CN110054927A - A kind of paint stripper of metal surface epoxy resin coating - Google Patents
A kind of paint stripper of metal surface epoxy resin coating Download PDFInfo
- Publication number
- CN110054927A CN110054927A CN201910348265.3A CN201910348265A CN110054927A CN 110054927 A CN110054927 A CN 110054927A CN 201910348265 A CN201910348265 A CN 201910348265A CN 110054927 A CN110054927 A CN 110054927A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- epoxy resin
- paint stripper
- resin coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of paint strippers of metal surface epoxy resin, paint stripper is made of the water of the n,N-Dimethylformamide of 50-70 parts by weight, the anionic surfactant of 1-5 parts by weight, the nonionic surfactant of 1-5 parts by weight, the organic base of 3-10 parts by weight, the ethyl alcohol of 20-30 parts by weight, the solvent naphtha of 5-7 parts by weight, the diphenylamine derivatives of 4-12 parts by weight and 3-9 parts by weight.The present invention has selected diphenylamine derivatives, can substantially reduce the adhesive force between epoxy resin and metal, can realize quick depainting in metal surface.
Description
Technical field
The present invention relates to a kind of paint strippers of metal surface epoxy resin coating.
Background technique
Organic paint stripper is the liquid mixed by chlorohydrocarbon, benzene homologues, ester, alcohol, ether equal solvent.There is invention machine depainting
Agent is because of the advantages that its is easy to use, paint removal efficiency is high, stability is good and metal protection is small, and invention has become in the market at present
Mainstream paint stripper.As disclosed matching for paint stripper in " for polyester, the paint stripper of polyesterimide enameled copper round wire paint film " patent
Side, component is by mass fraction are as follows: 30~50% formic acid, 30~40% chloroforms, 5~35% cresols, invention 0~
5% additive composition.In a kind of " powerful paint stripper " patent, disclose by quality distribute bright number be 0~5% surfactant,
72~78% methylene chloride, 0~3% ethyl acetate, 0.78~0.8% thickener, invention 0.6~0.7% paraffin, 4.85~
10% phenol, 5~9% ethyl alcohol, 0~6% formic acid, 0~6% ammonium hydroxide, 0~1% nitrous invent sour sodium composition.Though this kind of paint stripper
Depainting is thoroughly and applied widely, but not ideal enough in terms of the processing of metal surface epoxy resin coating.
Summary of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of depaintings of metal surface epoxy resin coating
Agent by the N,N-dimethylformamide of 50-70 parts by weight, the anionic surfactant of 1-5 parts by weight, 1-5 parts by weight it is non-from
Sub- surfactant, the organic base of 3-10 parts by weight, the ethyl alcohol of 20-30 parts by weight, the solvent naphtha of 5-7 parts by weight, 4-12 weight
The diphenylamine derivatives of part and the water composition of 3-9 parts by weight.
The anionic surfactant is selected from lauryl sodium sulfate, neopelex, laruyl alcohol polyoxy second
One or more of alkene ether sodium sulfate.
The nonionic surfactant is selected from nonylphenol polyoxyethylene ether, polyoxyethylene carboxylate, fatty acid methyl ester
One or more of ethoxylate.
The organic base is selected from one of sodium methoxide, potassium tert-butoxide, lithium diisopropyl amido, hexamethyldisilazane lithium
Or it is several.
The diphenylamine derivatives is selected to methyldiphenylamine, 4,4'- bis- (propyloxy phenyl base) diphenylamines, 2,4- diformazans
Base diphenylamines, dioctyl diphenylamine, styrenated diphenylamine, 4- octyl diphenylamine, 4- tert-butyl diphenylamine, Α, Α '-hexichol
One or more of amido paraxylene.
The present invention selects n,N-Dimethylformamide as bulk solvent, since n,N-Dimethylformamide has well
Small molecule component in the feature of environmental protection, with epoxy resin has good compatibility, can soon realize the swelling of epoxy resin,
Meanwhile the present invention has selected diphenylamine derivatives, can substantially reduce the adhesive force between epoxy resin and metal, it can be in gold
Metal surface realizes quick depainting.
The above-mentioned of the application and other features, aspects and advantages are more readily understood with reference to following detailed description.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention
Description, the technical solution of the embodiment of the present invention is clearly and completely described.Obviously, described embodiment is this hair
Bright a part of the embodiment, instead of all the embodiments.Based on described the embodiment of the present invention, ordinary skill
Personnel's all other embodiment obtained under the premise of being not necessarily to creative work, shall fall within the protection scope of the present invention.
