with above-mentioned seal rubber frame 8；After described
15 both ends of plate, top and bottom are respectively equipped with several card columns 16；It is equidistantly opened up on the inside of the both ends of the pedestal 1 and top plate 7
There are several card slots 9, the both ends of pedestal 1 and top plate 7 offer the first through hole 10 across card slot 9 respectively；Pedestal 1 and top plate 7
Inside back be equipped with first card hole 11 compatible with card column 16；The top and bottom of the side plate 4 are respectively equipped with and block
Several the compatible fixture blocks 13 of slot 9, the side of several fixture blocks 13 open position corresponding with first through hole 10 and are equipped with the
Two through-holes 14；The rear portion position corresponding with card column 16 of 4 inside of side plate is equipped with the second card hole 12；The first through hole
10 and second are coated with fixed mechanism 2 in through-hole 14.The support damping device 3 includes top and the pedestal 1 of fixed disk 21
Bottom is fixedly linked, and the bottom of fixed disk 21 is connected with support column 23, and the lower part of support column 23 is sleeved in support plate 22, support
Shock-absorbing spring 17 is equipped between the bottom of column 23 and the interior bottom of support plate 22.The top of the fixed disk 21 and the bottom of pedestal 1
It is welding between portion, is threadedly coupled between the bottom and the top of support column 23 of fixed disk 21.The fixed mechanism 2 includes solid
Fixed column 18, the both ends of fixed column 18 offer threaded hole 19 respectively, standing screw 20 are bolted with inside threaded hole 19；Standing screw
20 outboard end is equipped with the disk 24 of integral structure.The diameter of the fixed column 18 and first through hole 10 and the second through-hole 14
Diameter is adapted, and first through hole 10 is consistent with the diameter of the second through-hole 14, and the diameter of disk 24 is greater than first through hole 10 and second
The diameter of through-hole 14.
Experimental example
Experimental subjects: seal rubber frame obtained by the embodiment of the present invention three is randomly selected as experimental group one, embodiment
For seal rubber frame obtained by seven as experimental group two, the seal rubber frame chosen on the market is contrast groups one and contrast groups two.
Experiment purpose: it under the same conditions, is surveyed referring to GB/T531 using the pocket hardometer penetration hardness test method of rubber
The hardness for trying seal rubber frame carries out the measurement of tensile stress-strain performance referring to GB/T528 to seal rubber frame, referring to GB/
T529 carries out the measurement of elongation at break to seal rubber frame, obtains the performance of the seal rubber of each group seal rubber frame.
As the above experimental result table it is found that the hardness of seal rubber obtained by the embodiment of the present invention be respectively 72A and
71A, and the hardness of seal rubber on the market is 63A and 61A, therefore the hardness of seal rubber obtained by the embodiment of the present invention
Be better than seal rubber on the market, the tensile strength of seal rubber obtained by the embodiment of the present invention be 15MPa and
18.5MPa, and the tensile strength of seal rubber on the market is 8.6MPa and 9.2MPa, therefore obtained by the embodiment of the present invention
The tensile strength of seal rubber is better than seal rubber on the market, and the fracture of seal rubber obtained by the embodiment of the present invention is stretched
Long rate is 450% and 480%, and the elongation at break of seal rubber on the market is 280% and 285%, therefore the present invention is real
The elongation at break for applying seal rubber obtained by example is better than seal rubber on the market, close obtained by the embodiment of the present invention
The compression set for sealing rubber is 21 and 20.2%, and the compression set of seal rubber on the market is 30 and 35.3,
Therefore the compression set of seal rubber obtained by the embodiment of the present invention is better than seal rubber on the market, therefore, this
The obtained seal rubber properties of invention are superior to the performance of seal rubber common on the market, raw material oxidation in the present invention
The performance of seal rubber can be improved in the addition of zinc, so that seal rubber has good corrosion resistance, tear resistance and elasticity, lemon
Plasticizer of the lemon acid esters as reaction, and have it is cold-resistant, fast light, have excellent water-resistance, volatility is small, it is micro- it is malicious, have fungus resistance so that
Be conducive to keep good production environment, the addition of paraffin oil can be improved rubber ageing resistance and increase flexibility, terpene resin
Addition so that seal rubber has creep resistant after preferable tack cohesive force and anti-aging.
