CN110370834A - A kind of heat transfer colour ribbon and preparation method thereof - Google Patents
A kind of heat transfer colour ribbon and preparation method thereof Download PDFInfo
- Publication number
- CN110370834A CN110370834A CN201910184460.7A CN201910184460A CN110370834A CN 110370834 A CN110370834 A CN 110370834A CN 201910184460 A CN201910184460 A CN 201910184460A CN 110370834 A CN110370834 A CN 110370834A
- Authority
- CN
- China
- Prior art keywords
- substrate
- coating
- heat transfer
- ink layer
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of heat transfer colour ribbon and preparation method thereof, and the colour band is applied to the back coating of substrate two sides by substrate and respectively and ink layer is constituted, and preparation method uses coating process.A kind of heat transfer colour ribbon and preparation method thereof that the present invention mentions, it is simple using raw material, from a wealth of sources, and meet low-carbon, environmental protection concept, facilitate the extension that colour band uses field.
Description
Technical field
The present invention relates to thermal transfer consumptive material technical fields more particularly to a kind of heat transfer colour ribbon and preparation method thereof.
Background technique
Thermal transfer printing is exactly that ink is transferred to the process of paper or film with heat and pressure from colour band medium, when label is logical
When crossing the print head and last item of printer, ink is transferred on label.
Thermal transfer technology is exactly to utilize special colour band, will be on colour band through the working principle of similar facsimile machine print head
Carbon dust coating by heating mode, be transferred in paper or other kinds of material, since the coated substance on colour band can
To select as needed, stronger adhesive force is generated, in addition the selection of print media, more can guarantee the writing printed not
By external influence.And the process of this heating, how to heat, then can give computer to control, at present due to having opened
The various softwares for being specifically used to print label are issued, so, for the user, can say it is very convenient.
Colour band used at present can discharge a large amount of toxic organic substances, these objects during the preparation process in thermal transfer industry
Matter not only pollutes environment, damages human health, and there is fire hazard in the production, transportation and storage process.It is environmentally friendly, low toxicity
Colour band by be thermal transfer industry developing direction.
Summary of the invention
A series of concept of reduced forms is introduced in Summary, this will in the detailed description section into
One step is described in detail.Summary of the invention is not meant to attempt to limit technical solution claimed
Key feature and essential features do not mean that the protection scope for attempting to determine technical solution claimed more.
At least to be partially solved the above problem, the invention discloses a kind of heat transfer colour ribbons, are applied to by substrate and respectively
The back coating and ink layer of substrate two sides are constituted, and the substrate is PET film, primary raw material in the ink layer are as follows: resin, coloring
Agent, wax and auxiliary agent, the primary raw material of the back coating are wax, and the ratio of resin and wax is 1.5:1~5:1 in the ink layer,
The mass fraction of wax in the back coating is 10~15%.
A kind of preparation method of heat transfer colour ribbon, comprising the following steps:
1. being coated with ink layer, 2.5~3g/m of coating weight in the side of substrate2, drying, into subsequent processing;
2. being coated with back coating, 3.5~5.5g/m of coating weight in the other side of substrate2, dry to get colour band.
A kind of heat transfer colour ribbon and preparation method thereof that the present invention mentions, it is simple using raw material, from a wealth of sources, and meet
Low-carbon, environmental protection concept facilitate the extension that colour band uses field.
Specific embodiment
In the following description, a large amount of concrete details are given so as to provide a more thorough understanding of the present invention.So
And it will be apparent to one skilled in the art that embodiment of the present invention may not need it is one or more of these thin
It saves and is carried out.In other examples, in order to avoid obscuring with embodiment of the present invention, for well known in the art
Some technical characteristics are not described.
In order to thoroughly understand embodiment of the present invention, detailed structure will be proposed in following description.Obviously, of the invention
The execution of embodiment is not limited to the specific details that those skilled in the art is familiar with.