Unless otherwise defined, the technical term or scientific term used herein should be in fields of the present invention and has
The ordinary meaning that the personage of general technical ability is understood.Used in present patent application specification and claims " the
One ", " second " and similar word are not offered as any sequence, quantity or importance, and are used only to distinguish different
Component part.Equally, the similar word such as "one" or " one " does not indicate that quantity limits yet, but indicates that there are at least one.
A kind of N,N-dimethylformamide by 50-70 parts by weight of the paint stripper of metal surface epoxy resin coating, 1-5 weight
The anionic surfactant, the nonionic surfactant of 1-5 parts by weight, the organic base of 3-10 parts by weight, 20-30 weight of part
Measure the water composition of the ethyl alcohol of part, the solvent naphtha of 5-7 parts by weight, the diphenylamine derivatives of 4-12 parts by weight and 3-9 parts by weight.
The anionic surfactant is selected from lauryl sodium sulfate, neopelex, laruyl alcohol polyoxy second
One or more of alkene ether sodium sulfate.
The nonionic surfactant is selected from nonylphenol polyoxyethylene ether, polyoxyethylene carboxylate, fatty acid methyl ester
One or more of ethoxylate.
The organic base is selected from one of sodium methoxide, potassium tert-butoxide, lithium diisopropyl amido, hexamethyldisilazane lithium
Or it is several.
The diphenylamine derivatives is selected to methyldiphenylamine, 4,4'- bis- (propyloxy phenyl base) diphenylamines, 2,4- diformazans
Base diphenylamines, dioctyl diphenylamine, styrenated diphenylamine, 4- octyl diphenylamine, 4- tert-butyl diphenylamine, Α, Α '-hexichol
One or more of amido paraxylene.
In following embodiments, anionic surfactant is lauryl sodium sulfate, and nonionic surfactant is nonyl
Phenol polyethenoxy ether, organic base are lithium diisopropyl amido, and diphenylamine derivatives is 4- tert-butyl diphenylamine.
Embodiment 1
By several piece it is identical to depainting steel plate (surface be SIGMA company epoxy universal primer 280, steel plate is ordinary steel
Grinding process, 20 microns of thickness are passed through in plate, surface) it is dipped in the depainting agent solution completely, the operating temperature range of paint stripper
It is 50 DEG C.It every 1 minute, will be taken out to depainting steel plate, whether observation surface completes to remove epoxy resin coating.
Paint stripper is by the N,N-dimethylformamide of 70 parts by weight, the anionic surfactant of 3 parts by weight, 3 parts by weight
Nonionic surfactant, the organic base of 4 parts by weight, the ethyl alcohol of 25 parts by weight, the solvent naphthas of 6 parts by weight, 8 parts by weight
Diphenylamine derivatives and the water of 8 parts by weight composition.Testing the time completely removed is 11 minutes.
Embodiment 2
By several piece it is identical to depainting steel plate (surface be SIGMA company epoxy universal primer 280, steel plate is ordinary steel
Grinding process, 20 microns of thickness are passed through in plate, surface) it is dipped in the depainting agent solution completely, the operating temperature range of paint stripper
It is 50 DEG C.It every 1 minute, will be taken out to depainting steel plate, whether observation surface completes to remove epoxy resin coating.
Paint stripper is by the N,N-dimethylformamide of 65 parts by weight, the anionic surfactant of 4 parts by weight, 4 parts by weight
Nonionic surfactant, the organic base of 5 parts by weight, the ethyl alcohol of 22 parts by weight, the solvent naphthas of 7 parts by weight, 9 parts by weight
Diphenylamine derivatives and the water of 8 parts by weight composition.Testing the time completely removed is 12 minutes.
Embodiment 3
By several piece it is identical to depainting steel plate (surface be SIGMA company epoxy universal primer 280, steel plate is ordinary steel
Grinding process, 20 microns of thickness are passed through in plate, surface) it is dipped in the depainting agent solution completely, the operating temperature range of paint stripper
It is 50 DEG C.It every 1 minute, will be taken out to depainting steel plate, whether observation surface completes to remove epoxy resin coating.
Paint stripper is by the N,N-dimethylformamide of 70 parts by weight, the anionic surfactant of 6 parts by weight, 6 parts by weight
Nonionic surfactant, the organic base of 8 parts by weight, the ethyl alcohol of 12 parts by weight, the solvent naphthas of 10 parts by weight, 3 parts by weight
Diphenylamine derivatives and the water of 9 parts by weight composition.Testing the time completely removed is 17 minutes.
