CN110077707A - A kind of aluminium alloy packing box and its production technology - Google Patents
A kind of aluminium alloy packing box and its production technology Download PDFInfo
- Publication number
- CN110077707A CN110077707A CN201910359040.8A CN201910359040A CN110077707A CN 110077707 A CN110077707 A CN 110077707A CN 201910359040 A CN201910359040 A CN 201910359040A CN 110077707 A CN110077707 A CN 110077707A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- plate materials
- alloy plate
- packing box
- aluminium alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is suitable for packing technique field, provides a kind of aluminium alloy packing box and its production technology, which includes: to carry out surface removal of impurities processing to aluminum alloy plate materials;One layer of tempered oil film is coated on the surface of aluminum alloy plate materials after removal of impurities and is dried, and wherein the dosage of tempered oil film is 3g/m2~5g/m2;According to preset printing technology, preset pattern is stamped on the surface of above-mentioned aluminum alloy plate materials, and 10 ~ 15min is toasted under the conditions of 160 ~ 170 DEG C of temperature;The surface that aluminum alloy plate materials after printing are printed on predetermined pattern coats one layer of tempered oil film and dries, and wherein the dosage of tempered oil film is 10g/m2~15g/m2;According to preset bending molding process, bending is carried out to the aluminum alloy plate materials for completing surface treatment and forms packing box.Traditional polishing sandblasting oxidation processes process, the technique for not only simplifying production is omitted in present invention process, and reduces the defect rate of production, and significantly reduces damage of the dust generated in production process to environmental and human health impacts, and production cost is low.
Description
Technical field
The invention belongs to packing technique field more particularly to a kind of aluminium alloy packing box and its production technologies.
Background technique
In the whole market marketing process of commodity, packaging serves as particularly important role, it is with oneself distinctive shape
As language (appearance colour of such as packing box, pattern, shape) is linked up with consumer, and influence the first print of consumer
As just generating interest to the product packaged by it when consumer's First view sees them.It can promote successfully to can result in
Failure, does not show that the packaging of power can allow consumer to sweep and mistake.With the high speed development and people's living standard of modern industry
Continuous improvement, people will be continuously increased the demand of packing box, and quality for packing box and practicability also mention
Higher requirement is gone out.
Traditional paper printing packing box can only generate plane effect from visual sense, and color is stiff, vertical without beautiful and metal is dazzled
Constitution sense, and be easily damaged and deform in use, recycling rate of waterused is low.And metal packaging box is packed compared to papery
Box has cubic metal characters or patterns texture, and has both more preferably hardness and resistance to deformation characteristic, and reusable, so being widely used.
Traditional metal packaging box, for example, the processing technology of aluminium alloy packing box is usually first to make the list of product with aluminium alloy packaging material
Body structure, then the surface of the monomer structure is polished, sandblasting and oxidation processes are to cover monomer structure machine-shaping when institute
The flaws such as the crackle of generation, to improve smoothness and the aesthetics on its surface etc..
But most of polishing, sandblasting and surface oxidation treatment technique in the production technology of traditional aluminium alloy packing box
It is manual operation, operating process is complicated, and can generate a large amount of dust when polishing blasting treatment, not only can be to the body of operator
Body health threatens, but also will cause the pollution of environment.Also, when carrying out sandblasting to it, aluminium alloy packing box is easy
It deforms, thus defect rate is high.The appearance color of aluminium alloy packing box after surface oxidation treatment is single, and color difference is obvious.
As it can be seen that traditional aluminium alloy packing box production technology is there are production technology complexity, defect rate is high, high production cost,
And the dust generated in production process be easy to cause environmental pollution and damage human health.
Summary of the invention
The embodiment of the present invention provides a kind of aluminium alloy packing box production technology, it is intended to it is raw to solve traditional aluminium alloy packing box
Production. art is there are production technology complexity, and defect rate is high, high production cost, and the dust generated in production process be easy to cause environment
The problem of pollution and damage human health.
