CN110185226A - A kind of moisture retardant consolidated floor - Google Patents
A kind of moisture retardant consolidated floor Download PDFInfo
- Publication number
- CN110185226A CN110185226A CN201910456690.4A CN201910456690A CN110185226A CN 110185226 A CN110185226 A CN 110185226A CN 201910456690 A CN201910456690 A CN 201910456690A CN 110185226 A CN110185226 A CN 110185226A
- Authority
- CN
- China
- Prior art keywords
- layer
- adhesive
- water
- resistant
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of moisture retardant consolidated floors, fire retardant MDF ontology is by Wear-resistant corrosion-resistant layer, flame retardant layer, hollow-out sterilization net, the thermal insulation layer of impervious, fibrolamellar, anti- water fugacity adhesive layer and packing material, the upper surface of fibrolamellar is bonded by anti-water fugacity adhesive layer and the flame retardant layer high temperature and pressure, flame retardant layer upper surface is Nian Jie with top Wear-resistant corrosion-resistant layer high temperature and pressure by adhesive, the lower surface of fibrolamellar is Nian Jie with another flame retardant layer high temperature and pressure by anti-water fugacity adhesive layer, the lower surface of another flame retardant layer is Nian Jie with the thermal insulation layer of impervious high temperature and pressure by adhesive, the lower surface of the thermal insulation layer of impervious is Nian Jie with hollow-out sterilization net high temperature and pressure by adhesive, the lower surface bonds of the hollow-out sterilization net have Wear-resistant corrosion-resistant layer described in bottom, it is wear-resisting anti-described in the thermal insulation layer of impervious and bottom The gap that hollow-out sterilization net between corrosion layer is formed is equipped with packing material, invention except formaldehyde, moisture-proof, fire-retardant, weather resistance is strong.
Description
Technical field
The present invention relates to technical field of floor more particularly to a kind of moisture retardant consolidated floor and preparation method thereof.
Background technique
With the gradually improvement of living standard, the taste of the environment and finishing living, handle official business also is being continuously improved in people,
Interior is more and more common using the floor of large area.Common floor whether composite floor board or solid wood currently on the market
The wood fibres such as plate, bamboo flooring floor can there are the following problems: dampness will cause floor deform, after warpage, cracking not
Just it is replaced, and easily causes ground dash-board injury in replacement.But its change that can't prevent floor from occurring due to dampness
Shape, so that floor is damaged, or even reduction service life, the disadvantage that flooring material can not be prevented inflammable.
Summary of the invention
In view of the deficiencies of the prior art, it is an object of the present invention to provide a kind of moisture retardant consolidated floors.
The scheme of the invention is: a kind of moisture retardant consolidated floor, including fire retardant MDF, the fire retardant MDF ontology
By Wear-resistant corrosion-resistant layer, flame retardant layer, hollow-out sterilization net, the thermal insulation layer of impervious, fibrolamellar, anti-water fugacity adhesive layer and filling material
The upper surface of material, the fibrolamellar is bonded by the anti-water fugacity adhesive layer and the flame retardant layer high temperature and pressure, described
Flame retardant layer upper surface is Nian Jie with the top Wear-resistant corrosion-resistant layer high temperature and pressure by adhesive, the following table of the fibrolamellar
Face is Nian Jie with another flame retardant layer high temperature and pressure by the anti-water fugacity adhesive layer, the following table of another flame retardant layer
Face is Nian Jie with the thermal insulation layer of impervious high temperature and pressure by adhesive, and the lower surface of the thermal insulation layer of impervious is killed by adhesive and hollow out
Bacterium net high temperature and pressure bonding, the lower surface bonds of the hollow-out sterilization net have a Wear-resistant corrosion-resistant layer described in bottom, the antiseepage every
The gap that hollow-out sterilization net between Wear-resistant corrosion-resistant layer described in thermosphere and bottom is formed is equipped with packing material.
The surface of the top Wear-resistant corrosion-resistant layer is coated with water resistant absorbing formaldehyde dope layer as a preferred technical solution,.
