CN110344171A - A kind of simulating hemp-simulating surfacing material and preparation method thereof that moisture absorption is warming - Google Patents
A kind of simulating hemp-simulating surfacing material and preparation method thereof that moisture absorption is warming Download PDFInfo
- Publication number
- CN110344171A CN110344171A CN201910534752.9A CN201910534752A CN110344171A CN 110344171 A CN110344171 A CN 110344171A CN 201910534752 A CN201910534752 A CN 201910534752A CN 110344171 A CN110344171 A CN 110344171A
- Authority
- CN
- China
- Prior art keywords
- fiber
- simulating
- parts
- moisture absorption
- warming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This case discloses a kind of simulating hemp-simulating surfacing material that moisture absorption is warming, and fabric is weaved on four guide bar warp knitting machines by multiple fiber and formed again through dyeing and finishing；By weight, fabric includes the fiber of following parts by weight: hollow 16~20 parts by weight of dacron fibre；Two ester fiber of poly- 2,6- naphthalene diacid second, 13~15 parts by weight；3~5 parts by weight of breadfruit fiber.Poly- 2,6- naphthalene diacid second, two ester fiber and breadfruit fiber blend are obtained the first fiber by the present invention, obtain the second fiber for polyester filament FDY and long-staple cotton fiber are blended；First fiber is worn on four guide bar warp knitting machine GB1 and GB2 with certain sky and forms different structures in cloth cover with different band yarn methods；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3, and the second fiber is weaved on four guide bar warp knitting machine GB4, obtains fabric, obtains the product of imitative numb appearance and feel through dyeing and finishing, and have good moisture absorption thermal property.
Description
Technical field
The present invention relates to a kind of fabric, the simulating hemp-simulating surfacing material and preparation method thereof to keep warm more particularly to a kind of moisture absorption.
Background technique
With the improvement of living standards, leisure time increases, people propose higher want to the quality of clothing fabric
It asks, fashion, health, the dress ornament that comfortably lies fallow are more and more popular with consumers, and clothing fabric forward direction is superior, diversified, function
Direction can be changed to develop.Nylon-6 fiber is extensive due to it has excellent physics and chemical characteristic as one of four big synthetic fibers
Applied to textile garment and other non-woven fields.In terms of developing fibre in differentiation, Europe, the United States, the starting of day area are more early
Also more advanced, and many patent and product brand are obtained, but the overwhelming majority all concentrates on moisture absorption, warming, antistatic etc.
Aspect, and based on dacron product.
Due to conventional polyester product have wrinkle resistance, conformality very well, it is high-intensitive with elastic recovery capability, it is strong it is durable,
Wash and wear, not adhesive hair the characteristics of, but moisture absorption thermal property is bad, develops novel polyester fiber, textile is enable to obtain more
Add excellent moisture pick-up properties, thermal property, can be widely applied to the textile garment in direct contact with the skin such as underskirt, socks
Articles, therefore the polyester fiber with moisture absorption heat-preserving function, market prospects are quite wide.
Summary of the invention
In view of the above shortcomings, the purpose of the present invention is to provide a kind of warming simulating hemp-simulating surfacing material of moisture absorption and its preparation sides
Method.
Technical solution of the present invention is summarized as follows:
A kind of simulating hemp-simulating surfacing material that moisture absorption is warming, wherein the fabric is weaved again on four guide bar warp knitting machines by multiple fiber
It is formed through dyeing and finishing；By weight, the fabric includes the fiber of following parts by weight:
Hollow 16~20 parts by weight of dacron fibre；
Two ester fiber of poly- 2,6- naphthalene diacid second, 13~15 parts by weight；
3~5 parts by weight of breadfruit fiber.
Preferably, the warming simulating hemp-simulating surfacing material of the moisture absorption, wherein further include the polyester filament of 12~14 parts by weight
FDY。
Preferably, the warming simulating hemp-simulating surfacing material of the moisture absorption, wherein further include the long-staple cotton fiber of 4~6 parts by weight.