The basic principles, main features and advantages of the invention have been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, and the above embodiments and description only describe originals of the invention
Reason, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes and improvements
It all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appending claims and equivalents circle
It is fixed.
Claims (10)
1. a kind of seal rubber frame, it is characterised in that: the seal rubber frame is made of the raw material of following parts by weight: waste plastic
100-120 parts of crushed particles, 30-40 parts of ethylene propylene diene rubber, 8-10 parts of zinc oxide, 1.5-2 parts of citrate, mica powder 10-
2-4 parts of 20 parts, 1-6 parts of paraffin, calcium soap or zinc soap, 2-3 parts of sulphur, 26-34 parts of paraffin oil, 15-20 parts of calcium carbonate, tripolyphosphate
1-1.6 parts of sodium, 0.7-1.6 parts of aromatic amine, 1-4 parts of dibenzoyl peroxide, 4-6 parts of terpene resin, 15-30 parts of zinc borate, phosphorus
10-15 parts and 0.3-0.4 parts of a- tocopherol of acid esters.
2. a kind of seal rubber frame according to claim 1, it is characterised in that: the seal rubber frame is by following parts by weight
Raw material be made: 105 parts of waste plastic crushed particles, 40 parts of ethylene propylene diene rubber, 9 parts of zinc oxide, 1.8 parts of citrate, cloud
3 parts of 18 parts of female powder, 1 part of paraffin, calcium soap or zinc soap, 3 parts of sulphur, 28 parts of paraffin oil, 16 parts of calcium carbonate, 1.2 parts of sodium tripolyphosphate,
1 part of aromatic amine, 3 parts of dibenzoyl peroxide, 4 parts of terpene resin, 16 parts of zinc borate, 11 parts of phosphate and 0.3 part of a- tocopherol.
3. a kind of seal rubber frame according to claim 1, it is characterised in that: the seal rubber frame is by following parts by weight
Raw material be made: 120 parts of waste plastic crushed particles, 31 parts of ethylene propylene diene rubber, 10 parts of zinc oxide, 2 parts of citrate, mica
2 parts of 12 parts of powder, 5 parts of paraffin, calcium soap or zinc soap, 2 parts of sulphur, 33 parts of paraffin oil, 15 parts of calcium carbonate, 1.5 parts of sodium tripolyphosphate, virtue
1.3 parts of fragrant amine, 2 parts of dibenzoyl peroxide, 6 parts of terpene resin, 26 parts of zinc borate, 15 parts of phosphate and 0.4 part of a- tocopherol.
4. a kind of seal rubber frame according to claim 1, it is characterised in that: the seal rubber frame is by following parts by weight
Raw material be made: 115 parts of waste plastic crushed particles, 33 parts of ethylene propylene diene rubber, 8 parts of zinc oxide, 1.5 parts of citrate, cloud
4 parts of 14 parts of female powder, 3 parts of paraffin, calcium soap or zinc soap, 2 parts of sulphur, 30 parts of paraffin oil, 19 parts of calcium carbonate, 1 part of sodium tripolyphosphate, virtue
0.8 part of fragrant amine, 3 parts of dibenzoyl peroxide, 5 parts of terpene resin, 20 parts of zinc borate, 13 parts of phosphate and a- tocopherol 0.36
Part.
