CN110041574A - A kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material - Google Patents
A kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material Download PDFInfo
- Publication number
- CN110041574A CN110041574A CN201910368335.1A CN201910368335A CN110041574A CN 110041574 A CN110041574 A CN 110041574A CN 201910368335 A CN201910368335 A CN 201910368335A CN 110041574 A CN110041574 A CN 110041574A
- Authority
- CN
- China
- Prior art keywords
- corrosion
- resistant
- oil sump
- natural emulsion
- rubber material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of corrosion-resistant and high-temperature resistant oil sump seal rubber materials, the material is made of following raw materials according: natural emulsion, lauryl glucosyl, acrylic acid, sodium carbonate peroxide, ammonium persulfate, potassium peroxydisulfate, sodium thiosulfate, acrylic acid, N, N'- methylene-bisacrylamide, vinyl chloride-vinyl acetate resin, liquid nitrile rubber, vinyl ester resin, regulator, promotor, crosslinking agent, anti-aging agent, deionized water.Corrosion resistant seal rubber material disclosed by the invention, pass through the modification of acrylic acid, acrylamide, vinyl chloride-vinyl acetate resin etc., so that the reinforcing effect of natural emulsion improves, tensile strength and tearing strength increase, and prevent natural emulsion from cracking, so that the elongation of natural emulsion increases, convenient for the plasticity of rubber, natural emulsion stress deformation in use is prevented, the use of natural emulsion is influenced, it is poor to solve existing rubber corrosion resistance, the problem of higher cost.
Description
Technical field
The invention belongs to technical field of polymer materials, and in particular to a kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material
Material.
Background technique
Engine oil leakage main harm is loss machine oil, causes to waste, serious to may cause machine oil deficiency and then cause
Engine is impaired.Instead of oil leak does not cause for this, because it is insufficient caused to have leaked later engine oil pressure.Since most of vehicles do not have
Organic oil level shows, and there is a situation where unconsciously machine oil to occur lower than normal position, and engine oil pressure deficiency causes
Accident.Bottom-end gasket is used for engine sump tank, plays the role of sealing.Oil sump is the lower half portion of crankcase, again
Referred to as lower crankcase.Its effect is closed crankcase, as the shell of oil storage tank, prevents impurity from entering and collecting and stores by sending out
The lubricating oil that each friction surface of motivation flows back to, disperses partial heat, prevents ravine lubricating oil from aoxidizing.Oil sump mostly by sheet metal punching press and
At;Shape is more complicated general using cast iron or aluminium alloy moulding by casting.It is internal equipped with steady oil baffle, to avoid garage
The oscillation of pasta caused by when vehicle jolts, which swashs, splashes, and is conducive to the precipitating of impurity of lubricant, in addition, oil sump bottom lowest part is also equipped with
Purge cock.With the development of highstrenghtpiston, the oil sump through injection molding is increasingly by vast production firm
Pro-gaze, since plastic shaping is simple, moulding is easy, and traditional gasket type sealing ring has been abandoned by more and more manufacturers, usually exists
Plastic oil pan upper end setting straight trough is cooperated with sealing ring, mostly uses sulfurized nitrile rubber as sealing ring, due to butyronitrile
Rubber is softer, causes sealing position intensity and oil sump intensity inconsistent, will lead to oil sump after stress in weakness
Position breakage oil leak.With good sealability.A kind of good gasket must be able to keep its close within longer period
The ability of envelope.When bolt screws, gasket is simultaneously radially extended or is wriggled simultaneously by pressure, is let out so as to interface occur
Leakage, so gasket Ying Yougao anti-creep ability.With high compactness.There is gasket high compactness can prevent to permeate
Leakage, i.e., cause medium to leak into low-pressure side anti-height with higher by the micro chink of gasket from high-pressure side because of pressure difference
Mild resistance to chemical attack.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material is provided
Material.
