CN110093780A - The protectant preparation method of color lamp fabrics aqueous, environmental protective - Google Patents
The protectant preparation method of color lamp fabrics aqueous, environmental protective Download PDFInfo
- Publication number
- CN110093780A CN110093780A CN201910369349.5A CN201910369349A CN110093780A CN 110093780 A CN110093780 A CN 110093780A CN 201910369349 A CN201910369349 A CN 201910369349A CN 110093780 A CN110093780 A CN 110093780A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- mixture
- added
- fabrics
- color lamp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of protectant preparation method of color lamp fabrics aqueous, environmental protective, include the following steps: a, weigh 15-25 parts of organosilicons by weight, the aqueous color of no resin is respectively prepared in 50-70 parts of acrylic resins；B, mixture A is stirred evenly to obtain without addition aqueous dispersion in the aqueous color of resin to made of organosilicon, acrylic resin；C, 10-15 parts of pure water are weighed by weight, are added after aqueous dispersion, aqueous defoamer, aqueous levelling agent and are obtained mixture B after mixing evenly；D, continue to stir mixture B, while mixture A, 1-3 part aqueous wetting agent by weight is added, obtain mixture C after mixing evenly；E, continue to stir mixture C, and organosilicon is added and changes surname acrylic emulsion, preservative is then added；F, water-based thickener is added and adjusts water paint viscosity, by finished product packing after filtering.
Description
Technical field
The present invention relates to color lamp protective agent field, especially a kind of protectant preparation method of color lamp fabrics aqueous, environmental protective.
Background technique
Traditional fabrics only has the effect of antiultraviolet, but waterproofness is poor outdoors, and antiultraviolet fabrics is in printing and dyeing
Adhered to by auxiliary agent, short using the time outdoors, fabrics waterproof moisture resistance properties are poor.
Summary of the invention
To solve problems of the prior art, the present invention provides a kind of protectant systems of color lamp fabrics aqueous, environmental protective
Preparation Method.
The technical solution adopted by the present invention is that:
A kind of protectant preparation method of color lamp fabrics aqueous, environmental protective, includes the following steps:
A, 15-25 parts of organosilicons are weighed by weight, the aqueous color of no resin is respectively prepared in 50-70 parts of acrylic resins；
B, stir evenly mixed without addition aqueous dispersion in the aqueous color of resin to made of organosilicon, acrylic resin
Close object A；
C, 10-15 parts of pure water are weighed by weight, are stirred after aqueous dispersion, aqueous defoamer, aqueous levelling agent is added
Mixture B is obtained after uniformly；
D, continue to stir mixture B, while mixture A, 1-3 part aqueous dispersion by weight is added, stir evenly
Mixture C is obtained afterwards；
E, continue to stir mixture C, and organosilicon is added and changes surname acrylic emulsion, preservative is then added；
F, water-based thickener is added and adjusts water paint viscosity, by finished product packing after filtering.
Preferably, in stepb, speed of agitator is 900 revs/min, and mixing time is 25 minutes.
Preferably, step b further includes following steps:
Mixture A is ground 1-2 times, is subject to and is detected with fineness gauge less than 20 microns.
Preferably, in step d, when with 200 revs/min of stirring mixture B, mixture A, auxiliary agent is added, then with 900
Rev/min stirring 15-20 minute obtain mixture C.
Preferably, step d further includes following steps:
Mixture C, which is subject to, to be detected with fineness gauge less than 20 microns.
Preferably, in step e, when with 500 revs/min of stirring mixture C, organosilicon is added and changes surname acrylic emulsion,
Stirring 5-10 minutes, is then added preservative, then with 500 revs/min stirring 5-10 minutes.
Preferably, in step f, adjustment viscosity to be subject to rock field NK2 flow cup detect 80-90 seconds.
The beneficial effects of the present invention are:
Fabrics aqueous, environmental protective protective agent prepared by the present invention spontaneous curing can generate layer protecting film under the effect of the oxygen,
And the advantages that quickly the linear slit lattice of fabrics can be sealed, reach waterproof, anti-corrosion, UV resistant, when to the use of fabrics
Between extend 2-3 times, it is good to environmental protection effect.
