Rainbow mark die press technology for forming and rainbow mark
Technical field
The invention belongs to rainbow mark production technical fields, more particularly to mark die press technology for forming and rainbow mark.
Background technique
Rubber label has been obtained in real life to be widely applied;Rubber can be seen on clothing, shoes etc.
The figure of glue label.
Existing rubber label is typically all transparent materials, by different colors come display pattern, when class to be realized
When the purpose of rainbow gradient color, need first to concoct colorful rubber to form different colors then in order by different color pressures
It closes;
Alternatively, some gradient colors are to be coated to form gradient color in substrate surface by pigment;
The gradient color of above-mentioned rainbow labeling all can not achieve natural gradual change or ageing resistance is poor.
Existing some transparent labelings all do not have substrate, when it is used, are easy mutually to mix with other colors, cause color
Difference.
Summary of the invention
To solve the above-mentioned problems, the present invention adopts the following technical scheme:
Rainbow mark die press technology for forming, includes the following steps,
S1 places the first primary colors glue, the second primary colors glue, third primary color glue in pressing mold, has between adjacent two primary colors glue
Overlapping portion, the first primary colors glue, the second primary colors glue, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding;
S3, taking 1 molding is No.1 molding, n molding of matching superposition, 1 mould of every superposition on No.1 molding
Casting die is molded 1 time, molding chromatograph is formed, wherein 1≤n≤3, n are integer;
S4 is superimposed substrate on molding chromatograph, is molded.
Preferably, in S2, S3, mold pressing parameter is room temperature, time: 5s, 100~120kg/cm2 of pressure.
Preferably, in S4, mold pressing parameter is temperature: 160~165 DEG C, the time: and 240 "~280 ", pressure: 100~
120kg/cm2。
Preferably, having overlapping portion width in S1, between adjacent two primary colors glue is the 40-50% of molding width.
Preferably, n molding width of superposition is the 80-90% of No.1 molding width.
Preferably, the shapes of substrates matches with molding chromatograph shape, and the substrate is white.
Rainbow mark manufactured by rainbow mark die press technology for forming,
Including substrate, the substrate one side is equipped with molding chromatograph;
The molding chromatograph head end to end is successively arranged the first primary colors glue part, the second primary colors glue part and third primary color glue
Part;
The first primary colors glue part, the second primary colors glue part and third primary color glue part correspond respectively to a kind of face in three primary colors
Color;
Color part is laminated between the first primary colors glue part and the second primary colors glue part for first;The second primary colors glue part and
Color part is laminated between three primary colors glue part for second.
Preferably, the three primary colors are red, yellow, blue.
Preferably, the first primary colors glue part, first laminate color part, the second primary colors glue part, second laminate color part and third
Primary colors glue part is transparent material.
Preferably, it described first laminates color part and is overrided to form by the first primary colors glue and the second primary colors glue;Described second
Color part is laminated to be overrided to form by the second primary colors glue and third primary color glue.
The beneficial effects of the present invention are:
1. non-aging, color is more bright-coloured;
2. it can be used in more environment, it is not easy to change under white substrate protection;
3. the secondary superposition of molding so that chromatograph is superimposed, is had better effect, so that rainbow mark is more beautiful.
Detailed description of the invention
Fig. 1 is a kind of the schematic diagram of the section structure of the present invention;
Fig. 2 is a kind of overlooking structure diagram of the present invention.
In figure:
100 molding chromatographs, 110 first primary colors glue parts, 120 first laminate color part, and 130 second primary colors glue parts, 140 second is folded
Press color part, 150 third primary color glue parts, 200 substrates.
