CN110117433A - The molten environmentally friendly compound oil ink of BE230 ester - Google Patents
The molten environmentally friendly compound oil ink of BE230 ester Download PDFInfo
- Publication number
- CN110117433A CN110117433A CN201810117406.6A CN201810117406A CN110117433A CN 110117433 A CN110117433 A CN 110117433A CN 201810117406 A CN201810117406 A CN 201810117406A CN 110117433 A CN110117433 A CN 110117433A
- Authority
- CN
- China
- Prior art keywords
- parts
- molten
- ester
- ink
- compound oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of molten environmentally friendly compound oil inks of BE230 ester, it is made of raw material from the following weight, 25-35 parts of titanium dioxide, 20-30 parts of polyurethane resin, 20-30 parts of lignin modification phenolic resin, 15-20 parts of saturated polyester resin, 35-40 parts of isoamyl acetate, 4-5 parts of starch phosphate, 20-25 parts of isopropanol, 10-15 parts of dimethyl ether, 2-3 parts of energy stone, 2-3 parts of magnetite, 4-6 parts of hydrotalcite, 1-3 parts of n-propyl, 1-1.2 parts of sulforicinoleic acid, 1-1.5 parts of polysorbate, 1-2 parts of diacetylmonoxime, 0.8-1.5 parts of adhesion promoter, 1-2 parts and water 60-65 parts of iron octoate.The ink that the present invention obtains has faster rate of drying, good adhesive force and excellent heat resistance, especially filler uses energy stone, magnetite and hydrotalcite, the characteristic of obtained ink is much better than pearl filler ink, rise color is neat, bright in luster, glossiness is good, good leveling property, antistatic are excellent, thus printing adaptability is splendid, ink transfer is strong, chromatography excellent, combined strength bination are high, and solvent release is especially good, and residual solvent is few.
Description
Technical field
The present invention relates to the molten environmentally friendly compound oil inks of Printing ink producing technical field more particularly to a kind of BE230 ester.
Background technique
Ink is the substance that graph text information is used to form in printing process, directly decision printed matter on image contrast,
Color, clarity, therefore act in printing process huge.But existing some printing ink rate of dryings are excessively slow, printing
Phenomena such as set-off, page sticking are often resulted in brush.There are also some printing ink poor adhesive forces, be easy to produce print unevenness it is even,
Phenomena such as deinking, seriously affects printing quality.Moreover, these ink do not have heat resistance usually, the fortune of ink has been seriously affected
Use range.Therefore, need to design that a kind of rate of drying is fast, adhesive force is good, combined strength bination is high, and the oil with stronger heat resistance
Ink.
Summary of the invention
The purpose of the invention is to overcome the deficiencies of the prior art and provide a kind of molten environmentally friendly compound oil ink of BE230 ester.
The present invention is achieved through the following technical solutions:
The molten environmentally friendly compound oil ink of BE230 ester, is made of raw material from the following weight:
25-35 parts of titanium dioxide, 20-30 parts of polyurethane resin, 20-30 parts of lignin modification phenolic resin, saturated polyester tree
15-20 parts of rouge, 35-40 parts of isoamyl acetate, 4-5 parts of starch phosphate, 20-25 parts of isopropanol, dimethyl ether 10-15
Part, 2-3 parts of energy stone, 2-3 parts of magnetite, 4-6 parts of hydrotalcite, 1-3 parts of n-propyl, 1-1.2 parts of sulforicinoleic acid, polysorbate
1-1.5 parts, 1-2 parts of diacetylmonoxime, 0.8-1.5 parts of adhesion promoter, 1-2 parts of iron octoate and 60-65 parts of water.
Further, the molten environmentally friendly compound oil ink of the BE230 ester, is made of raw material from the following weight:
25 parts of titanium dioxide, 20 parts of polyurethane resin, 20 parts of lignin modification phenolic resin, 15 parts of saturated polyester resin, second
35 parts of isoamyl valerate, 4 parts of starch phosphate, 20 parts of isopropanol, 10 parts of dimethyl ether, 2 parts of energy stone, 2 parts of magnetite, water
It is 4 parts of talcum, 1 part of n-propyl, 1 part of sulforicinoleic acid, 1 part of polysorbate, 1 part of diacetylmonoxime, 0.8 part of adhesion promoter, pungent
1 part and 60 parts of water of sour iron.