The water resistant absorbing formaldehyde dope layer includes C as a preferred technical solution,2-C10Dialdehyde, C4-C12It is polynary
Alcohol and nanometer mine are brilliant.
The flame retardant layer is that phosphorus nitrogen boron multielement cooperates with fire-retarding of wood oxidant layer as a preferred technical solution,.
The packing material includes green mud, active oxidation aluminium powder, Strong oxdiative copper and kaolinite as a preferred technical solution,
Soil.
The anti-water fugacity adhesive layer includes water, dialdehyde, 30% sodium hydroxide water, enzymatic hydrolysis as a preferred technical solution,
Lignin and the melamine anti-water fugacity adhesive made of anti-water fugacity adhesive the preparation method.
The anti-water fugacity adhesive the preparation method as a preferred technical solution:
1) water and dialdehyde are added in reaction kettle, after ten minutes with 80r/min revolving speed mechanical stirring, 30% hydrogen-oxygen are added
Change sodium water solution, be gradually warmed up 40-70 DEG C, enzymolysis xylogen is added, is being gradually heated to 80-90 DEG C, and insulated and stirred
0.5-2h obtains the lignin graft containing aldehyde radical;
2) graft for obtaining step 1) is slow cooling to 50-70 DEG C, and melamine, and insulation reaction 0.5- is added
Then reaction temperature is down to 40 DEG C or less dischargings to get anti-water fugacity adhesive is arrived by 2h.
It is gradually warmed up in the step 1) as a preferred technical solution, to 70 DEG C, enzymolysis xylogen is added, is gradually rising
Temperature is to 90 DEG C, and insulated and stirred 1.5h, obtains the lignin graft containing aldehyde radical.
The graft that the step 2) obtains step 1) as a preferred technical solution, is slow cooling to 70 DEG C, is added
Melamine, and insulation reaction 0.5h.
By adopting the above-described technical solution, a kind of moisture retardant consolidated floor, the fire retardant MDF ontology is by wear-resisting
Etch resistant layer, flame retardant layer, hollow-out sterilization net, the thermal insulation layer of impervious, fibrolamellar, anti-water fugacity adhesive layer and packing material, institute
The upper surface for stating fibrolamellar is bonded by the anti-water fugacity adhesive layer and the flame retardant layer high temperature and pressure, the fire retardant
Layer upper surface is Nian Jie with the top Wear-resistant corrosion-resistant layer high temperature and pressure by adhesive, and the lower surface of the fibrolamellar passes through
The anti-water fugacity adhesive layer is Nian Jie with another flame retardant layer high temperature and pressure, and the lower surface of another flame retardant layer passes through
Adhesive is Nian Jie with the thermal insulation layer of impervious high temperature and pressure, and the lower surface of the thermal insulation layer of impervious is high by adhesive and hollow-out sterilization net
Warm high pressure bonding, the lower surface bonds of the hollow-out sterilization net have a Wear-resistant corrosion-resistant layer described in bottom, the thermal insulation layer of impervious with
The gap that hollow-out sterilization net between Wear-resistant corrosion-resistant layer described in bottom is formed is equipped with packing material.
Compared with prior art, advantages of the present invention: product environmental protection, flame retardant effect is obvious, removes formaldehyde, and properties
Index is greatly improved, and comprehensive performance improves, and free formaldehyde is reduced, and weatherability is improved, improves using the longevity
Life, while can be used for outdoor application, fire protecting performance waterproof performance is improved, floor deformation caused by wet gas is effectively avoided
Problem.
Detailed description of the invention
Fig. 1 is the sectional view of the embodiment of the present invention 1.
1- Wear-resistant corrosion-resistant layer;2- flame retardant layer;3- hollow-out sterilization layer;4- the thermal insulation layer of impervious;5- fibrolamellar;6- waterproof
Factor adhesive layer;7- packing material;8- water resistant absorbing formaldehyde dope layer.
