CN110093079A - Ensure the environment protecting water-based paint and production technology of cigarette wrapper printing planarization - Google Patents
Ensure the environment protecting water-based paint and production technology of cigarette wrapper printing planarization Download PDFInfo
- Publication number
- CN110093079A CN110093079A CN201910482388.6A CN201910482388A CN110093079A CN 110093079 A CN110093079 A CN 110093079A CN 201910482388 A CN201910482388 A CN 201910482388A CN 110093079 A CN110093079 A CN 110093079A
- Authority
- CN
- China
- Prior art keywords
- parts
- planarization
- based paint
- environment protecting
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the environment protecting water-based paints and production technology that ensure cigarette wrapper printing planarization, including 5-10 parts of deionized water, 3-5 parts of edible alcohol, 30-40 parts of styrol copolymer, 40-60 parts of acrylic resin, 1-5 parts of auxiliary agent；Deionized water, edible alcohol are mixed in Scattered Kettle, add antifoam additives mixing disperse cosolvent mixture is spare；Then acrylic resin, styrol copolymer, high density polyethylene waxes dispersion aids is taken to be mixed in Scattered Kettle, then by after the addition of dipropylene glycol monomethyl ether coalescing agent, persistently dispersed；The cosolvent mixture got ready is slowly finally filtered into addition, can be filtered and packaged after being uniformly dispersed.Coating is used for the backsizes such as packing cigarette art paper, transfer paper jam, composite card paper by the present invention, Paper Moisture is able to maintain to stablize, be unlikely to deform, avoid when UV offset press printing inspiration paper have some setbacks and when reel intaglio plate high speed printing paper back patch take turns printed caused by unstable appearances printing deviation etc. it is bad.
Description
Technical field
The present invention relates to cigarette wrapper technical fields, and specially guarantee cigarette wrapper printing planarization is environment-friendly water-based
Coating and production technology.
Background technique
Cigarette wrapper is that a kind of outer packing for carrying out decoration printing to cigarette uses, by wrapping paper main body and special
The composition such as radium-shine decorative pattern, structure is simple, but collective is very practical, has to internal packing material and preferably protects and be convenient for
Performance is carried, wrapping paper is comparatively relatively simple in production method, and apparent special radium-shine pattern structure plays product itself
Good decoration propaganda function is arrived, and consumption waste wood is lower, is widely used in every field.
But existing cigarette wrapper produce and use when, be easy because moisture loss and intrusion caused by paper warpage,
Turnup (under lie prone) etc. influences the deformation of paper formation degree, has some setbacks and reel secondly as inhaling (into) paper when UV offset press printing
When intaglio plate high speed printing paper back patch wheel it is unstable occur printing deviation etc. cause to print bad problem.
By the retrieval to prior art, also find no about the environment-friendly water-based of cigarette wrapper printing planarization
Coating the relevant technologies.
Summary of the invention
The purpose of the present invention is to provide ensure cigarette wrapper printing planarization environment protecting water-based paint and production technology,
Paper Moisture can be kept to stablize, not because caused by the loss of moisture and intrusion paper warpage, turnup etc. influence paper formation degree
Deformation；Keep the appropriate coefficient of friction of back side of paper, avoid when UV offset press printing inhale, paper feed has some setbacks and the high print duplication of reel intaglio plate
Paper back patch takes turns the problems such as printing caused by unstable appearance printing deviation etc. is bad when brush.
To achieve the above object, the invention provides the following technical scheme: ensureing the environmental protection of cigarette wrapper printing planarization
Water paint, the raw material including following parts by weight proportion: 5-10 parts of deionized water, 3-5 parts of edible alcohol, styrol copolymer
30-40 parts, 40-60 parts of acrylic resin, 1-5 parts of auxiliary agent.
Further, comprising: 5 parts of deionized water, 3 parts of edible alcohol, 30 parts of styrol copolymer, acrylic resin 40
Part, 1 part of auxiliary agent.
Further, comprising: 10 parts of deionized water, 5 parts of edible alcohol, 40 parts of styrol copolymer, acrylic resin
60 parts, 5 parts of auxiliary agent.
Further, comprising: 8 parts of deionized water, 4 parts of edible alcohol, 35 parts of styrol copolymer, acrylic resin 50
Part, 3 parts of auxiliary agent.
