CN110077050A - The preparation method of graphene glue, graphene fabric and graphene fabric - Google Patents
The preparation method of graphene glue, graphene fabric and graphene fabric Download PDFInfo
- Publication number
- CN110077050A CN110077050A CN201910462552.7A CN201910462552A CN110077050A CN 110077050 A CN110077050 A CN 110077050A CN 201910462552 A CN201910462552 A CN 201910462552A CN 110077050 A CN110077050 A CN 110077050A
- Authority
- CN
- China
- Prior art keywords
- graphene
- fabric
- glue
- precoat
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention discloses a kind of graphene fabrics, including graphene film layer and precoat, the graphene film layer is complex as a whole with the fabric layer stackup, graphene yarn is equipped in the precoat, or including graphene printed layer and precoat, the graphene printed layer is printed in the fabric layer surface.Present invention further teaches a kind of preparation method of graphene fabric and a kind of graphene glue.Graphene fabric of the invention has low-resistivity, the strong advantage of antistatic, antibacterial, thermal insulation property.
Description
Technical field
The present invention relates to functional fabric manufacturing technology fields, and in particular to a kind of graphene glue, graphene fabric and stone
The preparation method of black alkene fabric.
Background technique
With the improvement of living standards, people are increasingly diversified to the functional requirement of fabric, common functional fabric has height
Molecular film material and the compound obtained overlay film fabric of traditional fabric, have wind-proof performance.But do not occur also having at present low
The graphene fabric of resistivity, antistatic, antibacterial, thermal insulation property.
Summary of the invention
The purpose of the present invention is to provide the preparation methods of a kind of graphene glue, graphene fabric and graphene fabric.
One of for achieving the above object, the present invention adopts the following technical scheme:
A kind of graphene glue, the graphene glue are made of the component of following mass ratio:
Polyurethane resin 51%, solvent 30%, graphene powder 14%, flatting silica 3%, levelling agent 2%；
Either polyurethane resin 56%, solvent 36%, graphene powder 3%, flatting silica 3%, levelling agent 2%；
The solvent is butanone 10%, toluene 10%, dimethylformamide 10% or butanone 12%, toluene 12%, diformazan
Base formamide 12%.
For achieving the above object two, the present invention adopts the following technical scheme:
A kind of graphene fabric, including graphene film layer and precoat, the graphene film layer and the precoat
Stacking is complex as a whole, and graphene yarn is equipped in the precoat.
Technical solution as a further improvement of that present invention, the graphene film layer and precoat bonding are complex as
One.
For achieving the above object three, the present invention adopts the following technical scheme:
A kind of graphene fabric, including graphene printed layer and precoat, the graphene printed layer are printed on the face
On bed of material surface.
Technical solution as a further improvement of that present invention, the precoat are made by polyester and/or nylon fiber
Fabric.
For achieving the above object four, the present invention adopts the following technical scheme:
A kind of preparation method of graphene fabric, raw material is uniformly mixed and is prepared into graphene glue, the graphite
Alkene glue is made of the component of following mass ratio:
Polyurethane resin 51%, solvent 30%, graphene powder 14%, flatting silica 3%, levelling agent 2%；
The solvent is butanone 10%, toluene 10%, dimethylformamide 10%；
Graphene glue is applied on the coating machine for being loaded with release paper；
Release paper is separated by central coiling machine after drying by baking oven, then once thin up to graphene through rewinding machine rewinding
Film layer；
Graphene yarn is entered in precoat；
It will be compound up to graphene fabric with precoat lamination adhesive after the gluing of graphene film layer.
For achieving the above object five, the present invention adopts the following technical scheme:
A kind of preparation method of graphene fabric, raw material is uniformly mixed and is prepared into graphene glue, the graphite
Alkene glue is made of the component of following mass ratio:
Polyurethane resin 56%, solvent 36%, graphene powder 3%, flatting silica 3%, levelling agent 2%；
The solvent is butanone 12%, toluene 12%, dimethylformamide 12%；
Graphene glue is applied on the stamp wheel of printing machine；
Graphene glue is transferred in formation graphene printed layer on precoat by stamp wheel, drying winds up to graphite
Alkene fabric.
Compared with the existing technology, the technical effects of the invention are that:
Graphene fabric of the invention has low-resistivity, the strong advantage of antistatic, antibacterial, thermal insulation property.
Detailed description of the invention
Fig. 1 is a kind of schematic perspective view of graphene fabric in embodiment of the present invention.
Specific embodiment
Below with reference to specific embodiment shown in the drawings, the present invention will be described in detail.But these embodiments are simultaneously
The present invention is not limited, structure that those skilled in the art are made according to these embodiments, method or functionally
Transformation is included within the scope of protection of the present invention.
A kind of graphene glue, the graphene glue are made of the component of following mass ratio:
Polyurethane resin 51%, solvent 30%, graphene powder 14%, flatting silica 3%, levelling agent 2%；
Either polyurethane resin 56%, solvent 36%, graphene powder 3%, flatting silica 3%, levelling agent 2%；
The solvent is butanone 10%, toluene 10%, dimethylformamide 10% or butanone 12%, toluene 12%, diformazan
Base formamide 12%.