Preferably, the warming simulating hemp-simulating surfacing material of the moisture absorption, wherein by weight, the polyester filament FDY includes
100 parts of polyethylene terephthalate, 6~8 parts of polytrimethylene terephthalates, 3~5 parts of poly terephthalic acid-Isosorbide-5-Nitrae-hexamethylenes
Dimethyl ester, 0.5~1 part of ethylene glycol dimethacrylate, 2~4 parts of zeolites, 0.5~1 part of gamma-amino alkyltri silicon
Alkane.
Preferably, the warming simulating hemp-simulating surfacing material of the moisture absorption, wherein the polyester filament FDY is prepared by following step
It forms:
1) zeolite is crushed to the powder that average grain diameter is 70~90nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, poly- to benzene two
Formic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
4) it by the polyester slice heating melting, squeezes, spinneret；
5) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, wherein include the following steps:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3) polyethylene terephthalate is spinned hollow poly- pair using dry and wet spinning equipment under the spinning speed of setting
Polyethylene terephthalate fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth on four guide bar warp knitting machine GB1 and GB2
Face forms different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber exists
It is weaved on four guide bar warp knitting machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.
Preferably, the method for weaving of the warming simulating hemp-simulating surfacing material of the moisture absorption, wherein the arrangement specifically: will contaminate
Fabric after color drying soaks the antistatic agent that the softening agent, concentration that concentration is 20g/l are 4.1g/l, then dewatered drying；Exist again
It pads on sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, setting temperature is maintained at 180 DEG C.
Preferably, the method for weaving of the warming simulating hemp-simulating surfacing material of the moisture absorption, wherein the softening agent includes 24~
26wt% pentaerythritol fatty ester and the polyether-modified dimethyl silicone polymer of 74~76wt%.
Preferably, the method for weaving of the warming simulating hemp-simulating surfacing material of the moisture absorption, wherein the antistatic agent includes 56~
The cruel amine of 60wt% ethyoxyl laurel and 40~44wt% hexadecanyl phosphate sylvite.
Preferably, the method for weaving of the warming simulating hemp-simulating surfacing material of the moisture absorption, wherein four guide bar warp knitting machine is 28
Four guide bar warp knitting machine of needle.
The beneficial effects of the present invention are:
Poly- 2,6- naphthalene diacid second, two ester fiber and breadfruit fiber blend are obtained the first fiber by the present invention, and polyester is long
Silk FDY and long-staple cotton fiber is blended obtains the second fiber；By the first fiber with certain on four guide bar warp knitting machine GB1 and GB2
Sky, which is worn, forms different structures in cloth cover with different band yarn methods；Hollow dacron fibre is passed through in four sley bars
It is weaved on volume machine GB3, the second fiber is weaved on four guide bar warp knitting machine GB4, is obtained having imitative numb fabric, is obtained imitative fiber crops through dyeing and finishing
The product of appearance and feel, and there is good moisture absorption thermal property.
Specific embodiment
The present invention will be further described in detail below with reference to the embodiments, to enable those skilled in the art referring to specification
Text can be implemented accordingly.
The present invention provides a kind of simulating hemp-simulating surfacing material that moisture absorption is warming, and fabric is weaved again on four guide bar warp knitting machines by multiple fiber
It is formed through dyeing and finishing；By weight, fabric includes the fiber of following parts by weight:
Hollow 16~20 parts by weight of dacron fibre；
Two ester fiber of poly- 2,6- naphthalene diacid second, 13~15 parts by weight；
3~5 parts by weight of breadfruit fiber.
Hollow dacron fibre has bulkiness good, and warmth retention property gas permeability is fine, compression power conformality
Good, anti-caking deformation, quality is slim and graceful, and pull resistance is strong, water-fastness, is not afraid of and damages by worms, mildew resistant moistureproof；Poly- 2,6- naphthalene diacid second diester is fine
Dimension has excellent physical mechanical property, chemical stability and heat-resisting, UV resistant, radiation resistance；Breadfruit fiber improves
Its thermal property.