The embodiments of the present invention are implemented as follows, a kind of aluminium alloy packing box production technology, comprising: to aluminum alloy plate materials into
Row surface removal of impurities processing, the aluminum alloy plate materials after being cleaned;
One layer of tempered oil film is coated on the surface of the aluminum alloy plate materials after the removal of impurities and is dried, and aluminium to be printed is obtained
Sheet alloy, wherein the dosage of the tempered oil film is 3g/m2~5g/m2;
According to preset printing technology, preset pattern is stamped on the surface of the aluminum alloy plate materials to be printed, and
10~15min, the aluminum alloy plate materials after being printed are toasted under the conditions of 160~170 DEG C of temperature;
The surface that aluminum alloy plate materials after the printing are printed on predetermined pattern coats one layer of tempered oil film and dries, and obtains
The aluminum alloy plate materials of surface treatment are completed, wherein the dosage of the tempered oil film is 10g/m2~15g/m2;
According to preset bending molding process, bending is carried out to the aluminum alloy plate materials for completing surface treatment and forms packaging
Box.
The embodiment of the present invention also provides a kind of aluminium alloy packing box, and the aluminium alloy packing box is raw by above-mentioned aluminium alloy packing box
Production. art is made.
Aluminium alloy packing box production technology provided in an embodiment of the present invention is omitted in traditional aluminum alloy surface treatment process
A large amount of manually-operated polishing sandblasting oxidation treatment steps are needed, and traditional surface treatment procedure is changed to aluminum alloy plate materials
Surface clean, printing, coating tempered oil film processing are carried out, the complexity of production technology is reduced, saves a large amount of manpower money
Source and production cost, while the dust of traditional polishing sandblasting oxidation processes generation is avoided caused by environmental and human health impacts
Damage;Furthermore after the process of bending and molding is placed on surface treatment procedure, done at surface again after solving traditional molding
Reason, the problem of because being deformed caused by the factors such as the pressure of surface treatment, hence it is evident that reduce defect rate;And to aluminum alloy plate materials
The color on its surface can be made more bright, diversified after carrying out surface clean, printing, coating tempered oil film processing, surface is consistent
Property it is good, compensate for the single defect of traditional handicraft surface oxidation color, meet the increasingly diversified demand of people, improve aluminium conjunction
The overall market competitiveness of golden packing box.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
The term used in embodiments of the present invention is only to be not intended to be limiting merely for for the purpose of describing particular embodiments
The present invention.Packet is also intended in the "an" and "the" of the embodiment of the present invention and singular used in the attached claims
Most forms are included, unless the context clearly indicates other meaning.It is also understood that term "and/or" used herein is
Refer to and includes that one or more associated any or all of project listed may combine.
Aluminium alloy packing box production technology provided in an embodiment of the present invention is removed using first surface is carried out to aluminum alloy plate materials
Miscellaneous, printing treatment, then bending and molding, and traditional polishing sandblasting oxidized surface process flow is omitted, not only reduce life
At the complexity and defect rate of technique, while the dust that can avoid generating by polishing sandblasting oxidized surface processing is to environment and human body
The damage of health, and the surface conformance of the aluminum alloy plate materials after surface removal of impurities, printing treatment is more preferable, and color is more various
Change, meets people to the increasingly diversified demand of packaging material, and production cost is low.
The embodiment of the invention provides a kind of aluminium alloy packing box production technologies, comprising:
Removal of impurities processing in surface is carried out to aluminum alloy plate materials, the aluminum alloy plate materials after being cleaned;
One layer of tempered oil film is coated on the surface of the aluminum alloy plate materials after the removal of impurities and is dried, and aluminium to be printed is obtained
Sheet alloy, wherein the dosage of the tempered oil film is 3g/m2~5g/m2;
According to preset printing technology, preset pattern is stamped on the surface of the aluminum alloy plate materials to be printed, and
10~15min, the aluminum alloy plate materials after being printed are toasted under the conditions of 160~170 DEG C of temperature;
The surface that aluminum alloy plate materials after the printing are printed on predetermined pattern coats one layer of tempered oil film and dries, and obtains
The aluminum alloy plate materials of surface treatment are completed, wherein the dosage of the tempered oil film is 10g/m2~15g/m2;
According to preset bending molding process, bending is carried out to the aluminum alloy plate materials for completing surface treatment and forms packaging
Box.