Specific embodiment
In order to make up the above deficiency, the present invention provides a kind of moisture retardant consolidated floors to solve in above-mentioned background technique
The problem of.
A kind of moisture retardant consolidated floor, including fire retardant MDF, the fire retardant MDF ontology by Wear-resistant corrosion-resistant layer,
Flame retardant layer, hollow-out sterilization net, the thermal insulation layer of impervious, fibrolamellar, anti-water fugacity adhesive layer and packing material, the fibrolamellar
Upper surface bonded by the anti-water fugacity adhesive layer and the flame retardant layer high temperature and pressure, the flame retardant layer upper surface is logical
Cross that adhesive is Nian Jie with the top Wear-resistant corrosion-resistant layer high temperature and pressure, the lower surface of the fibrolamellar by the waterproof because
Sub- adhesive layer is Nian Jie with another flame retardant layer high temperature and pressure, and the lower surface of another flame retardant layer by adhesive and is prevented
Thermal insulation layer high temperature and pressure bonding is seeped, the lower surface of the thermal insulation layer of impervious is viscous by adhesive and hollow-out sterilization net high temperature and pressure
It connects, the lower surface bonds of the hollow-out sterilization net have a Wear-resistant corrosion-resistant layer described in bottom, described in the thermal insulation layer of impervious and bottom
The gap that hollow-out sterilization net between Wear-resistant corrosion-resistant layer is formed is equipped with packing material.
The surface of the top Wear-resistant corrosion-resistant layer is coated with water resistant absorbing formaldehyde dope layer.
The water resistant absorbing formaldehyde dope layer includes C2-C10Dialdehyde, C4-C12Polyalcohol and nanometer mine it is brilliant.
The flame retardant layer is that phosphorus nitrogen boron multielement cooperates with fire-retarding of wood oxidant layer.
The packing material includes green mud, active oxidation aluminium powder, Strong oxdiative copper and kaolin.
The anti-water fugacity adhesive layer includes that water, dialdehyde, 30% sodium hydroxide water, enzymolysis xylogen and melamine pass through
Anti- water fugacity adhesive made of anti-water fugacity adhesive the preparation method.
The anti-water fugacity adhesive the preparation method:
1) water and dialdehyde are added in reaction kettle, after ten minutes with 80r/min revolving speed mechanical stirring, 30% hydrogen-oxygen are added
Change sodium water solution, be gradually warmed up 40-70 DEG C, enzymolysis xylogen is added, is being gradually heated to 80-90 DEG C, and insulated and stirred
0.5-2h obtains the lignin graft containing aldehyde radical;
2) graft for obtaining step 1) is slow cooling to 50-70 DEG C, and melamine, and insulation reaction 0.5- is added
Then reaction temperature is down to 40 DEG C or less dischargings to get anti-water fugacity adhesive is arrived by 2h.
It is gradually warmed up in the step 1) to 70 DEG C, enzymolysis xylogen is added, is being gradually heated to 90 DEG C, and insulated and stirred
1.5h obtains the lignin graft containing aldehyde radical.
The graft that the step 2) obtains step 1) is slow cooling to 70 DEG C, and melamine, and insulation reaction is added
0.5h。
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1:
A kind of moisture retardant consolidated floor, including fire retardant MDF, the fire retardant MDF ontology is by Wear-resistant corrosion-resistant layer
1, flame retardant layer 2, hollow-out sterilization net 3, the thermal insulation layer of impervious 4, fibrolamellar 5, anti-water fugacity adhesive layer 6 and packing material 7, it is described
The upper surface of fibrolamellar 5 is bonded by the anti-water fugacity adhesive layer 6 with 2 high temperature and pressure of flame retardant layer, described fire-retardant
2 upper surface of oxidant layer is Nian Jie with top 1 high temperature and pressure of Wear-resistant corrosion-resistant layer by adhesive, the following table of the fibrolamellar 5
Face is Nian Jie with another 2 high temperature and pressure of flame retardant layer by the anti-water fugacity adhesive layer 6, another flame retardant layer 2
Lower surface is Nian Jie with 4 high temperature and pressure of the thermal insulation layer of impervious by adhesive, the lower surface of the thermal insulation layer of impervious 4 pass through adhesive and
3 high temperature and pressure of hollow-out sterilization net bonding, the lower surface bonds of the hollow-out sterilization net 3 have Wear-resistant corrosion-resistant layer 1 described in bottom, institute
It states the gap that the hollow-out sterilization net 3 between Wear-resistant corrosion-resistant layer 1 described in the thermal insulation layer of impervious 4 and bottom is formed and is equipped with filling material
Material 7.
