CN110181885A - A kind of marble composite material and preparation method of belt lock catch - Google Patents
A kind of marble composite material and preparation method of belt lock catch Download PDFInfo
- Publication number
- CN110181885A CN110181885A CN201910434122.4A CN201910434122A CN110181885A CN 110181885 A CN110181885 A CN 110181885A CN 201910434122 A CN201910434122 A CN 201910434122A CN 110181885 A CN110181885 A CN 110181885A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite material
- marble
- lock catch
- belt lock
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of composite materials, and in particular to a kind of marble composite material and preparation method of belt lock catch, the composite material include: marble+SPC substrate+muting pad from top to bottom;The marble thickness range is 2-3mm;The SPC substrate side is provided with buckle structure;The muting pad is foamed material;The SPC substrate includes the raw material of following parts by weight: 100 parts of polyvinyl chloride resin;250-350 parts of powdered whiting;PE3-10 parts of toughening agent C;2-8 parts of ACR processing aid;5-10 parts of calcium-zinc composite stabilizing agent;0.5-2 parts of PE wax, the technical problems to be solved by the present invention are: providing a kind of i.e. marble composite material and preparation method with aesthetic feeling and the convenient belt lock catch of processing.
Description
Technical field
The present invention relates to technical field of composite materials, and in particular to a kind of Dali stone composite material of belt lock catch and its preparation
Method.
Background technique
The advantages that marble is attractive and durable because of its, it is very popular, it is usually used in daily life, such as
Marble top, marble floor, marble wall brick etc.;However marble, as non-renewable resources, country manages more it
Come stringenter, source cost can be relatively high, and marble mass ratio itself is heavier, is beaten by external force and is easy to produce crack or damage
It is bad, therefore either transport or all sufficiently complex trouble of production.
And SPC substrate is a kind of hard PVC material, weight is lighter compared with marble, and less rapid wear in handling process
It is bad, how the two to be combined, forming one kind to have aesthetic feeling and the convenient composite material of processing is to be worth the problem of inquiring into.
Summary of the invention
The technical problems to be solved by the present invention are: providing a kind of i.e. with aesthetic feeling and the convenient belt lock catch of processing
Marble composite material and preparation method.
In order to solve the above-mentioned technical problem, a kind of the technical solution adopted by the present invention are as follows: marble composite wood of belt lock catch
Material, the composite material includes: marble, SPC substrate and muting pad from top to bottom;
The marble thickness range is 2-3mm;
The SPC substrate side is provided with buckle structure;
The muting pad is foamed material;
The SPC substrate includes the raw material of following parts by weight: 100 parts of polyvinyl chloride resin;250-350 parts of powdered whiting;Increase
Tough dose CPE3-10 parts;2-8 parts of ACR processing aid;5-10 parts of calcium-zinc composite stabilizing agent;0.5-2 parts of PE wax.
A kind of another technical solution of the invention are as follows: preparation method of Dali stone composite material, comprising:
(1) cutting marble is polishing to a thickness of 2-3mm;
(2) marble is wherein bonded by bicomponent epoxy resin glue with SPC substrate on one side;
(3) foamed material is pasted on SPC substrate another side, obtains the Dali stone composite material of belt lock catch;
The preparation flow of the SPC substrate includes:
1. high-speed mixer is added in the raw material of SPC substrate and controls temperature and carries out hot mixing;
Cold mixing is carried out 2. controlling high-speed mixer and reducing temperature, material is made to cool down;
3. by the feedstock transportation after hybrid cooling to storage tank;
4. double screw extruder is added in raw material in batches in storage tank, heating extrusion is carried out;
It gets to know extrusion molding 5. the raw material after squeezing out enters sheet material;
6. molding sheet material carries out fixed thickness by four-roller machine;
8. finally the sheet material of fixed thickness is cooled down and is cut.
The beneficial effects of the present invention are: marble raw material is saved, production cost is reduced;SPC substrate has been supplied original pure
The deficiency of marble material, the composite material toughness after combination is preferable, not easily broken;Composite material has with marble material one
The aesthetics of sample;Buckle structure keeps composite material more convenient when splicing installation, without using cement;Muting pad not only completely cuts off
Noise, moreover it is possible to keep feel of the composite material as floor when more preferable;Bicomponent epoxy resin glue is Environment-friendlyglue glue, and marble is multiple
It not can cause environmental pollution in condensation material production process, the cold mixing process in the preparation flow of SPC substrate can make raw material
Temperature reduces, and prevents raw material from agglomerating and changing colour.
