CN110183925A - A kind of solid material block and preparation method thereof applied for heat transfer colour ribbon back - Google Patents
A kind of solid material block and preparation method thereof applied for heat transfer colour ribbon back Download PDFInfo
- Publication number
- CN110183925A CN110183925A CN201910433880.4A CN201910433880A CN110183925A CN 110183925 A CN110183925 A CN 110183925A CN 201910433880 A CN201910433880 A CN 201910433880A CN 110183925 A CN110183925 A CN 110183925A
- Authority
- CN
- China
- Prior art keywords
- coupling agent
- heat transfer
- solid material
- material block
- hydroxyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of solid material blocks and preparation method thereof applied for heat transfer colour ribbon back, raw material including following weight percent: methyl methacrylate 30%-35%, isobornyl methacrylate 5%-10%, hydroxyl silane coupling agent 0.5%-1%, hydroxyl-terminated polydimethylsiloxane 7%-9%, 0.5%-1% containing amino silicane coupling agent, toluene 40%-45%, butanone 5%-10% and azodiisobutyronitrile 0.5%-1%, present invention employs vacuum drying methods to apply mother liquor solidification for back obtained for solid material block, facilitate the storage and transport of back coating material, it ensure that quality when back coating material uses.
Description
Technical field
The present invention relates to thermal transfer technology fields, and in particular to it is a kind of for heat transfer colour ribbon back apply solid material block and its
Preparation method.
Background technique
Heat transfer colour ribbon is the basic consumptive material of thermal transfer technology, with the fast development of electronic computer industry, this heat
The application field of quick consumable material is more and more wider, gradually expands to and can answer from the single temperature-sensitive typewriter applied to office realm
The printing of bar code for multiple fields such as food, drugs plays increasingly important role in national economy.
Heat transfer colour ribbon carbon ribbon is generally made of three parts such as basement membrane, heat-resisting back coating, ink coatings, is printed in thermal transfer
On machine, heat-resisting back coating is directly contacted with heat-transferring head, and thermal transfer ink is directly contacted with stock, heat-transferring head wink when work
Between heat release, the heat of heat release point sends thermal transfer ink coating to by heat-resisting back coating and basement membrane, ink melt and by thermoprint
Onto stock, text, image are formed, so there is heat-resisting back coating heat-insulated, reduction friction, reduction print head to attach dust,
Print head is protected, the effect in the service life of print head is extended.
Heat-resisting back coating is to form layer protecting film, the back on existing market after being coated on the solidification of the basement membrane back side by back coating liquid
Masking liquid is mostly to be formed with propylene using organic silicone oil, acrylate and some silane coupling agents (such as isocyanates coupling)
The modified organic siliconresin of acid esters, then it will be dissolved in toluene, ethyl acetate equal solvent is made into solid containing generally 20%-30%'s
Solution, however the low back coating liquid volume contained admittedly is big, all causes great inconvenience for storing and transporting, if but back coating liquid consolidate
Containing excessively high, since resulting resin still has the unreacted active site in part, it may occur that further cross-linking reaction,
The denaturation of resin is caused to fail to be unfavorable for storing.
Summary of the invention
It is an object of the invention to: can not be stored when for existing back coating liquid large arch dam, low reservoir volume containing when admittedly compared with
Greatly, it is not easy to the problem of storing and transporting, a kind of solid material block and preparation method thereof applied for heat transfer colour ribbon back is provided.
To solve the above problems, The technical solution adopted by the invention is as follows:
A kind of solid material block applied for heat transfer colour ribbon back, the raw material including following weight percent: methacrylic acid
Methyl esters 30%-35%, isobornyl methacrylate 5%-10%, hydroxyl silane coupling agent 0.5%-1%, hydroxy-end capped silicon
Rubber 7%-9%, 0.5%-1% containing amino silicane coupling agent, two isobutyl of toluene 40%-45%, butanone 5%-10% and azo
Nitrile 0.5%-1%.
Preferably, the hydroxyl silane coupling agent are as follows: 3- methacryloxypropyl trimethoxy silane.
Preferably, described to contain amino silicane coupling agent are as follows: 3- aminopropyl triethoxysilane.
A kind of preparation method of the solid material block applied for heat transfer colour ribbon back:
(1) by methyl methacrylate, isobornyl methacrylate, hydroxyl silane coupling agent and methylbenzene raw material,
It is added in reaction kettle by above-mentioned weight percent, dissolves azodiisobutyronitrile with appropriate butanone, reaction kettle is added after mixing
In, 70-72 DEG C of reaction 2-3h of temperature control;
(2) by hydroxyl-terminated polydimethylsiloxane and containing amino silicane coupling agent, suitable fourth is dissolved in by above-mentioned weight percent
It in ketone, is added in reaction kettle after mixing, after keeping the temperature 72 DEG C of sustained response 2-3h, closes heating, naturally cool to room temperature,
Discharging, obtains semi-finished product;
(3) it by semi-finished product obtained by step (2), is put into vacuum oven in batches, it is dry at being 60 DEG C in temperature, often
Drying time needed for 1kg semi-finished product is 1-2h, obtains white chunks product.
