CN110318264A - A kind of material and preparation method thereof for curtain of preventing fires - Google Patents
A kind of material and preparation method thereof for curtain of preventing fires Download PDFInfo
- Publication number
- CN110318264A CN110318264A CN201910597628.7A CN201910597628A CN110318264A CN 110318264 A CN110318264 A CN 110318264A CN 201910597628 A CN201910597628 A CN 201910597628A CN 110318264 A CN110318264 A CN 110318264A
- Authority
- CN
- China
- Prior art keywords
- curtain
- preventing fires
- agent
- foam stabilizer
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of materials of curtain of preventing fires, by weaving latex, foam stabilizer, bleeding agent, crosslinking agent, ammonium hydroxide, polyurethane, silicone oil, nano-titanium dioxide, dispersing agent composition, its component is by weight percentage are as follows: weaving latex 30-40%, foam stabilizer 10-16%, bleeding agent 2-4%, crosslinking agent 0.2-0.6%, ammonium hydroxide 0.5-1.0%, polyurethane 20-30%, silicone oil 4-8%, nano-titanium dioxide 10-16%, dispersing agent 6-8%；The invention also discloses a kind of preparation methods of curtain of preventing fires, the beneficial effects of the present invention are: the anti-flaming thermal-insulation interlayer as made from reasonable compatibility, increases the effect of the fire-proof and thermal-insulation of curtain；The ultraviolet resistant layer as made from reasonable compatibility increases the effect of the antiultraviolet of curtain, preferably protects user, improves the experience of user；Preparation is simple, improves the efficiency of preparation.
Description
Technical field
The invention belongs to curtain technical fields, and in particular to a kind of material for preventing fires curtain further relates to a kind of system of curtain
Preparation Method.
Background technique
Curtain is very important in the arrangement of house.It hangs on interior, not only concerning the beauty of indoor decoration, also closes
The construction of room atmosphere, but also it is closely bound up with the health of people.
There is the deficiencies of following lower aspect for existing curtain:
1. there is deficiencies for fire prevention aspect；
2. in terms of shading, antiultraviolet, there is deficiencies；
3. preparing cumbersome.
Summary of the invention
The purpose of the present invention is to provide a kind of materials and preparation method thereof of curtain of preventing fires, to solve above-mentioned background technique
There is deficiencies in terms of the fire prevention of middle proposition；There is deficiencies in terms of shading, antiultraviolet；Prepare cumbersome problem.
To achieve the above object, the invention provides the following technical scheme: a kind of material for curtain of preventing fires, by weaving latex,
Foam stabilizer, bleeding agent, crosslinking agent, ammonium hydroxide, polyurethane, silicone oil, nano-titanium dioxide, dispersing agent composition, component by weight hundred
Ratio is divided to be calculated as: weaving latex 30-40%, foam stabilizer 10-16%, bleeding agent 2-4%, crosslinking agent 0.2-0.6%, ammonium hydroxide 0.5-
1.0%, polyurethane 20-30%, silicone oil 4-8%, nano-titanium dioxide 10-16%, dispersing agent 6-8%.
As a preferred technical solution of the invention, the fire retardant is aluminium oxide, in ammonium polyphosphate, magnesia
It is one or more of.
As a preferred technical solution of the invention, the foam stabilizer is polyacrylamide, polyvinyl alcohol, dodecane
One or more of base dimethyl amine.
As a preferred technical solution of the invention, the bleeding agent be alcohol ether succinate, phenolic ether succinate,
One or more of alcohol ether phosphate.
As a preferred technical solution of the invention, the crosslinking agent cumyl peroxide, hydrogen peroxide two are different
One or more of propyl benzene, benzoyl peroxide.
As a preferred technical solution of the invention, the dispersing agent is sodium tripolyphosphate, calgon, burnt phosphorus
One or more of sour sodium.