Further, styrol copolymer by styrene, methyl methacrylate, butyl acrylate, ethyl acrylate,
Isooctyl acrylate monomer, hydroxy-ethyl acrylate, hydroxyethyl methacrylate, methacrylic acid, methyl propenoic acid glycidyl polymerization
It forms.
Further, acrylic resin is by the copolymer of 2-EHA and ethyl acrylate, metering system
The copolymer of sour methyl esters and acrylic acid, the copolymer of methacrylic acid and hydroxyethyl methacrylate, butyl acrylate, styrene
Copolymer composition.
Further, deionized water is using the reverse osmosis+EDI technique preparation of RO.
Further, the high-purity grain rectifying preparation of edible alcohol use > 95%.
Further, auxiliary agent is by dipropylene glycol monomethyl ether coalescing agent, high density polyethylene waxes dispersion aids, poly- silicon
Oxygen alkane mixture antifoam additives collectively constitute.
The present invention provides another technical solution are as follows: ensures the life of the environment protecting water-based paint of cigarette wrapper printing planarization
Production. art, comprising the following steps:
S1: successively removing ionized water, edible alcohol is mixed in Scattered Kettle, turn in 300-350/velocity conditions of min under
At the uniform velocity disperse 15 minutes；
S2: it after antifoam additives are added, can remain within continuous revolutions redisperse 10 minutes spare；
S3: acrylic resin, styrol copolymer, high density polyethylene waxes dispersion aids are successively taken to be mixed in Scattered Kettle
In, it is carried out high speed dispersion 20 minutes under the velocity conditions of 700-800 turns/min；
S4: after dipropylene glycol monomethyl ether coalescing agent is added, persistently disperse 15 minutes；
S5: slowly filtering addition for the cosolvent mixture got ready in S2 again, and the speed of 600 turns/min is kept uniformly to divide
It dissipates, after cosolvent is all added, lasting dispersion stirring 15 minutes, can filter and package.
Compared with prior art, the beneficial effects of the present invention are:
1, the environment protecting water-based paint and production technology provided by the invention for ensureing cigarette wrapper printing planarization, is being used for
The backsizes such as packing cigarette art paper, transfer paper jam, composite card paper, can keep Paper Moisture to stablize, not because of the stream of moisture
Intrusion of becoming estranged causes paper warpage, turnup (under lie prone) etc. to influence the deformation of paper formation degree.
2, the environment protecting water-based paint and production technology provided by the invention for ensureing cigarette wrapper printing planarization, additionally it is possible to
The appropriate coefficient of friction of back side of paper is kept, avoids inhaling (into) paper when UV offset press printing and has some setbacks and when reel intaglio plate high speed printing
Paper back patch wheel is unstable to there is the bad problem of printing caused by printing deviation etc..
Specific embodiment
It will be detailed below the embodiment of the present invention, however, the embodiment of the present invention is not limited thereto.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts,
It shall fall within the protection scope of the present invention.
In the embodiment of the present invention: providing safeguard the environment protecting water-based paint of cigarette wrapper printing planarization, including following heavy
The raw material of amount number proportion: 5-10 parts of deionized water, 3-5 parts of edible alcohol, 30-40 parts of styrol copolymer, acrylic resin
40-60 parts, 1-5 parts of auxiliary agent；Wherein, styrol copolymer is by styrene, methyl methacrylate, butyl acrylate, acrylic acid
Ethyl ester, Isooctyl acrylate monomer, hydroxy-ethyl acrylate, hydroxyethyl methacrylate, methacrylic acid, methyl propenoic acid glycidyl
It is polymerized；Acrylic resin is by the copolymer of 2-EHA and ethyl acrylate, methyl methacrylate and third
The copolymer group of the copolymer of olefin(e) acid, the copolymer of methacrylic acid and hydroxyethyl methacrylate, butyl acrylate, styrene
At；Deionized water is using the reverse osmosis+EDI technique preparation of RO；It is prepared by the high-purity grain rectifying of edible alcohol use > 95%；It helps
Agent is total to by dipropylene glycol monomethyl ether coalescing agent, high density polyethylene waxes dispersion aids, polysiloxane mixture antifoam additives
With composition.
