CN110193873A - A kind of tailings air entrained concrete plate production technology and its drill drawing machine structure used - Google Patents
A kind of tailings air entrained concrete plate production technology and its drill drawing machine structure used Download PDFInfo
- Publication number
- CN110193873A CN110193873A CN201910586633.8A CN201910586633A CN110193873A CN 110193873 A CN110193873 A CN 110193873A CN 201910586633 A CN201910586633 A CN 201910586633A CN 110193873 A CN110193873 A CN 110193873A
- Authority
- CN
- China
- Prior art keywords
- air entrained
- production technology
- entrained concrete
- concrete plate
- cutting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of tailings air entrained concrete plate production technology and its drill drawing machine structures used, are related to concrete plate production technical field.The drill drawing machine structure of the tailings air entrained concrete plate production technology, including L-type frame, the bottom of the L-type frame is fixedly connected with limited position mechanism by longitudinal extension bar, transversal stretching bar is provided at the top of L-type frame side, the right end of the transversal stretching bar is fixedly connected with the side of position-limit mechanism.The tailings air entrained concrete plate production technology and its drill drawing machine structure used, pass through position-limit mechanism, cutter and the improvement for limiting shell, and the improvement of process flow, the shape of concrete is limited by the way of plug in pricker, the rate of set of concrete is accelerated by the limitation to environment simultaneously, good crystallization operation can be carried out to it before concrete coagulation, avoided since the shape of tailings air entrained concrete plate caused by being influenced when concrete coagulation by gravity is different.
Description
Technical field
The present invention relates to concrete plate production technical field, specially a kind of tailings air entrained concrete plate production technology
And its drill drawing machine structure used.
Background technique
Tailings air entrained concrete plate is a kind of using tailings and concrete as the structural lumber of raw material, and tailings refers to ore dressing
Factory is under the conditions of specific economic technology, by grinde ore, chooses the waste discharged after useful component, concrete: refer to by
For cementitious material by the general designation for the cementing integral engineered composite material that gathers materials, one word of concrete usually said, which refers to, makees glue with cement
Gel material, sand, masonry gather materials;Cooperate by a certain percentage with water, it is agitated obtained by cement concrete, also referred to as normal concrete,
It is widely used in civil engineering.
In the prior art, it is difficult to good crystallization operation be carried out to it before concrete coagulation, be easy to appear due to mixed
The shape of tailings air entrained concrete plate is different caused by being influenced when solidifying soil condensation by gravity, while reducing product quality
Working efficiency is reduced, is made troubles to the use of user.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of tailings air entrained concrete plate production technology and its uses
Drill drawing machine structure, solve in the prior art, it is difficult to good crystallization operation is carried out to it before concrete coagulation, be easy
Now since the shape of tailings air entrained concrete plate caused by being influenced when concrete coagulation by gravity is different, product matter is reduced
The problem of working efficiency is reduced while amount.
(2) technical solution
In order to achieve the above object, the present invention is achieved by the following technical programs: a kind of tailings air entrained concrete plate
The bottom of the drill drawing machine structure of production technology, including L-type frame, the L-type frame is fixedly connected with limit by longitudinal extension bar
Mechanism, is provided with transversal stretching bar at the top of L-type frame side, and the one of the right end of the transversal stretching bar and position-limit mechanism
Side is fixedly connected.
The position-limit mechanism includes limit shell, is provided through displacement plate, the displacement on the left of the limit shell
Guide plate is provided on the left of plate, the top and bottom on the right side of the guide plate are provided with guide rod, the top of the displacement plate
Portion and bottom are provided through restriction plate, and the top and bottom of the restriction plate are run through the inner wall of limit shell and extended to
The outside of shell is limited, the right end of the guide rod is fixedly connected with restriction plate, and is limited and offered on shell for restriction plate
Mobile shifting chute, the front surface of the displacement plate are provided with driving mechanism, and the output end of the driving mechanism is provided with cutting
Knife is provided with the through-hole being equipped with cutter on the displacement plate.
The cutter include cutting ontology, and blade, the right side of the cutting ontology are provided on the left of the cutting ontology
Side is provided with limiting slot.
The limit shell includes outer cover body, and the becket being equipped with through-hole is inlaid on the outer cover body.
Preferably, it is welded with stable frame on the L-type frame, intersects on the stable frame and is provided with two steel wires
Rope.
