CN110292909A - A kind of modified active carbon fiber composite material and preparation method - Google Patents
A kind of modified active carbon fiber composite material and preparation method Download PDFInfo
- Publication number
- CN110292909A CN110292909A CN201910589601.3A CN201910589601A CN110292909A CN 110292909 A CN110292909 A CN 110292909A CN 201910589601 A CN201910589601 A CN 201910589601A CN 110292909 A CN110292909 A CN 110292909A
- Authority
- CN
- China
- Prior art keywords
- sizing carrier
- carrier
- carbon fiber
- auxiliary
- fiber composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of modified active carbon fiber composite material and preparation method, the modified active carbon fiber composite material includes: activated carbon fibre, is bonded in main sizing carrier, the auxiliary sizing carrier on the activated carbon fibre two sides respectively;Wherein the main sizing carrier and auxiliary sizing carrier are all made of gas permeability material;The main sizing carrier uses hard material;And the auxiliary sizing carrier uses soft material;Modified active carbon fiber composite material of the invention is by distinguishing compound main sizing carrier, auxiliary sizing carrier on the two sides of activated carbon fibre, solve the problems, such as existing activated carbon fiber material can not secondary operation so that this modified active carbon fiber composite material is applicable in civilian processing.
Description
Technical field
The present invention relates to activated carbon fiber material complex technique fields, and in particular to a kind of modified active carbon fiber composite wood
Material and preparation method thereof.
Background technique
Activated carbon fibre is a kind of good adsorbent material, can be adsorbed to the exhaust gas of benzene class, ketone, esters, petroleum-type
Recycling, and adsorption rate is fast, large amount of adsorption, can be widely used for Water warfare, air purification field, but is at present on industry environmental protection
It is used, civilian aspect is almost blank, and main cause is that activated carbon fibre is first to be carbonized to form through high-temperature activation again, property
Shape is ashes, without strength, cohesive force, therefore is unfavorable for secondary operation molding, more has no idea using production line volume production, thus
Cause in the market the product for civilian use be almost blank.
Present invention mainly solves the Complex Problem of activated carbon fibre, make it is compound after activated carbon fibre still maintain its absorption
Function, while having and can be used for production line volume production, so that various products are processed into, such as automobile air conditioner filter element, domestic air conditioning filter core, work
Industry filter core, bus air conditioner filter core, central air-conditioning filter core, filtering element for air purifier, filter core volume, breathing mask etc. expand activity
The application range of Carbon fibe.
Summary of the invention
The object of the present invention is to provide a kind of modified active carbon fiber composite material and preparation methods.
In order to solve the above-mentioned technical problems, the present invention provides a kind of modified active carbon fiber composite materials, comprising: activity
Carbon fibe is bonded in main sizing carrier, the auxiliary sizing carrier on the activated carbon fibre two sides respectively;Wherein the main sizing carries
Body and auxiliary sizing carrier are all made of gas permeability material;The main sizing carrier uses hard material;And the auxiliary sizing
Carrier uses soft material.
Further, the main sizing carrier is one such using eyelet fabric, mesh plastics or mesh metal;The auxiliary
Carrier of being formed is one such using eyelet fabric, looped fabric, woven fabric or non-woven fabrics.
Another aspect, the present invention also provides a kind of preparation methods of modified active carbon fiber composite material, comprising: step
S1, the main sizing carrier and auxiliary sizing carrier of size needed for preparing;And step S2, main sizing carrier and auxiliary sizing are carried
Body is respectively adhered to the two sides of activated carbon fibre.
Further, in the step S2, the main sizing carrier and auxiliary sizing carrier are all made of hot melt adhesive, with spray
The mode of painting, blade coating or spot printing is respectively adhered to the two sides of activated carbon fibre.
Further, the main sizing carrier and auxiliary sizing carrier are all made of gas permeability material;The main sizing carrier is adopted
Use hard material;And the auxiliary sizing carrier uses soft material.
Further, the main sizing carrier is one such using eyelet fabric, mesh plastics or mesh metal;The auxiliary
Carrier of being formed is one such using eyelet fabric, looped fabric, woven fabric or non-woven fabrics.
The invention has the advantages that modified active carbon fiber composite material of the invention passes through the two of activated carbon fibre
Compound main sizing carrier, auxiliary sizing carrier are distinguished in face, solve the problems, such as that existing activated carbon fiber material can not secondary operation;And
The main sizing carrier and auxiliary sizing carrier be all made of gas permeability material, with ensure it is compound after activated carbon fibre still maintain
Its absorption property;In addition, the main sizing carrier uses hard material, it can be ensured that this modified active Carbon fiber in the present embodiment
The molding effect of composite material is tieed up, such as folds fixed effect, molding fixed effect and hot-forming effect, and the auxiliary is fixed
Type carrier use soft material, it can be ensured that this modified active carbon fiber composite material has the enough power of pullling, meet it is different at
The demand of type shape, to play the role of auxiliary sizing.
Detailed description of the invention
Present invention will be further explained below with reference to the attached drawings and examples.
Fig. 1 is the structural schematic diagram of modified active carbon fiber composite material of the invention.
Wherein:
Main sizing carrier 10, auxiliary sizing carrier 20, activated carbon fibre 30.
Specific embodiment
In conjunction with the accompanying drawings, the present invention is further explained in detail.These attached drawings are simplified schematic diagram, only with
Illustration illustrates basic structure of the invention, therefore it only shows the composition relevant to the invention.
Embodiment 1
As shown in Figure 1, the present embodiment 1 provides a kind of modified active carbon fiber composite material, comprising: activated carbon fibre
30, it is bonded in main sizing carrier 10, the auxiliary sizing carrier 20 on 30 two sides of activated carbon fibre respectively;The wherein main sizing
Carrier 10 and auxiliary sizing carrier 20 are all made of gas permeability material;The main sizing carrier 10 uses hard material;And it is described
Auxiliary sizing carrier 20 uses soft material.