The invention is realized by the following technical scheme:
A kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material, is made: natural emulsion 46 ~ 62 of the raw material of following parts by weight
Part, 1 ~ 2 part of lauryl glucosyl, 40 ~ 60 parts of sodium carbonate peroxide, 0.1 ~ 0.2 part of ammonium persulfate, potassium peroxydisulfate 0.1 ~ 0.4
Part, 0.2 ~ 0.5 part of sodium thiosulfate, 85 ~ 98 parts of acrylic acid, N, 1 ~ 3 part of N'- methylene-bisacrylamide, vinyl chloride-vinyl acetate resin 20 ~ 25
Part, 2 ~ 4 parts of vinyl ester resin, 3 ~ 5 parts of liquid nitrile rubber, 0.5 ~ 0.9 part of regulator, 0.2 ~ 0.4 part of promotor, crosslinking agent
0.5 ~ 0.8 part, 0.4 ~ 1.8 part of anti-aging agent, 80 ~ 95 parts of deionized water.
Further, the vinyl chloride-vinyl acetate resin is the terpolymer of vinyl chloride and vinyl acetate, ethylene isobutyl ether, is sticked
23 DEG C of degree (ISO-3219) is 160 ~ 200mPas, and vinyl acetate content is 10 ~ 13%, and content of vinylchloride is that 84 ~ 87%, K value is
50~55。
Further, stating anti-aging agent is boronation alkyl benzene calcium sulfonate, p-t-butylphenyl salicylate, dialkyl dithio phosphorus
The mixture of sour zinc salt, proportion are 1 ~ 2: 2 ~ 4: 3 ~ 5.
Further, the regulator be curing tungsten powder, storax, asafoetide, acaroid gum it is one or more.
Further, the crosslinking agent is benzotriazole, double-(γ-triethoxy silicon substrate propyl) tetrasulfide, two rings
At least one of hexyl tetrathio diazine.
Further, the promotor is oxygen diethyl support group benzothiazole sulfenamide, diethyl benzothiazole time sulphonyl
At least one of amine, polyhexamethylene guanide.
Further, the natural dandelion that it is 15 ~ 70% that the natural emulsion, which is by mass concentration, extracts latex, the Pu
Public English is Herba Taraxaci ohwiani, 1 ~ 2 year Russian dandelion, variegated leaf dandelion dandelion herb.
Further, the vinyl ester resin is bisphenol type epoxy vinylite and phenolic epoxy vinyl
The mixture of one or more of resin;The liquid nitrile rubber is that molecular weight is 2000 ~ 4000,23 DEG C of (ISO-
It 3219) is 800 ~ 2500mPas, substituent group is carboxyl.
A kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material, which is characterized in that preparation method includes the following steps:
(1) electronic balance weighs acrylic monomers, the deionized water of total amount half is added, for use;(2) natural emulsion is added anti-
It answers in kettle, lauryl glucosyl is added, starts blender, adds acrylic acid solution and sodium carbonate peroxide;It is added and causes
Agent ammonium persulfate, sodium thiosulfate, potassium peroxydisulfate and N, N'- methylene-bisacrylamide are added remaining deionized water, then rise
Temperature is taken out 24 hours dry in 70 DEG C of baking ovens to 75 ~ 85 DEG C, after 2 ~ 3h of reaction time, obtains modified natural emulsion;(3) it will be modified
Natural emulsion is put into revolving surge tank and is extracted 24 ~ 36 hours at a temperature of water-bath is in 70 DEG C with acetone reflux, petroleum ether
(boiling range: 70 ~ 90 DEG C) extracts free rubber hydrocarbon, reflux extracting 24 ~ 36 hours at 80 DEG C of temperature;(4) in open kneading machine machine
On prepare 90 ~ 95 DEG C of rubber compound temperature, be kneaded charging sequence are as follows: modified natural emulsion rubber, vinyl chloride-vinyl acetate resin, vinyl esters tree
Rouge, liquid nitrile rubber, anti-aging agent, promotor, regulator, crosslinking agent, are kneaded 5 ~ 10min, then rubber compound age overnight is used
Vulcanizing press is at 145 ~ 155 DEG C, and vulcanized test specimens are under 15 ~ 25Mpa to get corrosion-resistant and high-temperature resistant oil sump seal rubber material.
