CN110055657A - A kind of Quality Pure Cotton Yarn Production and preparation method thereof with mould proof antistatic effect - Google Patents
A kind of Quality Pure Cotton Yarn Production and preparation method thereof with mould proof antistatic effect Download PDFInfo
- Publication number
- CN110055657A CN110055657A CN201910401735.8A CN201910401735A CN110055657A CN 110055657 A CN110055657 A CN 110055657A CN 201910401735 A CN201910401735 A CN 201910401735A CN 110055657 A CN110055657 A CN 110055657A
- Authority
- CN
- China
- Prior art keywords
- parts
- cotton yarn
- mould proof
- antistatic effect
- proof antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of Quality Pure Cotton Yarn Production and preparation method thereof with mould proof antistatic effect, raw material is made of the raw material of following parts by weight: 2.5~11.5 parts of pure-acrylic emulsion, 7~11 parts of gum arabic, 25.5~28.5 parts of waste and old cotton goods, 3.5~4.8 parts of aqueous polyurethane, 11.4~12.4 parts of cotton yarn leftover pieces, 2.2~3.6 parts of gellan gum, 2-7 parts of nano zine oxide, 5.5~12.5 parts of atoleine, 2~6 parts of water, the present invention provides a kind of Quality Pure Cotton Yarn Production and preparation method thereof with mould proof antistatic effect, compensate for the disadvantage of cotton fiber Yu the sun protection difference of polypropylene fibre, mechanical property greatly promotes, antibacterial effect is enhanced simultaneously, elasticity is good, it is wear-resisting, it is corrosion-resistant, warmth retention property is good, period of storage is long, technique is convenient for Industry Control, improve product quality , saved cost.
Description
Technical field
The present invention is a kind of Quality Pure Cotton Yarn Production and preparation method thereof with mould proof antistatic effect, is related to textile technology field.
Background technique
Polypropylene fibre is synthetic fibers made of the isotactic polypropylene obtained using propylene polymerization is spinned as raw material, polypropylene
Fiber is light, intensity is high, elasticity is good, it is wear-resisting, corrosion-resistant, have electrical insulating property and warmth retention property, regain is low, while price is low
Honest and clean, chemically-resistant property is good, has extensive use in drapery field.
But since the heat-resisting of polypropylene fibre, resistance to ag(e)ing are poor, it is limited in the application of garment industry.
Currently, as population in the world increases severely, countries in the world all will control arable land utilization, cotton, fiber crops, sericulture mulberry tree
Plantation is all limited, and traditional cotton textile raw material is by multiple restriction.
Summary of the invention
The technical problem to be solved by the present invention is in view of the deficiencies of the prior art, the present invention provides a kind of with mould proof anti-
Quality Pure Cotton Yarn Production of electrostatic efficiency and preparation method thereof, makes up the disadvantage of cotton fiber Yu the sun protection difference of polypropylene fibre, and mechanical property is big
It is big to be promoted, while enhancing antibacterial effect, elasticity is good, wear-resisting, corrosion-resistant, warmth retention property is good, and period of storage is long, and technique is convenient for industry control
System improves product quality, save the cost.
A kind of Quality Pure Cotton Yarn Production with mould proof antistatic effect, the raw material are made of the raw material of following parts by weight: pure
2.5~11.5 parts of acrylic emulsion, 7~11 parts of gum arabic, 25.5~28.5 parts of waste and old cotton goods, bamboo charcoal fiber 1.5~3.5
Part, 10.5~12.5 parts of graphene oxide, 1~4 part of epsilon-polylysine, 3~8 parts of nano-titanium dioxide, 5~13 parts of silica solution,
3.5~4.8 parts of aqueous polyurethane, 11.4~12.4 parts of cotton yarn leftover pieces, 2.2~3.6 parts of gellan gum, hydroxypropul starch 10~
12 parts, 4.1~5.4 parts of hydroxy-silicone-oil emulsion, 12.1~16.8 parts of polypropylene, 3~8 parts of carboxymethyl cellulose, glycerol stearate
12.5~16.5 parts of ester, 13.4~14.8 parts of Kathon CG, 2-7 parts of nano zine oxide, 5.5~12.5 parts of atoleine, 2~6 parts of water.
A kind of preparation method of the Quality Pure Cotton Yarn Production with mould proof antistatic effect, the specific steps are as follows:
(1) raw material will be prepared to be put into stirred tank by the components by weight percent, suitable water is added, has been heated to while stirring
Full gelatinization, is mixed evenly to form spare slurry;
(2) it is smashed, the composite fibre smashed is immersed into processing slurry and made using machine after mixing cotton yarn leftover pieces
Drying and processing is carried out with drying, then the fiber after drying is mixed with bamboo charcoal fiber, it is mixed that regeneration is made by cotton carding, combing
Condensating fiber sliver, it is spare;
(3) regenerative mixed fiber sliver, coarse sand, spinning process are handled up to a kind of with the pure of mould proof antistatic effect
Cotton yarn.