As the another embodiment of this case, wherein further include the polyester filament FDY of 12~14 parts by weight.Polyester filament FDY tool
There is warming, heat-resisting, antistatic, highly hygroscopic and high water absorption performance.
As the another embodiment of this case, wherein further include the long-staple cotton fiber of 4~6 parts by weight.Long-staple cotton is best in quality,
Its fiber is soft and long, and generally 33~39 millimeters, longest is up to 64 millimeters；Fineness is 7000~8500 meters/gram, and width 15~16 is micro-
Rice；Intensity is higher, is 4~5 gram forces/root, 33~40 km of breaking length；Turn bent more, is 80~120/centimetre.
As the another embodiment of this case, wherein by weight, polyester filament FDY includes 100 parts of poly terephthalic acid second
Diester, 6~8 parts of polytrimethylene terephthalates, 3~5 parts of poly terephthalic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalates, 0.5~1 part of diformazan
Base acrylic acid glycol ester, 2~4 parts of zeolites, 0.5~1 part of gamma-amino alkyltrialkoxysilaneand.Improved by the way that zeolite is added
The moisture pick-up properties of polyester filament；Improve the compatible of polyester filament FDY and zeolite by the way that gamma-amino alkyltrialkoxysilaneand is added
Performance.
As the another embodiment of this case, wherein polyester filament FDY is prepared by following step:
1) zeolite is crushed to the powder that average grain diameter is 70~90nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, poly- to benzene two
Formic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
4) it by polyester slice heating melting, squeezes, spinneret；
5) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, includes the following steps:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3) polyethylene terephthalate is spinned hollow poly- pair using dry and wet spinning equipment under the spinning speed of setting
Polyethylene terephthalate fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth on four guide bar warp knitting machine GB1 and GB2
Face forms different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber exists
It is weaved on four guide bar warp knitting machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.
As the another embodiment of this case, wherein arrange specifically: it is 20g/l's that the fabric after dyeing drying, which is soaked concentration,
Softening agent, concentration are the antistatic agent of 4.1g/l, then dewatered drying；Again on padding sizing all-in-one machine, first padding concentration is
3% anti-hook silk auxiliary agent, then be formed, setting temperature is maintained at 180 DEG C.
As the another embodiment of this case, wherein softening agent include 24~26wt% pentaerythritol fatty ester and 74~
The polyether-modified dimethyl silicone polymer of 76wt%.Softening agent is a kind of quiet, dynamic friction coefficient chemical substance that can change fiber,
When changing confficient of static friction, feel touch has smooth sense, is easy to move on fiber or fabric；When change dynamic friction coefficient
When, the fine structure between fiber and fiber is easy to be mutually shifted, that is, fiber or fabric it is easily deformable, there is fabric
Soft, smooth, comfortable feel, softening agent of the invention are pentaerythritol fatty ester and polyether-modified dimethyl silicone polymer
Synergistic effect.
As the another embodiment of this case, wherein antistatic agent include the cruel amine of 56~60wt% ethyoxyl laurel and 40~
44wt% hexadecanyl phosphate sylvite.The cruel amine of ethyoxyl laurel and the collaboration of hexadecanyl phosphate sylvite are used as antistatic agent,
There are wash resistant, rub resistance, antistatic effect is lasting.
As the another embodiment of this case, wherein four guide bar warp knitting machines are 28 needle, four guide bar warp knitting machine.
Specific embodiment and comparative example is listed below:
Embodiment 1:
A kind of warming simulating hemp-simulating surfacing material of moisture absorption, fabric weaved on four guide bar warp knitting machines by multiple fiber again through dyeing and finishing and
At；By weight, fabric includes the fiber of following parts by weight:
Polyester filament FDY includes 100 parts of polyethylene terephthalate, 6 parts of polytrimethylene terephthalates, and 3 parts poly- pair
Phthalic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, 0.5 part of ethylene glycol dimethacrylate, 2 parts of zeolites, 0.5 part of gamma-amino alkyl three
Alkoxy silane.
