CN110282888A - A kind of circulating fluid bed coal ash base supplementary cementitious material and its preparation method and application - Google Patents
A kind of circulating fluid bed coal ash base supplementary cementitious material and its preparation method and application Download PDFInfo
- Publication number
- CN110282888A CN110282888A CN201910597401.2A CN201910597401A CN110282888A CN 110282888 A CN110282888 A CN 110282888A CN 201910597401 A CN201910597401 A CN 201910597401A CN 110282888 A CN110282888 A CN 110282888A
- Authority
- CN
- China
- Prior art keywords
- coal ash
- cementitious material
- fluid bed
- circulating fluid
- supplementary cementitious
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of circulating fluid bed coal ash base supplementary cementitious material and its preparation method and application, that the purpose of the present invention is to solve the cement concrete early strengths of existing supplementary cementitious material preparation is low, shrinks the technical problems such as big, slump-loss, at high cost;The technical solution adopted by the present invention is that: a kind of circulating fluid bed coal ash base supplementary cementitious material comprises the following raw materials by weight percent: flyash 40~90%, clinker 5~50% and grain slag 2~10%;Al in the flyash2O3>=30%, f-CaO≤2%, SO3≤ 3%;Circulating fluid bed coal ash base supplementary cementitious material large specific surface area produced by the present invention, activity index are high, it can be used for making cement, or replacing partial cement prepares strong concrete, be conducive to improve the workability and durability of concrete, improve the intensity and seepage-resistant grade of concrete, with good workability, while the use of clinker is reduced, and then reduces carbon emission.
Description
Technical field
The invention belongs to field of cementing material technology, and in particular to a kind of circulating fluid bed coal ash base supplementary cementitious material
And its preparation method and application.
Background technique
With the development of cement, concrete technology, the effect that supplementary cementitious material plays becomes more and more important, not only can generation
Cement is prepared for part clinker, part of cement can also be replaced to be used for the production of concrete.
Currently, common supplementary cementitious material mainly has silicon ash, lime stone, slag, flyash etc..Single auxiliary gelling
Material has certain problems in application, such as because volcanic ash activity of coal ash effect is poor, causes the cement of adding coal ash mixed
Solidifying soil material early strength is low, and the performance of chloride-penetration resistance, anti-carbonation and anti-early-age shrinkage declines;Add the cement of slag
Concrete material shrinks larger;The surface area of silicon ash is larger, and water requirement is high, need to match with water-reducing agent when applied in cement concrete
It closes and uses, increase cost, and the loss of concrete slump can be caused to a certain extent.
While the fields such as electric power, metallurgy rapidly develop in China, a large amount of flyash, clinker, grain slag etc. one is produced
As industrial solid castoff.In recent years, circulating fluidized bed boiler generation technology is because such as gangue, wind oxidized coal can be used in it
Equal wastes or inferior fuel are widely used, but the flyash that generates of its power generation and clinker this 2 kinds of solid waste amounts are significantly larger than
The solid waste amount that same size coal-powder boiler generation technology generates.Further, since boiler hearth of circulating fluidized bed internal temperature is lower, adopt
With limestone desulfurization is sprayed into furnace, cause to restrict it in building materials there are a certain amount of free calcium oxide in flyash and clinker
Direct utilization in field causes it lower using level, it would be highly desirable to open up scale, resource utilization approach.
The stockpiling of the industrial solid castoffs such as circulating fluid bed coal ash and clinker and grain slag brings serious environment
Pollution problem restricts economic sustainable development.Therefore, the resource utilization of solid waste, which becomes, needs urgent solution
Problem.
Summary of the invention
Low, receipts that the purpose of the present invention is to solve the cement concrete early strengths of existing supplementary cementitious material preparation
Contracting is big, slump-loss, it is at high cost the problems such as, while solving circulating fluid bed coal ash directly application be limited in construction material
The problem of, a kind of energy saving, small circulating fluid bed coal ash Kiev low with production cost of environmental pollution is provided and helps gelling material
Material and its preparation method and application.
In order to solve the above technical problems, the technical solution adopted by the present invention is that:
A kind of circulating fluid bed coal ash base supplementary cementitious material, comprises the following raw materials by weight percent: flyash
40~90%, clinker 5~50% and grain slag 2~10%;
The flyash and clinker is the solid waste that circulating fluidized bed boiler power generation generates, and the grain slag is blast furnace
Generated fusant when manUfaCtUre of pig iron, the solid waste formed through water quenching;Al in the flyash2O3>=30%, f-
CaO≤2%, SO3≤ 3%.
Further, the specific surface area of the circulating fluid bed coal ash base supplementary cementitious material is 650~710m2/
Kg, 45 μm tail over≤8%.
Further, the activity index of the circulating fluid bed coal ash base supplementary cementitious material is not less than 65%.
The preparation method of above-mentioned circulating fluid bed coal ash base supplementary cementitious material, comprising the following steps: by weight percent
25~45min of grinding is cooperateed with through ball mill than flyash, 5~50% clinker and 2~10% grain slag for 40~90%, from
And circulating fluid bed coal ash base supplementary cementitious material is made.