Specific embodiment
The present invention will be further described below in conjunction with the embodiments:
Embodiment 1
Rainbow mark die press technology for forming, includes the following steps,
S1 places the first primary colors glue, the second primary colors glue, third primary color glue, the abutting end of adjacent two primary colors glue in pressing mold
With overlapping portion, the abutting end overlapping portion width of adjacent two primary colors glue is the 40% of molding width, the first primary colors glue, the second original
Coloring agent, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 100kg/cm2;
S3 takes 1 molding as No.1 molding, 1 molding of matching superposition, the mould of superposition on No.1 molding
Casting die width is the 80% of No.1 molding width, and mold pressing parameter is room temperature, time: 5 ", pressure 100kg/cm2, form molding
Chromatograph;
S4, superposition and the matched white substrate of its shape on molding chromatograph, molding, mold pressing parameter is temperature: 160 DEG C,
Time: 240 ", pressure: 100kg/cm2。
Embodiment 2
Rainbow mark die press technology for forming, includes the following steps,
S1 places the first primary colors glue, the second primary colors glue, third primary color glue, the abutting end of adjacent two primary colors glue in pressing mold
With overlapping portion, the abutting end overlapping portion width of adjacent two primary colors glue is the 50% of molding width, the first primary colors glue, the second original
Coloring agent, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 120kg/cm2;
S3 takes 1 molding as No.1 molding, 1 molding of matching superposition, the mould of superposition on No.1 molding
Casting die width is the 90% of No.1 molding width, and mold pressing parameter is room temperature, time: 5 ", pressure 120kg/cm2, form molding
Chromatograph;
S4, superposition and the matched white substrate of its shape on molding chromatograph, molding, mold pressing parameter is temperature: 165 DEG C,
Time: 280 ", pressure: 120kg/cm2。
Embodiment 3
Rainbow mark die press technology for forming, includes the following steps,
S1 places the first primary colors glue, the second primary colors glue, third primary color glue, the abutting end of adjacent two primary colors glue in pressing mold
With overlapping portion, the abutting end overlapping portion width of adjacent two primary colors glue is the 45% of molding width, the first primary colors glue, the second original
Coloring agent, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 110kg/cm2;
S3 takes 1 molding as No.1 molding, 1 molding of matching superposition, the mould of superposition on No.1 molding
Casting die width is the 85% of No.1 molding width, and mold pressing parameter is room temperature, time: 5 ", pressure 110kg/cm2, form molding
Chromatograph;
S4, superposition and the matched white substrate of its shape on molding chromatograph, molding, mold pressing parameter is temperature: 162 DEG C,
Time: 260 ", pressure: 110kg/cm2。
Embodiment 4
Rainbow mark die press technology for forming, includes the following steps,
S1 places the first primary colors glue, the second primary colors glue, third primary color glue, the abutting end of adjacent two primary colors glue in pressing mold
With overlapping portion, the abutting end overlapping portion width of adjacent two primary colors glue is the 40% of molding width, the first primary colors glue, the second original
Coloring agent, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 100kg/cm2;
S3 takes 1 molding as No.1 molding, 1 molding of matching superposition, the mould of superposition on No.1 molding
Casting die width is the 80% of No.1 molding width, and mold pressing parameter is room temperature, time: 5 ", pressure 100kg/cm2, form molding
Chromatograph.
