CN110343314A - A method of plastics activeness and quietness agent is prepared with waste textile opening fiber - Google Patents
A method of plastics activeness and quietness agent is prepared with waste textile opening fiber Download PDFInfo
- Publication number
- CN110343314A CN110343314A CN201910571434.XA CN201910571434A CN110343314A CN 110343314 A CN110343314 A CN 110343314A CN 201910571434 A CN201910571434 A CN 201910571434A CN 110343314 A CN110343314 A CN 110343314A
- Authority
- CN
- China
- Prior art keywords
- activeness
- quietness
- fiber
- tubing
- waste textile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of methods for preparing plastics activeness and quietness agent with waste textile opening fiber.It is a kind of high-quality activeness and quietness material it is characterized in that among this fiber dispersion, playing the effect of activeness and quietness according to plastic products activeness and quietness demand.
Description
Technical field
The invention discloses a kind of methods for preparing plastics activeness and quietness agent with waste textile opening fiber of our factory.
Technical background
It is well known that generally all it is applied to heat-preservation cotton after waste textile shredding, sound insulation, heat-barrier material etc,
Nobody considers to be applied to plastic products activeness and quietness material.
Summary of the invention
The present invention is in order to overcome drawbacks described above, according to plastic products activeness and quietness demand, using this fiber dispersed material
Among, the effect of activeness and quietness is played, is a kind of high-quality activeness and quietness material.
Specific implementation method
To the method that waste textile opening fiber of the present invention prepares activeness and quietness agent, its technical solution is described in detail
It is as follows, but embodiment should not be construed as limiting the invention.
Embodiment one:
Waste textile fabric is ground into the block of 100mm size, then carrying out shredding becomes fiber different in size.
Embodiment two:
On the basis of example 1, the compatilizer of fiber addition 3-5% shredding gone out mixes spare.
Embodiment three:
On the basis of example 2, by mixture and HDPE or PP raw material in 3:7 ratio or 4:6 ratio mixing for standby use.
Example IV:
It is this different in size with twin-screw or three screw rod plastic extruder extrusion boards or tubing on the basis of embodiment three
Fiber it is evenly dispersed wherein, due to the difference of material melting temperature, so that this fiber is become the enhancing in plate or tubing and increase
Tough skeleton forms prestressing force, achievees the purpose that plate or tubing activeness and quietness.
Embodiment five:
On the basis of example IV, to make tubing or plate surface more gloss, compound extruded technique can be used, make tubing or plate
The surfaces externally and internally of material achievees the purpose that gloss is had no time.
Obviously, those skilled in the art can carry out various modifications and changes without departing from essence of the invention to the present invention
Mind and range.In this way.If these modifications and variations of the invention belong to the range of the claims in the present invention and its equivalent technologies
Within, then including the present invention is also intended to encompass these changes and changes.
The content being not described in detail in this specification belongs to the prior art well known to professional and technical personnel in the field.
Claims (4)
1. a kind of method for preparing plastics activeness and quietness agent with waste textile opening fiber, it is characterized in that being increased according to plastic products
Strong toughening demand plays the effect of activeness and quietness among this fiber dispersed material, is a kind of high-quality activeness and quietness material
Material.
2. a kind of method for preparing plastics activeness and quietness agent with waste textile opening fiber according to claim 1, is
The fiber different in size that shredding is gone out, the compatilizer for adding 3-5% mixes, by mixture and HDPE or PP raw material in 3:7 ratio
Or 4:6 ratio mixing for standby use.
3. according to claim 1,2, it is this different in size with twin-screw or three screw rod plastic extruder extrusion boards or tubing
Fiber is evenly dispersed wherein, due to the difference of material melting temperature, this fiber is made to become the activeness and quietness in plate or tubing
Skeleton forms prestressing force, achievees the purpose that plate or tubing activeness and quietness.
4. according to claim 1,2,3, to make tubing or plate surface more gloss, compound extruded technique can be used, make tubing or
The surfaces externally and internally of plate achievees the purpose that gloss is had no time.