Polyester filament FDY is prepared by following step:
1) zeolite is crushed to the powder that average grain diameter is 70nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, poly- to benzene two
Formic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
4) it by the polyester slice heating melting, squeezes, spinneret；
5) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, includes the following steps:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3) polyethylene terephthalate is spinned hollow poly- pair using dry and wet spinning equipment under the spinning speed of setting
Polyethylene terephthalate fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth on four guide bar warp knitting machine GB1 and GB2
Face forms different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber exists
It is weaved on four guide bar warp knitting machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.
It arranges specifically: it is that resisting for 4.1g/l is quiet that the fabric after dyeing drying, which is soaked softening agent, concentration that concentration is 20g/l,
Electric agent, then dewatered drying；Again on padding sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, it is fixed
Type temperature is maintained at 180 DEG C；Softening agent includes 24wt% pentaerythritol fatty ester and the polyether-modified poly dimethyl silicon of 76wt%
Oxygen alkane；Antistatic agent includes the cruel amine of 56wt% ethyoxyl laurel and 44wt% hexadecanyl phosphate sylvite；Four guide bar warp knitting machines
For 28 needle, four guide bar warp knitting machine.
Embodiment 2:
A kind of warming simulating hemp-simulating surfacing material of moisture absorption, fabric weaved on four guide bar warp knitting machines by multiple fiber again through dyeing and finishing and
At；By weight, fabric includes the fiber of following parts by weight:
Polyester filament FDY includes 100 parts of polyethylene terephthalate, 7 parts of polytrimethylene terephthalates, and 4 parts poly- pair
Phthalic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, 0.7 part of ethylene glycol dimethacrylate, 3 parts of zeolites, 0.7 part of gamma-amino alkyl three
Alkoxy silane.
Polyester filament FDY is prepared by following step:
1) zeolite is crushed to the powder that average grain diameter is 80nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, poly- to benzene two
Formic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
4) it by the polyester slice heating melting, squeezes, spinneret；
5) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, includes the following steps:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3) polyethylene terephthalate is spinned hollow poly- pair using dry and wet spinning equipment under the spinning speed of setting
Polyethylene terephthalate fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth on four guide bar warp knitting machine GB1 and GB2
Face forms different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber exists
It is weaved on four guide bar warp knitting machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.It arranges specific
Are as follows: the fabric after drying dyeing soaks the antistatic agent that the softening agent, concentration that concentration is 20g/l are 4.1g/l, and then dehydration is dried
It is dry；Again on padding sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, setting temperature is maintained at 180
℃；Softening agent includes 25wt% pentaerythritol fatty ester and the polyether-modified dimethyl silicone polymer of 75wt%；Antistatic agent packet
Include the cruel amine of 58wt% ethyoxyl laurel and 42wt% hexadecanyl phosphate sylvite；Four guide bar warp knitting machines are 28 needle, four sley bar warp knit
Machine.
Embodiment 3:
A kind of warming simulating hemp-simulating surfacing material of moisture absorption, fabric weaved on four guide bar warp knitting machines by multiple fiber again through dyeing and finishing and
At；By weight, the fabric includes the fiber of following parts by weight:
Polyester filament FDY includes 100 parts of polyethylene terephthalate, 8 parts of polytrimethylene terephthalates, and 5 parts poly- pair
Phthalic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, 1 part of ethylene glycol dimethacrylate, 4 parts of zeolites, 1 part of three alcoxyl of gamma-amino alkyl
Base silane.