Embodiment 5
Rainbow mark die press technology for forming, includes the following steps,
S1 places the first primary colors glue, the second primary colors glue, third primary color glue, the abutting end of adjacent two primary colors glue in pressing mold
With overlapping portion, the abutting end overlapping portion width of adjacent two primary colors glue is the 50% of molding width, the first primary colors glue, the second original
Coloring agent, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 120kg/cm2;
S3 takes 1 molding as No.1 molding, 3 moldings of matching superposition on No.1 molding, every superposition 1
A molding is molded 1 time, selects or cut out molding, and the molding width of superposition is the 90% of No.1 molding width, molding
Condition is room temperature, time: 5 ", pressure 120kg/cm2, form molding chromatograph;
S4, superposition and the matched white substrate of its shape on molding chromatograph, molding, mold pressing parameter is temperature: 165 DEG C,
Time: 280 ", pressure: 120kg/cm2。
Embodiment 6
Rainbow mark die press technology for forming, includes the following steps,
S1 places the first primary colors glue, the second primary colors glue, third primary color glue, the abutting end of adjacent two primary colors glue in pressing mold
With overlapping portion, the abutting end overlapping portion width of adjacent two primary colors glue is the 50% of molding width, the first primary colors glue, the second original
Coloring agent, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 120kg/cm2;
S3 takes 1 molding as No.1 molding, 3 moldings of matching superposition on No.1 molding, every superposition 1
A molding is molded 1 time, and the molding width of superposition is the 100% of No.1 molding width, and mold pressing parameter is room temperature, the time:
5 ", pressure 120kg/cm2, form molding chromatograph;
S4, superposition and the matched white substrate of its shape on molding chromatograph, molding, mold pressing parameter is temperature: 165 DEG C,
Time: 280 ", pressure: 120kg/cm2。
Embodiment 7
Rainbow mark die press technology for forming, includes the following steps,
S1 places the first primary colors glue, the second primary colors glue, third primary color glue, the abutting end of adjacent two primary colors glue in pressing mold
With overlapping portion, the abutting end overlapping portion width of adjacent two primary colors glue is the 45% of molding width, the first primary colors glue, the second original
Coloring agent, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 110kg/cm2;
S3, the white substrate matched, molding, mold pressing parameter is temperature: 162 DEG C, the time: 260 " and, pressure: 110kg/cm2。
Embodiment 8
Rainbow mark die press technology for forming, includes the following steps,
S1 is sequentially placed the first primary colors glue, the second primary colors glue, third primary color glue, the phase of adjacent two primary colors glue in pressing mold
Neighboring terminal end connects, and the first primary colors glue, the second primary colors glue, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 110kg/cm2;
S3 takes 1 molding as No.1 molding, 1 molding of matching superposition, the mould of superposition on No.1 molding
Casting die width is the 85% of No.1 molding width, and mold pressing parameter is room temperature, time: 5 ", pressure 110kg/cm2, form molding
Chromatograph;
S4, superposition and the matched white substrate of its shape on molding chromatograph, molding, mold pressing parameter is temperature: 162 DEG C,
Time: 260 ", pressure: 110kg/cm2。
Embodiment 9
Rainbow mark die press technology for forming, includes the following steps,
S1 is sequentially placed the first primary colors glue, the second primary colors glue, third primary color glue, the phase of adjacent two primary colors glue in pressing mold
Neighboring terminal end connects, and the first primary colors glue, the second primary colors glue, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 110kg/cm2;
S3 takes 1 molding as No.1 molding, 3 moldings of matching superposition, the mould of superposition on No.1 molding
Casting die width is the 85% of No.1 molding width, often laminates one-step mould successively, mold pressing parameter is room temperature, time: 5 ", pressure
110kg/cm2, form molding chromatograph;
S4, superposition and the matched white substrate of its shape on molding chromatograph, molding, mold pressing parameter is temperature: 162 DEG C,
Time: 260 ", pressure: 110kg/cm2。
Embodiment 10
Rainbow mark die press technology for forming, includes the following steps,
S1 is sequentially placed the first primary colors glue, the second primary colors glue, third primary color glue, the phase of adjacent two primary colors glue in pressing mold
Neighboring terminal end connects, and the first primary colors glue, the second primary colors glue, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 110kg/cm2;
S3, superposition and the matched white substrate of its shape on molding chromatograph, molding, mold pressing parameter is temperature: 162 DEG C,
Time: 260 ", pressure: 110kg/cm2。
Embodiment 11
Rainbow mark die press technology for forming, includes the following steps,