Preferably, cold-trap is provided with before the vacuum pump of the vacuum oven of the step (3).
Preferably, according to required ratio, solvent appropriate is added into the blocky back paint, low-grade fever is sufficiently stirred
Dissolution can be used, and the solvent is toluene, any one in ethyl acetate.
In conclusion by adopting the above-described technical solution, the beneficial effects of the present invention are:
1, the present invention is made by the way that the solvent in back coating liquid to be drained to vacuum drying method and carries on the back painting solid material block, from
And the reactivity site in system is controlled, and overcome can not storing for the solid back coating liquid that the prior art is produced, it is low to contain admittedly
The disadvantages of back coating liquid reservoir volume is big, not readily transportable;
2, the present invention is made back by two-step method and applies mother liquor, and the first step is different by methyl methacrylate, methacrylic acid
Norbornene ester, hydroxyl silane coupling agent synthetic resin main chain and control introduce hydroxyl amount, facilitate second step reaction molecular
The control of amount prevents the appearance of excessive cross-linking reaction, avoids because of single step reaction, caused by synthetic resin structure be unfavorable for controlling
The problem of broadening is easy with molecular weight distribution;
3, extracted solvent is condensed back to by the present invention by the way that cold-trap is arranged before the vacuum pump of vacuum oven
It receives, effective utilization has been carried out to solvent, economizing on resources reduces cost.
Specific embodiment
All features disclosed in this specification can be with any other than mutually exclusive feature and/or step
Mode combines.
Embodiment 1
A kind of solid material block applied for heat transfer colour ribbon back, the raw material including following weight percent: methacrylic acid
Methyl esters 30%, isobornyl methacrylate 5%, hydroxyl silane coupling agent 0.5%, hydroxyl-terminated polydimethylsiloxane 7% contain amino
Silane coupling agent 0.5%, toluene 40%, butanone 5%% and azodiisobutyronitrile 0.5%.
The hydroxyl silane coupling agent are as follows: 3- methacryloxypropyl trimethoxy silane.
It is described to contain amino silicane coupling agent are as follows: 3- aminopropyl triethoxysilane.
A kind of preparation method of the solid material block applied for heat transfer colour ribbon back:
(1) by methyl methacrylate, isobornyl methacrylate, hydroxyl silane coupling agent and methylbenzene raw material,
It is added in reaction kettle by above-mentioned weight percent, dissolves azodiisobutyronitrile with appropriate butanone, reaction kettle is added after mixing
In, temperature control 70 reacts 2h;
(2) by hydroxyl-terminated polydimethylsiloxane and containing amino silicane coupling agent, suitable fourth is dissolved in by above-mentioned weight percent
It in ketone, is added in reaction kettle after mixing, after keeping the temperature 72 DEG C of sustained response 2h, closes heating, naturally cool to room temperature, out
Material, obtains semi-finished product;
(3) it by semi-finished product obtained by step (2), is put into vacuum oven in batches, it is dry at being 60 DEG C in temperature, often
Drying time needed for 1kg semi-finished product is 1h, obtains white chunks product.
Cold-trap is additionally provided with before the vacuum pump of the vacuum oven of the step (3).
A kind of application method of the solid material block applied for heat transfer colour ribbon back are as follows: according to required ratio, Xiang Suoshu
Solvent appropriate is added in blocky back paint, low-grade fever dissolution, which is sufficiently stirred, can be used, and the solvent is toluene, in ethyl acetate
Any one.
Embodiment 2
A kind of solid material block applied for heat transfer colour ribbon back, the raw material including following weight percent: methacrylic acid
Methyl esters 32%, isobornyl methacrylate 8%, hydroxyl silane coupling agent 0.7%, hydroxyl-terminated polydimethylsiloxane 8% contain amino
Silane coupling agent 0.8%, toluene 42%, butanone 8% and azodiisobutyronitrile 0.8%.
The hydroxyl silane coupling agent are as follows: 3- methacryloxypropyl trimethoxy silane.
It is described to contain amino silicane coupling agent are as follows: 3- aminopropyl triethoxysilane.
A kind of preparation method of the solid material block applied for heat transfer colour ribbon back:
(1) by methyl methacrylate, isobornyl methacrylate, hydroxyl silane coupling agent and methylbenzene raw material,
It is added in reaction kettle by above-mentioned weight percent, dissolves azodiisobutyronitrile with appropriate butanone, reaction kettle is added after mixing
In, 71 DEG C of reaction 2.5h of temperature control;
(2) by hydroxyl-terminated polydimethylsiloxane and containing amino silicane coupling agent, suitable fourth is dissolved in by above-mentioned weight percent
It in ketone, is added in reaction kettle after mixing, after keeping the temperature 72 DEG C of sustained response 2.5h, closes heating, naturally cool to room temperature,
Discharging, obtains semi-finished product;
(3) it by semi-finished product obtained by step (2), is put into vacuum oven in batches, it is dry at being 60 DEG C in temperature, often
Drying time needed for 1kg semi-finished product is 1.5h, obtains white chunks product.
