CN110184140B - 一种用于浴室与洁具的清洁剂 - Google Patents
一种用于浴室与洁具的清洁剂 Download PDFInfo
- Publication number
- CN110184140B CN110184140B CN201910566845.XA CN201910566845A CN110184140B CN 110184140 B CN110184140 B CN 110184140B CN 201910566845 A CN201910566845 A CN 201910566845A CN 110184140 B CN110184140 B CN 110184140B
- Authority
- CN
- China
- Prior art keywords
- parts
- titanium dioxide
- nano titanium
- agent
- carbon powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于清洁剂技术领域，具体涉及一种用于浴室与洁具的特效清洁剂，各组分按重量份计，由水85‑90份、酸性增稠剂4‑6份、光亮剂0.4‑0.5份、乙醇酸3.5‑5.0份、草酸1.6‑1.9份、二甲苯磺酸钠1.5‑2.0份、香精0.2‑0.4份、氯化钠1.5‑1.8份、EDTA‑2Na 0.8‑1.2份与活性剂0.5‑0.9份组成；本发明相较现有的清洁剂清洁与杀菌效果更佳，适宜进一步推广应用。
Description
技术领域
本发明属于清洁剂技术领域，具体涉及一种用于浴室与洁具的清洁剂。
背景技术
清洁剂，是一种液体状态的用来洗涤衣物或清洗用具或清洁家具等东西的清洁产品。它采用多种新型表面活性剂，去污力强，漂洗容易，对皮肤无刺激。最宜洗涤厨具，家具及水果瓜菜。
浴室清洁剂为清洁剂中较为常见的一分类，现有浴室清洁剂多为强酸性清洁剂，其虽有较好的除污效果，但清洁后的污垢仍易附着于洁具表面，造成洁具的再污染，进而影响浴室清洁剂的洁净效果；另，现有浴室清洁剂的灭菌效果也普遍较差。
发明内容
本发明的目的在于针对现有技术不足，提供一种用于浴室与洁具的清洁剂，已解决上述提出的问题。
为实现以上目的，本发明通过以下技术方案予以实现：
一种用于浴室与洁具的清洁剂，各组分按重量份计，由水85-90份、酸性增稠剂4-6份、光亮剂0.4-0.5份、乙醇酸3.5-5.0份、草酸1.6-1.9份、二甲苯磺酸钠1.5-2.0份、香精0.2-0.4份、氯化钠1.5-1.8份、EDTA-2Na 0.8-1.2份与活性剂0.5-0.9份组成。
一种用于浴室与洁具的清洁剂，其制备方法包括以下步骤：
S1:向水中依次加入酸性增稠剂、光亮剂、乙醇酸、草酸、香精与氯化钠并混合均匀，得到混合组分A；
S2：向将混合组分A加入二甲苯磺酸钠、EDTA-2Na与活性剂，并于真空下搅拌混合50-90min，制得上述清洁剂。
进一步的，所述活性剂的制备方法包括以下步骤：
a)将活性炭粉、纳米二氧化钛分别用2mol/L的HCl浸泡12-15h后，用蒸馏水抽滤洗涤至pH＝7.0，接着将处理后的活性炭粉、纳米二氧化钛分别放入到100℃的真空干燥箱中，干燥12h；
b)将处理后的纳米二氧化钛加入到硅烷偶联剂中，并于45-50℃下搅拌混合12-15h，接着将步骤a)中处理后活性炭粉与季戊四醇油酸酯依次加入到混合组分中，并于60-65℃下，进行搅拌混合，混合3-5h后，制得上述活性剂。