It is 180-220 revs/min that speed, which is mixed, in the step (1), and mixing time is 45-55 minutes.
Rear fibre length control is smashed at 3.5-5.5 millimeters using machine after step (2) the cotton yarn leftover pieces mixing.
And the composite fibre immersion processing slurry time is 65-85 minutes, removal sample carries out drying and processing at a temperature of 110-120 DEG C.
The utility model has the advantages that the present invention compensates for the disadvantage of cotton fiber Yu the sun protection difference of polypropylene fibre, mechanical property mentions significantly
It rises, while enhancing antibacterial effect, elasticity is good, wear-resisting, corrosion-resistant, warmth retention property is good, and period of storage is long, and technique is convenient for industry control
System, improves product quality, has saved cost.
Specific embodiment
The present invention is described in further details below by embodiment.
Embodiment 1
A kind of Quality Pure Cotton Yarn Production with mould proof antistatic effect, the raw material are made of the raw material of following parts by weight: pure
2.5 parts of acrylic emulsion, 7 parts of gum arabic, 25.5 parts of waste and old cotton goods, 1.5 parts of bamboo charcoal fiber, 10.5 parts of graphene oxide, ε-
1 part of polylysine, 3 parts of nano-titanium dioxide, 5 parts of silica solution, 3.5 parts of aqueous polyurethane, 11.4 parts of cotton yarn leftover pieces, ancient blue sugar
2.2 parts of glue, 10 parts of hydroxypropul starch, 4.1 parts of hydroxy-silicone-oil emulsion, 12.1 parts of polypropylene, 3 parts of carboxymethyl cellulose, glycerol are hard
12.5 parts of resin acid ester, 13.4 parts of Kathon CG, 2 parts of nano zine oxide, atoleine 5.5,2 parts of water.
A kind of preparation method of the Quality Pure Cotton Yarn Production with mould proof antistatic effect, the specific steps are as follows:
(1) raw material will be prepared to be put into stirred tank by the components by weight percent, suitable water is added, has been heated to while stirring
Full gelatinization, is mixed evenly to form spare slurry;
(2) it is smashed, the composite fibre smashed is immersed into processing slurry and made using machine after mixing cotton yarn leftover pieces
Drying and processing is carried out with drying, then the fiber after drying is mixed with bamboo charcoal fiber, it is mixed that regeneration is made by cotton carding, combing
Condensating fiber sliver, it is spare;
(3) regenerative mixed fiber sliver, coarse sand, spinning process are handled up to a kind of with the pure of mould proof antistatic effect
Cotton yarn.
Further, it is 180 revs/min that speed, which is mixed, in the step (1), and mixing time is 45 minutes.
Further, rear fibre length control is smashed 3.5 using machine after step (2) the cotton yarn leftover pieces mixing
Millimeter.And the composite fibre immersion processing slurry time is 65 minutes, removal sample carries out drying and processing at a temperature of 110 DEG C.
Embodiment 2
A kind of Quality Pure Cotton Yarn Production with mould proof antistatic effect, the raw material are made of the raw material of following parts by weight: pure
7 parts of acrylic emulsion, 9 parts of gum arabic, 27 parts of waste and old cotton goods, 2.5 parts of bamboo charcoal fiber, 11.5 parts of graphene oxide, ε-are poly- to be relied
2.5 parts of propylhomoserin, 5.5 parts of nano-titanium dioxide, 9 parts of silica solution, 4.2 parts of aqueous polyurethane, 12 parts of cotton yarn leftover pieces, gellan gum
2.8 parts, 11 parts of hydroxypropul starch, 4.9 parts of hydroxy-silicone-oil emulsion, 14.2 parts of polypropylene, 5.5 parts of carboxymethyl cellulose, glycerol it is hard
14.5 parts of resin acid ester, 14.1 parts of Kathon CG, nano zine oxide 4.5 divide, 7.5 parts of atoleine, 4 parts of water.
A kind of preparation method of the Quality Pure Cotton Yarn Production with mould proof antistatic effect, the specific steps are as follows:
(1) raw material will be prepared to be put into stirred tank by the components by weight percent, suitable water is added, has been heated to while stirring
Full gelatinization, is mixed evenly to form spare slurry;
(2) it is smashed, the composite fibre smashed is immersed into processing slurry and made using machine after mixing cotton yarn leftover pieces
Drying and processing is carried out with drying, then the fiber after drying is mixed with bamboo charcoal fiber, it is mixed that regeneration is made by cotton carding, combing
Condensating fiber sliver, it is spare;
(3) regenerative mixed fiber sliver, coarse sand, spinning process are handled up to a kind of with the pure of mould proof antistatic effect
Cotton yarn.
Further, it is 200 revs/min that speed, which is mixed, in the step (1), and mixing time is 50 minutes.
