CN110330898A - A kind of environment-protection nano water paint and preparation method thereof - Google Patents
A kind of environment-protection nano water paint and preparation method thereof Download PDFInfo
- Publication number
- CN110330898A CN110330898A CN201910720593.1A CN201910720593A CN110330898A CN 110330898 A CN110330898 A CN 110330898A CN 201910720593 A CN201910720593 A CN 201910720593A CN 110330898 A CN110330898 A CN 110330898A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- water paint
- nano
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to a kind of environment-protection nano water paints and preparation method thereof, including water: 180 parts；Ethylene glycol: 15 parts；Wetting agent: 2 parts；Dispersing agent: 20 parts；Defoaming agent: 1 part；10-12 parts of nano-titanium dioxide；1 part of polytetrafluoroethylene (PTFE) wax powder；0.2 part of organically-modified dimethyl silicone polymer levelling agent；Alumina silicate: 10 parts；Levelling agent: 5 parts；Lotion: 200-250 parts；Levelling agent: 2 parts；Diethylene glycol ethers: 2 parts；ASE:10 parts；AT-08:10 parts；10-12 parts of rutile titanium dioxide；Preservative: 1 part；Nanometer stain resistant agents: 5 parts；Nano-sized hydrophobic agent: 5 parts.Environment-friendly water-based paint disclosed by the invention, overcome that the existing construction of water paint in the prior art is difficult, not resistant to water, easily takes off the defects of poor skin, richness, difference of hardness, production cost is cheaper, paint vehicle comprehensive performance is more excellent, more environmentally protective, stronger with substrate adhesive force, stability is higher, hardness of paint film is bigger, and richness is higher, constructs more tolerant.
Description
Technical field
The invention belongs to water paint technical fields, and in particular to a kind of environment-protection nano water paint and preparation method thereof.
Background technique
In recent years, with the development of economy, people are higher and higher to quality of life level requirement, to home decoration in life
Decoration also has higher requirement, does not require nothing more than these decoration material strips and comes visual sense of beauty and comfort, at the same time, also needs
Want its low in cost, more environmentally-friendly, safety is non-stimulated, durable.Paint vehicle is common one of decoration material, is made extensively
With improving people's lives quality, but traditional paint vehicle contains the poisonous and hazardous substance such as methanol, these organic volatiles
Discharge, brings grievous injury to the physical and mental health of ecological environment for the survival of mankind and people.Therefore, one kind is developed not containing
Machine volatile matter, influencing small paint vehicle to air environment becomes the hot spot studied in the industry.
Water paint be exactly using water as diluent, without the coating of organic solvent, have and be free of benzene,toluene,xylene, first
Aldehyde, free TDI toxic heavy metal, nontoxic non-stimulated smell is harmless, free from environmental pollution, paint film is plentiful, it is sparkling and crystal-clear it is bright,
Flexibility is good and has the characteristics that water-fast, wear-resisting, ageing-resistant, color inhibition, fast drying, easy to use.It may be used at: woodenware,
In the various materials such as metal, plastics, glass, building surface.This kind of paint vehicle can fundamentally solve traditional solvent type coating to people
The harm of body and environment, compared with solvent based coating, water paint has very big superiority in terms of energy-saving and environmental protection.However, at present
The utilization rate of domestic water paint is not high, the main reason is that there are still technological deficiencies for traditional water paint, it is wear-resisting if hardness of paint film is low
Property, levelability, filming performance and gloss difference, defoaming is difficult.
Therefore, we thinks to propose that a kind of environment-protection nano water paint and preparation method thereof is necessary.
Summary of the invention
The present invention in view of the existing deficiencies of the prior art, provides environment-protection nano water paint and preparation method thereof, to solve to carry on the back
Technical problem in scape material.
To achieve the above object, the present invention is using following technical solution:
A kind of environment-protection nano water paint and preparation method thereof, 15-18 parts of aqueous epoxy resins are uniformly dispersed with cosolvent, and water is made
Property paint component is spare；Water: 180 parts；Ethylene glycol: 15 parts；Wetting agent: 2 parts；Dispersing agent: 20 parts；Defoaming agent: 1 part；Nano-silica
Change titanium 10-12 parts；1 part of polytetrafluoroethylene (PTFE) wax powder；0.2 part of organically-modified dimethyl silicone polymer levelling agent；Alumina silicate: 10 parts；
Levelling agent: 5 parts；Lotion: 200-250 parts；Levelling agent: 2 parts；Diethylene glycol ethers: 2 parts；ASE:10 parts；AT-08:10 parts；Rutile
10-12 parts of type titanium dioxide；Preservative: 1 part；Nanometer stain resistant agents: 5 parts；Nano-sized hydrophobic agent: 5 parts.