Embodiment one:
Remove 5 parts of ionized water, 3 parts of edible alcohol, 30 parts of styrol copolymer, 40 parts of acrylic resin, 1 part of auxiliary agent.
Based on the raw material of above-mentioned parts by weight proportion, the embodiment provided are as follows: ensure that cigarette wrapper prints planarization
Environment protecting water-based paint production technology, comprising the following steps:
Step 1: successively remove 5 parts of ionized water, 3 parts of edible alcohol be mixed in Scattered Kettle, turn/min in 300-350
It carries out at the uniform velocity dispersing 15 minutes under velocity conditions；Then after 0.4 part of antifoam additives being added, continuous revolutions redisperse 10 minutes i.e.
It can remain spare；
Step 2: 40 parts of acrylic resin, 30 parts of styrol copolymer, high density polyethylene waxes dispersion aids are successively taken
0.5 part is mixed in Scattered Kettle, carries out high speed dispersion 20 minutes under the velocity conditions of 700-800 turns/min；Then by dipropyl
After 0.1 part of glycol monomethyl ether coalescing agent is added, persistently disperse 15 minutes；The cosolvent mixture got ready in step 1 is delayed again
Slow filtering is added, and keeps the speed of 600 turns/min evenly dispersed, after cosolvent is all added, lasting dispersion stirring 15 minutes,
It can filter and package.
Embodiment two:
Remove 10 parts of ionized water, 5 parts of edible alcohol, 40 parts of styrol copolymer, 60 parts of acrylic resin, 5 parts of auxiliary agent.
Based on the raw material of above-mentioned parts by weight proportion, the embodiment provided are as follows: ensure that cigarette wrapper prints planarization
Environment protecting water-based paint production technology, comprising the following steps:
Step 1: successively remove 10 parts of ionized water, 5 parts of edible alcohol be mixed in Scattered Kettle, turn/min in 300-350
It carries out at the uniform velocity dispersing 15 minutes under velocity conditions；Then after 2 parts of antifoam additives being added, continuous revolutions redisperse 10 minutes
It remains spare；
Step 2: 60 parts of acrylic resin, 40 parts of styrol copolymer, high density polyethylene waxes dispersion aids are successively taken
2 parts are mixed in Scattered Kettle, carry out high speed dispersion 20 minutes under the velocity conditions of 700-800 turns/min；Then by dipropyl two
After 1 part of alcohol monomethyl ether coalescing agent is added, persistently disperse 15 minutes；The slow mistake of cosolvent mixture that will be got ready in step 1 again
Filter is added, and keeps the speed of 600 turns/min evenly dispersed, after cosolvent is all added, lasting dispersion stirring 15 minutes
It filters and packages.
Embodiment three:
Remove 8 parts of ionized water, 4 parts of edible alcohol, 35 parts of styrol copolymer, 50 parts of acrylic resin, 3 parts of auxiliary agent.
Based on the raw material of above-mentioned parts by weight proportion, the embodiment provided are as follows: ensure that cigarette wrapper prints planarization
Environment protecting water-based paint production technology, comprising the following steps:
Step 1: successively remove 8 parts of ionized water, 4 parts of edible alcohol be mixed in Scattered Kettle, turn/min in 300-350
It carries out at the uniform velocity dispersing 15 minutes under velocity conditions；Then after 1 part of antifoam additives being added, continuous revolutions redisperse 10 minutes
It remains spare；
Step 2: 50 parts of acrylic resin, 35 parts of styrol copolymer, high density polyethylene waxes dispersion aids are successively taken
1 part is mixed in Scattered Kettle, carries out high speed dispersion 20 minutes under the velocity conditions of 700-800 turns/min；Then by dipropyl two
After 1 part of alcohol monomethyl ether coalescing agent is added, persistently disperse 15 minutes；The slow mistake of cosolvent mixture that will be got ready in step 1 again
Filter is added, and keeps the speed of 600 turns/min evenly dispersed, after cosolvent is all added, lasting dispersion stirring 15 minutes
It filters and packages.