Specific embodiment
The present invention is described in detail combined with specific embodiments below.
Embodiment 1
A kind of protectant preparation method of color lamp fabrics aqueous, environmental protective, includes the following steps:
A, 15 parts of organosilicons are weighed by weight, the aqueous color of no resin is respectively prepared in 50 parts of acrylic resins；
B, stir evenly mixed without addition aqueous dispersion in the aqueous color of resin to made of organosilicon, acrylic resin
Close object A；
C, 10 parts of pure water are weighed by weight, are stirred evenly after aqueous dispersion, aqueous defoamer, aqueous levelling agent is added
Mixture B is obtained afterwards；
D, continue to stir mixture B, while mixture A, 1 part of aqueous dispersion by weight is added, after mixing evenly
Obtain mixture C；
E, continue to stir mixture C, and organosilicon is added and changes surname acrylic emulsion, preservative is then added；
F, water-based thickener is added and adjusts water paint viscosity, by finished product packing after filtering.
Specifically, in stepb, speed of agitator is 900 revs/min, and mixing time is 25 minutes.
Specifically, step b further includes following steps:
Mixture A is ground 1 time, is subject to and is detected with fineness gauge less than 20 microns.
Specifically, in step d, when with 200 revs/min of stirring mixture B, mixture A, auxiliary agent is added, then with 900
Rev/min stirring 15 minutes mixture C.
Specifically, step d further includes following steps:
Mixture C, which is subject to, to be detected with fineness gauge less than 20 microns.
Specifically, in step e, when with 500 revs/min of stirring mixture C, organosilicon is added and changes surname acrylic emulsion,
Then stirring 5 minutes is added preservative, then is stirred 5 minutes with 500 revs/min.
Specifically, in step f, adjustment viscosity to be subject to rock field NK2 flow cup detect 80 seconds.
Embodiment 2
A kind of protectant preparation method of color lamp fabrics aqueous, environmental protective, includes the following steps:
A, 20 parts of organosilicons are weighed by weight, the aqueous color of no resin is respectively prepared in 60 parts of acrylic resins；
B, stir evenly mixed without addition aqueous dispersion in the aqueous color of resin to made of organosilicon, acrylic resin
Close object A；
C, 13 parts of pure water are weighed by weight, are stirred evenly after aqueous dispersion, aqueous defoamer, aqueous levelling agent is added
Mixture B is obtained afterwards；
D, continue to stir mixture B, while mixture A, 2 parts of aqueous dispersions by weight is added, after mixing evenly
Obtain mixture C；
E, continue to stir mixture C, and organosilicon is added and changes surname acrylic emulsion, preservative is then added；
F, water-based thickener is added and adjusts water paint viscosity, by finished product packing after filtering.
Specifically, in stepb, speed of agitator is 900 revs/min, and mixing time is 25 minutes.
Specifically, step b further includes following steps:
Mixture A is ground 1 time, is subject to and is detected with fineness gauge less than 20 microns.
Specifically, in step d, when with 200 revs/min of stirring mixture B, mixture A, auxiliary agent is added, then with 900
Rev/min stirring 18 minutes mixture C.
Specifically, step d further includes following steps:
Mixture C, which is subject to, to be detected with fineness gauge less than 20 microns.
Specifically, in step e, when with 500 revs/min of stirring mixture C, organosilicon is added and changes surname acrylic emulsion,
Then stirring 8 minutes is added preservative, then is stirred 8 minutes with 500 revs/min.
Specifically, in step f, adjustment viscosity to be subject to rock field NK2 flow cup detect 85 seconds.