Painting is covered with one layer of tempered oil film after carrying out removal of impurities processing to aluminum alloy sheet material surface, it is ensured that aluminium alloy is subsequent to be added
Work performance prevents the surface of aluminum alloy plate materials to be scraped off, while the physics that can increase printing ink and aluminum alloy sheet material surface is inhaled
Attached power.
It is coated with upper one layer of tempered oil film after printing ink, can protect the aluminum alloy sheet material surface after being completed for printing
Ink subsequent bending and molding processing in be not in explosion the phenomenon that, thus keep printing pattern clarity and beauty
The property seen, and may make plentiful brightness, stain resistance and the hardness on the surface of aluminum alloy plate materials more preferable.
Preferably, described that removal of impurities processing in surface carried out to aluminum alloy plate materials, the step of aluminum alloy plate materials after being cleaned,
It specifically includes:
The aluminum alloy plate materials are placed in 5~10min of soak at room temperature in cleaning agent, rear take out washes with water completely, to remove
Remove the grease stain and other impurities of the aluminum alloy sheet material surface.Preferably, it can gently be wiped with soft hairbrush or sponge
Aluminum alloy sheet material surface, to improve its clean effect.
Preferably, the cleaning agent is the mixed solution of methyl ethyl ketone and thinner, their mixed volume ratio be 1:2~
2.5。
More preferably, the cleaning agent is the mixed solution of methyl ethyl ketone and thinner, their mixed volume ratio is 1:
2。
Preferably, the tempered oil film is polyester resin.More preferably, polyester resin is unsaturated polyester resin,
Viscosity is small, easy wetting, good manufacturability, the glue-line hardness after solidification is big, the transparency is good, brightness is high, can room temperature pressurization quickly consolidate
Change, heat resistance are preferable, excellent electrical properties.
Preferably, described according to preset printing technology, it is stamped on the surface of the aluminum alloy plate materials to be printed pre-
If pattern, and 10~15min is toasted under the conditions of 160~170 DEG C of temperature, the step of aluminum alloy plate materials after being printed,
It specifically includes:
According to preset printing technology, preset pattern is stamped on the surface of the aluminum alloy plate materials to be printed, and
12min is toasted under the conditions of 165 DEG C of temperature, the aluminum alloy plate materials after being printed.
Wherein, preset printing technology is the printing technology of this field routine, and details are not described herein.
Preferably, described according to preset printing technology, it is stamped on the surface of the aluminum alloy plate materials to be printed pre-
If pattern, and 10~15min is toasted under the conditions of 160~170 DEG C of temperature, the step of aluminum alloy plate materials after being printed,
It specifically includes:
According to preset printing technology, preset pattern is stamped on the surface of the aluminum alloy plate materials to be printed, and
10~15min, the aluminum alloy plate materials after being printed are toasted under the conditions of 60~70%, 160~170 DEG C of temperature of relative humidity.
Preset pattern can be character image, pictorial trademark, landscape painting etc., can specifically determine, not limit according to actual needs herein
It is fixed.
Preferably, according to preset bending molding process, bending is carried out to the aluminum alloy plate materials for completing surface treatment
The step of forming packing box, comprising:
According to laser boring method, the position of positioning hole of the aluminum alloy plate materials for completing surface treatment is captured automatically and is beaten
Hole;
On the basis of the location hole, blanking goes out the form factor after single aluminium alloy packing box expansion;
Bending is carried out according to the default bending position of the form factor after the single aluminium alloy packing box expansion, forms aluminium
Alloy packing box.
Preferably, the default bending position of the form factor after the expansion according to the aluminium alloy packing box is rolled over
It is curved, formed aluminium alloy packing box the step of, comprising:
There is R3.0 smooth fillet using corner molding position, forming gap is the thickness no more than the aluminum alloy plate materials
The Bending Mould of 0.05mm rolls over the default bending position of the form factor after the single aluminium alloy packing box expansion
It is curved, form aluminium alloy packing box.