The surface of the top Wear-resistant corrosion-resistant layer 1 is coated with water resistant absorbing formaldehyde dope layer 8.
The water resistant absorbing formaldehyde dope layer 8 includes C2-C10Dialdehyde, C4-C12Polyalcohol and nanometer mine it is brilliant.
The flame retardant layer 2 is that phosphorus nitrogen boron multielement cooperates with fire-retarding of wood oxidant layer.
The packing material 7 includes green mud, active oxidation aluminium powder, Strong oxdiative copper and kaolin.
The anti-water fugacity adhesive layer 6 includes that water, dialdehyde, 30% sodium hydroxide water, enzymolysis xylogen and melamine are logical
Cross anti-water fugacity adhesive made of anti-water fugacity adhesive the preparation method.
Embodiment 2:
The anti-water fugacity adhesive the preparation method:
1) 350 kg of water and 50 kilograms of dialdehydes are added in reaction kettle, after ten minutes with 80r/min revolving speed mechanical stirring,
5 kilogram of 30% sodium hydrate aqueous solution is added, is gradually warmed up to 40 DEG C, 140 kilograms of enzymolysis xylogens is added, are being gradually heated to
80 DEG C, and insulated and stirred 0.5h, obtain the lignin graft containing aldehyde radical;
2) graft for obtaining step 1) is slow cooling to 50 DEG C, and 150 kilograms of melamines, and insulation reaction is added
Then reaction temperature is down to 40 DEG C or less dischargings to get anti-water fugacity adhesive is arrived by 0.5h.
Embodiment 3:
The anti-water fugacity adhesive the preparation method:
1) 450 kg of water and 110 kilograms of dialdehydes are added in reaction kettle, after ten minutes with 80r/min revolving speed mechanical stirring,
15 kilogram of 30% sodium hydrate aqueous solution is added, is gradually warmed up to 70 DEG C, 280 kilograms of enzymolysis xylogens is added, are being gradually warmed up
To 90 DEG C, and insulated and stirred 2h, obtain the lignin graft containing aldehyde radical;
2) graft for obtaining step 1) is slow cooling to 70 DEG C, and 260 kilograms of melamines, and insulation reaction is added
Then reaction temperature is down to 40 DEG C or less dischargings to get anti-water fugacity adhesive is arrived by 2h.
Embodiment 4:
The anti-water fugacity adhesive the preparation method:
1) 400 kg of water and 100 kilograms of dialdehydes are added in reaction kettle, with 80r/min revolving speed mechanical stirring 10 minutes
Afterwards, 10 kilogram of 30% sodium hydrate aqueous solution is added, is gradually warmed up to 70 DEG C, 240 kilograms of enzymolysis xylogens is added, gradually rising
Temperature is to 90 DEG C, and insulated and stirred 1.5h, obtains the lignin graft containing aldehyde radical;
2) graft for obtaining step 1) is slow cooling to 70 DEG C, and 250 kilograms of melamines, and insulation reaction is added
Then reaction temperature is down to 40 DEG C or less dischargings to get anti-water fugacity adhesive is arrived by 0.5h.
Physico-chemical tests are carried out made of Example 1, indices are excellent horizontal in national standard and low in cost,
Water sucting thickness change rate reduces, and fire-retardant rank improves, and can effective restraining and sterilizing bacteria, and finishing formaldehyde and monster can be adsorbed
Different odor.