Further, the molten environmentally friendly compound oil ink of the BE230 ester, is made of raw material from the following weight:
30 parts of titanium dioxide, 25 parts of polyurethane resin, 25 parts of lignin modification phenolic resin, 18 parts of saturated polyester resin, second
38 parts of isoamyl valerate, 4.5 parts of starch phosphate, 23 parts of isopropanol, 13 parts of dimethyl ether, 2.5 parts of energy stone, magnetite
2.5 parts, 5 parts of hydrotalcite, 2 parts of n-propyl, 1.1 parts of sulforicinoleic acid, 1.3 parts of polysorbate, 1.5 parts of diacetylmonoxime, adhesive force
1.2 parts of promotor, 1.5 parts of iron octoate and 63 parts of water.
Further, the molten environmentally friendly compound oil ink of the BE230 ester, is made of raw material from the following weight:
35 parts of titanium dioxide, 30 parts of polyurethane resin, 30 parts of lignin modification phenolic resin, 20 parts of saturated polyester resin, second
40 parts of isoamyl valerate, 5 parts of starch phosphate, 25 parts of isopropanol, 15 parts of dimethyl ether, 3 parts of energy stone, 3 parts of magnetite, water
6 parts of talcum, 3 parts of n-propyl, 1.2 parts of sulforicinoleic acid, 1.5 parts of polysorbate, 2 parts of diacetylmonoxime, adhesion promoter 1.5
Part, 2 parts of iron octoate and 65 parts of water.
Further, the polyurethane resin is by isophorone diisocyanate and polypropylene -1,2- glycol ether
Polymer.
Compared with prior art, the beneficial effects of the present invention are:
(1) ink that the present invention obtains has faster rate of drying, good adhesive force and excellent heat resistance, especially
Filler uses energy stone, magnetite and hydrotalcite, and the characteristic of obtained ink is much better than pearl filler ink, plays that color is neat, color
It is color it is bright-coloured, glossiness is good, good leveling property, antistatic be excellent, thus printing adaptability it is splendid, ink transfer is strong, chromatography effect pole
It is good, combined strength bination is high, solvent release is especially good, and residual solvent is few;
(2) using agitating mode first quick and back slow, pigment (titanium dioxide) and binder (chlorine are added by several times in the process of stirring
Vinegar resin, lignin modification phenolic resin, saturated polyester resin) and filler (energy stone, magnetite, hydrotalcite), (acetic acid is different for solvent
Pentyl ester, isopropanol and dimethyl ether), the gentle dry agent (butanone of surfactant (sulforicinoleic acid and polysorbate)
Oxime) and desiccant (iron octoate), starch phosphate, keep solid powder mixture fully dispersed in water, is uniformly suspended in solvent
In, then ink is carried out to forge processing using alternately high temperature low temperature, alternate high-pressure low pressure, alternate illumination dark, finally be made
The ink arrived has a variety of good characteristics, and stemness as before is greater than 19mm/15s, and attachment fastness is greater than 99%, and heat resisting temperature is higher than
164 DEG C, and the first stemness of existing commercial inks is generally less than 14mm/15s, attachment fastness is generally less than 98%, and heat resisting temperature is not
More than 150 DEG C.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment 1
The molten environmentally friendly compound oil ink of BE230 ester, is made of raw material from the following weight:
25 parts of titanium dioxide, 20 parts of polyurethane resin, 20 parts of lignin modification phenolic resin, 15 parts of saturated polyester resin, second
35 parts of isoamyl valerate, 4 parts of starch phosphate, 20 parts of isopropanol, 10 parts of dimethyl ether, 2 parts of energy stone, 2 parts of magnetite, water
It is 4 parts of talcum, 1 part of n-propyl, 1 part of sulforicinoleic acid, 1 part of polysorbate, 1 part of diacetylmonoxime, 0.8 part of adhesion promoter, pungent
1 part and 60 parts of water of sour iron.Wherein, the polyurethane resin is by isophorone diisocyanate and polypropylene -1,2- second two
The polymer of alcohol ether.