Beneficial effects of the present invention:
The present invention solves natural emulsion and meets oil to expand, or the Additive contained in working fluid due to accelerates to dislike
Change, aggravation friction, abrasion, and intensity obviously drops.In addition to expansion, oil liquid to the hardness of rubber, tension stress, elongation and
The Physical and mechanical properties of residual deformation have significant impact, make rubber softening, contraction and decomposition, rubber performance deterioration.This hair
Bright improvement rubber latex performance uses rubber plastic blend, and acrylic acid, acrylamide component, the dispersion of generation rule are introduced in rubber
Active force stablizes the network molecular structure for constituting caoutchouc elasticity, and the introducing of vinyl chloride-vinyl acetate resin and vinyl ester resin improves material
The corrosion resistance of material, and raw material sources are extensive, reduce cost, there is collaboration facilitation well.If the solubility in rubber
Molecule is stable in the medium, and it is small that rubber shrinks amplitude, is conducive to improve sealing effect.
The present invention has the advantage that compared with prior art
Seal rubber material material compression resistant disclosed by the invention permanent deformation performance is good, corrosion-resistant, at low cost, temperature and pressure compared with
Under the conditions of great fluctuation process, elasticity is good has self-energized seal sealing function;Under low temperature, corrosive media or vacuum condition, also have
There is a good application effect, intensity with higher and has lower compression set, excellent oil resistivity, resistance at high temperature
Hot, physical mechanical property, workability and it is cheap the advantages that.
Specific embodiment
Illustrate the present invention with specific embodiment below, but is not limitation of the present invention.
Embodiment 1
A kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material, is made of the raw material of following parts by weight: 62 parts of natural emulsion,
2 parts of lauryl glucosyl, 60 parts of sodium carbonate peroxide, 0.2 part of ammonium persulfate, 0.4 part of potassium peroxydisulfate, sodium thiosulfate 0.5
Part, 98 parts of acrylic acid, N, 3 parts of N'- methylene-bisacrylamide, 25 parts of vinyl chloride-vinyl acetate resin, 2 parts of vinyl ester resin, liquid butyronitrile
5 parts of rubber, 0.9 part of regulator, 0.4 part of promotor, 0.8 part of crosslinking agent, 1.8 parts of anti-aging agent, 95 parts of deionized water.
Further, the vinyl chloride-vinyl acetate resin is the terpolymer of vinyl chloride and vinyl acetate, ethylene isobutyl ether, is sticked
23 DEG C of degree (ISO-3219) is 160 ~ 200mPas, and vinyl acetate content is 10 ~ 13%, and content of vinylchloride is that 84 ~ 87%, K value is
50~55。
Further, stating anti-aging agent is boronation alkyl benzene calcium sulfonate, p-t-butylphenyl salicylate, dialkyl dithio phosphorus
The mixture of sour zinc salt, proportion 1: 2: 3.
Further, the regulator is curing tungsten powder, storax, asafoetide.
Further, the crosslinking agent is benzotriazole, double-(γ-triethoxy silicon substrate propyl) tetrasulfide, two rings
Hexyl tetrathio diazine.
Further, the promotor is oxygen diethyl support group benzothiazole sulfenamide, diethyl benzothiazole time sulphonyl
Amine, polyhexamethylene guanide.
Further, the natural dandelion that it is 15 ~ 70% that the natural emulsion, which is by mass concentration, extracts latex, the Pu
Public English is 2 years dandelion herbs of variegated leaf dandelion.
Further, the vinyl ester resin is bisphenol type epoxy vinylite and phenolic epoxy vinyl
The mixture of one or more of resin;The liquid nitrile rubber is that molecular weight is 2000 ~ 4000,23 DEG C of (ISO-
It 3219) is 800 ~ 2500mPas, substituent group is carboxyl.
A kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material, which is characterized in that preparation method includes the following steps:
(1) electronic balance weighs acrylic monomers, the deionized water of total amount half is added, for use;(2) natural emulsion is added anti-
It answers in kettle, lauryl glucosyl is added, starts blender, adds acrylic acid solution and sodium carbonate peroxide;It is added and causes
Agent ammonium persulfate, sodium thiosulfate, potassium peroxydisulfate and N, N'- methylene-bisacrylamide are added remaining deionized water, then rise
Temperature is taken out 24 hours dry in 70 DEG C of baking ovens to 85 DEG C, after 2 ~ 3h of reaction time, obtains modified natural emulsion;It (3) will modified day
Right latex is put into revolving surge tank and is extracted 24 ~ 36 hours at a temperature of water-bath is in 70 DEG C with acetone reflux, petroleum ether (boiling
Journey: 70 ~ 90 DEG C) free rubber hydrocarbon is extracted, reflux extracting 24 ~ 36 hours at 80 DEG C of temperature;(4) it is made on open kneading machine machine
Standby 95 DEG C of rubber compound temperature, is kneaded charging sequence are as follows: modified natural emulsion rubber, vinyl chloride-vinyl acetate resin, vinyl ester resin, liquid fourth
Nitrile rubber, anti-aging agent, promotor, regulator, crosslinking agent, are kneaded 10min, then rubber compound age overnight uses vulcanizing press
At 155 DEG C, vulcanized test specimens are under 25Mpa to get corrosion-resistant and high-temperature resistant oil sump seal rubber material.
Embodiment 2
A kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material, is made of the raw material of following parts by weight: 46 parts of natural emulsion,
1 part of lauryl glucosyl, 40 parts of sodium carbonate peroxide, 0.1 part of ammonium persulfate, 0.1 part of potassium peroxydisulfate, sodium thiosulfate 0.2
Part, 85 parts of acrylic acid, N, 1 part of N'- methylene-bisacrylamide, 20 parts of vinyl chloride-vinyl acetate resin, 4 parts of vinyl ester resin, liquid butyronitrile
5 parts of rubber, 0.5 part of regulator, 0.2 part of promotor, 0.5 ~ part of crosslinking agent, 0.4 part of anti-aging agent, 80 parts of deionized water.
Further, the vinyl chloride-vinyl acetate resin is the terpolymer of vinyl chloride and vinyl acetate, ethylene isobutyl ether, is sticked
23 DEG C of degree (ISO-3219) is 160 ~ 200mPas, and vinyl acetate content is 10 ~ 13%, and content of vinylchloride is that 84 ~ 87%, K value is
50~55。
Further, stating anti-aging agent is boronation alkyl benzene calcium sulfonate, p-t-butylphenyl salicylate, dialkyl dithio phosphorus
The mixture of sour zinc salt, proportion 2: 4: 5.
Further, the regulator is curing tungsten powder, storax, asafoetide, acaroid gum.
Further, the crosslinking agent is benzotriazole, double-(γ-triethoxy silicon substrate propyl) tetrasulfide, two rings
Hexyl tetrathio diazine.
Further, the promotor is oxygen diethyl support group benzothiazole sulfenamide, diethyl benzothiazole time sulphonyl
Amine, polyhexamethylene guanide.
Further, the natural dandelion that it is 15 ~ 70% that the natural emulsion, which is by mass concentration, extracts latex, the Pu
Public English is 1 ~ 2 year dandelion herb of Russian dandelion.
Further, the vinyl ester resin is bisphenol type epoxy vinylite;The liquid nitrile rubber is point
It is 800 ~ 2500mPas that son amount, which is 2000 ~ 4000,23 DEG C (ISO-3219), and substituent group is carboxyl.
A kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material, which is characterized in that preparation method includes the following steps:
(1) electronic balance weighs acrylic monomers, the deionized water of total amount half is added, for use;(2) natural emulsion is added anti-
It answers in kettle, lauryl glucosyl is added, starts blender, adds acrylic acid solution and sodium carbonate peroxide;It is added and causes
Agent ammonium persulfate, sodium thiosulfate, potassium peroxydisulfate and N, N'- methylene-bisacrylamide are added remaining deionized water, then rise
Temperature is taken out 24 hours dry in 70 DEG C of baking ovens to 85 DEG C, after reaction time 3h, obtains modified natural emulsion;(3) by modified natural
Latex is put into revolving surge tank and is extracted 36 hours at a temperature of water-bath is in 70 DEG C with acetone reflux, petroleum ether (boiling range: 70 ~
90 DEG C) free rubber hydrocarbon is extracted, reflux extracting 24 hours at 80 DEG C of temperature;(4) rubber compound is prepared on open kneading machine machine
95 DEG C of temperature, be kneaded charging sequence are as follows: modified natural emulsion rubber, vinyl chloride-vinyl acetate resin, vinyl ester resin, liquid nitrile rubber,
Anti-aging agent, promotor, regulator, crosslinking agent are kneaded 10min, then rubber compound age overnight uses vulcanizing press at 155 DEG C,
Vulcanized test specimens are under 25Mpa to get corrosion-resistant and high-temperature resistant oil sump seal rubber material.
Comparative example 1
This comparative example compared with Example 2, weighs in step in raw material, saves liquid nitrile rubber ingredient, method in addition to this
Step is all the same.
Comparative example 2
This comparative example compared with Example 2, weighs in step in raw material, saves regulator ingredient, and method and step in addition to this is equal
It is identical.
Comparative example 3
This comparative example compared with Example 2, weighs in step in raw material, saves vinyl ester resin ingredient, method in addition to this
Step is all the same.
Comparative example 4
This comparative example compared with Example 2, weighs in step in raw material, saves vinyl chloride-vinyl acetate resin ingredient, method and step in addition to this
It is all the same.
Comparative example 5
This comparative example compared with Example 2, weighs in step in raw material, saves sodium carbonate peroxide ingredient, method step in addition to this
It is rapid all the same.
The performance test results of each embodiment and comparative example corrosion-resistant and high-temperature resistant oil sump seal rubber material of table 1
Note: the above test result is carried out with reference to following methods: GB/T528-2009 vulcanized rubber or thermoplastic elastomer tensile stress
The measurement of strain property;GB/T531.1-2008 vulcanized rubber or thermoplastic elastomer penetration hardness test method part 1: shore
Hardometer method (Shao Er hardness GB/T1690-2006 vulcanized rubber or thermoplastic elastomer seakeeping test method;GGB/T3512-
2014 vulcanized rubbers or the accelerated ageing of thermoplastic elastomer hot-air and heat resistant test;GB/T7759-2015 vulcanized rubber, thermoplasticity
Compression set measures under rubber normal-temperature, high temperature and low temperature;GB/T18426-2001 rubber or plastic coat fabric at low temperature are curved
Song test.
Claims (9)
1. a kind of corrosion-resistant and high-temperature resistant oil sump seal rubber material, which is characterized in that be made of the raw material of following parts by weight:
46 ~ 62 parts of natural emulsion, 1 ~ 2 part of lauryl glucosyl, 40 ~ 60 parts of sodium carbonate peroxide, 0.1 ~ 0.2 part of ammonium persulfate, mistake
0.1 ~ 0.4 part of potassium sulfate, 0.2 ~ 0.5 part of sodium thiosulfate, 85 ~ 98 parts of acrylic acid, N, 1 ~ 3 part of N'- methylene-bisacrylamide,
20 ~ 25 parts of vinyl chloride-vinyl acetate resin, 3 ~ 5 parts of liquid nitrile rubber, 0.5 ~ 0.9 part of regulator, 0.2 ~ 0.4 part of promotor, crosslinking agent 0.5 ~
0.8 part, 0.4 ~ 1.8 part of anti-aging agent, 2 ~ 4 parts of vinyl ester resin, 80 ~ 95 parts of deionized water.