The application of above-mentioned circulating fluid bed coal ash base supplementary cementitious material, described circulating fluid bed coal ash Kiev help glue
Gel material is used to prepare 42.5 cement.
The application of above-mentioned circulating fluid bed coal ash base supplementary cementitious material, described circulating fluid bed coal ash Kiev help glue
Gel material is used to prepare C40 concrete.
The beneficial effects of the present invention are:
1, the present invention uses the industrial solid castoffs such as circulating fluid bed coal ash and clinker, grain slag for raw material, produces work
Skill is simple, low production cost, energy consumption are small, economic and environment-friendly, it can be achieved that scale utilizes, while solving recirculating fluidized bed fine coal
Ash, clinker and the intractable status of grain slag, realize the effective use of solid waste resource, turn waste into wealth, at the same solve its stockpiling with
And the problems such as land occupation.
2, circulating fluid bed coal ash base supplementary cementitious material produced by the present invention, large specific surface area, activity index is high, can
Strong concrete is prepared for making cement or replacing partial cement, is conducive to the workability and durability that improve concrete,
The intensity and seepage-resistant grade of concrete are improved, there is good workability, while reducing the use of clinker, and then is reduced
Carbon emission.
3, circulating fluid bed coal ash base supplementary cementitious material produced by the present invention is applied to Shi Buxu in cement concrete
It to be used cooperatively with water-reducing agent, production cost can be reduced.
Specific embodiment
The present invention is described in further details below with reference to embodiment.
Embodiment 1
One of the present embodiment circulating fluid bed coal ash base supplementary cementitious material, by the raw material of following weight percent
Composition: flyash 40~90%, clinker 5~50% and grain slag 2~10%;
The flyash and clinker is the solid waste that circulating fluidized bed boiler power generation generates, and the grain slag is blast furnace
Generated fusant when manUfaCtUre of pig iron, the solid waste formed through water quenching;Al in the flyash2O3>=30%, f-
CaO≤2%, SO3≤ 3%.
The specific surface area of the circulating fluid bed coal ash base supplementary cementitious material is 650~710m2/ kg, 45 μm of sieves
Remaining≤8%, activity index is not less than 65%.
The preparation method of above-mentioned circulating fluid bed coal ash base supplementary cementitious material, comprising the following steps: by weight percent
25~45min of grinding is cooperateed with through ball mill than flyash, 5~50% clinker and 2~10% grain slag for 40~90%, from
And circulating fluid bed coal ash base supplementary cementitious material is made.
Embodiment 2
One of the present embodiment circulating fluid bed coal ash base supplementary cementitious material, by the raw material of following weight percent
Composition: flyash 40%, clinker 50% and grain slag 10%;Al in the flyash2O3Content be 35%, f-CaO content be
1.5%, SO3Content is 2.8%.
The preparation method of above-mentioned circulating fluid bed coal ash base supplementary cementitious material comprising the following steps: will be described heavy
Flyash, clinker and the grain slag for measuring percentage cooperate with grinding 45min through ball mill, so that circulating fluid bed coal ash Kiev be made
Help cementitious material.
The performance of circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment are as follows: moisture content 1.0% needs
Water ratio is 104%, 3 days, 7 days, 28 days activity indexs be respectively 65%, 87%, 94%, specific surface area 650m2/ kg,
It is 8% that 45 μm, which tail over,.
Circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment is used to prepare 42.5 cement, and incorporation is
When 40%, obtained cement normal consistency water consumption is 135ml, presetting period 160min, final setting time 270min;3d intensity
Up to 26.9MPa, 28d intensity reaches 48.8MPa.
The cement of the substitution of circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment 35% prepares C40 coagulation
Soil, concrete workability can be good, and 7 days and 28 days intensity are respectively 42.5MPa, 60.4MPa, and seepage-resistant grade is up to P12.
Embodiment 3
One of the present embodiment circulating fluid bed coal ash base supplementary cementitious material, by the raw material of following weight percent
Composition: flyash 90%, clinker 5% and grain slag 5%;Wherein, Al in flyash2O3Content be 34%, f-CaO content be
1.6%, SO3Content is 2.6%.
The preparation method of above-mentioned circulating fluid bed coal ash base supplementary cementitious material, comprising the following steps: by the weight
Flyash, clinker and the grain slag of percentage cooperate with grinding 25min through ball mill, help so that circulating fluid bed coal ash Kiev be made
Cementitious material.
The performance of circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment are as follows: moisture content 1.0% needs
Water ratio is 98.5%, 3 days, 7 days, 28 days activity indexs be respectively 63%, 85%, 103%, specific surface area 700m2/
Kg, it is 4.6% that 45 μm, which tail over,.
Circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment is used to prepare 42.5 cement, and incorporation is
When 40%, consumptive use of water normal consistence 136ml, pre-hardening used time 120min, final set used time 278min;3d intensity reaches 27.3MPa,
28d intensity reaches 50.3MPa.