The embodiment of the invention also provides a kind of aluminium alloy packing boxes, and the aluminium alloy packing box is by above-mentioned aluminium alloy packing box
Production technology is made.
Technical solution of the present invention and technical effect are described further below by way of specific embodiment.
Embodiment 1:
Removal of impurities processing in surface is carried out to aluminum alloy plate materials, the aluminium alloy plate of certain specification size is specifically taken by process requirements
Material, and the aluminum alloy plate materials are placed in the mixed solution of methyl ethyl ketone and thinner to (methyl ethyl ketone: the mixed volume ratio of thinner is
1:2), after soak at room temperature 5min, taking-up is rinsed well and is dried with clear water, the aluminum alloy plate materials after being cleaned;
One layer of polyester resin tempered oil film is coated on the surface of aluminum alloy plate materials after removal of impurities and is dried, and is obtained to be printed
Aluminum alloy plate materials, wherein the dosage of the tempered oil film be 3g/m2;
According to preset printing technology, preset pattern is stamped on the surface of aluminum alloy plate materials to be printed, and in 160
10min is toasted under the conditions of DEG C temperature, the aluminum alloy plate materials after being printed;
The surface that aluminum alloy plate materials after printing are printed on predetermined pattern coats one layer of polyester resin tempered oil film and dries,
Obtain completing the aluminum alloy plate materials of surface treatment, wherein the dosage of tempered oil film is 10g/m2;
It is automatic to capture the position of positioning hole for completing the aluminum alloy plate materials of surface treatment and punching according to laser boring method;
On the basis of location hole, blanking goes out the form factor after single aluminium alloy packing box expansion;
Bending is carried out according to the default bending position of the form factor after the expansion of single aluminium alloy packing box, forms aluminium alloy
Packing box.
Embodiment 2:
Removal of impurities processing in surface is carried out to aluminum alloy plate materials, the aluminium alloy plate of certain specification size is specifically taken by process requirements
Material, and the aluminum alloy plate materials are placed in the mixed solution of methyl ethyl ketone and thinner to (methyl ethyl ketone: the mixed volume ratio of thinner is
1:2.5), after soak at room temperature 10min, taking-up is rinsed well and is dried with clear water, the aluminum alloy plate materials after being cleaned;
One layer of polyester resin tempered oil film is coated on the surface of aluminum alloy plate materials after removal of impurities and is dried, and is obtained to be printed
Aluminum alloy plate materials, wherein the dosage of the tempered oil film be 5g/m2;
According to preset printing technology, preset pattern is stamped on the surface of aluminum alloy plate materials to be printed, and in phase
It is 70% to humidity, toasts 15min under the conditions of 170 DEG C of temperature, the aluminum alloy plate materials after being printed;
The surface that aluminum alloy plate materials after printing are printed on predetermined pattern coats one layer of polyester resin tempered oil film and dries,
Obtain completing the aluminum alloy plate materials of surface treatment, wherein the dosage of tempered oil film is 15g/m2;
It is automatic to capture the position of positioning hole for completing the aluminum alloy plate materials of surface treatment and punching according to laser boring method;
On the basis of location hole, blanking goes out the form factor after single aluminium alloy packing box expansion;
Bending is carried out according to the default bending position of the form factor after the expansion of single aluminium alloy packing box, forms aluminium alloy
Packing box.