The present invention provides a kind of heat transfer colour ribbons, are applied to the back coating and ink layer structure of substrate two sides by substrate and respectively
At the substrate is PET film, primary raw material in the ink layer are as follows: resin, colorant, wax and auxiliary agent, the master of the back coating
Wanting raw material is wax, and the ratio of resin and wax is 1.5:1~5:1, the mass fraction of the wax in the back coating in the ink layer
It is 10~15%.
A kind of preparation method of heat transfer colour ribbon, comprising the following steps:
1. being coated with ink layer, 2.5~3g/m of coating weight in the side of substrate2, drying, into subsequent processing;
2. being coated with back coating, 3.5~5.5g/m of coating weight in the other side of substrate2, dry to get colour band.
Embodiment 1
Base band used in the present invention is PET film, in the steps below applying layers, and heat transfer printing carbon tape is finally made.
1) ink layer
After the raw material of following each weight proportions is mixed, the face room temperature with coating machine in above-mentioned substrate is coated with, coating weight
2.5g/m2, drying forms ink layer after coating, into subsequent processing;
Ink layer composition:
15 parts by weight of resin;
10 parts by weight of wax;
12 parts by weight of colorant;
2 parts by weight of auxiliary agent.
2) back coating
After the raw material of following each weight proportions is mixed, the surface room temperature with coating machine in above-mentioned substrate is coated with, coating weight
For 3.5g/m2, drying forms back coating to get colour band after coating;
Back coating constituent:
10 parts by weight of wax.
Embodiment 2
Base band used in the present invention is PET film, in the steps below applying layers, and heat transfer printing carbon tape is finally made.
1) ink layer
After the raw material of following each weight proportions is mixed, the face room temperature with coating machine in above-mentioned substrate is coated with, coating weight
3g/m2, drying forms ink layer after coating, into subsequent processing;
Ink layer composition:
50 parts by weight of resin;
10 parts by weight of wax;
21 parts by weight of colorant;
3 parts by weight of auxiliary agent.
2) back coating
After the raw material of following each weight proportions is mixed, the surface room temperature with coating machine in above-mentioned substrate is coated with, coating weight
For 5.5g/m2, drying forms back coating to get colour band after coating;
Back coating constituent:
15 parts by weight of wax.
Embodiment 3
Base band used in the present invention is PET film, in the steps below applying layers, and heat transfer printing carbon tape is finally made.
1) ink layer
After the raw material of following each weight proportions is mixed, the face room temperature with coating machine in above-mentioned substrate is coated with, coating weight
2.8g/m2, drying forms ink layer after coating, into subsequent processing;
Ink layer composition:
40 parts by weight of resin;
10 parts by weight of wax;
18 parts by weight of colorant;
3 parts by weight of auxiliary agent.
2) back coating
After the raw material of following each weight proportions is mixed, the surface room temperature with coating machine in above-mentioned substrate is coated with, coating weight
For 4g/m2, drying forms back coating to get colour band after coating;
Back coating constituent:
13 parts by weight of wax.
It is simple using raw material, source is wide in conclusion a kind of heat transfer colour ribbon and preparation method thereof that the present invention mentions
It is general, and meet low-carbon, environmental protection concept, facilitate the extension that colour band uses field.
Claims (2)
1. a kind of heat transfer colour ribbon by substrate and is applied to the back coating of substrate two sides respectively and ink layer is constituted, which is characterized in that
The substrate is PET film, primary raw material in the ink layer are as follows: resin, colorant, wax and auxiliary agent, the back coating it is main
Raw material is wax, and the ratio of resin and wax is 1.5:1~5:1 in the ink layer, and the mass fraction of the wax in the back coating is
10~15%.
2. a kind of preparation method of heat transfer colour ribbon according to claim 1, which comprises the following steps:
1. being coated with ink layer, 2.5~3g/m of coating weight in the side of substrate2, drying, into subsequent processing;
2. being coated with back coating, 3.5~5.5g/m of coating weight in the other side of substrate2, dry to get colour band.