The cement of the substitution of circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment 35% prepares C40 coagulation
Soil, concrete workability can be good, and 7 days and 28 days intensity are respectively 42.7MPa, 61.2MPa, and seepage-resistant grade is up to P12.
Embodiment 4
One of the present embodiment circulating fluid bed coal ash base supplementary cementitious material, by the raw material of following weight percent
Composition: flyash 75%, clinker 23% and grain slag 2%;Wherein, Al in flyash2O3Content be 35%, f-CaO content be
1.5%, SO3Content is 2.8%.
The preparation method of above-mentioned circulating fluid bed coal ash base supplementary cementitious material comprising the following steps: will be described heavy
Flyash, clinker and the grain slag for measuring percentage cooperate with grinding 30min through ball mill in proportion, so that recirculating fluidized bed fine coal be made
Grey base supplementary cementitious material.
The performance of circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment are as follows: moisture content 1.0% needs
Water ratio is 100%, 3 days, 7 days, 28 days activity indexs be respectively 68%, 88%, 101%, specific surface area 686m2/ kg,
It is 6% that 45 μm, which tail over,.
Circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment is used to prepare 42.5 cement, and incorporation is
When 40%, consumptive use of water normal consistence 138ml, pre-hardening used time 129min, final set used time 293min;3d intensity reaches 26.7MPa,
28d intensity reaches 49.8MPa;
The cement of the substitution of circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment 35% prepares C40 coagulation
Soil, concrete workability can be good, and 7 days and 28 days intensity are respectively 42.6MPa, 60.3MPa, and seepage-resistant grade is up to P12.
Embodiment 5
One of the present embodiment circulating fluid bed coal ash base supplementary cementitious material, by the raw material of following weight percent
Composition: flyash 55%, clinker 38% and grain slag 7%;Wherein, Al in flyash2O3Content is that 34%, f-CaO content is
1.4%, SO3Content is 2.6%.
The preparation method of above-mentioned circulating fluid bed coal ash base supplementary cementitious material comprising the following steps: will be described heavy
Flyash, clinker and the grain slag for measuring percentage cooperate with grinding 35min through ball mill in proportion, so that recirculating fluidized bed fine coal be made
Grey base supplementary cementitious material.
The performance of circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment are as follows: moisture content 1.0% needs
Water ratio is 99.5%, 3 days, 7 days, 28 days activity indexs be respectively 66%, 85%, 104%, specific surface area 710m2/
Kg, it is 3.5% that 45 μm, which tail over,.
Circulating fluid bed coal ash base supplementary cementitious material made from the present embodiment substitutes 40% clinker and prepares 42.5 cement,
Consumptive use of water normal consistence is 135ml, pre-hardening used time 120min, final set used time 285min;3d intensity reaches 27.5MPa, and 28d intensity reaches
50.1MPa;The cement of substitution 35% prepares C40 concrete, and concrete workability can be good, and 7 days and 28 days intensity are respectively
42.8MPa, 60.8MPa, seepage-resistant grade reach P12.
Above-mentioned circulating fluid bed coal ash base supplementary cementitious material can also be used to prepare light-weight building material.
The weight percent of flyash of the invention, clinker and grain slag can also be: 40~90wt% of flyash, clinker 5
Any combination selects in 2~10wt% of~50wt% and grain slag, and protection scope is not restricted to the described embodiments.
Claims (6)
1. a kind of circulating fluid bed coal ash base supplementary cementitious material, which is characterized in that by the raw material group of following weight percent
At: flyash 40~90%, clinker 5~50% and grain slag 2~10%;
The flyash and clinker is the solid waste that circulating fluidized bed boiler power generation generates, and the grain slag is blast furnace process
Generated fusant when the pig iron, the solid waste formed through water quenching;Al in the flyash2O3>=30%, f-CaO
≤ 2%, SO3≤ 3%.
2. a kind of circulating fluid bed coal ash base supplementary cementitious material according to claim 1, it is characterised in that: described
The specific surface area of circulating fluid bed coal ash base supplementary cementitious material is 650~710m2/ kg, 45 μm tail over≤8%.
3. a kind of circulating fluid bed coal ash base supplementary cementitious material according to claim 1, it is characterised in that: described
The activity index of circulating fluid bed coal ash base supplementary cementitious material is not less than 65%.
4. a kind of preparation method of circulating fluid bed coal ash base supplementary cementitious material, feature described in claim 1-3 exist
In, comprising the following steps: by weight percent be 40~90% flyash, 5~50% clinker and 2~10% grain slag pass through
Ball mill cooperates with 25~45min of grinding, so that circulating fluid bed coal ash base supplementary cementitious material be made.
5. a kind of application of circulating fluid bed coal ash base supplementary cementitious material described in claim 1-3, it is characterised in that: institute
It states circulating fluid bed coal ash base supplementary cementitious material and is used to prepare 42.5 cement.
6. a kind of application of circulating fluid bed coal ash base supplementary cementitious material described in claim 1-3, it is characterised in that: institute
It states circulating fluid bed coal ash base supplementary cementitious material and is used to prepare C40 concrete.