Preferably, it is provided with guide pipe at the top and bottom of the limit shell, the guide pipe is sheathed on guide rod
Surface.
Preferably, the top and bottom of the displacement plate pass through shaft and are connected with displacement wheel, and displacement wheel and limit
The inner wall contact of position shell.
A kind of tailings air entrained concrete plate production technology, including pulling out for above-mentioned tailings air entrained concrete plate production technology
Pricker mechanism, the specific steps are as follows:
S1, slurry preparation: last mortar is stirred through pipeline to slurry storage tank and is stored, and being adjusted to specific gravity is 1.42~1.45
Slurry, then squeeze into slurry storage tank and store for future use, after land plaster is measured by automatic metering system, be added to gypsum pulping tank
In add water and stir, be made specific gravity be 1.42~1.45 slurry it is spare;
S2, reinforced mesh processing: reinforced mesh uses finished product steel mesh, and scene is transported after anti-corrosion, drying and processing by driving
It send to stand-by at steel mesh stacking;
S3, ingredient casting: the raw material that will be prepared are carried out accurate according to process recipe by automatic control system
Metering, by spare kemidol and cement respectively through lime cement weighing hopper total weight, last mortar, calcium plaster are through measuring tank
Weigh, aluminium powder is sequentially added after automatic weighing in casting blender, heated stirring be made within 5~7 minutes temperature be 40 DEG C~
45 DEG C or so, meet technique requirement slurry carry out moulding by casting, once-cast amount for be poured a mold, mould specification
For 6x1.2x0.6m, operated using fixed pouring type;
S4, plug in pricker: casting complete rear mold vehicle is moved to below plug in pricker machine, and pricker machine will be inserted after automatic positioning to be made in advance
Rebar cylinder mould insertion mould vehicle in it is fixed after, stop room into quiet;
S5, quiet stop just supporting: after the completion of plugging in pricker, mould vehicle being sent by ferry bus and quiet stops the quiet of indoor carry out 1.5h~2h
Stop, it is desirable that room temperature keeps hydration reaction in green body abundant at 50 DEG C or more, appropriate to foam, and stablizes hardening, and it is strong to reach cutting
Degree;
S6, pull out pricker: the green body for reaching cutting intensity comes out from quiet room of stopping, and is moved to Ba Qian workshop section, after automatic positioning, uses
The drill drawing machine structure of tailings air entrained concrete plate production technology steadily extracts the drill rod of fixed steel bars mesh sheet, and drill rod returns to saddle
Utilization is continued cycling through at frame circulator, product is moved to cutting workshop section;
S7, cutting: the green body come out in the room Cong Jingting is hung on cutting machine cutting bed, as required specification steel in length and breadth
Silk is cut, and cut lengths deviation is within 1.5mm;
It is S8, steam-cured: to use diameter 2.68m, the upward-acting door still kettle of long 32.5m carries out steam press maintenance, the steam-cured system of use
Degree are as follows: disengaging kettle 0.5h vacuumizes 0.5h, and boost 1.5h, constant pressure 7h, is depressured 1.5h, curing cycle, 11h, recycled 2 daily
It is secondary, steam constant temperature pressure be 1.25MPa, 194 DEG C of temperature or so;
S9, breaking board and packing: after product goes out kettle, after glass severing machine all separates adhesion part, by and base machine and base,
End product is packaged, forklift transport to warehouse for finished product.
(3) beneficial effect
The present invention provides a kind of tailings air entrained concrete plate production technology and its drill drawing machine structures used.Have following
The utility model has the advantages that the tailings air entrained concrete plate production technology and its drill drawing machine structure used, by position-limit mechanism, cutter and
The improvement for limiting improvement and the process flow of shell, limits the shape of concrete, while by ring by the way of plug in pricker
The limitation in border accelerates the rate of set of concrete, can carry out good crystallization operation to it before concrete coagulation, avoid
Since the shape of tailings air entrained concrete plate caused by being influenced when concrete coagulation by gravity is different, product matter is improved
It is improved work efficiency while amount, the use for the person of being convenient to use.
Detailed description of the invention
Fig. 1 is schematic structural view of the invention;
Fig. 2 is the structural schematic diagram of position-limit mechanism of the present invention;
Fig. 3 is the structural schematic diagram of cutter of the present invention;
Fig. 4 is the structural schematic diagram of present invention limit shell.