The above shows and describes the basic principle, main features and advantages of the invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent circle.
Claims (9)
1. a kind of moisture retardant consolidated floor, including fire retardant MDF, it is characterised in that: the fire retardant MDF ontology is by wear-resisting
Etch resistant layer, flame retardant layer, hollow-out sterilization net, the thermal insulation layer of impervious, fibrolamellar, anti-water fugacity adhesive layer and packing material, institute
The upper surface for stating fibrolamellar is bonded by the anti-water fugacity adhesive layer and the flame retardant layer high temperature and pressure, the fire retardant
Layer upper surface is Nian Jie with the top Wear-resistant corrosion-resistant layer high temperature and pressure by adhesive, and the lower surface of the fibrolamellar passes through
The anti-water fugacity adhesive layer is Nian Jie with another flame retardant layer high temperature and pressure, and the lower surface of another flame retardant layer passes through
Adhesive is Nian Jie with the thermal insulation layer of impervious high temperature and pressure, and the lower surface of the thermal insulation layer of impervious is high by adhesive and hollow-out sterilization net
Warm high pressure bonding, the lower surface bonds of the hollow-out sterilization net have a Wear-resistant corrosion-resistant layer described in bottom, the thermal insulation layer of impervious with
The gap that hollow-out sterilization net between Wear-resistant corrosion-resistant layer described in bottom is formed is equipped with packing material.
2. a kind of moisture retardant consolidated floor as described in claim 1, it is characterised in that: the top Wear-resistant corrosion-resistant layer
Surface is coated with water resistant absorbing formaldehyde dope layer.
3. a kind of moisture retardant consolidated floor as claimed in claim 2, it is characterised in that: the water resistant absorbing formaldehyde dope layer packet
Include C2-C10Dialdehyde, C4-C12Polyalcohol and nanometer mine it is brilliant.
4. a kind of moisture retardant consolidated floor as described in claim 1, it is characterised in that: the flame retardant layer is that phosphorus nitrogen boron is more
Element cooperates with fire-retarding of wood oxidant layer.
5. a kind of moisture retardant consolidated floor as described in claim 1, it is characterised in that: the packing material include green mud,
Active oxidation aluminium powder, Strong oxdiative copper and kaolin.
6. a kind of moisture retardant consolidated floor as described in claim 1, it is characterised in that: the anti-water fugacity adhesive layer includes
Water, dialdehyde, 30% sodium hydroxide water, enzymolysis xylogen and the melamine waterproof made of anti-water fugacity adhesive the preparation method
Factor adhesive.
7. a kind of moisture retardant consolidated floor as claimed in claim 1 or 2, which is characterized in that the anti-water fugacity adhesive
The preparation method:
1) water and dialdehyde are added in reaction kettle, after ten minutes with 80r/min revolving speed mechanical stirring, 30% sodium hydroxide water are added
Solution is gradually warmed up 40-70 DEG C, and enzymolysis xylogen is added, is being gradually heated to 80-90 DEG C, and insulated and stirred 0.5-2h, is obtaining
To the lignin graft containing aldehyde radical;
2) graft for obtaining step 1) is slow cooling to 50-70 DEG C, melamine, and insulation reaction 0.5-2h is added, so
Reaction temperature is down to 40 DEG C or less dischargings to get anti-water fugacity adhesive is arrived afterwards.
8. a kind of preparation method of moisture retardant consolidated floor as claimed in claim 7, it is characterised in that: in the step 1)
It is gradually warmed up to 70 DEG C, enzymolysis xylogen is added, is being gradually heated to 90 DEG C, and insulated and stirred 1.5h, is obtaining the wood containing aldehyde radical
Quality graft.
9. a kind of preparation method of moisture retardant consolidated floor as claimed in claim 7, it is characterised in that: the step 2) will
The graft that step 1) obtains is slow cooling to 70 DEG C, and melamine, and insulation reaction 0.5h is added.