CN110219205A - A kind of heat-resisting base paper for excursion press mark and preparation method thereof - Google Patents
A kind of heat-resisting base paper for excursion press mark and preparation method thereof Download PDFInfo
- Publication number
- CN110219205A CN110219205A CN201910336672.2A CN201910336672A CN110219205A CN 110219205 A CN110219205 A CN 110219205A CN 201910336672 A CN201910336672 A CN 201910336672A CN 110219205 A CN110219205 A CN 110219205A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- base paper
- press mark
- resisting base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat-resisting base paper for excursion press mark and preparation method thereof, the heat-resisting base paper for excursion press mark is made of following weight composition: 500-600 parts of softwood pulp, broad-leaved starches 300-400 parts, 100-200 parts of bast fiber, 50-70 parts of clear water, 10-30 parts of heat-resistant adhesive, 2-5 parts of drying cylinder remover, 10-30 parts of rosin, 10-30 parts of fire retardant, 20-50 parts and cationic polyacrylamide 1-5 parts of aluminum sulfate, after the heat-resisting base paper for excursion press mark is processed into calico paper, meet the requirement for needing high temperature to shift in heat transfer process, high temperature can reach bright in luster when shifting, fidelity is excellent, stereovision is good and color difference is small;And paper not embrittlement, it is easy to removing demoulding.
Description
Technical field
The present invention relates to a kind of heat-resisting base paper for excursion press mark and preparation method thereof.
Background technique
Heat Transfer Printing, as a kind of widely used transfering printing technology, the pattern of generation have it is bright in luster,
The advantages that fidelity is excellent, stereovision is good and color difference is small, and in practical applications, relative to traditional dyeing and finishing industry, has and save
Industrial water, the advantage for reducing printing and dyeing pollution.Therefore, it is applied to every field in large quantities.In fact, Heat Transfer Printing
Possessed advantage is undivided with the superperformance of thermal transfer printing body paper.Heat transfer printing paper currently on the market exists
When high temperature being needed to shift, there are ink or dyestuff residual quantity height, transfer color difference are big;Paper jaundice embrittlement, is difficult demoulding removing etc.
Drawback;Seriously affect transfer printing quality.My company spy, which sets up the project, thus carries out the research and development of heat-resisting base paper for excursion press mark.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of low production cost, more environmentally friendly heat-resisting turn of production process
Bat printing spends body paper.
To solve the above problems, the present invention is achieved through the following technical solutions: a kind of heat-resisting base paper for excursion press mark,
The heat-resisting base paper for excursion press mark is made of following weight composition: 500-600 parts of softwood pulp, broad-leaved starch 300-400
Part, 100-200 parts of bast fiber, 50-70 parts of clear water, 10-30 parts of heat-resistant adhesive, 2-5 parts of drying cylinder remover, 10-30 parts of rosin, resistance
Agent 10-30 parts of combustion, 20-50 parts of aluminum sulfate and 1-5 parts of cationic polyacrylamide.
Another technical problem to be solved by this invention is to provide a kind of preparation method of heat-resisting base paper for excursion press mark,
The present invention is achieved through the following technical solutions: the preparation process of the heat-resisting base paper for excursion press mark is as follows:
1) softwood pulp 500-600 parts, broad-leaved slurry 300-400 parts, bast fiber 100-200 are extracted by weight ratio
Part, 10-30 parts of fire retardant, 10-30 parts of heat-resistant adhesive, 50-70 parts of progress size degradations of clear water and mashing;Slurry concentration 4.5%;
2) it is poly- that 2-5 parts of drying cylinder remover, 10-30 parts of rosin, 20-50 parts of aluminum sulfate and cation are extracted by weight ratio
1-5 parts of acrylamide are added in the slurry of step 1, and stir evenly;
3) slurry obtained in step 2 is subjected to wet end forming processes;
4) by molding slurry carries out squeezing and cylinder dried in step 3;
5) it is batched after body paper of the step 4 after dry being carried out soft calendaring processing, as the heat-resisting base paper for excursion press mark of finished product.
The beneficial effect of the heat-resisting base paper for excursion press mark of the present invention is: the heat-resisting base paper for excursion press mark is processed into calico paper
Afterwards, the requirement for needing high temperature to shift is met in heat transfer process, high temperature can reach bright in luster when shifting, fidelity is excellent, layer
Secondary sense is good and color difference is small;And paper not embrittlement, it is easy to removing demoulding.
Specific embodiment
The following examples are used to illustrate the present invention, but are not intended to limit the scope of the present invention..
Embodiment 1
A kind of heat-resisting base paper for excursion press mark of the invention, the heat-resisting base paper for excursion press mark are by following weight composition
Composition: 500 parts of softwood pulp, broad-leaved starch 300 parts, 100 parts of bast fiber, 50 parts of clear water, 10 parts of heat-resistant adhesive, drying cylinder remover 2
Part, 10 parts of rosin, 10 parts of fire retardant, 20 parts of aluminum sulfate and 1 part of cationic polyacrylamide.