Embodiment 3:
Removal of impurities processing in surface is carried out to aluminum alloy plate materials, the aluminium alloy plate of certain specification size is specifically taken by process requirements
Material, and the aluminum alloy plate materials are placed in the mixed solution of methyl ethyl ketone and thinner to (methyl ethyl ketone: the mixed volume ratio of thinner is
1:2), after soak at room temperature 8min, taking-up is rinsed well and is dried with clear water, the aluminum alloy plate materials after being cleaned;
One layer of polyester resin tempered oil film is coated on the surface of aluminum alloy plate materials after removal of impurities and is dried, and is obtained to be printed
Aluminum alloy plate materials, wherein the dosage of the tempered oil film be 4g/m2;
According to preset printing technology, preset pattern is stamped on the surface of aluminum alloy plate materials to be printed, and in phase
It is 65% to humidity, toasts 12min under the conditions of 165 DEG C of temperature, the aluminum alloy plate materials after being printed;
The surface that aluminum alloy plate materials after printing are printed on predetermined pattern coats one layer of polyester resin tempered oil film and dries,
Obtain completing the aluminum alloy plate materials of surface treatment, wherein the dosage of tempered oil film is 12g/m2;
It is automatic to capture the position of positioning hole for completing the aluminum alloy plate materials of surface treatment and punching according to laser boring method;
On the basis of location hole, blanking goes out the form factor after single aluminium alloy packing box expansion;
Bending is carried out according to the default bending position of the form factor after the expansion of single aluminium alloy packing box, forms aluminium alloy
Packing box.
Embodiment 4:
Removal of impurities processing in surface is carried out to aluminum alloy plate materials, the aluminium alloy plate of certain specification size is specifically taken by process requirements
Material, and the aluminum alloy plate materials are placed in the mixed solution of methyl ethyl ketone and thinner to (methyl ethyl ketone: the mixed volume ratio of thinner is
1:2), after soak at room temperature 5min, taking-up is rinsed well and is dried with clear water, the aluminum alloy plate materials after being cleaned;
One layer of polyester resin tempered oil film is coated on the surface of aluminum alloy plate materials after removal of impurities and is dried, and is obtained to be printed
Aluminum alloy plate materials, wherein the dosage of the tempered oil film be 5g/m2;
According to preset printing technology, preset pattern is stamped on the surface of aluminum alloy plate materials to be printed, and in phase
It is 60% to humidity, toasts 10min under the conditions of 160 DEG C of temperature, the aluminum alloy plate materials after being printed;
The surface that aluminum alloy plate materials after printing are printed on predetermined pattern coats one layer of polyester resin tempered oil film and dries,
Obtain completing the aluminum alloy plate materials of surface treatment, wherein the dosage of tempered oil film is 15g/m2;
It is automatic to capture the position of positioning hole for completing the aluminum alloy plate materials of surface treatment and punching according to laser boring method;
On the basis of location hole, blanking goes out the form factor after single aluminium alloy packing box expansion;
Bending is carried out according to the default bending position of the form factor after the expansion of single aluminium alloy packing box, forms aluminium alloy
Packing box.
After the molding of above-mentioned aluminium alloy packing box, whether the appearance for observing each packing box has crackle, and whether pattern is clear
It is distinguishable.Test result shows aluminium alloy made from the aluminium alloy packing box production technology provided using the embodiment of the present invention 1~4
The equal surfacing of packing box, appearance are visible by naked eyes crackle, and pattern does not burst, and do not drag that flower, bedraggle phenomenon, and full, color
It is color distinct.
Using single factor experiment method to the guarantor coated on the aluminum alloy sheet material surface after the removal of impurities in the embodiment of the present invention 1
The dosage for protecting oil film carries out preferably.It fixes that other process conditions are constant, changes and coated on the aluminum alloy sheet material surface after removal of impurities
Tempered oil film dosage be 1g/m2、2g/m2、3g/m2、4g/m2、5g/m2、6g/m2.Ink printing is carried out after to be dried, according to
GB/T9286-1998 " cross cut test of paint and varnish paint film " measures adhesive force, and test result is divided into 0 grade to 5 grades, wherein
0 grade illustrates that adhesive force is best, and 5 grades are worst.As a result, it has been found that tempered oil film dosage is 1g/m2、2g/m2When, ink and aluminium alloy
The adsorption effect of plate surface is 3g/m less than dosage2、4g/m2、5g/m2And 6g/m2.But dosage is 6g/m2When, after molding
The printing layer of aluminium alloy packing box there is subtle embrittlement line.Therefore, the usage amount of tempered oil film is 3g/m after removal of impurities2~
5g/m2When, can not only aluminum alloy sheet material surface be protected to be scraped off, but also the attachment of printing ink and aluminum alloy sheet material surface can be increased
Power.Test result is detailed in shown in the following table 1.