In figure: 1, L-type frame;2, longitudinal extension bar;3, position-limit mechanism;301, guide rod;302, through-hole;303, it cuts
Knife;3031, blade;3032, ontology is cut;3033, limiting slot;304, displacement wheel;305, guide pipe;306, restriction plate;307,
Shifting chute;308, displacement plate;309, driving mechanism;310, shell is limited;3101, outer cover body;3102, becket;311, it leads
To plate;4, transversal stretching bar;5, stable frame;6, wirerope.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Fig. 1-4 is please referred to, the present invention provides a kind of technical solution: a kind of tailings air entrained concrete plate production technology is pulled out
Pricker mechanism, including L-type frame 1 are welded with stable frame 5 on L-type frame 1, intersect on stable frame 5 and be provided with two wirerope
6, for avoiding the deformation of L-type frame 1, the bottom of L-type frame 1 is fixed by longitudinal extension bar 2 for wirerope 6 and stable frame 5
Limited position mechanism 3 is connected, is provided with transversal stretching bar 4, the right end and position restrainer of transversal stretching bar 4 at the top of 1 side of L-type frame
The side of structure 3 is fixedly connected.
Position-limit mechanism 3 includes limit shell 310, and the top and bottom of limit shell 310 are provided with guide pipe 305, lead
The surface of guide rod 301 is sheathed on to pipe 305, guide pipe 305 is used for the moving range of restricted guidance bar 301, limits shell 310
Left side be provided through displacement plate 308, the top and bottom of displacement plate 308 pass through shaft and are connected with displacement wheel 304,
And displacement wheel 304 is contacted with the inner wall of limit shell 310, displacement wheel 304 is used for the moving range of limiting displacement plate 308, displacement
The left side of plate 308 is provided with guide plate 311, and the top and bottom on 311 right side of guide plate are provided with guide rod 301, displacement plate
308 top and bottom are provided through restriction plate 306, and limit shell 310 is run through in the top and bottom of restriction plate 306
Inner wall and the outside for extending to limit shell 310, the right end of guide rod 301 are fixedly connected with restriction plate 306, and limit shell
The shifting chute 307 mobile for restriction plate 306 is offered on 310, the front surface of displacement plate 308 is provided with driving mechanism 309, drives
The output end of motivation structure 309 is provided with cutter 303, and the through-hole being equipped with cutter 303 is provided on displacement plate 308
302。
Cutter 303 include cutting ontology 3032, and the left side of cutting ontology 3032 is provided with blade 3031, cuts ontology
3032 right side is provided with limiting slot 3033.
Limiting shell 310 includes outer cover body 3101, is inlaid with the gold being equipped with through-hole 302 on outer cover body 3101
Belong to ring 3102.
A kind of tailings air entrained concrete plate production technology, including pulling out for above-mentioned tailings air entrained concrete plate production technology
Pricker mechanism, the specific steps are as follows:
S1, slurry preparation: last mortar is stirred through pipeline to slurry storage tank and is stored, and being adjusted to specific gravity is 1.42~1.45
Slurry, then squeeze into slurry storage tank and store for future use, after land plaster is measured by automatic metering system, be added to gypsum pulping tank
In add water and stir, be made specific gravity be 1.42~1.45 slurry it is spare;
S2, reinforced mesh processing: reinforced mesh uses finished product steel mesh, and scene is transported after anti-corrosion, drying and processing by driving
It send to stand-by at steel mesh stacking;
S3, ingredient casting: the raw material that will be prepared are carried out accurate according to process recipe by automatic control system
Metering, by spare kemidol and cement respectively through lime cement weighing hopper total weight, last mortar, calcium plaster are through measuring tank
Weigh, aluminium powder is sequentially added after automatic weighing in casting blender, heated stirring be made within 5~7 minutes temperature be 40 DEG C~
45 DEG C or so, meet technique requirement slurry carry out moulding by casting, once-cast amount for be poured a mold, mould specification
For 6x1.2x0.6m, operated using fixed pouring type;
S4, plug in pricker: casting complete rear mold vehicle is moved to below plug in pricker machine, and pricker machine will be inserted after automatic positioning to be made in advance
Rebar cylinder mould insertion mould vehicle in it is fixed after, stop room into quiet;
S5, quiet stop just supporting: after the completion of plugging in pricker, mould vehicle being sent by ferry bus and quiet stops the quiet of indoor carry out 1.5h~2h
Stop, it is desirable that room temperature keeps hydration reaction in green body abundant at 50 DEG C or more, appropriate to foam, and stablizes hardening, and it is strong to reach cutting
Degree;
S6, pull out pricker: the green body for reaching cutting intensity comes out from quiet room of stopping, and is moved to Ba Qian workshop section, after automatic positioning, uses