Cold-trap is provided with before the vacuum pump of the vacuum oven of the step (3).
A kind of application method of the solid material block applied for heat transfer colour ribbon back are as follows: according to required ratio, Xiang Suoshu
Solvent appropriate is added in blocky back paint, low-grade fever dissolution, which is sufficiently stirred, can be used, and the solvent is toluene, in ethyl acetate
Any one.
Embodiment 3
A kind of solid material block applied for heat transfer colour ribbon back, the raw material including following weight percent: methacrylic acid
Methyl esters 35%, isobornyl methacrylate 10%, hydroxyl silane coupling agent 1%, hydroxyl-terminated polydimethylsiloxane 9% contain amino
Silane coupling agent 1%, toluene 45%, butanone 10% and azodiisobutyronitrile 1%.
The hydroxyl silane coupling agent are as follows: 3- methacryloxypropyl trimethoxy silane.
It is described to contain amino silicane coupling agent are as follows: 3- aminopropyl triethoxysilane.
A kind of preparation method of the solid material block applied for heat transfer colour ribbon back:
(1) by methyl methacrylate, isobornyl methacrylate, hydroxyl silane coupling agent and methylbenzene raw material,
It is added in reaction kettle by above-mentioned weight percent, dissolves azodiisobutyronitrile with appropriate butanone, reaction kettle is added after mixing
In, 72 DEG C of reaction 3h of temperature control;
(2) by hydroxyl-terminated polydimethylsiloxane and containing amino silicane coupling agent, suitable fourth is dissolved in by above-mentioned weight percent
It in ketone, is added in reaction kettle after mixing, after keeping the temperature 72 DEG C of sustained response 3h, closes heating, naturally cool to room temperature, out
Material, obtains semi-finished product;
(3) it by semi-finished product obtained by step (2), is put into vacuum oven in batches, it is dry at being 60 DEG C in temperature, often
Drying time needed for 1kg semi-finished product is 2h, obtains white chunks product.
Cold-trap is provided with before the vacuum pump of the vacuum oven of the step (3).
A kind of application method of the solid material block applied for heat transfer colour ribbon back are as follows: according to required ratio, Xiang Suoshu
Solvent appropriate is added in blocky back paint, low-grade fever dissolution, which is sufficiently stirred, can be used, and the solvent is toluene, in ethyl acetate
Any one.
Finally, it is stated that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although passing through ginseng
According to the preferred embodiment of the present invention, invention has been described, it should be appreciated by those of ordinary skill in the art that can
To make various changes to it in the form and details, without departing from the present invention defined by the appended claims
Spirit and scope.
Claims (6)
1. a kind of solid material block applied for heat transfer colour ribbon back, it is characterised in that: the raw material including following weight percent: first
Base methyl acrylate 30%-35%, isobornyl methacrylate 5%-10%, hydroxyl silane coupling agent 0.5%-1%, hydroxyl
Base blocks silicon rubber 7%-9%, 0.5%-1% containing amino silicane coupling agent, toluene 40%-45%, butanone 5%-10% and idol
Nitrogen bis-isobutyronitrile 0.5%-1%.
2. a kind of solid material block applied for heat transfer colour ribbon back according to claim 1, it is characterised in that: described to contain hydroxyl
Base silane coupling agent are as follows: 3- methacryloxypropyl trimethoxy silane.
3. a kind of solid material block applied for heat transfer colour ribbon back according to claim 1, it is characterised in that: described to contain ammonia
Base silane coupling agent are as follows: 3- aminopropyl triethoxysilane.
4. a kind of preparation method of the solid material block applied for heat transfer colour ribbon back, it is characterised in that:
(1) by methyl methacrylate, isobornyl methacrylate, hydroxyl silane coupling agent and methylbenzene raw material, by upper
It states weight percent to be added in reaction kettle, dissolves azodiisobutyronitrile with appropriate butanone, be added in reaction kettle after mixing, control
Warm 70-72 DEG C of reaction 2-3h;
(2) it by hydroxyl-terminated polydimethylsiloxane and containing amino silicane coupling agent, is dissolved in suitable butanone by above-mentioned weight percent,
It is added in reaction kettle after mixing, after keeping the temperature 72 DEG C of sustained response 2-3h, stops heating, after naturally cooling to room temperature,
Discharging, obtains semi-finished product;
(3) it by semi-finished product obtained by step (2), is put into vacuum oven in batches, dry at being 60 DEG C in temperature, every 1kg half
Drying time needed for finished product is 1-2h, obtains white chunks product.
5. a kind of preparation method of solid material block applied for heat transfer colour ribbon back according to claim 4, feature exist
In: cold-trap is provided with before the vacuum pump of the vacuum oven of the step (3).
6. a kind of application method of solid material block applied for heat transfer colour ribbon back according to claim 1, feature exist
In: according to required ratio, solvent appropriate is added into the blocky back paint, low-grade fever dissolution, which is sufficiently stirred, to be made
It is toluene, any one in ethyl acetate with, the solvent.