进一步的，步骤a)中所述活性炭粉的粒径为300-500nm，所述纳米二氧化钛的粒径为20-30nm。
进一步的，步骤b)中所述硅烷偶联剂由γ-甲基丙烯酰氧基丙基三甲氧基硅烷与甲醇按体积比1：12混合而成。
进一步的，步骤b)中所述纳米二氧化钛与硅烷偶联剂的W/V为2：15；所述纳米二氧化钛、活性炭粉与季戊四醇油酸酯的质量比为3：1：1.5。
进一步的，S2中的真空度为0.2-0.3Mpa，搅拌速度为150-300r/min。
有益效果：
本发明相较现有的清洁剂清洁与杀菌效果更佳。本发明中酸性增稠剂的加入能够提升清洁剂存放过程中的稳定性；通过乙醇酸、草酸、二甲苯磺酸钠的加入能够对浴室洁具表面的污垢具有较好的清洁效果；EDTA-2Na的加入能够使水垢软化以避免洁具表面水垢的沉积，光亮剂的加入能够于洁具表面形成光滑亮面，提升了洁具表面的抗再沉积能力，防止了洁具表面的二次污染；活性剂中二氧化钛经硅氧烷的接枝改性后能够提升其分散稳定性，活性炭粉与二氧化钛按特定比例加入能够使活性炭粉表面部分吸附纳米二氧化钛，在清洁过程中部分吸附纳米二氧化钛的活性炭粉能够对污渍、恶臭物质及细菌进行吸附，提升了光催化纳米二氧化钛与污渍等物质的接触概率，提升了纳米二氧化钛的光催化降解、杀菌效果，活性剂中季戊四醇油酸酯可以通过酯键作用吸附在活性炭表面，减小了活性炭粉团聚、沉降的风险，提升了其分散稳定性；香精的加入能够对清理后洁具的气味进行改善。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：
一种用于浴室与洁具的清洁剂，各组分按重量份计，由水85份，酸性增稠剂6份，其中酸性增稠剂选用ARLYPON VPC，光亮剂0.5份，其中光亮剂选用POLYQUART AMPHO 149，乙醇酸3.5份，草酸1.8份，二甲苯磺酸钠1.8份，其中二甲苯磺酸钠选用二甲苯磺酸钠SX-40，香精0.2份，其中香精选用香精21007B，氯化钠1.6份，EDTA-2Na 0.8份与活性剂0.7份组成。
一种用于浴室与洁具的清洁剂，其制备方法包括以下步骤：
S1:向水中依次加入酸性增稠剂、光亮剂、乙醇酸、草酸、香精与氯化钠并混合均匀，得到混合组分A；
S2：向将混合组分A加入二甲苯磺酸钠、EDTA-2Na与活性剂，并于真空下搅拌混合50-90min，制得上述清洁剂。
活性剂的制备方法包括以下步骤：
a)将活性炭粉、纳米二氧化钛分别用2mol/L的HCl浸泡12-15h后，用蒸馏水抽滤洗涤至pH＝7.0，接着将处理后的活性炭粉、纳米二氧化钛分别放入到100℃的真空干燥箱中，干燥12h；
b)将处理后的纳米二氧化钛加入到硅烷偶联剂中，并于45-50℃下搅拌混合12-15h，接着将步骤a)中处理后活性炭粉与季戊四醇油酸酯依次加入到混合组分中，并于60-65℃下，进行搅拌混合，混合3-5h后，制得上述活性剂。
步骤a)中活性炭粉的粒径为300-500nm，纳米二氧化钛的粒径为20-30nm。
步骤b)中硅烷偶联剂由γ-甲基丙烯酰氧基丙基三甲氧基硅烷与甲醇按体积比1：12混合而成。
步骤b)中纳米二氧化钛与硅烷偶联剂的W/V为2：15；纳米二氧化钛、活性炭粉与季戊四醇油酸酯的质量比为3：1：1.5。
S2中的真空度为0.2-0.3Mpa，搅拌速度为150-300r/min。
实施例2：
一种用于浴室与洁具的清洁剂，各组分按重量份计，由水86份，酸性增稠剂5份，其中酸性增稠剂选用ARLYPON VPC，光亮剂0.4份，其中光亮剂选用POLYQUART AMPHO 149，乙醇酸4.0份，草酸1.6份，二甲苯磺酸钠1.8份，其中二甲苯磺酸钠选用二甲苯磺酸钠SX-40，香精0.4份，其中香精选用香精21007B，氯化钠1.7份，EDTA-2Na 1.2份与活性剂0.5份组成。