The invention also discloses a kind of preparation methods of curtain of preventing fires, and include the following steps:
Step 1: material and substrate prepare: substrate is curtain fabric；Material is by weight percentage are as follows: weaving latex 30-
40%, foam stabilizer 10-16%, bleeding agent 2-4%, crosslinking agent 0.2-0.6%, ammonium hydroxide 0.5-1.0%, polyurethane 20-30%, silicone oil
4-8%, nano-titanium dioxide 10-16%, dispersing agent 6-8%；Wherein weave latex 30-40%, foam stabilizer 10-16%, bleeding agent 2-
4%, crosslinking agent 0.2-0.6%, ammonium hydroxide 0.5-1.0% constitute anti-flaming thermal-insulation interlayer；Polyurethane 20-30%, silicone oil 4-8%, nanometer two
Titanium oxide 10-16%, dispersing agent 6-8% constitute ultraviolet resistant layer；
Step 2: it is mixed: preparing two agitator tanks, the material for constituting anti-flaming thermal-insulation interlayer is placed on one of stirring
In tank, the material for constituting ultraviolet resistant layer is placed in another agitator tank, it is stirred evenly respectively；
Step 3: coating, drying: coating adhesive on curtain fabric, and anti-flaming thermal-insulation interlayer is coated on curtain fabric
On adhesive, and dried；
Step 4: finished product: coating adhesive on the anti-flaming thermal-insulation interlayer of drying, and ultraviolet resistant layer is pressed from both sides coated in anti-flaming thermal-insulation
On adhesive on layer, and dried to get curtain finished product.
As a preferred technical solution of the invention, in the step 2,5-10min is stirred with 200r/min.
As a preferred technical solution of the invention, in the step 3, anti-flaming thermal-insulation interlayer is coated in curtain
On adhesive on fabric, the drying 10-15min at 140-160 DEG C.
As a preferred technical solution of the invention, in the step 4, by ultraviolet resistant layer be coated in it is fire-retardant every
On adhesive on hot interlayer, the drying 10-15min at 140-160 DEG C.
Compared with prior art, the beneficial effects of the present invention are:
(1) the anti-flaming thermal-insulation interlayer as made from reasonable compatibility increases the effect of the fire-proof and thermal-insulation of curtain；
(2) ultraviolet resistant layer as made from reasonable compatibility increases the effect of the antiultraviolet of curtain, preferably to user into
Row protection, improves the experience of user；
(3) preparation is simple, improves the efficiency of preparation.
Detailed description of the invention
Fig. 1 is fire prevention Window curtain structure schematic diagram of the invention；
Fig. 2 is curtain finished product schematic cross-sectional view of the invention；
Fig. 3 is preparation flow figure of the invention；
In figure: 1, curtain finished product；2, anti-flaming thermal-insulation interlayer；3, ultraviolet resistant layer；4, curtain fabric.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Embodiment 1
Fig. 1, Fig. 2 and Fig. 3 are please referred to, the present invention provides a kind of technical solution: a kind of material for curtain of preventing fires, by weaving latex,
Foam stabilizer, bleeding agent, crosslinking agent, ammonium hydroxide, polyurethane, silicone oil, nano-titanium dioxide, dispersing agent composition, component by weight hundred
Ratio is divided to be calculated as: weaving latex 30%, foam stabilizer 10%, bleeding agent 2%, crosslinking agent 0.2%, ammonium hydroxide 0.8%, polyurethane 30%, silicon
Oil 5%, nano-titanium dioxide 15%, dispersing agent 7%.
Fire retardant is one or more of aluminium oxide, ammonium polyphosphate, magnesia.
Foam stabilizer is one or more of polyacrylamide, polyvinyl alcohol, dodecyldimethylamine oxide.
Bleeding agent is one or more of alcohol ether succinate, phenolic ether succinate, alcohol ether phosphate.
One or more of crosslinking agent cumyl peroxide, di-isopropylbenzene hydroperoxide, benzoyl peroxide.
Dispersing agent is one or more of sodium tripolyphosphate, calgon, sodium pyrophosphate.