Further, rear fibre length control is smashed 4.5 using machine after step (2) the cotton yarn leftover pieces mixing
Millimeter.And the composite fibre immersion processing slurry time is 75 minutes, removal sample carries out drying and processing at a temperature of 115 DEG C.
Embodiment 3
A kind of Quality Pure Cotton Yarn Production with mould proof antistatic effect, the raw material are made of the raw material of following parts by weight: pure
11.5 parts of acrylic emulsion, 11 parts of gum arabic, 28.5 parts of waste and old cotton goods, 3.5 parts of bamboo charcoal fiber, 12.5 parts of graphene oxide,
4 parts of epsilon-polylysine, 8 parts of nano-titanium dioxide, 13 parts of silica solution, 4.8 parts of aqueous polyurethane, 12.4 parts of cotton yarn leftover pieces, Gu
It is 3.6 parts of blue carbohydrate gum, 12 parts of hydroxypropul starch, 5.4 parts of hydroxy-silicone-oil emulsion, 16.8 parts of polypropylene, 8 parts of carboxymethyl cellulose, sweet
16.5 parts of oleostearin acid esters, 14.8 parts of Kathon CG, 7 parts of nano zine oxide, 12.5 parts of atoleine, 6 parts of water.
A kind of preparation method of the Quality Pure Cotton Yarn Production with mould proof antistatic effect, the specific steps are as follows:
(1) raw material will be prepared to be put into stirred tank by the components by weight percent, suitable water is added, has been heated to while stirring
Full gelatinization, is mixed evenly to form spare slurry;
(2) it is smashed, the composite fibre smashed is immersed into processing slurry and made using machine after mixing cotton yarn leftover pieces
Drying and processing is carried out with drying, then the fiber after drying is mixed with bamboo charcoal fiber, it is mixed that regeneration is made by cotton carding, combing
Condensating fiber sliver, it is spare;
(3) regenerative mixed fiber sliver, coarse sand, spinning process are handled up to a kind of with the pure of mould proof antistatic effect
Cotton yarn.
Further, it is 220 revs/min that speed, which is mixed, in the step (1), and mixing time is 55 minutes.
Further, rear fibre length control is smashed 5.5 using machine after step (2) the cotton yarn leftover pieces mixing
Millimeter.And the composite fibre immersion processing slurry time is 85 minutes, removal sample carries out drying and processing at a temperature of 120 DEG C.
Claims (4)
1. a kind of Quality Pure Cotton Yarn Production with mould proof antistatic effect, it is characterised in that: be made of the raw material of following parts by weight: pure
2.5~11.5 parts of acrylic emulsion, 7~11 parts of gum arabic, 25.5~28.5 parts of waste and old cotton goods, bamboo charcoal fiber 1.5~3.5
Part, 10.5~12.5 parts of graphene oxide, 1~4 part of epsilon-polylysine, 3~8 parts of nano-titanium dioxide, 5~13 parts of silica solution,
3.5~4.8 parts of aqueous polyurethane, 11.4~12.4 parts of cotton yarn leftover pieces, 2.2~3.6 parts of gellan gum, hydroxypropul starch 10~
12 parts, 4.1~5.4 parts of hydroxy-silicone-oil emulsion, 12.1~16.8 parts of polypropylene, 3~8 parts of carboxymethyl cellulose, glycerol stearate
12.5~16.5 parts of ester, 13.4~14.8 parts of Kathon CG, 2-7 parts of nano zine oxide, 5.5~12.5 parts of atoleine, 2~6 parts of water.
2. a kind of preparation method of Quality Pure Cotton Yarn Production with mould proof antistatic effect according to claim 1, which is characterized in that
It is made by the following specific steps:
(1) above-mentioned raw materials component by weight is put into stirred tank, suitable water is added, be heated to being gelatinized completely while stirring,
It is mixed evenly to form spare slurry;
(2) it is smashed after mixing cotton yarn leftover pieces using machine, the composite fibre smashed is immersed processing slurry and used and is dried
Dry machine carries out drying and processing, then the fiber after drying is mixed with bamboo charcoal fiber, and regenerative mixed is made by cotton carding, combing
Fiber sliver, it is spare;
(3) regenerative mixed fiber sliver, coarse sand, spinning process are handled up to a kind of pure cotton with mould proof antistatic effect
Yarn.
3. a kind of preparation method of Quality Pure Cotton Yarn Production with mould proof antistatic effect according to claim 2, the step (1)
It is 180-220 revs/min that speed, which is mixed, and mixing time is 45-55 minutes.
4. a kind of preparation method of Quality Pure Cotton Yarn Production with mould proof antistatic effect according to claim 2, the step (2)
Rear fibre length control is smashed at 3.5-5.5 millimeters using machine after the mixing of cotton yarn leftover pieces, and composite fibre immersion is handled
The slurry time is 65-85 minutes, and removal sample carries out drying and processing at a temperature of 110-120 DEG C.