Preferably, after high speed dispersion, grinding, then it is slowly added to 10 parts of nano material dispersion liquid under stirring, stirs
It mixes uniformly, it is spare that water paint B component is made；Water paint component A and water paint B component is mixed according to the ratio of mass ratio 1: 5
It closes, stirs evenly, obtain finished product.
Preferably, the levelling agent is preferably polyacrylate flow agent, cellaburate levelling agent, polyvinyl alcohol contracting fourth
One or more of aldehyde levelling agent.
The beneficial effects of the present invention are:
Environment-friendly water-based paint disclosed by the invention, overcomes that the existing construction of water paint in the prior art is difficult, not resistant to water, easily takes off
The defects of skin, richness be poor, difference of hardness, production cost is cheaper, and paint vehicle comprehensive performance is more excellent, more environmentally protective, with
Substrate adhesive force is stronger, and stability is higher, and hardness of paint film is bigger, and richness is higher, constructs more tolerant.
Specific embodiment
Below with reference to embodiment, the present invention will be further described.
The following examples are intended to illustrate the invention, but cannot be used to limit the scope of the invention.Item in embodiment
Part can be adjusted according to actual conditions are further, under concept thereof of the invention all to method simple modifications of the invention
Belong to the scope of protection of present invention.
The present invention provides a kind of technical solution: a kind of environment-protection nano water paint and preparation method thereof, aqueous epoxy resins 15-
18 parts are uniformly dispersed with cosolvent, and it is spare that water paint component is made；Water: 180 parts；Ethylene glycol: 15 parts；Wetting agent: 2 parts；Dispersion
Agent: 20 parts；Defoaming agent: 1 part；10-12 parts of nano-titanium dioxide；1 part of polytetrafluoroethylene (PTFE) wax powder；Organically-modified poly dimethyl silicon
0.2 part of oxygen alkane levelling agent；Alumina silicate: 10 parts；Levelling agent: 5 parts；Lotion: 200-250 parts；Levelling agent: 2 parts；Diethylene glycol ethers: 2
Part；ASE:10 parts；AT-08:10 parts；10-12 parts of rutile titanium dioxide；Preservative: 1 part；Nanometer stain resistant agents: 5 parts；Nanometer
Hydrophobing agent: 5 parts.
Preferably, after high speed dispersion, grinding, then it is slowly added to 10 parts of nano material dispersion liquid under stirring, stirs
It mixes uniformly, it is spare that water paint B component is made；Water paint component A and water paint B component is mixed according to the ratio of mass ratio 1: 5
It closes, stirs evenly, obtain finished product.
Preferably, the levelling agent is preferably polyacrylate flow agent, cellaburate levelling agent, polyvinyl alcohol contracting fourth
One or more of aldehyde levelling agent.
Environment-friendly water-based paint disclosed by the invention, overcome the existing construction of water paint in the prior art it is difficult, not resistant to water,
The defects of easily taking off poor skin, richness, difference of hardness, production cost is cheaper, and paint vehicle comprehensive performance is more excellent, more green ring
It protects, stronger with substrate adhesive force, stability is higher, and hardness of paint film is bigger, and richness is higher, constructs more tolerant.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
1. a kind of environment-protection nano water paint and preparation method thereof, it is characterised in that: 15-18 parts of aqueous epoxy resins are divided with cosolvent
It dissipates uniformly, it is spare that water paint component is made；Water: 180 parts；Ethylene glycol: 15 parts；Wetting agent: 2 parts；Dispersing agent: 20 parts；Defoaming agent:
1 part；10-12 parts of nano-titanium dioxide；1 part of polytetrafluoroethylene (PTFE) wax powder；0.2 part of organically-modified dimethyl silicone polymer levelling agent；
Alumina silicate: 10 parts；Levelling agent: 5 parts；Lotion: 200-250 parts；Levelling agent: 2 parts；Diethylene glycol ethers: 2 parts；ASE:10 parts；AT-08:
10 parts；10-12 parts of rutile titanium dioxide；Preservative: 1 part；Nanometer stain resistant agents: 5 parts；Nano-sized hydrophobic agent: 5 parts.
2. a kind of environment-protection nano water paint according to claim 1 and preparation method thereof, it is characterised in that: through high speed point
It dissipates, after grinding, then is slowly added to 10 parts of nano material dispersion liquid under stirring, stir evenly, it is standby that water paint B component is made
With；Water paint component A and water paint B component are mixed according to the ratio of mass ratio 1: 5, stirs evenly, obtains finished product.
3. a kind of environment-protection nano water paint according to claim 1 and preparation method thereof, it is characterised in that: the levelling agent
Preferably one or more of polyacrylate flow agent, cellaburate levelling agent, polyvinyl butyral levelling agent.