The preparation process of the heat-resisting base paper for excursion press mark is as follows:
1) by weight ratio extract 500 parts of softwood pulp, broad-leaved starch 300 parts, 100 parts of bast fiber, 10 parts of fire retardant,
10 parts of heat-resistant adhesive, 50 parts of progress size degradations of clear water and mashing;Slurry concentration 4.5%;
2) 2 parts of drying cylinder remover, 10 parts of rosin, 20 parts of aluminum sulfate and cationic polyacrylamide are extracted by weight ratio
1 part is added in the slurry of step 1, and stirs evenly;
3) slurry obtained in step 2 is subjected to wet end forming processes;
4) by molding slurry carries out squeezing and cylinder dried in step 3;
5) it is batched after body paper of the step 4 after dry being carried out soft calendaring processing, as the heat-resisting base paper for excursion press mark of finished product.
Embodiment 2
Its difference from Example 1 is that the heat-resisting base paper for excursion press mark is made of following weight composition:
600 parts of softwood pulp, broad-leaved starch 400 parts, 200 parts of bast fiber, 70 parts of clear water, 30 parts of heat-resistant adhesive, 5 parts of drying cylinder remover, pine
30 parts fragrant, 30 parts of fire retardant, 50 parts of aluminum sulfate and 5 parts of cationic polyacrylamide.
Embodiment 3
Its difference from Example 1 is that the heat-resisting base paper for excursion press mark is made of following weight composition:
555 parts of softwood pulp, broad-leaved starch 355 parts, 155 parts of bast fiber, 60 parts of clear water, 20 parts of heat-resistant adhesive, 3 parts of drying cylinder remover, pine
20 parts fragrant, 20 parts of fire retardant, 35 parts of aluminum sulfate and 3 parts of cationic polyacrylamide.
Embodiment 4
Its difference from Example 1 is that the heat-resisting base paper for excursion press mark is made of following weight composition:
512 parts of softwood pulp, broad-leaved starch 325 parts, 111 parts of bast fiber, 53 parts of clear water, 13 parts of heat-resistant adhesive, 2.5 parts of drying cylinder remover,
12 parts of rosin, 16 parts of fire retardant, 22 parts of aluminum sulfate and 2 parts of cationic polyacrylamide.
Embodiment 5
Its difference from Example 1 is that the heat-resisting base paper for excursion press mark is made of following weight composition:
585 parts of softwood pulp, broad-leaved starch 390 parts, 196 parts of bast fiber, 67 parts of clear water, 26 parts of heat-resistant adhesive, 4.7 parts of drying cylinder remover,
26 parts of rosin, 22 parts of fire retardant, 44 parts of aluminum sulfate and 4 parts of cationic polyacrylamide.
Embodiment 6
Its difference from Example 1 is that the heat-resisting base paper for excursion press mark is made of following weight composition:
576 parts of softwood pulp, broad-leaved starch 313 parts, 184 parts of bast fiber, 56 parts of clear water, 15 parts of heat-resistant adhesive, 4.6 parts of drying cylinder remover,
11 parts of rosin, 28 parts of fire retardant, 23 parts of aluminum sulfate and 3.9 parts of cationic polyacrylamide.
Embodiment 7
Its difference from Example 1 is that the heat-resisting base paper for excursion press mark is made of following weight composition:
543 parts of softwood pulp, broad-leaved starch 339 parts, 163 parts of bast fiber, 66 parts of clear water, 17 parts of heat-resistant adhesive, 3.7 parts of drying cylinder remover,
16 parts of rosin, 19 parts of fire retardant, 33 parts of aluminum sulfate and 2 parts of cationic polyacrylamide.
Embodiment 8
Its difference from Example 1 is that the heat-resisting base paper for excursion press mark is made of following weight composition:
500 parts of softwood pulp, broad-leaved starch 330 parts, 150 parts of bast fiber, 65 parts of clear water, 25 parts of heat-resistant adhesive, 5 parts of drying cylinder remover, pine
25 parts fragrant, 15 parts of fire retardant, 45 parts of aluminum sulfate and 5 parts of cationic polyacrylamide.
The present invention is not limited to above-mentioned preferred forms, anyone obtain under the inspiration of the present invention other it is any with
The identical or similar product of the present invention, is within the scope of the present invention.
Claims (2)
1. a kind of heat-resisting base paper for excursion press mark and preparation method thereof, it is characterised in that: the heat-resisting base paper for excursion press mark is by following
Weight composition composition: 500-600 parts of softwood pulp, broad-leaved starch 300-400 parts, 100-200 parts of bast fiber, clear water
50-70 parts, 10-30 parts of heat-resistant adhesive, 2-5 parts of drying cylinder remover, 10-30 parts of rosin, 10-30 parts of fire retardant, 20-50 parts of aluminum sulfate
With 1-5 parts of cationic polyacrylamide.
2. a kind of preparation method for preparing heat-resisting base paper for excursion press mark described in claim 1, it is characterised in that: this method includes
Following steps:
1) softwood pulp 500-600 parts, 300-400 parts of broad-leaved slurry, 100-200 parts of bast fiber, resistance are extracted by weight ratio
Agent 10-30 parts of combustion, 10-30 parts of heat-resistant adhesive, 50-70 parts of progress size degradations of clear water and mashing;Slurry concentration 4.5%;
2) 2-5 parts of drying cylinder remover, 10-30 parts of rosin, 20-50 parts of aluminum sulfate and cation polypropylene are extracted by weight ratio
1-5 parts of amide are added in the slurry of step 1, and stir evenly;
3) slurry obtained in step 2 is subjected to wet end forming processes;
4) by molding slurry carries out squeezing and cylinder dried in step 3;
5) it is batched after body paper of the step 4 after dry being carried out soft calendaring processing, as the heat-resisting base paper for excursion press mark of finished product.