Table 1
Using single factor experiment method to being stamped on the surface of aluminum alloy plate materials to be printed in the embodiment of the present invention 1
The baking time of predetermined pattern carries out preferred.It fixes that other process conditions are constant, changes in aluminum alloy sheet material surface to be printed
Baking time after upper printing predetermined pattern is 5min, 10min, 15min and 20min.Each aluminum alloy plate materials table is observed after baking
The adhesion condition of the ink in face and the solidification situation of ink.Test result surface, when baked between be 5min when, aluminum alloy plate materials
The ink on surface is in semi-cured state, and part ink has mobility, is easy to appear when carrying out subsequent processing operations and drags flower, drags
Dirty phenomenon reduces the quality of the pattern of printing, and when baked between more than 15min when, ink is fully cured, but occur it is subtle
Cracking phenomena, and ink starts to become fragile.Therefore, it is complete to be not only conducive to ink between 10min~15min for baking time
Solidification, and ink embrittlement phenomena will not be generated, it is ensured that the quality of subsequent printed patterns.
Using single factor experiment method to the guarantor coated on the aluminum alloy sheet material surface after the printing in the embodiment of the present invention 1
The dosage for protecting oil film carries out preferably.It fixes that other process conditions are constant, changes and coated on the aluminum alloy sheet material surface after removal of impurities
Tempered oil film dosage be 5g/m2、10g/m2、15g/m2、20g/m2.After the molding of aluminium alloy packing box, each packet is visually observed
The apparent condition of mounted box.Test result is detailed in the following table 2.The test result shows that aluminum alloy sheet material surface after printing coats
The dosage of tempered oil film is less than 10g/m2When, be printed on ink on aluminum alloy sheet material surface due to pressure of following process etc. because
Element and be easy to appear Decrepitation Phenomena, the effect of protection is unobvious, and comprehensively consider the factor of cost, therefore it is preferred that tempered oil film
Dosage is 10~15g/m2。
Table 2
Aluminium alloy packing box production technology provided in an embodiment of the present invention is omitted in traditional aluminum alloy surface treatment process
A large amount of manually-operated polishing sandblasting oxidation treatment steps are needed, and traditional surface treatment procedure is changed to aluminum alloy plate materials
Surface clean, printing, coating tempered oil film processing are carried out, reduces the complexity of production technology, saving a large amount of manpower needs
It asks, production efficiency is made to improve 10 times or more, production cost is greatly saved, while avoiding traditional polishing sandblasting oxidation
The dust that processing generates is damaged caused by environmental and human health impacts;Furthermore the process of bending and molding is placed on surface treatment work
It after sequence, is surface-treated again after solving traditional molding, because what is deformed caused by the factors such as the pressure of surface treatment asks
Topic, so that defect rate has decreased to 5%~10% by the 20%~25% of traditional handicraft;And surface is carried out to aluminum alloy plate materials
The color on its surface can be made more to become clear after cleaning, printing, coating tempered oil film processing, diversification, surface conformance is good, makes up
Traditional handicraft surface oxidation color single defect, and when visual angle is in 30~35 degree light reflectors, aluminium conjunction
Golden packing box surface can reflect reflective general color and discoloration effect, meet the increasingly diversified demand of people, improve aluminium conjunction
The overall market competitiveness of golden packing box.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (10)
1. a kind of aluminium alloy packing box production technology characterized by comprising
Removal of impurities processing in surface is carried out to aluminum alloy plate materials, the aluminum alloy plate materials after being cleaned;
One layer of tempered oil film is coated on the surface of the aluminum alloy plate materials after the removal of impurities and is dried, and aluminium alloy to be printed is obtained
Plate, wherein the dosage of the tempered oil film is 3g/m2~5g/m2;
According to preset printing technology, preset pattern is stamped on the surface of the aluminum alloy plate materials to be printed, and in 160
10 ~ 15min, the aluminum alloy plate materials after being printed are toasted under the conditions of ~ 170 DEG C of temperature;
The surface that aluminum alloy plate materials after the printing are printed on predetermined pattern coats one layer of tempered oil film and dries, and is completed
The aluminum alloy plate materials of surface treatment, wherein the dosage of the tempered oil film is 10g/m2~15g/m2;
According to preset bending molding process, bending is carried out to the aluminum alloy plate materials for completing surface treatment and forms packing box.