A kind of preparation method for curtain of preventing fires, includes the following steps:
Step 1: material and substrate prepare: substrate is curtain fabric 4；Material is by weight percentage are as follows: weaving latex 30%,
Foam stabilizer 10%, bleeding agent 2%, crosslinking agent 0.2%, ammonium hydroxide 0.8%, polyurethane 30%, silicone oil 5%, nano-titanium dioxide 15%, point
Powder 7%；Wherein weaving latex 30%, foam stabilizer 10%, bleeding agent 2%, crosslinking agent 0.2%, ammonium hydroxide 0.8% constitute anti-flaming thermal-insulation
Interlayer 2；Polyurethane 30%, silicone oil 5%, nano-titanium dioxide 15%, dispersing agent 7% constitute ultraviolet resistant layer 3；
Step 2: it is mixed: preparing two agitator tanks, the material for constituting anti-flaming thermal-insulation interlayer 2 is placed on one of them and is stirred
It mixes in tank, the material for constituting ultraviolet resistant layer 3 is placed in another agitator tank, it is stirred evenly respectively；
Step 3: coating, drying: coating adhesive on curtain fabric 4, and anti-flaming thermal-insulation interlayer 2 is coated on curtain fabric 4
Adhesive on, and dried；
Step 4: finished product: coating adhesive on the anti-flaming thermal-insulation interlayer 2 of drying, and ultraviolet resistant layer 3 is coated in anti-flaming thermal-insulation
On adhesive on interlayer 2, and dried to get curtain finished product 1.
In step 2,5min is stirred with 200r/min.
In step 3, anti-flaming thermal-insulation interlayer 2 is coated on the adhesive on curtain fabric 4, the drying at 140 DEG C
15min。
In step 4, ultraviolet resistant layer 3 is coated on the adhesive on anti-flaming thermal-insulation interlayer 2, the drying at 140 DEG C
15min。
Embodiment 2
Fig. 1, Fig. 2 and Fig. 3 are please referred to, the present invention provides a kind of technical solution: a kind of material for curtain of preventing fires, by weaving latex,
Foam stabilizer, bleeding agent, crosslinking agent, ammonium hydroxide, polyurethane, silicone oil, nano-titanium dioxide, dispersing agent composition, component by weight hundred
Ratio is divided to be calculated as: weaving latex 35%, foam stabilizer 15%, bleeding agent 3%, crosslinking agent 0.4%, ammonium hydroxide 0.6%, polyurethane 22%, silicon
Oil 6%, nano-titanium dioxide 12%, dispersing agent 6%.
Fire retardant is one or more of aluminium oxide, ammonium polyphosphate, magnesia.
Foam stabilizer is one or more of polyacrylamide, polyvinyl alcohol, dodecyldimethylamine oxide.
Bleeding agent is one or more of alcohol ether succinate, phenolic ether succinate, alcohol ether phosphate.
One or more of crosslinking agent cumyl peroxide, di-isopropylbenzene hydroperoxide, benzoyl peroxide.
Dispersing agent is one or more of sodium tripolyphosphate, calgon, sodium pyrophosphate.
A kind of preparation method for curtain of preventing fires, includes the following steps:
Step 1: material and substrate prepare: substrate is curtain fabric 4；Material is by weight percentage are as follows: weaving latex 35%,
Foam stabilizer 15%, bleeding agent 3%, crosslinking agent 0.4%, ammonium hydroxide 0.6%, polyurethane 22%, silicone oil 6%, nano-titanium dioxide 12%, point
Powder 6%；Wherein weaving latex 35%, foam stabilizer 15%, bleeding agent 3%, crosslinking agent 0.4%, ammonium hydroxide 0.6% constitute anti-flaming thermal-insulation
Interlayer 2；Polyurethane 22%, silicone oil 6%, nano-titanium dioxide 12%, dispersing agent 6% constitute ultraviolet resistant layer 3；
Step 2: it is mixed: preparing two agitator tanks, the material for constituting anti-flaming thermal-insulation interlayer 2 is placed on one of them and is stirred
It mixes in tank, the material for constituting ultraviolet resistant layer 3 is placed in another agitator tank, it is stirred evenly respectively；
Step 3: coating, drying: coating adhesive on curtain fabric 4, and anti-flaming thermal-insulation interlayer 2 is coated on curtain fabric 4
Adhesive on, and dried；
Step 4: finished product: coating adhesive on the anti-flaming thermal-insulation interlayer 2 of drying, and ultraviolet resistant layer 3 is coated in anti-flaming thermal-insulation
On adhesive on interlayer 2, and dried to get curtain finished product 1.