Polyester filament FDY is prepared by following step:
1) zeolite is crushed to the powder that average grain diameter is 70~90nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, poly- to benzene two
Formic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
4) it by the polyester slice heating melting, squeezes, spinneret；
5) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, includes the following steps:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3) polyethylene terephthalate is spinned hollow poly- pair using dry and wet spinning equipment under the spinning speed of setting
Polyethylene terephthalate fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth on four guide bar warp knitting machine GB1 and GB2
Face forms different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber exists
It is weaved on four guide bar warp knitting machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.It arranges specific
Are as follows: the fabric after drying dyeing soaks the antistatic agent that the softening agent, concentration that concentration is 20g/l are 4.1g/l, and then dehydration is dried
It is dry；Again on padding sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, setting temperature is maintained at 180
DEG C, softening agent includes 26wt% pentaerythritol fatty ester and the polyether-modified dimethyl silicone polymer of 76wt%；Antistatic agent packet
The cruel amine of 60wt% ethyoxyl laurel and 40wt% hexadecanyl phosphate sylvite are included, four guide bar warp knitting machines are 28 needle, four sley bar warp knit
Machine.
Comparative example 1:
A kind of warming simulating hemp-simulating surfacing material of moisture absorption, fabric weaved on four guide bar warp knitting machines by multiple fiber again through dyeing and finishing and
At；By weight, fabric includes the fiber of following parts by weight:
Polyester filament FDY include 100 parts of polyethylene terephthalate, 6 parts of polytrimethylene terephthalates, 0.5 part two
Methacrylic acid glycol ester, 2 parts of zeolites, 0.5 part of gamma-amino alkyltrialkoxysilaneand.
Polyester filament FDY is prepared by following step:
1) zeolite is crushed to the powder that average grain diameter is 70nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, dimethyl propylene
Olefin(e) acid glycol ester is blended, and squeezes out, slice, polyester slice is made；
4) it by the polyester slice heating melting, squeezes, spinneret；
5) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, includes the following steps:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3) polyethylene terephthalate is spinned hollow poly- pair using dry and wet spinning equipment under the spinning speed of setting
Polyethylene terephthalate fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth on four guide bar warp knitting machine GB1 and GB2
Face forms different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber exists
It is weaved on four guide bar warp knitting machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.
It arranges specifically: it is that resisting for 4.1g/l is quiet that the fabric after dyeing drying, which is soaked softening agent, concentration that concentration is 20g/l,
Electric agent, then dewatered drying；Again on padding sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, it is fixed
Type temperature is maintained at 180 DEG C；Softening agent includes 24wt% pentaerythritol fatty ester and the polyether-modified poly dimethyl silicon of 76wt%
Oxygen alkane；Antistatic agent includes the cruel amine of 56wt% ethyoxyl laurel and 44wt% hexadecanyl phosphate sylvite；Four guide bar warp knitting machines
For 28 needle, four guide bar warp knitting machine.
Comparative example 2:
A kind of warming simulating hemp-simulating surfacing material of moisture absorption, fabric weaved on four guide bar warp knitting machines by multiple fiber again through dyeing and finishing and
At；By weight, fabric includes the fiber of following parts by weight:
Polyester filament FDY includes 100 parts of polyethylene terephthalate, 6 parts of polytrimethylene terephthalates, and 3 parts poly- pair
Phthalic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, 0.5 part of ethylene glycol dimethacrylate, 0.5 part of gamma-amino alkyltri silicon
Alkane.
Polyester filament FDY is prepared by following step:
1) by polyethylene terephthalate, polytrimethylene terephthalate, poly terephthalic acid -1,4- hexamethylene diformazan
Ester, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
2) it by the polyester slice heating melting, squeezes, spinneret；
3) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, includes the following steps:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3) polyethylene terephthalate is spinned hollow poly- pair using dry and wet spinning equipment under the spinning speed of setting
Polyethylene terephthalate fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth on four guide bar warp knitting machine GB1 and GB2
Face forms different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber exists
It is weaved on four guide bar warp knitting machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.
It arranges specifically: it is that resisting for 4.1g/l is quiet that the fabric after dyeing drying, which is soaked softening agent, concentration that concentration is 20g/l,
Electric agent, then dewatered drying；Again on padding sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, it is fixed
Type temperature is maintained at 180 DEG C；Softening agent includes 24wt% pentaerythritol fatty ester and the polyether-modified poly dimethyl silicon of 76wt%
Oxygen alkane；Antistatic agent includes the cruel amine of 56wt% ethyoxyl laurel and 44wt% hexadecanyl phosphate sylvite；Four guide bar warp knitting machines
For 28 needle, four guide bar warp knitting machine.
