CN110079908A - Fiber yarn and its manufacturing method - Google Patents
Fiber yarn and its manufacturing method Download PDFInfo
- Publication number
- CN110079908A CN110079908A CN201910437425.1A CN201910437425A CN110079908A CN 110079908 A CN110079908 A CN 110079908A CN 201910437425 A CN201910437425 A CN 201910437425A CN 110079908 A CN110079908 A CN 110079908A
- Authority
- CN
- China
- Prior art keywords
- fiber
- yarn
- fiber yarn
- forms
- polyester ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fiber yarn and its manufacturing methods, the method comprising the steps of: plant fiber and polyester ether elastic fiber are mixed, cotton roll is made, wherein it is 0.1%~10% that polyester ether elastic fiber, which accounts for plant fiber and the mass ratio of polyester ether elastic fiber,;Cotton roll is subjected to carding step, forms sliver;A plurality of sliver is subjected to mixing in doubling step, forms ripe bar;Ripe bar is subjected to Roving Frames, forms rove;Rove is subjected to spinning process, forms spun yarn;By spun yarn-winding, bobbin is formed;The spun yarn of multiple bobbins is merged, forms fiber yarn.The manufacturing method of the fiber yarn mixes polyester ether elastic fiber and plant fiber to promote the elastic property of fiber yarn, and inventor has found polyester ether elastic fiber when the mass ratio in composite fibre is between 0.1%~10%, and the elongation at break of the fiber yarn produced has with the fiber yarn only produced by plant fiber to be obviously improved.
Description
Technical field
The present invention relates to a kind of fiber yarn and its manufacturing methods.
Background technique
Fiber yarn is for woven fabric, rope making, line processed, knitting and embroidery etc..Elastic property is the important indicator of fiber yarn,
There is important influence to the quality of finished product.In general, characterizing the elastic property of fiber yarn with elongation at break.Extension at break
Rate refers to the ratio of fiber yarn length before by external force to the difference and stretching for when breaking, stretching anterior-posterior length.
But the elongation at break of current fiber yarn is all lower, illustrate the elastic properties of these fiber yarns all compared with
It is low, it needs to improve in preparation process to promote the elastic property of fiber yarn.
Summary of the invention
The purpose of the present invention is to provide a kind of manufacturing methods of elastic property for being able to ascend fiber yarn.
In order to reach the purpose of the present invention, a kind of fiber yarn manufacturing method is adopted the following technical scheme that, comprising steps of
Plant fiber and polyester ether elastic fiber are mixed, cotton roll is made, wherein polyester ether elastic fiber accounts for plant fiber and polyether ester
The mass ratio of elastomer is 0.1%~10%;Cotton roll is subjected to carding step, forms sliver;A plurality of sliver is carried out simultaneously
Process forms ripe bar;Ripe bar is subjected to Roving Frames, forms rove;Rove is subjected to spinning process, forms spun yarn;It will be thin
Yarn reel is around formation bobbin;The spun yarn of multiple bobbins is merged, forms fiber yarn.
The manufacturing method of the fiber yarn mixes polyester ether elastic fiber and plant fiber to promote the bullet of fiber yarn
Property performance, and inventor find polyester ether elastic fiber the mass ratio in composite fibre be 0.1%~10% between when, system
The elongation at break for the fiber yarn produced has with the fiber yarn only produced by plant fiber to be obviously improved.
In a wherein embodiment, before plant fiber and polyester ether elastic fiber mixing, by plant fiber and
Polyester ether elastic fiber cleans 24 hours in the mixed liquor of antistatic agent and water.
After plant fiber and polyester ether elastic fiber are cleaned 24 hours in the mixed liquor of antistatic agent and water, not only mention
The antistatic effect of fiber is risen.Due also to antistatic agent and water have the work of infiltration to plant fiber and polyester ether elastic fiber
With the elastic property of promotion plant fiber and polyester ether elastic fiber, so as to improve the disconnected of the fiber yarn produced
Elongation is split, therefore improves the elastic property of fiber yarn.