To sum up, after environment protecting water-based paint obtained by above-mentioned three kinds of embodiments being filtered and packaged, it is respectively used to cigarette pack
With backsizes such as art paper, transfer paper jam, composite card papers, Paper Moisture can be kept to stablize, not because of the loss of moisture and intrusion
Paper warpage, turnup (under lie prone) etc. is caused to influence the deformation of paper formation degree；The appropriate coefficient of friction of back side of paper can also be kept,
Avoid inhaling that (into) paper has some setbacks and paper back patch takes turns unstable appearances printing partially when reel intaglio plate high speed printing when UV offset press printing
The bad problem of printing caused by position etc..
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (10)
1. ensureing the environment protecting water-based paint of cigarette wrapper printing planarization, which is characterized in that matched including following parts by weight
Raw material: 5-10 parts of deionized water, 3-5 parts of edible alcohol, 30-40 parts of styrol copolymer, 40-60 parts of acrylic resin, help
1-5 parts of agent.
2. the environment protecting water-based paint according to claim 1 for ensureing cigarette wrapper printing planarization, which is characterized in that packet
It includes: 5 parts of deionized water, 3 parts of edible alcohol, 30 parts of styrol copolymer, 40 parts of acrylic resin, 1 part of auxiliary agent.
3. the environment protecting water-based paint according to claim 1 for ensureing cigarette wrapper printing planarization, which is characterized in that packet
It includes: 10 parts of deionized water, 5 parts of edible alcohol, 40 parts of styrol copolymer, 60 parts of acrylic resin, 5 parts of auxiliary agent.
4. the environment protecting water-based paint according to claim 1 for ensureing cigarette wrapper printing planarization, which is characterized in that packet
It includes: 8 parts of deionized water, 4 parts of edible alcohol, 35 parts of styrol copolymer, 50 parts of acrylic resin, 3 parts of auxiliary agent.
5. the environment protecting water-based paint according to any one of claims 1-4 for ensureing cigarette wrapper printing planarization,
It is characterized in that, styrol copolymer is different pungent by styrene, methyl methacrylate, butyl acrylate, ethyl acrylate, acrylic acid
Ester, hydroxy-ethyl acrylate, hydroxyethyl methacrylate, methacrylic acid, methyl propenoic acid glycidyl are polymerized.
6. the environment protecting water-based paint according to any one of claims 1-4 for ensureing cigarette wrapper printing planarization,
It is characterized in that, acrylic resin is by the copolymer of 2-EHA and ethyl acrylate, methyl methacrylate and third
The copolymer group of the copolymer of olefin(e) acid, the copolymer of methacrylic acid and hydroxyethyl methacrylate, butyl acrylate, styrene
At.
7. the environment protecting water-based paint according to any one of claims 1-4 for ensureing cigarette wrapper printing planarization,
It is characterized in that, deionized water is using the reverse osmosis+EDI technique preparation of RO.
8. the environment protecting water-based paint according to any one of claims 1-4 for ensureing cigarette wrapper printing planarization,
It is characterized in that, the high-purity grain rectifying preparation of edible alcohol use > 95%.
9. the environment protecting water-based paint according to any one of claims 1-4 for ensureing cigarette wrapper printing planarization,
It is characterized in that, auxiliary agent is by dipropylene glycol monomethyl ether coalescing agent, high density polyethylene waxes dispersion aids, polysiloxane mixture
Antifoam additives collectively constitute.
10. ensureing the production technology of the environment protecting water-based paint of cigarette wrapper printing planarization, which is characterized in that including following step
It is rapid:
S1: successively removing ionized water, edible alcohol is mixed in Scattered Kettle, turn in 300-350/velocity conditions of min under carry out
At the uniform velocity disperse 15 minutes；
S2: it after antifoam additives are added, can remain within continuous revolutions redisperse 10 minutes spare；
S3: successively taking acrylic resin, styrol copolymer, high density polyethylene waxes dispersion aids to be mixed in Scattered Kettle,
It is carried out high speed dispersion 20 minutes under the velocity conditions of 700-800 turns/min；
S4: after dipropylene glycol monomethyl ether coalescing agent is added, persistently disperse 15 minutes；
S5: slowly filtering addition for the cosolvent mixture got ready in S2 again, keeps the speed of 600 turns/min evenly dispersed, to
After cosolvent is all added, lasting dispersion stirring 15 minutes, it can filter and package.