The molten environmentally friendly compound oil ink of the BE230 ester of above-mentioned constituent, is prepared by the following steps:
Step 1: by the titanium dioxide of above-mentioned parts by weight, polyurethane resin, lignin modification phenolic resin, saturated polyester tree
It is 3 microns that rouge, energy stone, magnetite, hydrotalcite powder, which are broken to average grain diameter, and is uniformly mixed, and solid powder mixture is obtained;
Step 2: taking the water of above-mentioned parts by weight, the solid powder mixture that step 1 obtains is added, with blender 800
Rev/min revolving speed under stir 30 minutes, n-propyl, isoamyl acetate, isopropanol and the dipropyl two of above-mentioned parts by weight is then added
The revolving speed of blender is reduced to 500 revs/min to continue stirring 100 minutes, the sulfonation of above-mentioned parts by weight is then added by diethylene glycol dimethyl ether
The revolving speed of blender is reduced to 300 revs/min to continue stirring 200 minutes by ricinoleic acid, polysorbate, diacetylmonoxime and iron octoate,
Then the starch phosphate of above-mentioned parts by weight is added, is reduced to 100 revs/min to continue stirring 300 minutes the revolving speed of blender, obtains
Solidliquid mixture;
Step 3: the solidliquid mixture that step 2 is obtained is put into a container, and container is sealed, being put into temperature is
In 150 DEG C of insulating box, shelves and be immediately placed in the refrigerator-freezer that temperature is -10 DEG C after sixty minutes, shelve and be immediately placed in after sixty minutes
In the insulating box that temperature is 100 DEG C, it is immediately placed in after shelving 120 minutes in the refrigerator-freezer that temperature is -3 DEG C, is put after shelving 120 minutes
Enter in a reaction kettle, kept for 30 minutes under conditions of 0.03MPa, is forced into 18MPa and holding 30 minutes immediately after, then
Immediately by pressure reduction to 0.5MPa and holding 60 minutes, it is finally forced into 4MPa immediately and is kept for 60 minutes, takes out the container,
Obtain ink.
The preparation method of the ink, after the step 2, further includes:
The solidliquid mixture that step 2 is obtained pours into a glassware, and makes the solidliquid mixture in glassware
Depth be 3 centimetres, irradiated 30 minutes with intensity is 15J/cm2, wavelength is 500~1000nm light, immediately after by glass
Vessel, which are put into dark surrounds, to be shelved 60 minutes, immediately irradiates 60 points with the light that intensity is 5J/cm2, wavelength is 500nm
Glassware is finally put into dark surrounds immediately and shelves 120 minutes by clock.
The preparation method of the ink, in said step 1, by titanium dioxide, polyurethane resin, lignin modification phenol
It is 5 microns that urea formaldehyde, saturated polyester resin, energy stone, magnetite, hydrotalcite powder, which are broken to average grain diameter,.
Embodiment 2
The molten environmentally friendly compound oil ink of BE230 ester, is made of raw material from the following weight:
25 parts of titanium dioxide, 20 parts of polyurethane resin, 20 parts of lignin modification phenolic resin, 15 parts of saturated polyester resin, second
35 parts of isoamyl valerate, 4 parts of starch phosphate, 20 parts of isopropanol, 10 parts of dimethyl ether, 2 parts of energy stone, 2 parts of magnetite, water
It is 4 parts of talcum, 1 part of n-propyl, 1 part of sulforicinoleic acid, 1 part of polysorbate, 1 part of diacetylmonoxime, 0.8 part of adhesion promoter, pungent
1 part and 60 parts of water of sour iron.Wherein, the polyurethane resin is by isophorone diisocyanate and polypropylene -1,2- second two
The polymer of alcohol ether.
The molten environmentally friendly compound oil ink of the BE230 ester of said components ingredient, is prepared into according to the preparation step in embodiment 1
Product ink.
Embodiment 3
The molten environmentally friendly compound oil ink of BE230 ester, is made of raw material from the following weight:
35 parts of titanium dioxide, 30 parts of polyurethane resin, 30 parts of lignin modification phenolic resin, 20 parts of saturated polyester resin, second
40 parts of isoamyl valerate, 5 parts of starch phosphate, 25 parts of isopropanol, 15 parts of dimethyl ether, 3 parts of energy stone, 3 parts of magnetite, water
6 parts of talcum, 3 parts of n-propyl, 1.2 parts of sulforicinoleic acid, 1.5 parts of polysorbate, 2 parts of diacetylmonoxime, adhesion promoter 1.5
Part, 2 parts of iron octoate and 65 parts of water.Wherein, the polyurethane resin is by isophorone diisocyanate and polypropylene -1,2- second
The polymer of glycol ethers.