2. aluminium alloy packing box production technology as described in claim 1, which is characterized in that described to carry out table to aluminum alloy plate materials
It the step of face removal of impurities processing, aluminum alloy plate materials after being cleaned, specifically includes:
The aluminum alloy plate materials are placed in 5 ~ 10min of soak at room temperature in cleaning agent, rear take out washes with water completely, described in removing
The grease stain and other impurities of aluminum alloy sheet material surface.
3. aluminium alloy packing box production technology as claimed in claim 2, which is characterized in that the cleaning agent is methyl ethyl ketone and day
By the mixed solution of water, their mixed volume ratio is 1:2 ~ 2.5.
4. aluminium alloy packing box production technology as claimed in claim 3, which is characterized in that the cleaning agent is methyl ethyl ketone and day
By the mixed solution of water, their mixed volume ratio is 1:2.
5. aluminium alloy packing box production technology as described in claim 1, which is characterized in that the tempered oil film is polyester tree
Rouge.
6. aluminium alloy packing box production technology as described in claim 1, which is characterized in that described according to preset printer
Skill stamps preset pattern on the surface of the aluminum alloy plate materials to be printed, and toasts under the conditions of 160 ~ 170 DEG C of temperature
It the step of 10 ~ 15min, aluminum alloy plate materials after being printed, specifically includes:
According to preset printing technology, preset pattern is stamped on the surface of the aluminum alloy plate materials to be printed, and in 165
12min is toasted under the conditions of DEG C temperature, the aluminum alloy plate materials after being printed.
7. aluminium alloy packing box production technology as described in claim 1, which is characterized in that described according to preset printer
Skill stamps preset pattern on the surface of the aluminum alloy plate materials to be printed, and toasts under the conditions of 160 ~ 170 DEG C of temperature
It the step of 10 ~ 15min, aluminum alloy plate materials after being printed, specifically includes:
According to preset printing technology, preset pattern is stamped on the surface of the aluminum alloy plate materials to be printed, and in phase
Aluminum alloy plate materials to 10 ~ 15min of baking under the conditions of 60 ~ 70%, 160 ~ 170 DEG C of temperature of humidity, after being printed.
8. aluminium alloy packing box production technology as described in claim 1, which is characterized in that according to preset bending and molding work
Skill carries out the step of bending forms packing box to the aluminum alloy plate materials for completing surface treatment, comprising:
According to laser boring method, the position of positioning hole of the aluminum alloy plate materials for completing surface treatment and punching are captured automatically;
On the basis of the location hole, blanking goes out the form factor after single aluminium alloy packing box expansion;
Bending is carried out according to the default bending position of the form factor after the single aluminium alloy packing box expansion, forms aluminium alloy
Packing box.
9. aluminium alloy packing box production technology as claimed in claim 8, which is characterized in that described to be packed according to the aluminium alloy
The step of default bending position of form factor after box expansion carries out bending, forms aluminium alloy packing box, comprising:
There is R3.0 smooth fillet using corner molding position, forming gap is the thickness 0.05mm no more than the aluminum alloy plate materials
Bending Mould, bending is carried out to the default bending position of the form factor after the single aluminium alloy packing box expansion, is formed
Aluminium alloy packing box.
10. a kind of aluminium alloy packing box, which is characterized in that the aluminium alloy packing box is by such as claim 1 ~ 9 any one institute
The aluminium alloy packing box production technology stated is made.