CN110144763A - A kind of paper hook manufacturing process - Google Patents
A kind of paper hook manufacturing process Download PDFInfo
- Publication number
- CN110144763A CN110144763A CN201910501886.0A CN201910501886A CN110144763A CN 110144763 A CN110144763 A CN 110144763A CN 201910501886 A CN201910501886 A CN 201910501886A CN 110144763 A CN110144763 A CN 110144763A
- Authority
- CN
- China
- Prior art keywords
- mold
- hot pressing
- product
- molding machine
- manufacturing process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of papers to link up with manufacturing process, comprising the following steps: S1: production product forming mould;S2: prepare paper raw material;S3: the raw material are beaten to form slurry by beater;S4: slurry pumping is poured into the stock tank of molding machine, is formed and hot-forming by the wet embryo that the molding machine completes product, is formed semi-finished product;S5: bead cutter trimming is passed through to the semi-finished product after hot-forming, T-type structure is formed, is provided with bending slot on T-type structure;S6: T-type structure is bent 90 degree along bending slot and forms L shape to get finished product.This paper links up with manufacturing process, and production hook product is integrally formed, and high-efficient, energy conservation and environmental protection is easy to use.
Description
Technical field
The present invention relates to paper plastic technology fields more particularly to a kind of paper to link up with manufacturing process.
Background technique
Paper products are currently on the market using a kind of relatively more extensive product.But for hook, currently on the market
It is to be made by plastic material, is difficult to degrade, it is big to environmental hazard.
In paper products production process, generally by hot-forming.But in existing production process, it will use more
Platform equipment is respectively completed a process, and manual intervention is more, and the degree of automation is low, and production efficiency is low.
Summary of the invention
In view of the above shortcomings of the prior art, present patent application the technical problem to be solved is that: how a kind of energy is provided
Enough preferably production hooks, high degree of automation is high-efficient, and more environmentally-friendly paper links up with manufacturing process.
To achieve the goals above, present invention employs following technical solutions:
A kind of paper hook manufacturing process, comprising the following steps:
S1: production product forming mould;
S2: prepare paper raw material;
S3: the raw material are beaten to form slurry by beater;
S4: by the slurry pumping be poured into the stock tank of molding machine, by the molding machine complete product wet embryo molding and
It is hot-forming, form semi-finished product;
S5: bead cutter trimming is passed through to the semi-finished product after hot-forming, T-type structure is formed, is provided with bending on T-type structure
Slot;
S6: T-type structure is bent 90 degree along bending slot and forms L shape to get finished product.
Wherein, in step S1, production product forming mould the following steps are included:
A1: product drawing is drawn;
A2: mold drawing is drawn according to product drawing;
A3: product mold is manufactured according to die drawing paper, including the vaccum pulp absorbing mold of the molding machine, extrusion die, heat
Press the shaving die of mold, transfer mold and bead cutter under upper mold, hot pressing.
Wherein, in step S2, the paper raw material include bamboo pulp plate and sugarcane pulpboard.
Wherein, the ratio of the bamboo pulp plate and sugarcane pulpboard is 6:4.
Wherein, in step S4, wet embryo molding and it is hot-forming the following steps are included:
P1: vaccum pulp absorbing mold being fixedly mounted on molding machine, is sunk in the stock tank of molding machine, the vaccum pulp absorbing mould
Tool carries out vacuum suction filter, and slurry is adsorbed on vaccum pulp absorbing die surface, adsorbs the wet embryo of formation required thickness after the set time;
P2: vaccum pulp absorbing mold is carried out overturning rising by molding machine, using extrusion die and vaccum pulp absorbing mold clamping with
Extrusion forming is carried out to the wet embryo of the adsorption of vaccum pulp absorbing mold, so that wet embryo forms the preliminary profile of product;
P3: mold is moved to below vaccum pulp absorbing mold under hot pressing, and mold is located above the stock tank of molding machine under hot pressing, at
Vaccum pulp absorbing mold is carried out overturning reset by type machine, and the wet embryo for obtaining preliminary profile is transferred to hot pressing lower die by vaccum pulp absorbing mold
On tool;
P4: mold resets under hot pressing, is molded using mold under hot pressing upper mold and hot pressing to obtaining preliminary profile
Wet embryo is formed and is dried, and semi-finished product are obtained;
P5: mold is opened under hot pressing upper mold and hot pressing, and semi-finished product are adsorbed on hot pressing upper mold, molding machine mobilization
Mold is moved under hot pressing upper mold and hot pressing between mold, and semi-finished product are transferred on transfer mold by hot pressing upper mold;
P6: transfer mold resets, and semi-finished product are put into receiver and are collected.
