CN110372300B - Preparation method of fiber concrete capable of uniformly dispersing basalt fibers - Google Patents
Preparation method of fiber concrete capable of uniformly dispersing basalt fibers Download PDFInfo
- Publication number
- CN110372300B CN110372300B CN201910680493.0A CN201910680493A CN110372300B CN 110372300 B CN110372300 B CN 110372300B CN 201910680493 A CN201910680493 A CN 201910680493A CN 110372300 B CN110372300 B CN 110372300B
- Authority
- CN
- China
- Prior art keywords
- fiber
- stirring
- concentration
- concrete
- basalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a preparation method of fiber concrete for uniformly dispersing basalt fibers. The fiber dispersing agent A is composed of 1-3 g/L4-amino-1, 2-catechol hydrochloride solution and 10-12g/L trihydroxymethyl aminomethane solution; the fiber dispersing agent B consists of a sodium chloroacetate solution with the concentration of 12-15g/L, a sodium bicarbonate solution with the concentration of 3-5g/L and a dimethylformamide solution with the concentration of 15-20 g/L. And (3) putting the basalt fiber into the dispersant A, stirring for 3-5 minutes, then putting the basalt fiber into the dispersant B, and stirring for 1-3 minutes to obtain the treated basalt fiber. Firstly, mixing and stirring the weighed cementing material and the treated basalt fiber for 1-3 minutes, then adding sandstone, clear water and a polycarboxylic acid water reducing agent, and placing on a horizontal vibration table for vibration stirring for 2-5 minutes to obtain the fiber concrete with uniformly dispersed basalt fiber. The method effectively overcomes the defect that the fibers are not easy to be uniformly dispersed in the concrete.
Description
Technical Field
The invention relates to a preparation method of fiber concrete for uniformly dispersing basalt fibers, belongs to the technical field of building materials, and can effectively solve the problem of nonuniform fiber dispersion in the fiber concrete.
Background
The common concrete has the defects of low tensile/flexural strength, poor impact resistance and the like, and the application range of the concrete is limited by the defects. The addition of fibers to concrete is the primary method to solve the above problems. Compared with common concrete, the tensile strength and the flexural strength of the fiber concrete can be improved by more than 10 percent, the impact energy value can reach 5 times of that of the common concrete, and the mechanical property is obviously improved.
Although the mechanical properties of the fiber concrete are remarkably improved, the fiber concrete has the following main problems in the preparation process: the fibers are unevenly dispersed in the concrete, so that the fibers are agglomerated in the concrete, and the improvement of the mechanical property and the durability of the concrete is greatly limited.
Basalt fiber is a new fiber rapidly developed in recent years, which is a continuous fiber drawn from natural basalt. The pure natural basalt fiber is generally brown in color and has metallic luster, is a novel inorganic environment-friendly green high-performance fiber material, and consists of oxides such as silicon dioxide, aluminum oxide, calcium oxide, magnesium oxide, iron oxide, titanium dioxide and the like. The basalt continuous fiber has high strength, and also has various excellent performances of electrical insulation, corrosion resistance, high temperature resistance and the like. In addition, the production process of the basalt fiber determines that the produced waste is less, the environmental pollution is less, and the product can be directly degraded in the environment after being discarded without any harm, so the basalt fiber is an environment-friendly material. Basalt fibers are four major fibers which are mainly developed in China. However, basalt fiber still has the problem of difficult uniform dispersion when applied to concrete materials, and in order to improve the dispersibility of the fiber in concrete, researchers have proposed many methods, for example, adding a blade to a concrete stirring shaft to enhance the dispersion of the fiber during stirring, or using an ultrasonic dispersion method to disperse the fiber in water before stirring. However, the method is simple and has a limit to improve the dispersibility of the fiber in the concrete.
Therefore, in order to solve the above problems, the present invention provides a method for preparing fiber concrete in which basalt fibers are uniformly dispersed. The method simultaneously adopts a chemical method and a physical method to improve the dispersibility of the fiber in the concrete, and effectively overcomes the defect that the improvement of the fiber dispersibility by a single method is limited.
Disclosure of Invention
The technical problem to be solved by the invention is as follows: aiming at the problem that basalt fibers are not easy to disperse in concrete, the invention provides the preparation method of the fiber concrete for uniformly dispersing the basalt fibers.
The invention adopts the following technical scheme that the special fiber dispersing agent, the fiber treatment method and the fiber concrete stirring and forming method are included.
(1) Special fiber dispersants fall into two categories:
the fiber dispersing agent A is a mixed solution of 4-amino-1, 2-catechol hydrochloride and tris (hydroxymethyl) aminomethane, the concentration of the 4-amino-1, 2-catechol hydrochloride in the mixed solution is 1-3g/L, and the concentration of the tris (hydroxymethyl) aminomethane is 10-12 g/L;
the fiber dispersing agent B is a mixed solution of sodium chloroacetate, sodium bicarbonate and dimethylformamide, the concentration of the sodium chloroacetate in the mixed solution is 12-15g/L, the concentration of the sodium bicarbonate in the mixed solution is 3-5g/L, and the concentration of the dimethylformamide is 15-20 g/L.