一种用于浴室与洁具的清洁剂，其制备方法包括以下步骤：
S1:向水中依次加入酸性增稠剂、光亮剂、乙醇酸、草酸、香精与氯化钠并混合均匀，得到混合组分A；
S2：向将混合组分A加入二甲苯磺酸钠、EDTA-2Na与活性剂，并于真空下搅拌混合50-90min，制得上述清洁剂。
活性剂的制备方法包括以下步骤：
a)将活性炭粉、纳米二氧化钛分别用2mol/L的HCl浸泡12-15h后，用蒸馏水抽滤洗涤至pH＝7.0，接着将处理后的活性炭粉、纳米二氧化钛分别放入到100℃的真空干燥箱中，干燥12h；
b)将处理后的纳米二氧化钛加入到硅烷偶联剂中，并于45-50℃下搅拌混合12-15h，接着将步骤a)中处理后活性炭粉与季戊四醇油酸酯依次加入到混合组分中，并于60-65℃下，进行搅拌混合，混合3-5h后，制得上述活性剂。
步骤a)中活性炭粉的粒径为300-500nm，纳米二氧化钛的粒径为20-30nm。
步骤b)中硅烷偶联剂由γ-甲基丙烯酰氧基丙基三甲氧基硅烷与甲醇按体积比1：12混合而成。
步骤b)中纳米二氧化钛与硅烷偶联剂的W/V为2：15；纳米二氧化钛、活性炭粉与季戊四醇油酸酯的质量比为3：1：1.5。
S2中的真空度为0.2-0.3Mpa，搅拌速度为150-300r/min。
实施例3：
一种用于浴室与洁具的清洁剂，各组分按重量份计，由水88份，酸性增稠剂4份，其中酸性增稠剂选用ARLYPON VPC，光亮剂0.5份，其中光亮剂选用POLYQUART AMPHO 149，乙醇酸4.5份，草酸1.7份，二甲苯磺酸钠1.5份，其中二甲苯磺酸钠选用二甲苯磺酸钠SX-40，香精0.3份，其中香精选用香精21007B，氯化钠1.8份，EDTA-2Na 0.9份与活性剂0.9份组成。
一种用于浴室与洁具的清洁剂，其制备方法包括以下步骤：
S1:向水中依次加入酸性增稠剂、光亮剂、乙醇酸、草酸、香精与氯化钠并混合均匀，得到混合组分A；
S2：向将混合组分A加入二甲苯磺酸钠、EDTA-2Na与活性剂，并于真空下搅拌混合50-90min，制得上述清洁剂。
活性剂的制备方法包括以下步骤：
a)将活性炭粉、纳米二氧化钛分别用2mol/L的HCl浸泡12-15h后，用蒸馏水抽滤洗涤至pH＝7.0，接着将处理后的活性炭粉、纳米二氧化钛分别放入到100℃的真空干燥箱中，干燥12h；
b)将处理后的纳米二氧化钛加入到硅烷偶联剂中，并于45-50℃下搅拌混合12-15h，接着将步骤a)中处理后活性炭粉与季戊四醇油酸酯依次加入到混合组分中，并于60-65℃下，进行搅拌混合，混合3-5h后，制得上述活性剂。
步骤a)中活性炭粉的粒径为300-500nm，纳米二氧化钛的粒径为20-30nm。
步骤b)中硅烷偶联剂由γ-甲基丙烯酰氧基丙基三甲氧基硅烷与甲醇按体积比1：12混合而成。
步骤b)中纳米二氧化钛与硅烷偶联剂的W/V为2：15；纳米二氧化钛、活性炭粉与季戊四醇油酸酯的质量比为3：1：1.5。
S2中的真空度为0.2-0.3Mpa，搅拌速度为150-300r/min。
实施例4：
一种用于浴室与洁具的清洁剂，各组分按重量份计，由水89份，酸性增稠剂5份，其中酸性增稠剂选用ARLYPON VPC，光亮剂0.4份，其中光亮剂选用POLYQUART AMPHO 149，乙醇酸4.0份，草酸1.9份，二甲苯磺酸钠1.9份，其中二甲苯磺酸钠选用二甲苯磺酸钠SX-40，香精0.2份，其中香精选用香精21007B，氯化钠1.5份，EDTA-2Na 1.0份与活性剂0.8份组成。
