CN110152437A - A kind of digester preparation method of microenvironment pollution control - Google Patents
A kind of digester preparation method of microenvironment pollution control Download PDFInfo
- Publication number
- CN110152437A CN110152437A CN201810126831.1A CN201810126831A CN110152437A CN 110152437 A CN110152437 A CN 110152437A CN 201810126831 A CN201810126831 A CN 201810126831A CN 110152437 A CN110152437 A CN 110152437A
- Authority
- CN
- China
- Prior art keywords
- powder
- catalyst
- pottery
- shell
- biological particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of digester preparation methods of microenvironment pollution control, belong to environmental technology field.Pottery powder, zeolite, diatom ooze, biological particles, conch meal, catalyst are uniformly mixed by it, rod is made, it is prepared into charcoal in the case where temperature is 500~900 DEG C, the time is 5-10h and oxygen free condition, is then 800~1200 DEG C, handles 3-60min, cooling in steam atmosphere in temperature.A kind of digester preparation method of microenvironment pollution control of the invention, simple process and low cost, and obtained product treatment effect is good, long service life.
Description
Technical field
The present invention relates to a kind of digester preparation methods of microenvironment pollution control, belong to environmental technology field.
Background technique
Microenvironment refers to public transport environment inside car, environment in subway, hires out environment inside car, domestic environment and all public fields
The environment of conjunction." microenvironment " contacted at any time in our daily lifes, for example, just renovated new family, father secondhand smoke, new
Love vehicle started with etc..These microenvironments are easy to produce the pollutants such as dust, formaldehyde, ozone, and harmfulness is no less than overall situation
The pollutants such as haze.
For the product such as diatom ooze, active carbon, nano-titanium dioxide etc. of microenvironment pollution control, there are properties of product
The disadvantages of single, at high cost, service life is short.
Summary of the invention
In view of this, the present invention provides a kind of digester preparation method of microenvironment pollution control, simple process, cost
It is low, and obtained product treatment effect is good, long service life.
The technical solution adopted by the present invention to solve the technical problems is:
A kind of digester preparation method of microenvironment pollution control, will make pottery powder, zeolite, diatom ooze, biological particles, shellfish
Shell powder, catalyst are uniformly mixed, and rod is made, is prepared into the case where temperature is 500~900 DEG C, the time is 5-10h and oxygen free condition
Then charcoal is 800~1200 DEG C, handles 3-60min, cooling in vapor in temperature.Wherein pottery powder, zeolite, diatom
Mud, catalyst, conch meal and biological particles mass ratio are 0.1~10:0.1~10:0.1~10:0.1~10:0.1~10:
10；Pottery powder is the powder that pottery piece is ground；Biological particles are the one or more of bamboo powder, wood powder, grass meal, shell powder；Conch meal
Refer to crab, shell, tortoise shell, shrimp shell one or more of powder；Catalyst be iron oxide, ferroso-ferric oxide, titanium dioxide,
The powder that silver oxide, copper oxide are mixed to get according to 0.1~10:0.1 of mass ratio~10:0.1~10:0.1~10:10；It is made
The process of rod be will make pottery powder, zeolite, diatom ooze, biological particles, conch meal, catalyst mixture be added mass fraction be 5-
20% water is pressed by 1-5 atmospheric pressure.
The present invention uses pottery powder, zeolite, diatom ooze, biological particles, conch meal, catalyst for raw material, by under high pressure
Squeeze, be carbonized under high temperature and vapor under high-temperature process, the active carbon of available high activity, while making make pottery powder, zeolite, silicon
Algal gel, conch meal, catalyst uniform load on the activated carbon, while the characteristics of each component can be played, so that the property of product
It can obtain maximum performance.
The invention has the following beneficial effects: simple process and low cost, product can quickly eliminate the organic gas in microenvironment,
And high treating effect, long service life.
Specific embodiment
Presently in connection with embodiment, specifically the present invention is described in further detail.
A kind of digester preparation method of microenvironment pollution control, will make pottery powder, zeolite, diatom ooze, biological particles, shellfish
Shell powder, catalyst are uniformly mixed, and rod is made, is prepared into the case where temperature is 500~900 DEG C, the time is 5-10h and oxygen free condition
Then charcoal is 800~1200 DEG C, handles 3-60min, cooling in steam atmosphere in temperature.Wherein pottery powder, zeolite, silicon
Algal gel, catalyst, conch meal and biological particles mass ratio be 0.1~10:0.1~10:0.1~10:0.1~10:0.1~
10:10；Pottery powder is the powder that pottery piece is ground；Biological particles are the one or more of bamboo powder, wood powder, grass meal, shell powder；Shell
Powder refer to crab, shell, tortoise shell, shrimp shell one or more of powder；Catalyst is iron oxide, ferroso-ferric oxide, titanium dioxide
The powder that titanium, silver oxide, copper oxide are mixed to get according to 0.1~10:0.1 of mass ratio~10:0.1~10:0.1~10:10；System
Process at rod be will make pottery powder, zeolite, diatom ooze, biological particles, conch meal, catalyst mixture be added mass fraction be
The water of 5-20% is pressed by 1-5 atmospheric pressure.