Comparative example 3:
A kind of warming simulating hemp-simulating surfacing material of moisture absorption, fabric weaved on four guide bar warp knitting machines by multiple fiber again through dyeing and finishing and
At；By weight, fabric includes the fiber of following parts by weight:
Polyester filament FDY includes 100 parts of polyethylene terephthalate, 7 parts of polytrimethylene terephthalates, and 4 parts poly- pair
Phthalic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, 0.7 part of ethylene glycol dimethacrylate, 3 parts of zeolites, 0.7 part of gamma-amino alkyl three
Alkoxy silane.
Polyester filament FDY is prepared by following step:
1) zeolite is crushed to the powder that average grain diameter is 80nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, poly- to benzene two
Formic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
4) it by the polyester slice heating melting, squeezes, spinneret；
5) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, includes the following steps:
1) using poly- two ester fiber of 2,6- naphthalene diacid second as the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3) polyethylene terephthalate is spinned hollow poly- pair using dry and wet spinning equipment under the spinning speed of setting
Polyethylene terephthalate fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth on four guide bar warp knitting machine GB1 and GB2
Face forms different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber exists
It is weaved on four guide bar warp knitting machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.It arranges specific
Are as follows: the fabric after drying dyeing soaks the antistatic agent that the softening agent, concentration that concentration is 20g/l are 4.1g/l, and then dehydration is dried
It is dry；Again on padding sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, setting temperature is maintained at 180
℃；Softening agent includes 25wt% pentaerythritol fatty ester and the polyether-modified dimethyl silicone polymer of 75wt%；Antistatic agent packet
Include the cruel amine of 58wt% ethyoxyl laurel and 42wt% hexadecanyl phosphate sylvite；Four guide bar warp knitting machines are 28 needle, four sley bar warp knit
Machine.
Comparative example 4:
A kind of warming simulating hemp-simulating surfacing material of moisture absorption, fabric weaved on four guide bar warp knitting machines by multiple fiber again through dyeing and finishing and
At；By weight, fabric includes the fiber of following parts by weight:
Polyester filament FDY includes 100 parts of polyethylene terephthalate, 7 parts of polytrimethylene terephthalates, and 4 parts poly- pair
Phthalic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, 0.7 part of ethylene glycol dimethacrylate, 3 parts of zeolites, 0.7 part of gamma-amino alkyl three
Alkoxy silane.
Polyester filament FDY is prepared by following step:
1) zeolite is crushed to the powder that average grain diameter is 80nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, poly- to benzene two
Formic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
4) it by the polyester slice heating melting, squeezes, spinneret；
5) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, includes the following steps:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) using polyester filament FDY as the second fiber；
3) polyethylene terephthalate is spinned hollow poly- pair using dry and wet spinning equipment under the spinning speed of setting
Polyethylene terephthalate fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth on four guide bar warp knitting machine GB1 and GB2
Face forms different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber exists
It is weaved on four guide bar warp knitting machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.It arranges specific
Are as follows: the fabric after drying dyeing soaks the antistatic agent that the softening agent, concentration that concentration is 20g/l are 4.1g/l, and then dehydration is dried
It is dry；Again on padding sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, setting temperature is maintained at 180
℃；Softening agent includes 25wt% pentaerythritol fatty ester and the polyether-modified dimethyl silicone polymer of 75wt%；Antistatic agent packet
Include the cruel amine of 58wt% ethyoxyl laurel and 42wt% hexadecanyl phosphate sylvite；Four guide bar warp knitting machines are 28 needle, four sley bar warp knit
Machine.