Specifically, this modified active carbon fiber composite material is by distinguishing compound main sizing on the two sides of activated carbon fibre 30
Carrier 10, auxiliary sizing carrier 20, solve the problems, such as that existing activated carbon fiber material can not secondary operation;And the main sizing carries
Body 10 and auxiliary sizing carrier 20 be all made of gas permeability material, with ensure it is compound after activated carbon fibre still maintain its adsorptivity
Energy;In addition, the main sizing carrier 10 uses hard material, it can be ensured that this modified active carbon fiber is compound in the present embodiment
The molding effect of material, such as fixed effect, molding fixed effect and hot-forming effect are folded, and auxiliary sizing carrier
20 use soft material, it can be ensured that this modified active carbon fiber composite material has the enough power of pullling, and meets different molding shapes
The demand of shape, to play the role of auxiliary sizing.
Specifically, the main sizing carrier 10 can use eyelet fabric, mesh plastics or net according to different application requirements
Eye metal is one such;The auxiliary sizing carrier 20 is using eyelet fabric, looped fabric, woven fabric or non-woven fabrics therein one
Kind.
Embodiment 2
On the basis of embodiment 1, the present embodiment 2 provides a kind of preparation side of modified active carbon fiber composite material
Method, comprising: step S1, the main sizing carrier 10 and auxiliary sizing carrier 20 of size needed for preparing;And step S2, by main sizing
Carrier 10 and auxiliary sizing carrier 20 are respectively adhered to the two sides of activated carbon fibre 30.
Specifically, the preparation method of this modified active carbon fiber composite material uses hot melt adhesive, with spraying, blade coating or spot printing
Mode distinguish compound main sizing carrier 10 on the two sides of activated carbon fibre 30, auxiliary is formed carrier 20, solve existing activity
Carbon fibe material can not secondary operation the problem of, so that activated carbon fiber material be made to be applicable in civilian processing.
In the step S2, the main sizing carrier 10 and auxiliary sizing carrier 20 are all made of hot melt adhesive, to spray, scrape
The mode of painting or spot printing is respectively adhered to the two sides of activated carbon fibre 30.
The main sizing carrier 10 and auxiliary sizing carrier 20 are all made of gas permeability material;The main sizing carrier 10 uses
Hard material;And the auxiliary sizing carrier 20 uses soft material.
The main sizing carrier 10 is one such using eyelet fabric, mesh plastics or mesh metal;The auxiliary sizing
Carrier 20 is one such using eyelet fabric, looped fabric, woven fabric or non-woven fabrics.
Specifically, the main sizing carrier 10 and auxiliary sizing carrier 20 are all made of gas permeability material, with ensure it is compound after
Activated carbon fibre still maintain its absorption property;In addition, the main sizing carrier 10 uses hard material in the present embodiment,
It may insure the molding effect of this modified active carbon fiber composite material, such as fold fixed effect, molding fixed effect and hot pressing
Molding effect etc., and auxiliary sizing carrier 20 uses soft material, it can be ensured that this modified active carbon fiber composite material
There is the enough power of pullling, meet the needs of different forming shapes, to play the role of auxiliary sizing.
Specifically, the sizing to finished product can be made in the modified active carbon fiber composite material made of this preparation method
The higher product of effect requirements, as automobile air conditioner filter element, domestic air conditioning filter core, industrial filter core, bus air conditioner filter element, strainer,
Strainer volume, breathing mask or filtering element for air purifier etc..
Taking the above-mentioned ideal embodiment according to the present invention as inspiration, through the above description, relevant staff is complete
Various changes and amendments can be carried out without departing from the scope of the technological thought of the present invention' entirely.The technology of this invention
Property range is not limited to the contents of the specification, it is necessary to which the technical scope thereof is determined according to the scope of the claim.
Claims (6)
1. a kind of modified active carbon fiber composite material characterized by comprising
Activated carbon fibre is bonded in main sizing carrier, the auxiliary sizing carrier on the activated carbon fibre two sides respectively;Wherein
The main sizing carrier and auxiliary sizing carrier are all made of gas permeability material;
The main sizing carrier uses hard material;And
The auxiliary sizing carrier uses soft material.
2. modified active carbon fiber composite material according to claim 1, which is characterized in that
The main sizing carrier is one such using eyelet fabric, mesh plastics or mesh metal;
The auxiliary sizing carrier is one such using eyelet fabric, looped fabric, woven fabric or non-woven fabrics.
3. a kind of preparation method of modified active carbon fiber composite material characterized by comprising
Step S1, the main sizing carrier and auxiliary sizing carrier of size needed for preparing;And
Main sizing carrier and auxiliary sizing carrier are respectively adhered to the two sides of activated carbon fibre by step S2.
4. the preparation method of modified active carbon fiber composite material according to claim 3, which is characterized in that
In the step S2, the main sizing carrier and auxiliary sizing carrier are all made of hot melt adhesive, with spraying, blade coating or spot printing
Mode be respectively adhered to the two sides of activated carbon fibre.
5. the preparation method of modified active carbon fiber composite material according to claim 4, which is characterized in that
The main sizing carrier and auxiliary sizing carrier are all made of gas permeability material;
The main sizing carrier uses hard material;And
The auxiliary sizing carrier uses soft material.
6. the preparation method of modified active carbon fiber composite material according to claim 5, which is characterized in that
The main sizing carrier is one such using eyelet fabric, mesh plastics or mesh metal;
The auxiliary sizing carrier is one such using eyelet fabric, looped fabric, woven fabric or non-woven fabrics.