Embodiment one
A kind of digester preparation method of microenvironment pollution control, will make pottery powder, zeolite, diatom ooze, biological particles, shellfish
Shell powder, catalyst are uniformly mixed, and rod is made, is prepared into charcoal in the case where temperature is 700 DEG C, the time is 7h and oxygen free condition, then
It is 1050 DEG C, handles 51min, cooling in steam atmosphere in temperature.Wherein pottery powder, zeolite, diatom ooze, catalyst, shellfish
Shell powder and biological particles mass ratio are 6:0.1~10:6:8:7:10；Pottery powder is the powder that pottery piece is ground；Biological particles are
Bamboo powder, wood powder and grass meal；Conch meal refers to crab, shell, tortoise shell；Catalyst is iron oxide, ferroso-ferric oxide, titanium dioxide
The powder that titanium, silver oxide, copper oxide are mixed to get according to mass ratio 4:5:6:5:10；The process that rod is made is will make pottery powder, boiling
The water that mass fraction is 12% is added in stone, diatom ooze, biological particles, conch meal, catalyst mixture, is pressed by 3 atmosphere
Row compression moulding.
Embodiment two
A kind of digester preparation method of microenvironment pollution control, will make pottery powder, zeolite, diatom ooze, biological particles, shellfish
Shell powder, catalyst are uniformly mixed, and rod is made, is prepared into charcoal in the case where temperature is 700 DEG C, the time is 7h and oxygen free condition, then
It is 1100 DEG C, handles 40min, cooling in vapor in temperature.Wherein pottery powder, zeolite, diatom ooze, catalyst, conch meal
It is 5:6:6:7:6:10 with biological particles mass ratio；Pottery powder is the powder that pottery piece is ground；Biological particles are bamboo powder, wood powder；
Conch meal refers to tortoise shell, shrimp shell；Catalyst is iron oxide, ferroso-ferric oxide, titanium dioxide, silver oxide, copper oxide according to matter
Measure the powder being mixed to get than 4:6:8:5:10；The process that rod is made is will make pottery powder, zeolite, diatom ooze, biological particles, shellfish
The water that mass fraction is 13% is added in shell powder, catalyst mixture, is pressed by 4 atmospheric pressure.
Embodiment 3
A kind of digester preparation method of microenvironment pollution control, will make pottery powder, zeolite, diatom ooze, biological particles, shellfish
Shell powder, catalyst are uniformly mixed, and rod is made, is prepared into charcoal in the case where temperature is 750 DEG C, the time is 7h and oxygen free condition, then
It is 930 DEG C, handles 40min, cooling in steam atmosphere in temperature.Wherein pottery powder, zeolite, diatom ooze, catalyst, shellfish
Shell powder and biological particles mass ratio are 6:6:8:5:4:10；Pottery powder is the powder that pottery piece is ground；Biological particles are grass meal, fruit
Shell powder；Conch meal refers to tortoise shell, shrimp shell；Catalyst be iron oxide, ferroso-ferric oxide, titanium dioxide, silver oxide, copper oxide by
The powder being mixed to get according to mass ratio 5:5:3:5:10；The process that rod is made is will make pottery powder, zeolite, diatom ooze, biomass
The water that mass fraction is 10% is added in grain, conch meal, catalyst mixture, is pressed by 4 atmospheric pressure.
Finally, it is stated that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although referring to compared with
Good embodiment describes the invention in detail, those skilled in the art should understand that, it can be to skill of the invention
Art scheme is modified or replaced equivalently, and without departing from the objective and range of technical solution of the present invention, should all be covered at this
In the scope of the claims of invention.
Claims (1)
1. a kind of digester preparation method of microenvironment pollution control, which is characterized in that by the powder, zeolite, diatom ooze, biomass of making pottery
Particle, conch meal, catalyst are uniformly mixed, and rod are made, temperature is 500~900 DEG C, the time is 5-10h and oxygen free condition
Under be prepared into charcoal, be then 800~1200 DEG C, handle 3-60min, cooling in vapor in temperature.Wherein pottery powder, boiling
Stone, diatom ooze, catalyst, conch meal and biological particles mass ratio are 0.1~10: 0.1~10: 0.1~10: 0.1~10:
0.1~10: 10；Pottery powder is the powder that pottery piece is ground；Biological particles are one kind or several of bamboo powder, wood powder, grass meal, shell powder
Kind；Conch meal refer to crab, shell, tortoise shell, shrimp shell one or more of powder；Catalyst be iron oxide, ferroso-ferric oxide,
Titanium dioxide, silver oxide, copper oxide are mixed to get according to mass ratio 0.1~10: 0.1~10: 0.1~10: 0.1~10: 10
Powder；The process that rod is made is will make pottery powder, zeolite, diatom ooze, biological particles, conch meal, catalyst mixture addition matter
The water that number is 5-20% is measured, is pressed by 1-5 atmospheric pressure.