Embodiment 4
By several piece it is identical to depainting steel plate (surface be SIGMA company epoxy universal primer 280, steel plate is ordinary steel
Grinding process, 20 microns of thickness are passed through in plate, surface) it is dipped in the depainting agent solution completely, the operating temperature range of paint stripper
It is 50 DEG C.It every 1 minute, will be taken out to depainting steel plate, whether observation surface completes to remove epoxy resin coating.
Paint stripper is by the N,N-dimethylformamide of 60 parts by weight, the anionic surfactant of 2 parts by weight, 9 parts by weight
Nonionic surfactant, the organic base of 13 parts by weight, the ethyl alcohol of 27 parts by weight, the solvent naphthas of 2 parts by weight, 14 parts by weight
Diphenylamine derivatives and the water of 3 parts by weight composition.Testing the time completely removed is 18 minutes.
Comparative example 1
By several piece it is identical to depainting steel plate (surface be SIGMA company epoxy universal primer 280, steel plate is ordinary steel
Grinding process, 20 microns of thickness are passed through in plate, surface) it is dipped in the depainting agent solution completely, the operating temperature range of paint stripper
It is 50 DEG C.It every 1 minute, will be taken out to depainting steel plate, whether observation surface completes to remove epoxy resin coating.
Paint stripper is by the N,N-dimethylformamide of 70 parts by weight, the anionic surfactant of 3 parts by weight, 3 parts by weight
Nonionic surfactant, the organic base of 4 parts by weight, the ethyl alcohol of 25 parts by weight, the solvent naphtha of 6 parts by weight and 8 parts by weight
Water composition.Testing the time completely removed is 21 minutes.
Comparative example 2
By several piece it is identical to depainting steel plate (surface be SIGMA company epoxy universal primer 280, steel plate is ordinary steel
Grinding process, 20 microns of thickness are passed through in plate, surface) it is dipped in the depainting agent solution completely, the operating temperature range of paint stripper
It is 50 DEG C.It every 1 minute, will be taken out to depainting steel plate, whether observation surface completes to remove epoxy resin coating.
Paint stripper is by the N,N-dimethylformamide of 70 parts by weight, the anionic surfactant of 3 parts by weight, 3 parts by weight
Nonionic surfactant, the ethyl alcohol of 25 parts by weight, the solvent naphtha of 6 parts by weight, 8 parts by weight diphenylamine derivatives and 8
The water of parts by weight forms.Testing the time completely removed is 25 minutes.
As can be seen that formula of the invention, which has, preferably removes epoxy resin coating.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or
In the case where essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention
It is interior.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, narrating mode is merely for the sake of clarity in this of specification, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (5)
1. a kind of paint stripper of metal surface epoxy resin coating, which is characterized in that the paint stripper N by 50-70 parts by weight, N-
Dimethylformamide, the anionic surfactant of 1-5 parts by weight, the nonionic surfactant of 1-5 parts by weight, 3-10 weight
Part organic base, the ethyl alcohol of 20-30 parts by weight, the solvent naphtha of 5-7 parts by weight, 4-12 parts by weight diphenylamine derivatives and 3-
The water of 9 parts by weight forms.
2. a kind of paint stripper of metal surface epoxy resin coating according to claim 1, which is characterized in that the anion
Surfactant is selected from one of lauryl sodium sulfate, neopelex, ethoxylated dodecyl alcohol sodium sulphate
Or it is several.
3. a kind of paint stripper of metal surface epoxy resin coating according to claim 1, which is characterized in that the nonionic
Surfactant is selected from one of nonylphenol polyoxyethylene ether, polyoxyethylene carboxylate, fatty acid methyl ester ethoxylate
Or it is several.
4. a kind of paint stripper of metal surface epoxy resin coating according to claim 1, which is characterized in that the organic base
Selected from one or more of sodium methoxide, potassium tert-butoxide, lithium diisopropyl amido, hexamethyldisilazane lithium.
5. a kind of paint stripper of metal surface epoxy resin coating according to claim 1, which is characterized in that the diphenylamines
Derivative is selected to methyldiphenylamine, 4,4'- bis- (propyloxy phenyl base) diphenylamines, 2,4- dimethyl diphenylamines, dioctyl hexichol
Amine, styrenated diphenylamine, 4- octyl diphenylamine, 4- tert-butyl diphenylamine, Α, one of Α '-hexichol amido paraxylene
Or it is several.