(2) The fiber treatment method comprises two steps:
the method comprises the following steps: mixing and stirring the dispersing agent A and the metered basalt fibers together for 3-5 minutes according to the mass ratio of 3:1-5: 1; after draining the solution, adding clear water to clean the fibers, and draining the clear water;
step two: mixing and stirring the dispersant B and the basalt fiber obtained in the step (1) according to the mass ratio of 2:1-4:1 for 1-3 minutes, draining the solution, adding clear water to clean the fiber, draining the clear water, and taking the fiber out for later use.
(3) The fiber concrete stirring and forming method comprises two steps:
the method comprises the following steps: mixing and stirring the measured cement, fly ash, mineral powder and silica fume (collectively referred to as cementing materials) and the treated basalt fiber for 1-3 minutes, and then adding the sandstone, clear water and polycarboxylic acid water reducing agent;
step two: the stirring machine is placed on a horizontal vibration table, the stirring machine and the vibration table are started simultaneously, the frequency of the horizontal vibration table is 10-20Hz, the amplitude is 2-5mm, and the fiber concrete with the basalt fibers uniformly dispersed is obtained after the horizontal vibration table is vibrated and stirred for 2-3 minutes.
Compared with the prior art, the invention has the following advantages:
(1) the basalt fiber is subjected to surface modification through a fiber dispersing agent, so that the basalt fiber is not easy to bond into lumps and can be uniformly dispersed in concrete;
(2) horizontally vibrating in the stirring process, and separating the fibers which are still bonded together through the vibration effect to further disperse the fibers;
(3) compared with the traditional method, the method is simple to operate and is suitable for preparing the fiber concrete on site.
Detailed Description
In order to further embody the efficacy of the present invention, the present invention is further described in detail with reference to specific application cases.
The reference blending ratio of concrete is shown in Table 1 (unit: kg):
TABLE 1 concrete base mix ratio
In table 1, cement, silica fume, fly ash and mineral powder are collectively referred to as cementitious materials.
The material parameters are as follows:
(1) the specification of the cement is P.O.42.5;
(2) the specification of the fly ash is F class I grade;
(3) the specification of the mineral powder is S95 superfine;
(4) the specific surface area of the silica fume is 18m2(iv)/g, silica content greater than 92%;
(5) the sand grain diameter is 0.25mm-0.5 mm;
(6) the particle size of the stones is 5mm-15 mm;
(7) the type of the water reducing agent is a polycarboxylic acid water reducing agent, the solid content is 25%, and the water reducing efficiency is 45%.
The concrete mix ratios used in examples 1-3 were the reference mix ratios in Table 1.
Example 1:
(1) concentration of fiber dispersant:
concentration of fiber dispersant A: the concentration of 4-amino-1, 2-catechol hydrochloride is 1g/L, and the concentration of trihydroxymethyl aminomethane is 12g/L
Concentration of the fiber dispersant B: the concentration of sodium chloroacetate is 12g/L, the concentration of sodium bicarbonate is 4g/L, and the concentration of dimethylformamide is 20g/L
(2) The length of basalt fiber is 12mm, and the mixing amount is as follows: 5.6kg
(3) The preparation process of the fiber concrete for uniformly dispersing the basalt fibers comprises the following steps
Firstly, mixing and stirring a dispersing agent A and metered basalt fibers together for 3 minutes according to a mass ratio of 3: 1; after draining the solution, adding clear water to clean the fibers, and draining the clear water;
secondly, mixing and stirring the dispersant B and the basalt fiber obtained in the step (1) for 2 minutes according to a mass ratio of 4:1, draining the solution, adding clear water to clean the fiber, draining the clear water, and taking the fiber out for later use;
thirdly, the measured cementing material and the processed basalt fiber are mixed and stirred for 1 minute, and then other materials are added
Fourthly, the mixer is placed on a horizontal vibration table, the mixer and the vibration table are started simultaneously, the frequency of the horizontal vibration table is 10Hz, the amplitude is 5mm, the vibration and the stirring are carried out for 2 minutes, and the fiber concrete with the basalt fibers uniformly dispersed is obtained
(4) Method for testing fiber dispersion performance
Firstly, the fresh concrete is randomly placed into 10 moulds with the size of 100 multiplied by 100mm, then various raw materials of the concrete are immediately cleaned by clear water, the fiber in each test mould is obtained, and the weight of the fiber is weighed.
And testing slump of the fiber concrete, 28d compressive strength and flexural strength.