Wherein, mold and transfer mold cooperate under the vaccum pulp absorbing mold, extrusion die, hot pressing upper mold, hot pressing
It is mounted on the molding machine, the molding machine is automated production all-in-one machine.
Wherein, midge hole is provided on the vaccum pulp absorbing mold, indent is provided with molding on the vaccum pulp absorbing mold
Slot, face forming tank is provided with molding protrusion on the extrusion die.
Wherein, in step P4, the temperature of mold is respectively 140 DEG C and 150 DEG C, hot pressing under the hot pressing upper mold, hot pressing
Time is 90min.
Wherein, in step S5, combination product drawing size, using the bead cutter using shaving die to half after drying
The side of finished product is cut, and the drawing of retained product draws part.
In conclusion a kind of paper provided by the invention links up with manufacturing process, have the advantages that
1. paper hook is integrally formed, environmental protection is easy to use.
2. production process uses automated production all-in-one machine, an equipment completes wet embryo molding and hot-forming behaviour
Make, preferably reduce cost, make full use of space, improves the quality of production efficiency and product.
3. production process technology is simple, product disposal molding, sound construction, intensity is big, and the service life is long, preferably reaches ring
It protects, energy saving purpose preferably improves efficiency.
Detailed description of the invention
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, below in conjunction with attached drawing and reality
Applying example, the present invention is further described, and the accompanying drawings in the following description is only section Example of the invention, general for this field
For logical technical staff, without creative efforts, it can also be obtained according to these attached drawings other accompanying drawings:
Fig. 1 is the process flow chart that paper disclosed by the invention links up with manufacturing process.
Fig. 2 is the process flow chart for manufacturing product forming mould.
Fig. 3 is wet embryo molding and hot-forming process flow chart.
Fig. 4 is the explosive view of vaccum pulp absorbing mold, semi-finished product and extrusion die.
Fig. 5 is the schematic diagram in another orientation Fig. 4.
Fig. 6 is the schematic enlarged-scale view of vaccum pulp absorbing mold in Fig. 4.
Fig. 7 is the schematic enlarged-scale view of extrusion die in Fig. 4.
Fig. 8 is the schematic enlarged-scale view of semi-finished product in Fig. 4.
Fig. 9 is the structure chart of finished product.
Specific embodiment
In order to keep the purposes, technical schemes and advantages of the embodiment of the present invention clearer, implement below in conjunction with the present invention
Technical solution in example carries out clear, complete description, it is clear that and described embodiment is section Example of the invention, and
It is not all of embodiment.Based on the embodiment of the present invention, those of ordinary skill in the art are not before making the creative labor
Every other embodiment obtained is put, protection scope of the present invention is belonged to.
Therefore, the detailed description of the embodiment of the present invention provided in the accompanying drawings is not intended to limit below claimed
The scope of the present invention, but be merely representative of selected embodiment of the invention.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without creative efforts belongs to the model that the present invention protects
It encloses.
Term " first ", " second ", " third " etc. are only used for distinguishing description, are not understood to indicate or imply relatively heavy
The property wanted.
In the description of the present invention, it is also necessary to which explanation is unless specifically defined or limited otherwise, term " setting ",
" installation ", " connected ", " connection " shall be understood in a broad sense, for example, it may be fixedly connected, may be a detachable connection or one
Connect to body;It can be directly connected, the connection inside two elements can also be can be indirectly connected through an intermediary.