In step 2,8min is stirred with 200r/min.
In step 3, anti-flaming thermal-insulation interlayer 2 is coated on the adhesive on curtain fabric 4, the drying at 150 DEG C
12min。
In step 4, ultraviolet resistant layer 3 is coated on the adhesive on anti-flaming thermal-insulation interlayer 2, the drying at 150 DEG C
12min。
Embodiment 3
Fig. 1, Fig. 2 and Fig. 3 are please referred to, the present invention provides a kind of technical solution: a kind of material for curtain of preventing fires, by weaving latex,
Foam stabilizer, bleeding agent, crosslinking agent, ammonium hydroxide, polyurethane, silicone oil, nano-titanium dioxide, dispersing agent composition, component by weight hundred
Ratio is divided to be calculated as: weaving latex 40%, foam stabilizer 10%, bleeding agent 4%, crosslinking agent 0.5%, ammonium hydroxide 0.5%, polyurethane 20%, silicon
Oil 4%, nano-titanium dioxide 13%, dispersing agent 8%.
Fire retardant is one or more of aluminium oxide, ammonium polyphosphate, magnesia.
Foam stabilizer is one or more of polyacrylamide, polyvinyl alcohol, dodecyldimethylamine oxide.
Bleeding agent is one or more of alcohol ether succinate, phenolic ether succinate, alcohol ether phosphate.
One or more of crosslinking agent cumyl peroxide, di-isopropylbenzene hydroperoxide, benzoyl peroxide.
Dispersing agent is one or more of sodium tripolyphosphate, calgon, sodium pyrophosphate.
A kind of preparation method for curtain of preventing fires, includes the following steps:
Step 1: material and substrate prepare: substrate is curtain fabric 4；Material is by weight percentage are as follows: weaving latex 40%,
Foam stabilizer 10%, bleeding agent 4%, crosslinking agent 0.5%, ammonium hydroxide 0.5%, polyurethane 20%, silicone oil 4%, nano-titanium dioxide 13%, point
Powder 8%；Wherein weaving latex 40%, foam stabilizer 10%, bleeding agent 4%, crosslinking agent 0.5%, ammonium hydroxide 0.5% constitute anti-flaming thermal-insulation
Interlayer 2；Polyurethane 20%, silicone oil 4%, nano-titanium dioxide 13%, dispersing agent 8% constitute ultraviolet resistant layer 3；
Step 2: it is mixed: preparing two agitator tanks, the material for constituting anti-flaming thermal-insulation interlayer 2 is placed on one of them and is stirred
It mixes in tank, the material for constituting ultraviolet resistant layer 3 is placed in another agitator tank, it is stirred evenly respectively；
Step 3: coating, drying: coating adhesive on curtain fabric 4, and anti-flaming thermal-insulation interlayer 2 is coated on curtain fabric 4
Adhesive on, and dried；
Step 4: finished product: coating adhesive on the anti-flaming thermal-insulation interlayer 2 of drying, and ultraviolet resistant layer 3 is coated in anti-flaming thermal-insulation
On adhesive on interlayer 2, and dried to get curtain finished product 1.
In step 2,10min is stirred with 200r/min.