Embodiment 3
A kind of protectant preparation method of color lamp fabrics aqueous, environmental protective, includes the following steps:
A, 25 parts of organosilicons are weighed by weight, the aqueous color of no resin is respectively prepared in 70 parts of acrylic resins；
B, stir evenly mixed without addition aqueous dispersion in the aqueous color of resin to made of organosilicon, acrylic resin
Close object A；
C, 15 parts of pure water are weighed by weight, are stirred evenly after aqueous dispersion, aqueous defoamer, aqueous levelling agent is added
Mixture B is obtained afterwards；
D, continue to stir mixture B, while mixture A, 3 parts of aqueous dispersions by weight is added, after mixing evenly
Obtain mixture C；
E, continue to stir mixture C, and organosilicon is added and changes surname acrylic emulsion, preservative is then added；
F, water-based thickener is added and adjusts water paint viscosity, by finished product packing after filtering.
Specifically, in stepb, speed of agitator is 900 revs/min, and mixing time is 25 minutes.
Specifically, step b further includes following steps:
Mixture A is ground 2 times, is subject to and is detected with fineness gauge less than 20 microns.
Specifically, in step d, when with 200 revs/min of stirring mixture B, mixture A, auxiliary agent is added, then with 900
Rev/min stirring 20 minutes mixture C.
Specifically, step d further includes following steps:
Mixture C, which is subject to, to be detected with fineness gauge less than 20 microns.
Specifically, in step e, when with 500 revs/min of stirring mixture C, organosilicon is added and changes surname acrylic emulsion,
Then stirring 10 minutes is added preservative, then is stirred 10 minutes with 500 revs/min.
Specifically, in step f, adjustment viscosity to be subject to rock field NK2 flow cup detect 90 seconds.
A specific embodiment of the invention above described embodiment only expresses, the description thereof is more specific and detailed, but simultaneously
Limitations on the scope of the patent of the present invention therefore cannot be interpreted as.It should be pointed out that for those of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to guarantor of the invention
Protect range.
Claims (7)
1. a kind of protectant preparation method of color lamp fabrics aqueous, environmental protective, which comprises the steps of:
A, 15-25 parts of organosilicons are weighed by weight, the aqueous color of no resin is respectively prepared in 50-70 parts of acrylic resins；
B, mixture is stirred evenly to obtain without addition aqueous dispersion in the aqueous color of resin to made of organosilicon, acrylic resin
A；
C, 10-15 parts of pure water are weighed by weight, are stirred evenly after aqueous dispersion, aqueous defoamer, aqueous levelling agent is added
Mixture B is obtained afterwards；
D, continue to stir mixture B, while mixture A, 1-3 part aqueous dispersion by weight is added, after mixing evenly
Mixture C；
E, continue to stir mixture C, and organosilicon is added and changes surname acrylic emulsion, preservative is then added；
F, water-based thickener is added and adjusts water paint viscosity, by finished product packing after filtering.
2. the protectant preparation method of color lamp fabrics aqueous, environmental protective according to claim 1, which is characterized in that in step b
In, speed of agitator is 900 revs/min, and mixing time is 25 minutes.
3. the protectant preparation method of color lamp fabrics aqueous, environmental protective according to claim 2, which is characterized in that step b is also
Include the following steps:
Mixture A is ground 1-2 times, is subject to and is detected with fineness gauge less than 20 microns.
4. the protectant preparation method of color lamp fabrics aqueous, environmental protective according to claim 1, which is characterized in that in step d
In, when with 200 revs/min of stirring mixture B, mixture A, auxiliary agent is added, is then obtained within stirring 15-20 minutes with 900 revs/min
Mixture C.
5. the protectant preparation method of color lamp fabrics aqueous, environmental protective according to claim 4, which is characterized in that step d is also
Include the following steps:
Mixture C, which is subject to, to be detected with fineness gauge less than 20 microns.
6. the preparation method of color lamp steelwork epoxy-modified acrylic acid aqueous anticorrosion paint according to claim 1, feature
It is, in step e, when with 500 revs/min of stirring mixture C, organosilicon is added and changes surname acrylic emulsion, stirring 5-10 divides
Clock, is then added preservative, then with 500 revs/min stirring 5-10 minutes.
7. the protectant preparation method of color lamp fabrics aqueous, environmental protective according to claim 1, which is characterized in that in step f
In, adjustment viscosity to be subject to rock field NK2 flow cup detect 80-90 seconds.