CN110028729A - Armoured cable aluminium-plastic tape - Google Patents

Armoured cable aluminium-plastic tape Download PDF

Info

Publication number
CN110028729A
CN110028729A CN201910319854.9A CN201910319854A CN110028729A CN 110028729 A CN110028729 A CN 110028729A CN 201910319854 A CN201910319854 A CN 201910319854A CN 110028729 A CN110028729 A CN 110028729A
Authority
CN
China
Prior art keywords
plastic film
parts
aluminium
aluminium foil
plastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910319854.9A
Other languages
Chinese (zh)
Inventor
孙玉飞
孙建华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Hengli Communications Material Co Ltd
Original Assignee
Suzhou Hengli Communications Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Hengli Communications Material Co Ltd filed Critical Suzhou Hengli Communications Material Co Ltd
Priority to CN201910319854.9A priority Critical patent/CN110028729A/en
Publication of CN110028729A publication Critical patent/CN110028729A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of armoured cable aluminium-plastic tapes, including aluminium foil and plastic film, the plastic film is covered on aluminium foil, one or both sides in lower surface, the plastic film includes the material of following parts by weight: 65 ~ 80 parts of ethylene acrylic acid co polymer, 5 ~ 15 parts of Kynoar, 3 ~ 12 parts of low density polyethylene (LDPE), 1 ~ 3 part of titanium dioxide, 1 ~ 3 part of calcium carbonate powder, 0.5 ~ 2.5 part of nano silica, 0.1 ~ 0.5 part of styrene-ethylene-butadiene-styrene copolymer grafted maleic anhydride, 0.3 ~ 1 part of dibutyl hydroxy toluene, β-(3, 5- di-tert-butyl-hydroxy phenyl) 0.3 ~ 1 part of propionic acid octadecanol ester, 0.1 ~ 0.5 part of acid chrome blue, oleic diethanola mide borate ester BODEA0.2 ~ 1 part, coupling 0.3 ~ 1 part of agent.The aluminium-plastic tape can be obtained by heat posted method technique, and there is good product quality, and even if plastic film, which still is able to realize under hot paste method technique, to be merged with the hot sticky of aluminium foil with good Hot Tack strength in the case where aluminium foil surface has a small amount of pollutant.