In a wherein embodiment, the mass ratio of antistatic agent and water is 1: 5~15.
Inventor is found surprisingly that, when the mass ratio of antistatic agent and water is in above range, antistatic agent and water pair
It is the most significant to the elastic property of plant fiber and polyester ether elastic fiber, therefore the further elasticity for promoting fiber yarn
Energy.
In a wherein embodiment, antistatic agent includes 10~20 parts of hydrogenated castor oleic acid, anion pp acyl
1~5 part of amine, 0.5~2 part of poly glycol monomethyl ether, 0.5~2 part of hydroxypropyl PASELLI EASYGEL, polyethylene glycol oxide 0.1~0.5
Part, 0.1~0.5 part of sorbitol anhydride tristearate, 0.05~0.1 part of sesbania gum.
In a wherein embodiment, when cotton roll carries out carding step, the relative humidity of cotton roll local environment is
50%~70%.
Inventors have found that when the relative humidity of control cotton roll local environment is in above range.It will not be because of the phase of cotton roll
It is lower to humidity, and cause that the toughness of cotton roll is lower and adversely affects to the elastic property of fiber yarn.It will not be because of
The relative humidity of cotton roll is higher, and generates adverse effect to the quality of fiber yarn.
In a wherein embodiment, when a plurality of sliver carries out mixing in doubling step, the quantity of sliver is 5~7.
A kind of fiber yarn is manufactured to obtain by above-mentioned fiber yarn manufacturing method.
Detailed description of the invention
To describe the technical solutions in the embodiments of the present invention more clearly, below by embodiment describe in required use
Attached drawing be briefly described.
Fig. 1 is the manufacturing method flow diagram of fiber yarn in the embodiment of the present invention.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, is clearly and completely retouched to the technical solution in the present invention
It states.
Embodiment 1:
Referring to FIG. 1, the present embodiment disclose fiber yarn manufacturing method the following steps are included:
Step S11: plant fiber and polyester ether elastic fiber are cleaned 24 hours in the mixed liquor of antistatic agent and water.
Specifically, the antistatic agent includes 15 parts of hydrogenated castor oleic acid, 3 parts of anionic polyacrylamide, polyethyleneglycol
1 part of methyl ether, 1 part of hydroxypropyl PASELLI EASYGEL, 0.3 part of polyethylene glycol oxide, 0.3 part of sorbitol anhydride tristearate, sesbania gum
0.1 part.
The mass ratio of antistatic agent and water is 1: 10.
Step S12: plant fiber and polyester ether elastic fiber are mixed, cotton roll is made.
Specifically, the mass ratio of plant fiber and polyester ether elastic fiber is 1: 19.Plant fiber and polyetherester elastomer are fine
Dimension is processed into cotton roll, cotton rolling quantity is respectively 400g/m by opening picking mechanical mixture, shredding, removal of impurities.
Step S13: cotton roll is subjected to carding step, forms sliver.
Specifically, cotton roll is resolved into single fiber state, weight of card sliver 3.5g/m, licker-in speed 750r/min, tin
Woods speed is 250r/min, obtains sliver, cotton strip quantity 20g/m, and the uneven rate of weight is 5%.
Step S14: a plurality of sliver is subjected to mixing in doubling step, forms ripe bar.
Specifically, by 5 slivers and being sent into drawing frame, sliver exporting speed is respectively 280mm/min, obtains ripe bar, weight is not
Evening ratio is 0.5%, quantitatively respectively 2g/m.
Step S15: the ripe bar is subjected to Roving Frames, forms rove.
Specifically, ripe bar obtained in step S14 is carried out drawing-off, twists, be wound into rove, quantitative respectively 4g/
10m, total draft are respectively 7 times, and the twist is respectively 40 twirls/m, and ingot speed is respectively 750r/min.
Step S16: the rove is subjected to spinning process, forms spun yarn.
Specifically, increasing the twist to 300 twirls/m, back zone drafting multiple is 1.5 times, ingot speed 15000r/min, spacing block
3mm obtains spun yarn.