2. corrosion-resistant and high-temperature resistant oil sump seal rubber material according to claim 1, which is characterized in that the chlorine vinegar
Resin is the terpolymer of vinyl chloride and vinyl acetate, ethylene isobutyl ether, 23 DEG C of viscosity (ISO-3219) for 160 ~
200mPas, vinyl acetate content are 10 ~ 13%, and content of vinylchloride is that 84 ~ 87%, K value is 50 ~ 55.
3. corrosion-resistant and high-temperature resistant oil sump seal rubber material according to claim 1, which is characterized in that described anti-old
Agent is the mixture of boronation alkyl benzene calcium sulfonate, p-t-butylphenyl salicylate, zinc dialkyl dithiophosphate, proportion
It is 1 ~ 2: 2 ~ 4: 3 ~ 5.
4. corrosion-resistant and high-temperature resistant oil sump seal rubber material according to claim 1, which is characterized in that the adjusting
Agent be curing tungsten powder, storax, asafoetide, acaroid gum it is one or more.
5. corrosion-resistant and high-temperature resistant oil sump seal rubber material according to claim 1, which is characterized in that the crosslinking
Agent is benzotriazole, double-(γ-triethoxy silicon substrate propyl) tetrasulfide, at least one in dicyclohexyl tetrathio diazine
Kind.
6. corrosion-resistant and high-temperature resistant oil sump seal rubber material according to claim 1, which is characterized in that the promotor
For at least one of oxygen diethyl support group benzothiazole sulfenamide, diethyl benzo thiazolesulfenamide, polyhexamethylene guanide.
7. corrosion-resistant and high-temperature resistant oil sump seal rubber material according to claim 1, which is characterized in that the genuine milk
The natural dandelion that it is 15 ~ 70% that glue, which is by mass concentration, extracts latex, and the dandelion is Herba Taraxaci ohwiani, Russian Pu public affairs
1 ~ 2 year English, variegated leaf dandelion dandelion herb.
8. corrosion-resistant and high-temperature resistant oil sump seal rubber material according to claim 1, which is characterized in that the vinyl
Ester resin is the mixed of one or more of bisphenol type epoxy vinylite and phenolic epoxy vinylite
Close object;The liquid nitrile rubber is that molecular weight is 2000 ~ 4000,23 DEG C (ISO-3219) for 800 ~ 2500mPas, is replaced
Base is carboxyl.
9. corrosion-resistant and high-temperature resistant oil sump seal rubber material according to claim 1, which is characterized in that preparation method
The following steps are included:
(1) electronic balance weighs acrylic monomers, the deionized water of total amount half is added, for use;(2) natural emulsion is added anti-
It answers in kettle, lauryl glucosyl is added, starts blender, adds acrylic acid solution and sodium carbonate peroxide;It is added and causes
Agent ammonium persulfate, sodium thiosulfate, potassium peroxydisulfate and N, N'- methylene-bisacrylamide are added remaining deionized water, then rise
Temperature is taken out 24 hours dry in 70 DEG C of baking ovens to 75 ~ 85 DEG C, after 2 ~ 3h of reaction time, obtains modified natural emulsion;(3) it will be modified
Natural emulsion is put into revolving surge tank and is extracted 24 ~ 36 hours at a temperature of water-bath is in 70 DEG C with acetone reflux, petroleum ether
(boiling range: 70 ~ 90 DEG C) extracts free rubber hydrocarbon, reflux extracting 24 ~ 36 hours at 80 DEG C of temperature;(4) in open kneading machine machine
On prepare 90 ~ 95 DEG C of rubber compound temperature, be kneaded charging sequence are as follows: modified natural emulsion rubber, vinyl chloride-vinyl acetate resin, vinyl esters tree
Rouge, liquid nitrile rubber, anti-aging agent, promotor, regulator, crosslinking agent, are kneaded 5 ~ 10min, then rubber compound age overnight is used
Vulcanizing press is at 145 ~ 155 DEG C, and vulcanized test specimens are under 15 ~ 25Mpa to get corrosion-resistant and high-temperature resistant oil sump seal rubber material.