Specific embodiment
To explain the technical content, the achieved purpose and the effect of the present invention in detail, it is explained below in conjunction with embodiment.
A kind of Dali stone composite material of belt lock catch, the composite material include: from top to bottom marble, SPC substrate and
Muting pad;
The marble thickness range is 2-3mm;
The SPC substrate side is provided with buckle structure;
The muting pad is foamed material;
The SPC substrate includes the raw material of following parts by weight: 100 parts of polyvinyl chloride resin;250-350 parts of powdered whiting;Increase
Tough dose CPE3-10 parts;2-8 parts of ACR processing aid;5-10 parts of calcium-zinc composite stabilizing agent;0.5-2 parts of PE wax.
The principle of the invention are as follows: marble slab is cut into thin slice, is pasted on SPC substrate surface, and SPC substrate bottom surface is also pasted with
Muting pad, three-decker are combined into Dali stone composite material, and the buckle structure of SPC substrate side setting makes two pieces or more to answer
Condensation material can be spliced by the direct clamping of buckle structure, make a combination thereof at a bigger composite material face, SPC substrate
Include a large amount of powdered whiting ingredients in raw material, keeps the hardness of SPC substrate and marble hardness suitable.
The beneficial effects of the present invention are: marble raw material is saved, production cost is reduced;SPC substrate has been supplied original pure
The deficiency of marble material, the composite material toughness after combination is preferable, not easily broken;Composite material has with marble material one
The aesthetics of sample;Buckle structure keeps composite material more convenient when splicing installation, without using cement;Muting pad not only completely cuts off
Noise, moreover it is possible to keep feel of the composite material as floor when more preferable.
Further, the polymerization scope of polyvinyl chloride resin is 800~1300 in the SPC raw substrate.
From the above description it is recognised that since SPC substrate contains more powdered whiting ingredient, the polymerization of polyvinyl chloride resin
Degree require it is lower, be conducive to control production cost.
Further, the buckle structure is the cooperation of groove and convex block.
From the above description it is recognised that convex block and groove clamping, keep the splicing installation process of composite material easier.
Further, the muting pad is IXPE foam.
From foregoing description it is recognised that IXPE foam is environment-protecting and non-poisonous, moisture-proof, antibiotic and mute shock resistance are more excellent.
The preparation method of above-mentioned Dali stone composite material, comprising:
(1) cutting marble is polishing to a thickness of 2-3mm;
(2) marble is wherein bonded by bicomponent epoxy resin glue with SPC substrate on one side;
(3) foamed material is pasted on SPC substrate another side;
The preparation flow of the SPC substrate includes:
1. high-speed mixer is added in the raw material of SPC substrate and controls temperature and carries out hot mixing;
Cold mixing is carried out 2. controlling high-speed mixer and reducing temperature, raw material is made to cool down;
3. by the feedstock transportation after hybrid cooling to storage tank;
4. double screw extruder is added in raw material in batches in storage tank, heating extrusion is carried out;
5. the raw material after squeezing out enters sheet die extrusion molding;
6. molding sheet material carries out fixed thickness by four-roller machine;
8. finally the sheet material of fixed thickness is cooled down and is cut.
From foregoing description it is recognised that bicomponent epoxy resin glue is Environment-friendlyglue glue, Dali stone composite material was produced
It not can cause environmental pollution in journey, the cold mixing process in the preparation flow of SPC substrate can be such that material temperature reduces, and prevent
Raw material agglomeration and discoloration.
Further, the temperature of hot mixing is 120-150 DEG C in the preparation flow of the SPC substrate.
From foregoing description it is recognised that high-speed mixer hot mixing temperature be 120-150 DEG C when, raw material mixed effect compared with
It is good.
Embodiment one
A kind of Dali stone composite material of belt lock catch, the composite material include: from top to bottom marble, SPC substrate and
Muting pad;The marble thickness range is 2-3mm;The SPC substrate side is provided with buckle structure;The muting pad is hair
Foam material;The SPC substrate includes the raw material of following parts by weight: 100 parts of polyvinyl chloride resin;250-350 parts of powdered whiting;Increase
Tough dose CPE3-10 parts;2-8 parts of ACR processing aid;5-10 parts of calcium-zinc composite stabilizing agent;0.5-2 parts of PE wax;Further, described
The polymerization scope of polyvinyl chloride resin is 800~1300 in SPC raw substrate;Further, the buckle structure is groove and convex block
Cooperation;Further, the muting pad is IXPE foam.