For the ordinary skill in the art, the concrete meaning of above-mentioned term in the present invention can be understood with concrete condition.
Referring to Fig.1-9, a kind of paper links up with manufacturing process, comprising the following steps:
S1: production product forming mould:
A1: 9 drawing of product is drawn;
A2: mold drawing is drawn according to 9 drawing of product;
A3: manufacturing product mold according to die drawing paper, vaccum pulp absorbing mold 1, extrusion die 2 including the molding machine,
The shaving die of mold, transfer mold and bead cutter under hot pressing upper mold, hot pressing.
S2: prepare paper raw material;The paper raw material include bamboo pulp plate and sugarcane pulpboard;The bamboo pulp plate and sugarcane
The ratio of pulpboard is 6:4.Bamboo pulp has biggish intensity, and cane syrup quantity is big, and raw material is easy to get, and can quickly explain,
Environmental protection.The ratio of bamboo pulp plate is big, preferably improves the intensity of hook product, preferably carries out stress, improves quality.
S3: the raw material are beaten to form slurry by beater.
S4: by the slurry pumping be poured into the stock tank of molding machine, by the molding machine complete product wet embryo molding and
It is hot-forming, form semi-finished product 3;
P1: vaccum pulp absorbing mold 1 being fixedly mounted on molding machine, is sunk in the stock tank of molding machine, the vaccum pulp absorbing
Midge hole 4 is provided on mold 1, the vaccum pulp absorbing mold 1 carries out vacuum suction filter, slurry is adsorbed on vaccum pulp absorbing mold 1
The wet embryo of formation required thickness after the set time is adsorbed on surface;Indent is provided with forming tank 5 on the vaccum pulp absorbing mold 1;
P2: vaccum pulp absorbing mold 1 is carried out overturning rising by molding machine, is molded using extrusion die 2 and vaccum pulp absorbing mold 1
Extrusion forming is carried out with the wet embryo of the adsorption to vaccum pulp absorbing mold 1, face forming tank is provided on the extrusion die 2
Molding protrusion 6, so that wet embryo forms the preliminary profile of product;
P3: mold is moved to 1 lower section of vaccum pulp absorbing mold under hot pressing, and mold is located above the stock tank of molding machine under hot pressing,
Vaccum pulp absorbing mold 1 is carried out overturning reset by molding machine, and the wet embryo for obtaining preliminary profile is transferred to hot pressing by vaccum pulp absorbing mold 1
On lower mold;
P4: mold resets under hot pressing, is molded using mold under hot pressing upper mold and hot pressing to obtaining preliminary profile
Wet embryo is formed and is dried, and semi-finished product are obtained;Under the hot pressing upper mold, hot pressing the temperature of mold be respectively 140 DEG C and
150 DEG C, hot pressing time 90min.
P5: mold is opened under hot pressing upper mold and hot pressing, and semi-finished product are adsorbed on hot pressing upper mold, molding machine mobilization
Mold is moved under hot pressing upper mold and hot pressing between mold, and semi-finished product are transferred on transfer mold by hot pressing upper mold;
P6: transfer mold resets, and semi-finished product are put into receiver and are collected.
Wherein, mold and transfer mold are matched under the vaccum pulp absorbing mold 1, extrusion die 2, hot pressing upper mold, hot pressing
Conjunction is mounted on the molding machine, and the molding machine is automated production all-in-one machine.
S5: bead cutter trimming is passed through to the semi-finished product after hot-forming, T-type structure is formed, is provided with bending on T-type structure
Slot;Combination product drawing size is cut using the bead cutter using side of the shaving die to the semi-finished product after drying,
The drawing of retained product draws part.
S6: T-type structure is bent 90 degree along bending slot and forms L shape to get finished product.Artificial bending, it is convenient.