Step S17: by the spun yarn-winding, bobbin is formed.
Specifically, bobbin weight is 1.5kg/, winder speed is 900m/min.
Step S18: the spun yarn of multiple bobbins is merged, forms fiber yarn.
Specifically, by two spun yarns feeding two-for-one twisters, ply twist multiplier 450, the twist 4000, double twisting speed 8000r/min,
Obtain fiber yarn.
Embodiment 2:
The manufacturing method for the fiber yarn that the present embodiment discloses and the method difference of embodiment 1 are, are combed in cotton roll
When cotton process, the relative humidity of cotton roll local environment is 50%.
Embodiment 3:
The manufacturing method for the fiber yarn that the present embodiment discloses and the method for embodiment 1 are distinguished and are, antistatic agent and water
Mass ratio be 1: 15.
Comparative example 1:
The manufacturing method for the fiber yarn that this comparative example discloses and the method difference of embodiment 1 are, are preparing cotton roll
In the process, without polyester ether elastic fiber, that is to say, that plant fiber is only utilized in this method, cotton roll has been made, without
Admixtured polyether ester elastomer fiber.
The elongation at break of the fiber yarn manufactured through the foregoing embodiment with comparative example is measured, specific fracture is stretched
Long rate see the table below:
Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | |
Elongation at break | 35.1% | 30.7% | 32.2% | 21.8% |
From above table as can be seen that the fracture of the fiber yarn manufactured by the revealed method of above-described embodiment is stretched
Long rate is apparently higher than the elongation at break of the fiber yarn of the revealed method of comparative example 1 preparation.It can be seen that the present invention manufactures
Fiber yarn out has good elastic property.
Present embodiment further discloses a kind of fiber yarn, which can be manufactured to obtain by above-described embodiment.
Various modifications to these embodiments will be readily apparent to those skilled in the art, herein
Defined General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.
Claims (7)
1. a kind of fiber yarn manufacturing method, comprising steps of
Plant fiber and polyester ether elastic fiber are mixed, cotton roll is made, wherein the polyester ether elastic fiber accounts for the plant
The mass ratio of fiber and polyester ether elastic fiber is 0.1%~10%;
The cotton roll is subjected to carding step, forms sliver;
A plurality of sliver is subjected to mixing in doubling step, forms ripe bar;
The ripe bar is subjected to Roving Frames, forms rove;
The rove is subjected to spinning process, forms spun yarn;
By the spun yarn-winding, bobbin is formed;
The spun yarn of multiple bobbins is merged, forms fiber yarn.
2. fiber yarn manufacturing method according to claim 1, which is characterized in that in the plant fiber and polyether ester bullet
Property fiber mixing before, it is small that the plant fiber and polyester ether elastic fiber are cleaned to 24 in the mixed liquor of antistatic agent and water
When.
3. fiber yarn manufacturing method according to claim 2, which is characterized in that the mass ratio of the antistatic agent and water
It is 1: 5~15.
4. fiber yarn manufacturing method according to claim 2 or 3, which is characterized in that antistatic agent includes hydrogenated castor
10~20 parts of oleic acid, 1~5 part of anionic polyacrylamide, 0.5~2 part of poly glycol monomethyl ether, hydroxypropyl PASELLI EASYGEL
0.5~2 part, 0.1~0.5 part of polyethylene glycol oxide, 0.1~0.5 part of sorbitol anhydride tristearate, 0.05~0.1 part of sesbania gum.
5. fiber yarn manufacturing method according to claim 1, which is characterized in that carry out carding step in the cotton roll
When, the relative humidity of the cotton roll local environment is 50%~70%.
6. fiber yarn manufacturing method according to claim 1, which is characterized in that a plurality of sliver carries out mixing in doubling step
When, the quantity of sliver is 5~7.
7. a kind of fiber yarn, which is characterized in that by fiber yarn manufacturer legal system described in any one of claims 1 to 6
It makes to obtain.