Example 2:
(1) concentration of fiber dispersant:
concentration of fiber dispersant 1: the concentration of 4-amino-1, 2-catechol hydrochloride is 3g/L, and the concentration of trihydroxymethyl aminomethane is 10g/L
Concentration of fiber dispersant 2: the concentration of sodium chloroacetate is 13g/L, the concentration of sodium bicarbonate is 3g/L, and the concentration of dimethylformamide is 15g/L
(2) The length of basalt fiber is 12mm, and the mixing amount is as follows: 8.4kg
(3) The preparation process of the fiber concrete with the basalt fibers uniformly dispersed is as follows
Firstly, mixing and stirring a dispersing agent 1 and metered basalt fibers together for 3 minutes according to a mass ratio of 5: 1; after the solution is drained, clear water with the mass 4 times that of the fiber is added to clean the fiber, and then the clear water is drained;
secondly, mixing and stirring the dispersing agent 2 and the basalt fibers obtained in the step (1) for 2 minutes according to the mass ratio of 2:1, adding clear water to clean the fibers after drying the solution, then drying the clear water, and taking the fibers out for later use;
thirdly, the measured cementing material and the processed basalt fiber are mixed and stirred for 2 minutes, and then other materials are added
Fourthly, the mixer is placed on a horizontal vibration table, the mixer and the vibration table are started simultaneously, the frequency of the horizontal vibration table is 15Hz, the amplitude is 3mm, the vibration and the stirring are carried out for 2 minutes, and the fiber concrete with the basalt fibers uniformly dispersed is obtained
(4) Method for testing fiber dispersion performance
Firstly, the fresh concrete is randomly placed into 10 moulds with the size of 100 multiplied by 100mm, then various raw materials of the concrete are immediately cleaned by clear water, the fiber in each test mould is obtained, and the weight of the fiber is weighed.
And testing slump of the fiber concrete, 28d compressive strength and flexural strength.
Example 3:
(1) concentration of fiber dispersant:
concentration of fiber dispersant 1: the concentration of 4-amino-1, 2-catechol hydrochloride is 2g/L, and the concentration of tris (hydroxymethyl) aminomethane is 11g/L
Concentration of fiber dispersant 2: the concentration of sodium chloroacetate is 15g/L, the concentration of sodium bicarbonate is 5g/L, and the concentration of dimethylformamide is 17g/L
(2) The length of basalt fiber is 12mm, and the mixing amount is as follows: 11.2kg
(3) The preparation process of the fiber concrete with the basalt fibers uniformly dispersed is as follows
Firstly, mixing and stirring a dispersing agent 1 and metered basalt fibers together for 3 minutes according to a mass ratio of 4: 1; after draining the solution, adding clear water to clean the fibers, and draining the clear water;
secondly, mixing and stirring the dispersing agent 2 and the basalt fibers obtained in the step (1) for 2 minutes according to the mass ratio of 3:1, adding clear water with the mass 5 times of that of the fibers after draining the solution to clean the fibers, draining the clear water, and taking the fibers out for later use;
thirdly, the measured cementing material and the processed basalt fiber are mixed and stirred for 3 minutes, and then other materials are added
Fourthly, the mixer is placed on a horizontal vibration table, the mixer and the vibration table are started simultaneously, the frequency of the horizontal vibration table is 20Hz, the amplitude is 2mm, the vibration and the stirring are carried out for 2 minutes, and the fiber concrete with the basalt fibers uniformly dispersed is obtained
(4) Method for testing fiber dispersion performance
Firstly, the fresh concrete is randomly placed into 10 moulds with the size of 100 multiplied by 100mm, then various raw materials of the concrete are immediately cleaned by clear water, the fiber in each test mould is obtained, and the weight of the fiber is weighed.
And testing slump of the fiber concrete, 28d compressive strength and flexural strength.
Test results
3 groups of comparison groups (serial numbers 1-3) are set, the mixing ratio of the comparison groups 1-3 is the same as the reference mixing ratio, the mixing amount of basalt is respectively 5.6kg, 8.4kg and 11.2kg, but the surface modification treatment is not carried out on the basalt fiber, a horizontal vibration table is not started in the stirring process, and other preparation and test methods are consistent with those of the invention group.
TABLE 2 test results for each group of samples
Description of the drawings: the control and invention numbers 1,2,3 represent the test results of examples 1,2, 3.
Table 2 shows the test results of the invention group and the control group. Compared with the control group, the difference between the average weight of the fibers in 10 test molds of the invention groups 1,2 and 3 and the mass of the doped basalt fibers is less than 5 percent, which shows that the dispersibility of the basalt fibers of the invention group is obviously higher than that of the control group. Slump of the invention groups 1,2 and 3 is higher than that of the comparison group, which shows that the invention group has high fiber dispersibility and better fluidity, and the comparison group has fibers agglomerated into lumps and poor fluidity; the 28d compressive strength of the invention groups 1,2 and 3 is increased by 8-10 percent compared with that of the control group, and the 28d flexural strength is increased by about 10 percent, which shows that the fiber dispersion of the invention groups is more uniform, and the mechanical strength of the concrete needs to be obviously improved.
The results in table 2 show that the basalt fibers of the invention group are uniformly dispersed compared to the control group.
Claims (2)
1. The preparation method of the fiber concrete for uniformly dispersing the basalt fibers is characterized by comprising a special fiber dispersing agent, a fiber treatment method and a fiber concrete stirring and forming method:
(1) the special fiber dispersing agent is specifically as follows:
(2) the fiber treatment method specifically comprises the following steps:
(3) the method for stirring and forming the fiber concrete comprises the following steps:
2. The method for stirring and forming fiber concrete according to claim 1, wherein the horizontal vibration table has a vibration frequency of 10 to 20Hz and an amplitude of 2 to 5 mm.