The ink that the present invention obtains has faster rate of drying, good adhesive force and excellent heat resistance, especially fills out
Material uses energy stone, magnetite and hydrotalcite, and the characteristic of obtained ink is much better than pearl filler ink, plays that color is neat, color
It is bright-coloured, glossiness is good, good leveling property, antistatic be excellent, thus printing adaptability is splendid, ink transfer is strong, chromatography excellent,
Combined strength bination is high, and solvent release is especially good, and residual solvent is few;Using agitating mode first quick and back slow, in the process of stirring
Pigment (titanium dioxide) and binder (vinyl chloride-vinyl acetate resin, lignin modification phenolic resin, saturated polyester resin) and filler are added by several times
(energy stone, magnetite, hydrotalcite), solvent (isoamyl acetate, isopropanol and dimethyl ether), surfactant (sulfonation
Ricinoleic acid and polysorbate) ease up dry agent (diacetylmonoxime) and desiccant (iron octoate), starch phosphate, and mix solid powder
Object is fully dispersed in water, and even suspension in a solvent, then utilizes alternately high temperature low temperature, alternate high-pressure low pressure, alternate illumination
Dark carries out ink to forge processing, and the ink finally made has a variety of good characteristics, and stemness as before is greater than 19mm/15s,
Attachment fastness is greater than 99%, and heat resisting temperature is higher than 164 DEG C, and the first stemness of existing commercial inks is generally less than 14mm/15s, attached
Fastness be generally less than 98%, heat resisting temperature is no more than 150 DEG C.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (5)
- The molten environmentally friendly compound oil ink of 1.BE230 ester, which is characterized in that be made of raw material from the following weight:25-35 parts of titanium dioxide, 20-30 parts of polyurethane resin, 20-30 parts of lignin modification phenolic resin, saturated polyester resin 15- 20 parts, 35-40 parts of isoamyl acetate, 4-5 parts of starch phosphate, 20-25 parts of isopropanol, 10-15 parts of dimethyl ether, energy Measure stone 2-3 parts, 2-3 parts of magnetite, 4-6 parts of hydrotalcite, 1-3 parts of n-propyl, 1-1.2 parts of sulforicinoleic acid, polysorbate 1-1.5 Part, 1-2 parts of diacetylmonoxime, 0.8-1.5 parts of adhesion promoter, 1-2 parts of iron octoate and 60-65 parts of water.
- 2. the molten environmentally friendly compound oil ink of BE230 ester according to claim 1, which is characterized in that the molten environmental protection of BE230 ester Compound oil ink is made of raw material from the following weight:25 parts of titanium dioxide, 20 parts of polyurethane resin, 20 parts of lignin modification phenolic resin, 15 parts of saturated polyester resin, acetic acid are different 35 parts of pentyl ester, 4 parts of starch phosphate, 20 parts of isopropanol, 10 parts of dimethyl ether, 2 parts of energy stone, 2 parts of magnetite, hydrotalcite 4 parts, 1 part of n-propyl, 1 part of sulforicinoleic acid, 1 part of polysorbate, 1 part of diacetylmonoxime, 0.8 part of adhesion promoter, iron octoate 1 Part and 60 parts of water.
- 3. the molten environmentally friendly compound oil ink of BE230 ester according to claim 1, which is characterized in that the molten environmental protection of BE230 ester Compound oil ink is made of raw material from the following weight:30 parts of titanium dioxide, 25 parts of polyurethane resin, 25 parts of lignin modification phenolic resin, 18 parts of saturated polyester resin, acetic acid are different 38 parts of pentyl ester, 4.5 parts of starch phosphate, 23 parts of isopropanol, 13 parts of dimethyl ether, 2.5 parts of energy stone, 2.5 parts of magnetite, 5 parts of hydrotalcite, 2 parts of n-propyl, 1.1 parts of sulforicinoleic acid, 1.3 parts of polysorbate, 1.5 parts of diacetylmonoxime, adhesion promoter 1.2 parts, 1.5 parts of iron octoate and 63 parts of water.
- 4. the molten environmentally friendly compound oil ink of BE230 ester according to claim 1, which is characterized in that the molten environmental protection of BE230 ester Compound oil ink is made of raw material from the following weight:35 parts of titanium dioxide, 30 parts of polyurethane resin, 30 parts of lignin modification phenolic resin, 20 parts of saturated polyester resin, acetic acid are different 40 parts of pentyl ester, 5 parts of starch phosphate, 25 parts of isopropanol, 15 parts of dimethyl ether, 3 parts of energy stone, 3 parts of magnetite, hydrotalcite 6 parts, it is 3 parts of n-propyl, 1.2 parts of sulforicinoleic acid, 1.5 parts of polysorbate, 2 parts of diacetylmonoxime, 1.5 parts of adhesion promoter, pungent 2 parts and 65 parts of water of sour iron.
- 5. the molten environmentally friendly compound oil ink of BE230 ester according to claim 1-4, which is characterized in that the polyurethane Resin is by the polymer of isophorone diisocyanate and polypropylene -1,2- glycol ether.