S1 places the first primary colors glue, the second primary colors glue, third primary color glue, the abutting end of adjacent two primary colors glue in pressing mold
With overlapping portion, the abutting end overlapping portion width of adjacent two primary colors glue is the 45% of molding width, the first primary colors glue, the second original
Coloring agent, third primary color glue respectively correspond a kind of color in three primary colors;
S2, molding is primary, forms molding, mold pressing parameter is room temperature, time: 5 ", pressure 110kg/cm2;
S3 takes 1 molding as No.1 molding, 3 moldings of matching superposition, the mould of superposition on No.1 molding
Casting die width is the 85% of No.1 molding width, and after the superposition of 3 moldings, molding is primary, and mold pressing parameter is room temperature, the time:
5 ", pressure 110kg/cm2, form molding chromatograph;
S4, superposition and the matched white substrate of its shape on molding chromatograph, molding, mold pressing parameter is temperature: 162 DEG C,
Time: 260 ", pressure: 110kg/cm2。
Rainbow mark manufactured by embodiment 3, including substrate 200,200 one side of substrate are equipped with molding chromatograph 100;
100 head end of molding chromatograph to end is successively arranged the first primary colors glue part 110, the second primary colors glue part 130 and
Three primary colors glue part 150;
The first primary colors glue part 110, the second primary colors glue part 130 and third primary color glue part 150 correspond respectively to three primary colors
A kind of middle color;
Color part 120 is laminated between the first primary colors glue part 110 and the second primary colors glue part 130 for first;Described second is former
Color part 150 is laminated between coloring agent part 130 and third primary color glue part 150 for second.
Glue part uses IR transparent adhesive tape.
The three primary colors are red, yellow, blue.
It is yellow that a kind of situation, which is the first primary colors glue part 110, and the second primary colors glue part 130 is red, described the
Three primary colors glue part 150 is blue;In order to make it easy to understand, being illustrated on this basis, do not have restriction effect;
Than as shown in Figure 2, from the side A to the side B;The side A is close to the first primary colors glue part 110, the side B close to the second primary colors glue part
130, in molding, the former material of the first coloring agent element 110 also can partially shift the side A arrival first and laminate 120 left side of color part, from
And make first to laminate color part 120 yellow former material gradually decreases from left to right, red former material gradually increases;
Since yellow and red fusion form orange, so that the gradual change chromatograph of yellow-orange-red colors is formed from the side A to the side B,
And it is orange also orange for gradual change, it is done certainly to right color and is gradually deepened;
Yellow is different with red former material fusion proportion, so that first laminates color part 120 and form yellow from left to right to red
Graduated colors.
For another situation herein in connection with content in Fig. 2, setting third primary color glue part 150 at this time is yellow, the second primary colors glue
Part 130 is red, and the first primary colors glue part 110 is blue;
From the side A to the side B;The side A close to the first primary colors glue part 110, the side B close to the second primary colors glue part 130, in molding, the
The former material of one coloring agent element 110 also can partially shift the side A arrival first and laminate 120 left side of color part, so that first laminates
Blue former material gradually decreases color part 120 from left to right, and red former material gradually increases;
Formation purple is merged with blue due to red, so that purple-red gradual change chromatograph of blue-is formed from the side A to the side B, and
And purple is also gradual change purple, is done certainly to right color and is gradually deepened;
Red and blue former material fusion proportion is different, thus first laminate color part 120 formed from left to right it is blue to red
Graduated colors.
The first primary colors glue part 110, first laminates color part 120, the second primary colors glue part 130, second laminates 140 and of color part
Third primary color glue part 150 is transparent material.
Described first, which laminates color part 120 and second, laminates 140 width L1 of color part as the 130 width L2 of the second primary colors glue part
40-50%.
Described first, which laminates the second primary colors glue described in color part 120 first primary colors glue and multilayer as described in multilayer, is overrided to form;
Described second, which laminates third primary color glue described in color part 140 second primary colors glue and multilayer as described in multilayer, is overrided to form.
The test of the made rainbow mark color inhibition of embodiment 3
Those skilled in the art can define, can in the case of not departing from overall spirit of the invention and design
To make the various modifications for above embodiments.It falls within the scope of protection of the present invention.Protection scheme of the invention
It is subject to claims appended hereto.