The drill drawing machine structure of tailings air entrained concrete plate production technology steadily extracts the drill rod of fixed steel bars mesh sheet, and drill rod returns to saddle
Utilization is continued cycling through at frame circulator, product is moved to cutting workshop section;
S7, cutting: the green body come out in the room Cong Jingting is hung on cutting machine cutting bed, as required specification steel in length and breadth
Silk is cut, and cut lengths deviation is within 1.5mm;
It is S8, steam-cured: to use diameter 2.68m, the upward-acting door still kettle of long 32.5m carries out steam press maintenance, the steam-cured system of use
Degree are as follows: disengaging kettle 0.5h vacuumizes 0.5h, and boost 1.5h, constant pressure 7h, is depressured 1.5h, curing cycle, 11h, recycled 2 daily
It is secondary, steam constant temperature pressure be 1.25MPa, 194 DEG C of temperature or so;
S9, breaking board and packing: after product goes out kettle, after glass severing machine all separates adhesion part, by and base machine and base,
End product is packaged, forklift transport to warehouse for finished product.
When the drill drawing machine structure work of tailings air entrained concrete plate production technology, drill rod is sequentially passed through into 3102 He of becket
Through-hole 302 controls transversal stretching bar 4 by the control mechanism of peripheral hardware and carries out shrinkage operation so that displacement plate 308 relative to
The movement of shell 310 is limited, so that becket 3102 and the dislocation of through-hole 302 are to limit the position of drill rod, while passing through peripheral hardware
Control mechanism controls driving mechanism 309 and cutter 303 is driven to rotate, to open up under the action of blade 3031 in drill rod side position
One osculum controls limiting slot 3033 towards its adjacent through-hole 302 with rear drive mechanism 309, and in the drawing of transversal stretching bar 4
So that limiting slot 3033 is inserted into the osculum that drill rod side opens up under stretching, the position of fixing concrete, while passing through peripheral hardware
Control mechanism controls longitudinal extension bar 2 and carries out shrinkage operation, is separated drill rod with concrete with this, by transversal stretching bar 4 and indulges
It is restored to the position of telescopic rod 2, takes out drill rod, carry out pulling out pricker operation with this.
In conclusion the tailings air entrained concrete plate production technology and its drill drawing machine structure used, pass through position-limit mechanism
3, the improvement of improvement and the process flow of cutter 303 and limit shell 310, limits concrete by the way of plug in pricker
Shape, while the rate of set of concrete is accelerated by the limitation to environment, it can be carried out very before concrete coagulation
Good crystallization operation, avoids the shape due to tailings air entrained concrete plate caused by being influenced when concrete coagulation by gravity
Shape is different, improves work efficiency while improving product quality, the use for the person of being convenient to use.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (5)
1. a kind of drill drawing machine structure of tailings air entrained concrete plate production technology, including L-type frame (1), it is characterised in that: described
The bottom of L-type frame (1) is fixedly connected limited position mechanism (3) by longitudinal extension bar (2), the top of L-type frame (1) side
Portion is provided with transversal stretching bar (4), and the right end of the transversal stretching bar (4) is fixedly connected with the side of position-limit mechanism (3);
The position-limit mechanism (3) includes limit shell (310), is provided through displacement plate on the left of the limit shell (310)
(308), it is provided with guide plate (311) on the left of the displacement plate (308), the top and bottom on the right side of the guide plate (311)
It is provided with guide rod (301), the top and bottom of the displacement plate (308) are provided through restriction plate (306), the limit
The top and bottom of making sheet (306) run through the inner wall of limit shell (310) and extend to the outside of limit shell (310), institute
The right end for stating guide rod (301) is fixedly connected with restriction plate (306), and is limited and offered on shell (310) for restriction plate
(306) mobile shifting chute (307), the front surface of the displacement plate (308) are provided with driving mechanism (309), the driving machine
The output end of structure (309) is provided with cutter (303), is provided on the displacement plate (308) and is equipped with cutter (303)
Through-hole (302);
The cutter (303) include cutting ontology (3032), are provided with blade on the left of the cutting ontology (3032)
(3031), limiting slot (3033) are provided on the right side of the cutting ontology (3032);
The limit shell (310) includes outer cover body (3101), is inlaid on the outer cover body (3101) and through-hole (302)
The becket (3102) being equipped with.