Description

Armoured cable aluminium-plastic tape
Technical field
The present invention relates to a kind of polyethylene film more particularly to a kind of armoured cable aluminium-plastic tapes.
Background technique
Aluminium-plastic tape is mainly used for communications optical cable, communication cable outer jacket, is bonded together composition synthesis with protective cover material Sheath acts the moisture-proof layer for protecting cable core to corrode from moisture, while having armouring effect to cable core, resists extraneous effect Power lay etc. in various applications for communications optical cable, communication cable and provides mechanical protection, guarantees the stability, reliably of application Property.It is plastic-aluminum combined to generally use plastic film gluing composite metal belt and curtain coating composite metal belt production technology acquisition, production Process was not only complicated but also cumbersome.And the hot paste method production of use is just much simplified and is convenient for control, the high reliablity of product quality, However requirement of the hot paste method to raw material (aluminium foil and compound plastic film) is high, the quality of the two is to influence composite band product matter An important factor for amount.
Summary of the invention
It is an object of that present invention to provide a kind of armoured cable aluminium-plastic tape, the plastics of the armoured cable aluminium-plastic tape are thin Film can be very good to be bonded with aluminium foil by heat posted method technique completely, while guarantee the product quality of aluminium-plastic tape, and Even if still being able to realize the heat bonding with aluminium foil under hot paste method technique in the case where aluminium foil surface has a small amount of pollutant And there is good Hot Tack strength.
In order to achieve the above objectives, the technical solution adopted by the present invention is that: a kind of armoured cable aluminium-plastic tape, including aluminium foil And plastic film, the plastic film are covered on the one or both sides in aluminium foil upper and lower surfaces, the plastic film includes following The material of parts by weight:
65 ~ 80 parts of ethylene acrylic acid co polymer,
5 ~ 15 parts of Kynoar,
3 ~ 12 parts of low density polyethylene (LDPE),
1 ~ 3 part of titanium dioxide,
1 ~ 3 part of calcium carbonate powder,
0.5 ~ 2.5 part of nano silica,
0.1 ~ 0.5 part of styrene-ethylene-butadiene-styrene copolymer grafted maleic anhydride,
0.3 ~ 1 part of dibutyl hydroxy toluene,
0.3 ~ 1 part of ester of β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid octadecanol,
0.1 ~ 0.5 part of acid chrome blue,
0.2 ~ 1 part of oleic diethanola mide borate ester BODEA,
0.3 ~ 1 part of coupling agent.
Further improved technical solution is as follows in above-mentioned technical proposal:
1. in above scheme, the coupling agent be one of methyl-silicone oil, butyl titanate or trichloro ethylene base silane or Two kinds.
2. in above scheme, the average grain diameter of the titanium dioxide and calcium carbonate powder is 0.5 ~ 50 micron.
Due to the application of the above technical scheme, compared with the prior art, the invention has the following advantages:
Armoured cable aluminium-plastic tape of the present invention, using 65 ~ 80 parts of ethylene acrylic acid co polymers as base in the formula of plastic film Material is added 5 ~ 15 parts of Kynoar blendings, so that the plastic film has good thermal bonding and flexibility, and is added to 3 ~ 12 parts of low density polyethylene (LDPE), the Hot Tack strength of plastic film is further enhanced, so that plastic film passes through heat posted method technique It can be very good to be bonded with aluminium foil, guarantee the product quality of aluminium-plastic tape, can also reduce between plastic film and aluminium foil Thermal-adhering temperature；In addition, being also added into 0.5 ~ 2.5 part of nano silica and oleic diethanola mide borate ester in its formula BODEA0.2 ~ 1 part, the two are cooperateed with Kynoar, so that plastic film has good antistatic and antifouling property, it can Guarantee the clean type of plastic film itself, and there is good antifouling property, even if it is few to have plastic film in aluminium foil surface In the case where measuring pollutant, it still is able to the realization under hot paste method technique and merges with the hot sticky of aluminium foil with good hot sticky strong Degree.
Specific embodiment
The present invention will be further described below with reference to examples:
Embodiment 1 ~ 4: a kind of armoured cable aluminium-plastic tape, including aluminium foil and plastic film, the plastic film are covered on aluminium One or both sides in foil upper and lower surfaces, it is characterised in that: the plastic film includes the material of following parts by weight:
Table 1
The coupling agent is one or both of methyl-silicone oil, butyl titanate or trichloro ethylene base silane, the titanium white The average grain diameter of powder and calcium carbonate powder is 0.5 ~ 50 micron.
The plastic film of the armoured cable aluminium-plastic tape is made by following steps:
S1. 65 ~ 80 parts of ethylene acrylic acid co polymer, 1 ~ 3 part of titanium dioxide, 1 ~ 3 part of calcium carbonate powder, dibutyl hydroxy toluene are weighed 0.3 ~ 1 part, 0.3 ~ 1 part of β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid octadecanol ester, 0.1 ~ 0.5 part of acid chrome blue, idol Join in 0.3 ~ 1 part of investment high-speed mixer of agent, put into double screw extruder extruding pelletization after mixing, obtains material A；
S2. 0.5 ~ 2.5 part of nano silica, styrene-ethylene-butadiene-styrene copolymer grafted maleic anhydride are weighed 0.1 ~ 0.5 part, in the investment magnetic stirrer of oleic diethanola mide borate ester BODEA0.2 ~ 1 part, be stirred 20min, obtain Material B；
S3. by 3 ~ 12 parts of 5 ~ 15 parts of material A, material B and Kynoar, low density polyethylene (LDPE) investment mixers, at mixing It discharges after reason 15min, obtains mixing masterbatch；
S4. mixing masterbatch is fed into inflation film manufacturing machine, is squeezed out blown film to get the plastic film of the armoured cable aluminium-plastic tape.
Comparative example 1 ~ 3: a kind of aluminium-plastic tape, including aluminium foil and plastic film, the plastic film is covered on aluminium foil, One or both sides in lower surface, it is characterised in that: the plastic film includes the material of following parts by weight:
Table 2
The coupling agent is one or both of methyl-silicone oil, butyl titanate or trichloro ethylene base silane, the titanium white The average grain diameter of powder and calcium carbonate powder is 0.5 ~ 50 micron.
Preparation method is common method.
The film performance detection data of the aluminium-plastic tape of each embodiment and comparative example preparation is as follows:
Table 3
Wherein, peel strength test method are as follows: batten is made in the thermal-adhering product of film obtained and aluminium foil, along test length Film and aluminium foil are peeled off about 30mm by direction in advance, batten are placed in measurer for pulling force, by the glass rate of 100mm/min It is removed, the peel strength between film and aluminium foil is as unit of N/Cm.
As shown in table 3, the plastic film prepared in various embodiments of the present invention either mechanical stretching performance or heat seal is strong Degree is significantly better than that the plastic film of comparative example, meanwhile, the peel strength of the plastic film prepared in various embodiments of the present invention Better than the plastic film of comparative example, plastic film produced by the present invention can be can be very good completely by heat posted method technique and aluminium Foil fitting, while guaranteeing the product quality of aluminium-plastic tape, and even if in the case where aluminium foil surface has a small amount of pollutant, still It can so realize under hot paste method technique and merge with the hot sticky of aluminium foil with good Hot Tack strength.
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art Scholar cans understand the content of the present invention and implement it accordingly, and it is not intended to limit the scope of the present invention.It is all according to the present invention Equivalent change or modification made by Spirit Essence, should be covered by the protection scope of the present invention.

Claims (3)

1. a kind of armoured cable aluminium-plastic tape, including aluminium foil and plastic film, the plastic film is covered on the upper and lower table of aluminium foil One or both sides in face, it is characterised in that: the plastic film includes the material of following parts by weight:
65 ~ 80 parts of ethylene acrylic acid co polymer,
5 ~ 15 parts of Kynoar,
3 ~ 12 parts of low density polyethylene (LDPE),
1 ~ 3 part of titanium dioxide,
1 ~ 3 part of calcium carbonate powder,
0.5 ~ 2.5 part of nano silica,
0.1 ~ 0.5 part of styrene-ethylene-butadiene-styrene copolymer grafted maleic anhydride,
0.3 ~ 1 part of dibutyl hydroxy toluene,
0.3 ~ 1 part of ester of β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid octadecanol,
0.1 ~ 0.5 part of acid chrome blue,
0.2 ~ 1 part of oleic diethanola mide borate ester BODEA,
0.3 ~ 1 part of coupling agent.
2. armoured cable aluminium-plastic tape according to claim 1, it is characterised in that: the coupling agent be methyl-silicone oil, One or both of butyl titanate or trichloro ethylene base silane.
3. armoured cable aluminium-plastic tape according to claim 1, it is characterised in that: the titanium dioxide and calcium carbonate powder Average grain diameter be 0.5 ~ 50 micron.
CN201910319854.9A 2019-04-19 2019-04-19 Armoured cable aluminium-plastic tape Pending CN110028729A (en)