The preparation method of above-mentioned Dali stone composite material, comprising:
(1) cutting marble is polishing to a thickness of 2-3mm;
(2) marble is wherein bonded by bicomponent epoxy resin glue with SPC substrate on one side;
(3) foamed material is pasted on SPC substrate another side;
The preparation flow of the SPC substrate includes:
1. high-speed mixer is added in the raw material of SPC substrate and controls temperature and carries out hot mixing, the temperature of hot mixing is
120-150℃;
Cold mixing is carried out 2. controlling high-speed mixer and reducing temperature, raw material is made to cool down;
3. by the feedstock transportation after hybrid cooling to storage tank;
4. double screw extruder is added in raw material in batches in storage tank, heating extrusion is carried out;
5. the raw material after squeezing out enters sheet die extrusion molding;
6. molding sheet material carries out fixed thickness by four-roller machine;
8. finally the sheet material of fixed thickness is cooled down and is cut.
The stone plastic floor of above-mentioned low-shrinkage and preparation method thereof the utility model has the advantages that save marble raw material, reduce production
Cost;SPC substrate has supplied the deficiency of original pure marble material, and the composite material toughness after combination is preferable, not easily broken;It is multiple
Condensation material has the aesthetics the same with marble material;Buckle structure makes composite material more convenient, nothing when splicing installation
Cement need to be used;Muting pad not only completely cuts off noise, moreover it is possible to keep feel of the composite material as floor when more preferable;Due to SPC substrate
Containing more powdered whiting ingredient, therefore the degree of polymerization requirement of polyvinyl chloride resin is lower, is conducive to control production cost;Convex block and recessed
Slot clamping, keeps the splicing installation process of composite material easier;IXPE foam is environment-protecting and non-poisonous, moisture-proof, antibiotic and mute antidetonation
Property is more excellent;The rubber-plastic foamed plate of EVA is nontoxic, and heat insulation property is preferable, and easy to process;Bicomponent epoxy resin glue is ring
Glue is protected, do not can cause environmental pollution in marble composite manufacturing process, the cold mixing in the preparation flow of SPC substrate
Process can be such that material temperature reduces, and prevent raw material from agglomerating and changing colour.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalents made by bright description are applied directly or indirectly in relevant technical field, are similarly included in this hair
In bright scope of patent protection.
Claims (6)
1. a kind of Dali stone composite material of belt lock catch, which is characterized in that the composite material include: from top to bottom marble,
SPC substrate and muting pad;
The marble thickness range is 2-3mm;
The SPC substrate side is provided with buckle structure;
The muting pad is foamed material;
The SPC substrate includes the raw material of following parts by weight: 100 parts of polyvinyl chloride resin;250-350 parts of powdered whiting;Toughener
CPE3-10 parts;2-8 parts of ACR processing aid;5-10 parts of calcium-zinc composite stabilizing agent;0.5-2 parts of PE wax.
2. the Dali stone composite material of belt lock catch according to claim 1, which is characterized in that PVC in the SPC raw substrate
The polymerization scope of resin is 800~1300.
3. the Dali stone composite material of belt lock catch according to claim 1, which is characterized in that the buckle structure be groove and
The cooperation of convex block.
4. the Dali stone composite material of belt lock catch according to claim 1, which is characterized in that the muting pad is IXPE bubble
Cotton.
5. a kind of preparation method of the Dali stone composite material of belt lock catch described in claim 1, which is characterized in that including walking as follows
It is rapid:
(1) cutting marble is polishing to a thickness of 2-3mm;
(2) marble is wherein bonded by bicomponent epoxy resin glue with SPC substrate on one side;
(3) foamed material is pasted on SPC substrate another side, obtains the Dali stone composite material of belt lock catch;
The preparation flow of the SPC substrate includes:
1. high-speed mixer is added in the raw material of SPC substrate and controls temperature and carries out hot mixing;
Cold mixing is carried out 2. controlling high-speed mixer and reducing temperature, raw material is made to cool down;
3. by the feedstock transportation after hybrid cooling to storage tank;
4. double screw extruder is added in raw material in batches in storage tank, heating extrusion is carried out;
5. the raw material after squeezing out enters sheet die extrusion molding;
6. molding sheet material carries out fixed thickness by four-roller machine;
8. finally the sheet material of fixed thickness is cooled down and is cut.
6. the preparation method of the Dali stone composite material of belt lock catch according to claim 5, which is characterized in that the SPC base
The temperature of hot mixing is 120-150 DEG C in the preparation flow of plate.