2. a kind of drill drawing machine structure of tailings air entrained concrete plate production technology according to claim 1, it is characterised in that:
It is welded with stable frame (5) on the L-type frame (1), intersects on the stable frame (5) and be provided with two wirerope (6).
3. a kind of drill drawing machine structure of tailings air entrained concrete plate production technology according to claim 1, it is characterised in that:
It is provided with guide pipe (305) at the top and bottom of the limit shell (310), the guide pipe (305) is sheathed on guide rod
(301) surface.
4. a kind of drill drawing machine structure of tailings air entrained concrete plate production technology according to claim 1, it is characterised in that:
The top and bottom of the displacement plate (308) pass through shaft and are connected with displacement wheel (304), and displacement wheel (304) and limit
The inner wall contact of position shell (310).
5. a kind of tailings air entrained concrete plate production technology, it is characterised in that: raw including above-mentioned tailings air entrained concrete plate
The drill drawing machine structure of production. art, the specific steps are as follows:
S1, slurry preparation: last mortar is stirred through pipeline to slurry storage tank and is stored, and is adjusted to the slurry that specific gravity is 1.42~1.45
Then body is squeezed into slurry storage tank and is stored for future use, after land plaster is measured by automatic metering system, be added in gypsum pulping tank and add
It is spare that the slurry that specific gravity is 1.42~1.45 is made in water stirring;
S2, reinforced mesh processing: reinforced mesh uses finished product steel mesh, and scene is transported to after anti-corrosion, drying and processing by driving
It is stand-by at steel mesh stacking;
S3, ingredient casting: the raw material that will be prepared accurately are measured according to process recipe by automatic control system,
By spare kemidol and cement respectively through lime cement weighing hopper total weight, last mortar, calcium plaster are weighed through measuring tank,
Aluminium powder is sequentially added after automatic weighing in casting blender, and it is 40 DEG C~45 DEG C left sides that temperature is made for 5~7 minutes in heated stirring
Right, to meet technique requirement slurry progress moulding by casting, once-cast amount are for being poured a mold, mould specification
6x1.2x0.6m is operated using fixed pouring type;
S4, plug in pricker: casting complete rear mold vehicle is moved to below plug in pricker machine, and the steel that pricker machine will be made in advance is inserted after automatic positioning
After fixing in muscle cylinder mould insertion mould vehicle, stop room into quiet;
S5, it is quiet stop just support: plug in pricker after the completion of, mould vehicle is sent into quiet quiet the stopping for stopping indoor carry out 1.5h~2h by ferry bus,
It asks room temperature at 50 DEG C or more, keeps hydration reaction in green body abundant, it is appropriate to foam, stablize hardening, reaches cutting intensity;
S6, pull out pricker: the green body for reaching cutting intensity comes out from quiet room of stopping, and is moved to Ba Qian workshop section, after automatic positioning, uses tailings
The drill drawing machine structure of air entrained concrete plate production technology steadily extracts the drill rod of fixed steel bars mesh sheet, and drill rod returns to saddletree and follows
Utilization is continued cycling through at ring machine, product is moved to cutting workshop section;
S7, cutting: the green body come out in the room Cong Jingting is hung on cutting machine cutting bed, as required specification with steel wire in length and breadth into
Row cutting, cut lengths deviation is within 1.5mm;
It is S8, steam-cured: to use diameter 2.68m, the upward-acting door still kettle of long 32.5m carries out steam press maintenance, the steam curing system of use are as follows:
Kettle 0.5h is passed in and out, 0.5h is vacuumized, boost 1.5h, constant pressure 7h, is depressured 1.5h, curing cycle, 11h, recycled 2 times, steam daily
Constant temperature and pressure is 1.25MPa, 194 DEG C of temperature or so;
S9, breaking board and packing: after product goes out kettle, after glass severing machine all separates adhesion part, by simultaneously base machine and base, finally
Finished product is packaged, forklift transport to warehouse for finished product.