一种用于浴室与洁具的清洁剂，其制备方法包括以下步骤：
S1:向水中依次加入酸性增稠剂、光亮剂、乙醇酸、草酸、香精与氯化钠并混合均匀，得到混合组分A；
S2：向将混合组分A加入二甲苯磺酸钠、EDTA-2Na与活性剂，并于真空下搅拌混合50-90min，制得上述清洁剂。
活性剂的制备方法包括以下步骤：
a)将活性炭粉、纳米二氧化钛分别用2mol/L的HCl浸泡12-15h后，用蒸馏水抽滤洗涤至pH＝7.0，接着将处理后的活性炭粉、纳米二氧化钛分别放入到100℃的真空干燥箱中，干燥12h；
b)将处理后的纳米二氧化钛加入到硅烷偶联剂中，并于45-50℃下搅拌混合12-15h，接着将步骤a)中处理后活性炭粉与季戊四醇油酸酯依次加入到混合组分中，并于60-65℃下，进行搅拌混合，混合3-5h后，制得上述活性剂。
步骤a)中活性炭粉的粒径为300-500nm，纳米二氧化钛的粒径为20-30nm。
步骤b)中硅烷偶联剂由γ-甲基丙烯酰氧基丙基三甲氧基硅烷与甲醇按体积比1：12混合而成。
步骤b)中纳米二氧化钛与硅烷偶联剂的W/V为2：15；纳米二氧化钛、活性炭粉与季戊四醇油酸酯的质量比为3：1：1.5。
S2中的真空度为0.2-0.3Mpa，搅拌速度为150-300r/min。
实施例5：
一种用于浴室与洁具的清洁剂，各组分按重量份计，由水90份，酸性增稠剂6份，其中酸性增稠剂选用ARLYPON VPC，光亮剂0.5份，其中光亮剂选用POLYQUART AMPHO 149，乙醇酸5.0份，草酸1.6份，二甲苯磺酸钠2.0份，其中二甲苯磺酸钠选用二甲苯磺酸钠SX-40，香精0.4份，其中香精选用香精21007B，氯化钠1.6份，EDTA-2Na 1.1份与活性剂0.6份组成。
一种用于浴室与洁具的清洁剂，其制备方法包括以下步骤：
S1:向水中依次加入酸性增稠剂、光亮剂、乙醇酸、草酸、香精与氯化钠并混合均匀，得到混合组分A；
S2：向将混合组分A加入二甲苯磺酸钠、EDTA-2Na与活性剂，并于真空下搅拌混合50-90min，制得上述清洁剂。
活性剂的制备方法包括以下步骤：
a)将活性炭粉、纳米二氧化钛分别用2mol/L的HCl浸泡12-15h后，用蒸馏水抽滤洗涤至pH＝7.0，接着将处理后的活性炭粉、纳米二氧化钛分别放入到100℃的真空干燥箱中，干燥12h；
b)将处理后的纳米二氧化钛加入到硅烷偶联剂中，并于45-50℃下搅拌混合12-15h，接着将步骤a)中处理后活性炭粉与季戊四醇油酸酯依次加入到混合组分中，并于60-65℃下，进行搅拌混合，混合3-5h后，制得上述活性剂。
步骤a)中活性炭粉的粒径为300-500nm，纳米二氧化钛的粒径为20-30nm。
步骤b)中硅烷偶联剂由γ-甲基丙烯酰氧基丙基三甲氧基硅烷与甲醇按体积比1：12混合而成。
步骤b)中纳米二氧化钛与硅烷偶联剂的W/V为2：15；纳米二氧化钛、活性炭粉与季戊四醇油酸酯的质量比为3：1：1.5。
S2中的真空度为0.2-0.3Mpa，搅拌速度为150-300r/min。
性能检测：
1、清洁剂去污能力测试
硬水配置
洗涤试验中配制清洁剂溶液采用250mg/kg(以碳酸钙表示)硬水，钙离子与镁离子物质的量比为6：4。配制方法如下CaCl2 16.7g和MgSO4·7H2O 24.7g，配制10L，即为2500mg/kg硬水，使用时稀释至250mg/kg，硬水标定按GB/T6367进行。