5. a kind of preparation method of the seal rubber frame as described in claim any one of 1-4, it is characterised in that: the preparation method packet
Include following steps:
Step 1: weighing waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin, calcium soap
Or zinc soap, sulphur, paraffin oil, calcium carbonate, sodium tripolyphosphate, aromatic amine, dibenzoyl peroxide, terpene resin, zinc borate, phosphorus
Acid esters and a- tocopherol, it is spare；
Step 2: by above-mentioned waste plastic crushed particles, ethylene propylene diene rubber, zinc oxide, citrate, mica powder, paraffin, calcium
Soap or zinc soap, sulphur, paraffin oil, calcium carbonate, terpene resin, zinc borate, phosphate and a- tocopherol are added in high speed agitator
Mixing, stirs 30 minutes in the environment of 80 DEG C, obtains mixture A；
Step 3: sodium tripolyphosphate and aromatic amine being added in the mixture A in Xiang Suoshu step 2, stirs 10 in the environment of 70 DEG C
Minute, obtain mixture B；
Step 4: dibenzoyl peroxide is added in the mixture B in Xiang Suoshu step 3,15 points are stirred in the environment of 75 DEG C
Clock obtains mixture C；
Step 5: the mixture C in the step 4 being sent into extruding pelletization on double screw extruder, 135 DEG C of extrusion temperature, is obtained
Sealing strip rubber；
Step 6: after rubber described in step 5 is cooled to room temperature, seal rubber frame being cut by rubber cutting machine.
6. a kind of quickly dismantled power distribution cabinet, including pedestal (1), it is characterised in that: the rear surface of the pedestal (1) is equipped with back plate
(15), the both ends of pedestal (1) are equipped with side plate (4), and wherein the side plate (4) of one end is connected by hinge (5) with cabinet door (6), pedestal
(1) bottom, which is surrounded by, supports damping device (3), and the top of back plate (15) and side plate (4) is equipped with top plate (7), the cabinet door
(6) the described in any item seal rubber frames (8) of the claims 1-4 are installed on the inside of；
Back plate (15) both ends, top and bottom are respectively equipped with several card columns (16)；
Equidistantly offer several card slots (9) on the inside of the both ends of the pedestal (1) and top plate (7), pedestal (1) and top plate (7)
Both ends offer the first through hole (10) across card slot (9) respectively；The inside back of pedestal (1) and top plate (7) is equipped with and card column
(16) compatible first card hole (11)；
The top and bottom of the side plate (4) are respectively equipped with and card slot (9) several compatible fixture blocks (13), several cards
The side of block (13) offers the second through-hole (14) on position corresponding with first through hole (10)；On the inside of the side plate (4)
Rear portion position corresponding with card column (16) is equipped with the second card hole (12)；
Fixed mechanism (2) are coated in the first through hole (10) and the second through-hole (14).
7. a kind of quickly dismantled power distribution cabinet according to claim 6, it is characterised in that: the support damping device (3)
The bottom at top and pedestal (1) including fixed disk (21) is fixedly linked, and the bottom of fixed disk (21) is connected with support column (23),
The lower part of support column (23) is sleeved in support plate (22), is set between the bottom of support column (23) and the interior bottom of support plate (22)
There are shock-absorbing spring (17).
8. a kind of quickly dismantled power distribution cabinet according to claim 7, it is characterised in that: the top of the fixed disk (21)
It is welding between the bottom of pedestal (1), is threadedly coupled between the bottom and the top of support column (23) of fixed disk (21).
9. a kind of quickly dismantled power distribution cabinet according to claim 6, it is characterised in that: the fixed mechanism (2) includes
Fixed column (18), the both ends of fixed column (18) offer threaded hole (19) respectively, are bolted with standing screw inside threaded hole (19)
(20)；The outboard end of standing screw (20) is equipped with the disk (24) of integral structure.
10. a kind of quickly dismantled power distribution cabinet according to claim 9, it is characterised in that: outside the fixed column (18)
Diameter is adapted with the internal diameter of first through hole (10) and the second through-hole (14), the internal diameter one of first through hole (10) and the second through-hole (14)
It causes, the outer diameter of disk (24) is greater than the internal diameter of first through hole (10) and the second through-hole (14).