In step 3, anti-flaming thermal-insulation interlayer 2 is coated on the adhesive on curtain fabric 4, the drying at 160 DEG C
10min。
In step 4, ultraviolet resistant layer 3 is coated on the adhesive on anti-flaming thermal-insulation interlayer 2, the drying at 160 DEG C
10min。
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (10)
1. a kind of material for curtain of preventing fires, which is characterized in that by weaving latex, foam stabilizer, bleeding agent, crosslinking agent, ammonium hydroxide, poly- ammonia
Ester, silicone oil, nano-titanium dioxide, dispersing agent composition, component is by weight percentage are as follows: weaving latex 30-40%, foam stabilizer
10-16%, bleeding agent 2-4%, crosslinking agent 0.2-0.6%, ammonium hydroxide 0.5-1.0%, polyurethane 20-30%, silicone oil 4-8%, nanometer two
Titanium oxide 10-16%, dispersing agent 6-8%.
2. a kind of material of curtain of preventing fires according to claim 1, it is characterised in that: the fire retardant is aluminium oxide, gathers
One or more of ammonium phosphate, magnesia.
3. a kind of material of curtain of preventing fires according to claim 1, it is characterised in that: the foam stabilizer is polyacrylamide
One or more of amine, polyvinyl alcohol, dodecyldimethylamine oxide.
4. a kind of material of curtain of preventing fires according to claim 1, it is characterised in that: the bleeding agent is alcohol ether succinic acid
One or more of salt, phenolic ether succinate, alcohol ether phosphate.
5. a kind of material of curtain of preventing fires according to claim 1, it is characterised in that: the crosslinking agent peroxidating diisopropyl
One or more of benzene, di-isopropylbenzene hydroperoxide, benzoyl peroxide.
6. a kind of material of curtain of preventing fires according to claim 1, it is characterised in that: the dispersing agent is tripolyphosphate
One or more of sodium, calgon, sodium pyrophosphate.
7. a kind of preparation method of curtain of preventing fires according to claim 1-6, it is characterised in that: including walking as follows
It is rapid:
Step 1: material and substrate prepare: substrate is curtain fabric (4)；Material is by weight percentage are as follows: weaving latex 30-
40%, foam stabilizer 10-16%, bleeding agent 2-4%, crosslinking agent 0.2-0.6%, ammonium hydroxide 0.5-1.0%, polyurethane 20-30%, silicone oil
4-8%, nano-titanium dioxide 10-16%, dispersing agent 6-8%；Wherein weave latex 30-40%, foam stabilizer 10-16%, bleeding agent 2-
4%, crosslinking agent 0.2-0.6%, ammonium hydroxide 0.5-1.0% constitute anti-flaming thermal-insulation interlayer (2)；Polyurethane 20-30%, silicone oil 4-8%, receives
Rice titanium dioxide 10-16%, dispersing agent 6-8% constitute ultraviolet resistant layer (3)；
Step 2: it is mixed: preparing two agitator tanks, the material for constituting anti-flaming thermal-insulation interlayer (2) is placed on one of them
In agitator tank, the material for constituting ultraviolet resistant layer (3) is placed in another agitator tank, it is stirred evenly respectively；
Step 3: coating, drying: coating adhesive on curtain fabric (4), and anti-flaming thermal-insulation interlayer (2) are coated in curtain base
On adhesive on cloth (4), and dried；
Step 4: finished product: coating adhesive on the anti-flaming thermal-insulation interlayer (2) of drying, ultraviolet resistant layer (3) is coated in fire-retardant
On adhesive on insulating sandwich (2), and dried to get curtain finished product (1).
8. a kind of preparation method of curtain of preventing fires according to claim 7, it is characterised in that: in the step 2, with
200r/min stirs 5-10min.
9. a kind of preparation method of curtain of preventing fires according to claim 9, it is characterised in that: in the step 3, will hinder
It fires on the adhesive that insulating sandwich (2) are coated on curtain fabric (4), the drying 10-15min at 140-160 DEG C.
10. a kind of preparation method of curtain of preventing fires according to claim 10, it is characterised in that:, will in the step 4
Ultraviolet resistant layer (3) is coated on the adhesive on anti-flaming thermal-insulation interlayer (2), the drying 10-15min at 140-160 DEG C.