人工污垢的配制
标准黄土的配制
| 化学成分 | 二氧化硅 | 三氧化铝 | 氧化钙 | 三氧化二铁 |
| 含量(％) | 54.0-72.0 | 10.0-14.0 | 4.0-9.0 | 0.3-5.0 |
污垢土的比例
| 名称 | 含量/g | 名称 | 含量/g |
| 磷酸氢二钠 | 15.0 | 奶粉 | 15.0 |
| 磷酸钠 | 7.5 | 硬脂酸钙 | 5.0 |
| 硫尿 | 5.0 | 标准黄土 | 5.0 |
| 尿素 | 10.0 | 2500mg/kg硬水 | 75.0 |
| 鸡蛋 | 24.2 |
配制方法：
先将新鲜的鸡蛋去壳在烧杯中搅拌均匀备用，将硬脂酸钙、硬水的烧杯中加热到80℃融化，将全脂奶粉、鸡蛋液加入搅拌均匀，再将其它物质加入混和，搅拌，即为细腻的人工污垢。
去污率测定：
对本发明各实施例制备的清洁剂与对比例1的清洁剂的去污率进行检测，去污率测定按GB9985-2000附录B方法进行，以机械力清洗玻璃片去掉污垢，去污率如下表所示：(对比例1为一市售清洁剂)
由上表可知，本发明制备的清洁剂相比市售清洁剂清洁效果更佳。
2、清洁剂灭菌能力测试
根据卫生部2002年《消毒技术规范》对本发明各实施例制备的清洁剂与对比例1的清洁剂的杀菌力进行检测，具体检测结果如下表所示：(对比例1为一市售清洁剂)
由上表可明确得知，本发明制备的清洁剂相比市售清洁剂灭菌效果更佳。
以上实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的精神和范围。
Claims (5)
1.一种用于浴室与洁具的清洁剂，其特征在于，各组分按重量份计，由水85-90份、酸性增稠剂4-6份、光亮剂0.4-0.5份、乙醇酸3.5-5.0份、草酸1.6-1.9份、二甲苯磺酸钠1.5-2.0份、香精0.2-0.4份、氯化钠1.5-1.8份、EDTA-2Na 0.8-1.2份与活性剂0.5-0.9份组成；
其制备方法包括以下步骤：
S1:向水中依次加入酸性增稠剂、光亮剂、乙醇酸、草酸、香精与氯化钠并混合均匀，得到混合组分A；
S2：向将混合组分A加入二甲苯磺酸钠、EDTA-2Na与活性剂，并于真空下搅拌混合50-90min，制得上述清洁剂；
所述活性剂的制备方法包括以下步骤：
a)将活性炭粉、纳米二氧化钛分别用2mol/L的HCl浸泡12-15h后，用蒸馏水抽滤洗涤至pH＝7.0，接着将处理后的活性炭粉、纳米二氧化钛分别放入到100℃的真空干燥箱中，干燥12h；
b)将处理后的纳米二氧化钛加入到硅烷偶联剂中，并于45-50℃下搅拌混合12-15h，接着将步骤a)中处理后活性炭粉与季戊四醇油酸酯依次加入到混合组分中，并于60-65℃下，进行搅拌混合，混合3-5h后，制得上述活性剂。
2.根据权利要求1所述的一种用于浴室与洁具的清洁剂，其特征在于，步骤a)中所述活性炭粉的粒径为300-500nm，所述纳米二氧化钛的粒径为20-30nm。
3.根据权利要求1所述的一种用于浴室与洁具的清洁剂，其特征在于，步骤b)中所述硅烷偶联剂由γ-甲基丙烯酰氧基丙基三甲氧基硅烷与甲醇按体积比1：12混合而成。
4.根据权利要求1所述的一种用于浴室与洁具的清洁剂，其特征在于，步骤b)中所述纳米二氧化钛与硅烷偶联剂的W/V为2：15；所述纳米二氧化钛、活性炭粉与季戊四醇油酸酯的质量比为3：1：1.5。
5.根据权利要求1所述的一种用于浴室与洁具的清洁剂，其特征在于，S2中的真空度为0.2-0.3Mpa，搅拌速度为150-300r/min。