It is good to have the advantages that filming performance using above quality graphene glue more prepared than the raw material of component, and has
The characteristic of graphene.
Referring to Figure 1, a kind of graphene fabric, including graphene film layer 1 and precoat 2, the graphene film layer 1
It is complex as a whole with the precoat 2 stacking, graphene yarn is equipped in the precoat 2.
Technical solution as a further improvement of that present invention, the graphene film layer 1 and the precoat 3 are bonded compound
It is integrated.
A kind of graphene fabric, including graphene printed layer and precoat, the graphene printed layer are printed on the face
On bed of material surface (surface refers to the biggish surface of precoat area).
Technical solution as a further improvement of that present invention, the precoat are made by polyester and/or nylon fiber
Fabric.
For example, the fabrics such as spandex fabric, mechanical elastic, spring Asia spinning, Nylon Taffeta, Oxford cloth.
It is of course also possible to use other common fabrics of weaving are as precoat.
A kind of preparation method of graphene fabric, raw material is uniformly mixed and is prepared into graphene glue, the graphite
Alkene glue is made of the component of following mass ratio:
Polyurethane resin 51%, solvent 30%, graphene powder 14%, flatting silica 3%, levelling agent 2%；
The solvent is butanone 10%, toluene 10%, dimethylformamide 10%；
Graphene glue is applied on the coating machine for being loaded with release paper；
Release paper is separated by central coiling machine after drying by baking oven, then once thin up to graphene through rewinding machine rewinding
Film layer；
Graphene yarn is entered in precoat；
It will be compound up to graphene fabric with precoat lamination adhesive after the gluing of graphene film layer.
A kind of preparation method of graphene fabric, raw material is uniformly mixed and is prepared into graphene glue, the graphite
Alkene glue is made of the component of following mass ratio:
Polyurethane resin 56%, solvent 36%, graphene powder 3%, flatting silica 3%, levelling agent 2%；
The solvent is butanone 12%, toluene 12%, dimethylformamide 12%；
Graphene glue is applied on the stamp wheel of printing machine；
Graphene glue is transferred in formation graphene printed layer on precoat by stamp wheel, drying winds up to graphite
Alkene fabric.
Compared with the existing technology, the technical effects of the invention are that:
Graphene fabric of the invention has low-resistivity, the strong advantage of antistatic, antibacterial, thermal insulation property.
Finally, it should be noted that embodiment of above is merely illustrative of the technical solution of the present invention, rather than its limitations；To the greatest extent
Invention is explained in detail referring to aforementioned embodiments for pipe, those skilled in the art should understand that: its according to
It can so modify to technical solution documented by aforementioned each embodiment, or part of technical characteristic is equal
Replacement；And these are modified or replaceed, each embodiment technical solution of the present invention that it does not separate the essence of the corresponding technical solution
Spirit and scope.
Claims (7)
1. a kind of graphene glue, which is characterized in that the graphene glue is made of the component of following mass ratio:
Polyurethane resin 51%, solvent 30%, graphene powder 14%, flatting silica 3%, levelling agent 2%；
Either polyurethane resin 56%, solvent 36%, graphene powder 3%, flatting silica 3%, levelling agent 2%；
The solvent is butanone 10%, toluene 10%, dimethylformamide 10% or butanone 12%, toluene 12%, dimethyl methyl
Amide 12%.
2. a kind of graphene fabric, which is characterized in that including graphene film layer and precoat, the graphene film layer and institute
It states fabric layer stackup to be complex as a whole, graphene yarn is equipped in the precoat.
3. a kind of graphene fabric according to claim 2, which is characterized in that the graphene film layer and the fabric
Layer bonding is complex as a whole.
4. a kind of graphene fabric, which is characterized in that including graphene printed layer and precoat, the graphene printed layer printing
In the fabric layer surface.
5. a kind of graphene fabric according to Claims 2 or 3 or 4, which is characterized in that the precoat be polyester and/
Or fabric made by nylon fiber.
6. a kind of preparation method of graphene fabric, which is characterized in that raw material is uniformly mixed and is prepared into graphene glue,
The graphene glue is made of the component of following mass ratio:
Polyurethane resin 51%, solvent 30%, graphene powder 14%, flatting silica 3%, levelling agent 2%；
The solvent is butanone 10%, toluene 10%, dimethylformamide 10%；
Graphene glue is applied on the coating machine for being loaded with release paper；
Release paper is separated by central coiling machine after drying by baking oven, then through rewinding machine rewinding once up to graphene film
Layer；
Graphene yarn is entered in precoat；
It will be compound up to graphene fabric with precoat lamination adhesive after the gluing of graphene film layer.
7. a kind of preparation method of graphene fabric, which is characterized in that raw material is uniformly mixed and is prepared into graphene glue,
The graphene glue is made of the component of following mass ratio:
Polyurethane resin 56%, solvent 36%, graphene powder 3%, flatting silica 3%, levelling agent 2%；
The solvent is butanone 12%, toluene 12%, dimethylformamide 12%；
Graphene glue is applied on the stamp wheel of printing machine；
Graphene glue is transferred in formation graphene printed layer on precoat by stamp wheel, drying winds up to graphene face
Material.