The manufacturing process that the present invention uses manufactures paper hook, and disposal molding, it is convenient to manufacture, technique letter
It is single, it is practical, and energy conservation and environmental protection, production efficiency can be preferably improved, cost is reduced.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (9)
1. a kind of paper links up with manufacturing process, which comprises the following steps:
S1: production product forming mould;
S2: prepare paper raw material;
S3: the raw material are beaten to form slurry by beater;
S4: slurry pumping is poured into the stock tank of molding machine, and the wet embryo molding and hot pressing of product are completed by the molding machine
Molding forms semi-finished product;
S5: bead cutter trimming is passed through to the semi-finished product after hot-forming, T-type structure is formed, is provided with bending slot on T-type structure;
S6: T-type structure is bent 90 degree along bending slot and forms L shape to get finished product.
2. a kind of paper according to claim 1 links up with manufacturing process, which is characterized in that in step S1, production product at
Pattern tool the following steps are included:
A1: product drawing is drawn;
A2: mold drawing is drawn according to product drawing;
A3: according to die drawing paper manufacture product mold, on vaccum pulp absorbing mold, extrusion die, hot pressing including the molding machine
The shaving die of mold, transfer mold and bead cutter under mold, hot pressing.
3. a kind of paper according to claim 2 links up with manufacturing process, which is characterized in that in step S2, the paper is former
Material includes bamboo pulp plate and sugarcane pulpboard.
4. a kind of paper according to claim 3 links up with manufacturing process, which is characterized in that the bamboo pulp plate and sugarcane pulpboard
Ratio be 6:4.
5. a kind of paper according to claim 4 links up with manufacturing process, which is characterized in that in step S4, the wet embryo at
Type and it is hot-forming the following steps are included:
P1: vaccum pulp absorbing mold being fixedly mounted on molding machine, is sunk in the stock tank of molding machine, the vaccum pulp absorbing mold into
Slurry is adsorbed on vaccum pulp absorbing die surface by row vacuum suction filter, adsorbs the wet embryo of formation required thickness after the set time;
P2: vaccum pulp absorbing mold is carried out overturning rising by molding machine, using extrusion die with vaccum pulp absorbing mold clamping to true
The wet embryo that the adsorption of mold is starched in suction carries out extrusion forming, so that wet embryo forms the preliminary profile of product;
P3: mold is moved to below vaccum pulp absorbing mold under hot pressing, and mold is located above the stock tank of molding machine under hot pressing, molding machine
Vaccum pulp absorbing mold is subjected to overturning reset, the wet embryo for obtaining preliminary profile is transferred to mold under hot pressing by vaccum pulp absorbing mold
On;
P4: mold resets under hot pressing, is molded using mold under hot pressing upper mold and hot pressing to obtaining the wet embryo of preliminary profile
It is formed and is dried, obtain semi-finished product;
P5: mold is opened under hot pressing upper mold and hot pressing, and semi-finished product are adsorbed on hot pressing upper mold, molding machine mobilization mold
It is moved under hot pressing upper mold and hot pressing between mold, semi-finished product are transferred on transfer mold by hot pressing upper mold;
P6: transfer mold resets, and semi-finished product are put into receiver and are collected.
6. a kind of paper according to claim 5 links up with manufacturing process, which is characterized in that the vaccum pulp absorbing mold squeezes
Mold and transfer mold are fitted on the molding machine under compression mould, hot pressing upper mold, hot pressing, and the molding machine is certainly
Dynamic metaplasia produces all-in-one machine.
7. a kind of paper according to claim 6 links up with manufacturing process, which is characterized in that set on the vaccum pulp absorbing mold
It is equipped with midge hole, indent is provided with forming tank on the vaccum pulp absorbing mold, and face forming tank is provided on the extrusion die
Molding protrusion.
8. a kind of paper according to claim 7 links up with manufacturing process, which is characterized in that in step P4, in the hot pressing
The temperature of mold is respectively 140 DEG C and 150 DEG C, hot pressing time 90min under mold, hot pressing.
9. a kind of paper according to claim 8 links up with manufacturing process, which is characterized in that in step S5, combination product figure
Paper size is cut using the bead cutter using side of the shaving die to the semi-finished product after drying, the figure of retained product
Paper draws part.