Comparative example 5:
A kind of warming simulating hemp-simulating surfacing material of moisture absorption, fabric weaved on four guide bar warp knitting machines by multiple fiber again through dyeing and finishing and
At；By weight, the fabric includes the fiber of following parts by weight:
Polyester filament FDY includes 100 parts of polyethylene terephthalate, 8 parts of polytrimethylene terephthalates, and 5 parts poly- pair
Phthalic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, 1 part of ethylene glycol dimethacrylate, 4 parts of zeolites, 1 part of three alcoxyl of gamma-amino alkyl
Base silane.
Polyester filament FDY is prepared by following step:
1) zeolite is crushed to the powder that average grain diameter is 70~90nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, poly- to benzene two
Formic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
4) it by the polyester slice heating melting, squeezes, spinneret；
5) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, includes the following steps:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3 wear the first fiber with different band yarn methods with certain sky in cloth cover on four guide bar warp knitting machine GB1 and GB2
Form different structures；Dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber is in four sley bars
It is weaved on tricot machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.It arranges specific
Are as follows: the fabric after drying dyeing soaks the antistatic agent that the softening agent, concentration that concentration is 20g/l are 4.1g/l, and then dehydration is dried
It is dry；Again on padding sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, setting temperature is maintained at 180
DEG C, softening agent includes 26wt% pentaerythritol fatty ester and the polyether-modified dimethyl silicone polymer of 76wt%；Antistatic agent packet
The cruel amine of 60wt% ethyoxyl laurel and 40wt% hexadecanyl phosphate sylvite are included, four guide bar warp knitting machines are 28 needle, four sley bar warp knit
Machine.
Comparative example 6:
A kind of warming simulating hemp-simulating surfacing material of moisture absorption, fabric weaved on four guide bar warp knitting machines by multiple fiber again through dyeing and finishing and
At；By weight, the fabric includes the fiber of following parts by weight:
Polyester filament FDY includes 100 parts of polyethylene terephthalate, 8 parts of polytrimethylene terephthalates, and 5 parts poly- pair
Phthalic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, 1 part of ethylene glycol dimethacrylate, 4 parts of zeolites, 1 part of three alcoxyl of gamma-amino alkyl
Base silane.
Polyester filament FDY is prepared by following step:
1) zeolite is crushed to the powder that average grain diameter is 70~90nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, poly- to benzene two
Formic acid-Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
4) it by the polyester slice heating melting, squeezes, spinneret；
5) it is wound that obtain polyester long with 4500~5000m/min by oiling directly to be stretched after strand solidification
Silk FDY.
A kind of method for weaving for the simulating hemp-simulating surfacing material that moisture absorption is warming, includes the following steps:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3) polyethylene terephthalate is spinned hollow poly- pair using dry and wet spinning equipment under the spinning speed of setting
Polyethylene terephthalate fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth on four guide bar warp knitting machine GB1 and GB2
Face forms different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber exists
It is weaved on four guide bar warp knitting machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.It arranges specific
Are as follows: the fabric after drying dyeing soaks the antistatic agent that the softening agent, concentration that concentration is 20g/l are 4.1g/l, and then dehydration is dried
It is dry；Again on padding sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, setting temperature is maintained at 180
DEG C, softening agent includes 26wt% pentaerythritol fatty ester and the polyether-modified dimethyl silicone polymer of 76wt%；Antistatic agent is
Cruel four guide bar warp knitting machine of amine of ethyoxyl laurel is 28 needle, four guide bar warp knitting machine.
The performance test results are listed below:
By the test data in table 1 it is found that Examples 1 to 3 is compared with comparative example 1~6, not only there is excellent warmth retention property
Can, and there is good moisture absorption antistatic property.
Although the embodiments of the present invention have been disclosed as above, but its is not only in the description and the implementation listed
With it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can be easily
Realize other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, the present invention is simultaneously unlimited
In specific details.
Claims (10)
1. a kind of warming simulating hemp-simulating surfacing material of moisture absorption, which is characterized in that the fabric is knitted on four guide bar warp knitting machines by multiple fiber
It makes and is formed again through dyeing and finishing；By weight, the fabric includes the fiber of following parts by weight:
Hollow 16~20 parts by weight of dacron fibre；
Two ester fiber of poly- 2,6- naphthalene diacid second, 13~15 parts by weight；
3~5 parts by weight of breadfruit fiber.
