CN1102196A - 一种高级轿车用丙烯酸罩光清漆 - Google Patents

一种高级轿车用丙烯酸罩光清漆 Download PDF

Info

Publication number
CN1102196A
CN1102196A CN 93115171 CN93115171A CN1102196A CN 1102196 A CN1102196 A CN 1102196A CN 93115171 CN93115171 CN 93115171 CN 93115171 A CN93115171 A CN 93115171A CN 1102196 A CN1102196 A CN 1102196A
Authority
CN
China
Prior art keywords
agent
macromolecular compound
mixed solvent
acrylic resin
limousine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 93115171
Other languages
English (en)
Inventor
钟月栋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 93115171 priority Critical patent/CN1102196A/zh
Publication of CN1102196A publication Critical patent/CN1102196A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高级轿车用罩光清漆。它由丙 烯酸树酯溶液20～50％、高分子化合物改性溶液10 ～40％、增塑剂2～10％、助剂适量、混合溶剂10～ 70％组成。其中，丙烯酸树脂溶液含有：甲基丙烯酸 酯20～30％、丙烯酸酯10～25％、甲基丙烯酸1～ 8％、引发剂1～4％、链转移剂1～4％、有机溶剂25 ～29％；高分子化合物改性溶液含有：高分子改性剂 10～40％、混合溶剂50～60％。本产品干燥速度快， 漆膜硬度高，色浅，保光，耐候性、耐久性优异，是高级 轿车必需的装饰材料。

Description

本发明涉及一种涂装材料，尤其是由经特殊工艺制成的丙烯酸树脂溶液和高分子化合物改性剂为主要成分组成的，用于高级轿车的罩光清漆。
国内已有的各种罩光漆，均存在着色深、施工性能差、保光保色性差的不足，与国外产品相比存在较大差距。而从国外进口的罩光清漆和色漆产品，性能虽较好，但价格昂贵。
本发明的目的在于提供一种高级轿车用罩光清漆，用以克服已有产品存在的不足，提高性能，降低成本，取代国外产品。
本发明采用经过特殊工艺制成的丙烯酸树脂溶液，和作为成膜物质的高分子化合物改性剂，并加入增塑剂助剂等及专用溶剂混合而成。其重量百分比配方及其生产工艺如下：
1∶丙烯酸树脂溶液的合成：
a：配方
甲基丙烯酸酯    20～40%
丙烯酸酯    10～30%
甲基丙烯酸    1～8%
引发剂    1～4%
链转移剂    1～4%
有机溶剂    30～50%
b：合成工艺
先将溶剂加入反应釜内，开动搅拌升温，然后将溶有引发剂的混合单体恒速加入反应釜内，加完料后保持反应2～3小时，取样测定其分子结构、固体含量和粘度，符合要求后出锅备用。
2：高分子化合物改性剂溶液
a：配方
丙烯酸树脂溶液    20～50%
高分子化合物改性溶液    10～40%
增塑剂    2～10%
助剂    5～10%
混合溶剂    30～60%
b：制造工艺
按配方重量份将各组份加入溶化釜中，经搅拌混合均匀、过滤包装，经检验合格后出厂
本发明同已有产品相比具有优点：干燥速度快，漆膜硬度高，机械性好，保光、保色、耐候性、耐久性优异
本发明可通过以下实施例加以实现：
实施例1
1.丙烯酸酯溶液的制备：
甲基丙烯酸酯    25%
丙烯酸酯    25%
甲基丙烯酸    3%
引发剂    1%
链转移剂    1%
有机溶剂    45%
先将有机溶剂34%加入反应釜内，开动搅拌升温然后将溶有引发剂的混合单体恒速加入反应釜内，加完料后保持反应2～3小时，取样测定其分子结构、固体含量和粘度，符合要求后出锅备用
2.高分子化合物改性剂溶液制备
高分子改性剂    30%
混合溶剂    70%
将高分子化合物加入溶化釜中，然后将混合溶剂加入，开动搅拌溶化，达到完全溶解透明为止，出料备用。
3.罩光清漆的制备
丙烯酸树脂溶液    20%
高分子化合物改性溶液    20%
增塑剂    10%
助剂    10%
混合溶剂    40%
按配方重量份将各组份加入溶化釜中，经搅拌混合均匀、过滤包装，经检验合格后出厂。
实施例2、实施例3
丙烯酸酯溶液的配方：
甲基丙烯酸酯    20%    30%
丙烯酸酯    30%    20%
甲基丙烯酸    4%    7%
引发剂    3%    4%
链转移剂    3%    4%
有机溶剂    40%    35%
高分子化合物改性剂溶液配方
高分子改性剂    40%    20%
混合溶剂    60%    80%
罩光清漆的配方
丙烯酸树脂溶液    30%    40%
高分子化合物改性液    20%    15%
增塑剂    10%    5%
助剂    5%    5%
混合溶剂    35%    35%
以上两实施例均按实施例1所述工艺制备。

Claims (1)

1、一种高级轿车用丙烯酸罩光漆，其特征在于具有如下重量百分比组成：
丙烯酸树酯溶液        20～50%
高分子化合物改性溶液  10～40%
增塑剂                2～10%
助剂                  5～10%
混合溶剂              30～60%
其中：
丙烯酸树脂溶液具有如下百分比组成：
甲基丙烯酸酯  20～40%
丙烯酸酯      10～30%
甲基丙烯酸    1～8%
引发剂        1～4%
链转移剂      1～4%
有机溶剂      30～50%
高分子化合物改性溶液具有如下百分比组成：
高分子改性剂  10～40%
混合溶剂      60～90%
CN 93115171 1993-10-23 1993-10-23 一种高级轿车用丙烯酸罩光清漆 Pending CN1102196A (zh)