2. the warming simulating hemp-simulating surfacing material of moisture absorption according to claim 1, which is characterized in that further include the poly- of 12~14 parts by weight
Ester long filament FDY.
3. the warming simulating hemp-simulating surfacing material of moisture absorption according to claim 1, which is characterized in that further include the long wool of 4~6 parts by weight
Cotton fiber.
4. the warming simulating hemp-simulating surfacing material of moisture absorption according to claim 2, which is characterized in that by weight, the polyester is long
Silk FDY includes 100 parts of polyethylene terephthalate, 6~8 parts of polytrimethylene terephthalates, 3~5 parts of poly terephthalic acids-
Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, 0.5~1 part of ethylene glycol dimethacrylate, 2~4 parts of zeolites, 0.5~1 part of gamma-amino alkyl three
Alkoxy silane.
5. the warming simulating hemp-simulating surfacing material of moisture absorption according to claim 4, which is characterized in that the polyester filament FDY is by following
Step is prepared:
1) zeolite is crushed to the powder that average grain diameter is 70~90nm；
2) gamma-amino alkyltrialkoxysilaneand is mixed with zeolite, obtains modified zeolite powder；
3) by the modified zeolite powder and polyethylene terephthalate, polytrimethylene terephthalate, poly terephthalic acid-
Isosorbide-5-Nitrae-cyclohexanedimethylene terephthalate, ethylene glycol dimethacrylate are blended, and squeeze out, slice, polyester slice is made；
4) it by the polyester slice heating melting, squeezes, spinneret；
5) polyester filament is obtained by oiling directly to be stretched to be wound with 4500~5000m/min after strand solidification
FDY。
6. the method for weaving of the warming simulating hemp-simulating surfacing material of described in any item moisture absorptions according to claim 1~5, which is characterized in that packet
Include following step:
1) poly- two ester fiber of 2,6- naphthalene diacid second and breadfruit fiber blend are obtained into the first fiber；
2) the second fiber is obtained by polyester filament FDY and long-staple cotton fiber are blended；
3) polyethylene terephthalate is spinned under the spinning speed of setting using dry and wet spinning equipment hollow poly- to benzene two
Formic acid second diester fiber filament；
4) the first fiber is worn with different band yarn methods with certain sky in cloth cover shape on four guide bar warp knitting machine GB1 and GB2
At different structures；Hollow dacron fibre is weaved on four guide bar warp knitting machine GB3；Second fiber is in four combs
It is weaved on comb tricot machine GB4, obtains fabric；
5) dye vat dyeing is added in fabric at 30 DEG C, arranges the simulating hemp-simulating surfacing material for obtaining the moisture absorption and keeping warm.
7. the method for weaving of the warming simulating hemp-simulating surfacing material of moisture absorption according to claim 6, which is characterized in that described to arrange specifically
Are as follows: the fabric after drying dyeing soaks the antistatic agent that the softening agent, concentration that concentration is 20g/l are 4.1g/l, and then dehydration is dried
It is dry；Again on padding sizing all-in-one machine, first pads concentration and be 3% anti-hook silk auxiliary agent, then be formed, setting temperature is maintained at 180
℃。
8. the method for weaving of the warming simulating hemp-simulating surfacing material of moisture absorption according to claim 7, which is characterized in that the softening agent packet
Include 24~26wt% pentaerythritol fatty ester and the polyether-modified dimethyl silicone polymer of 74~76wt%.
9. the method for weaving of the warming simulating hemp-simulating surfacing material of moisture absorption according to claim 7, which is characterized in that the antistatic agent
Including the cruel amine of 56~60wt% ethyoxyl laurel and 40~44wt% hexadecanyl phosphate sylvite.
10. the method for weaving of the warming simulating hemp-simulating surfacing material of moisture absorption according to claim 1, which is characterized in that four sley bar
Tricot machine is 28 needle, four guide bar warp knitting machine.