CN110027078A - A kind of carbonization summer sleeping bamboo mat production technology - Google Patents
A kind of carbonization summer sleeping bamboo mat production technology Download PDFInfo
- Publication number
- CN110027078A CN110027078A CN201910479434.7A CN201910479434A CN110027078A CN 110027078 A CN110027078 A CN 110027078A CN 201910479434 A CN201910479434 A CN 201910479434A CN 110027078 A CN110027078 A CN 110027078A
- Authority
- CN
- China
- Prior art keywords
- bamboo chip
- bamboo
- carbonization
- retort
- summer sleeping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to summer sleeping mat processing technique field, specially a kind of carbonization summer sleeping bamboo mat production technology, steps are as follows: the bamboo chip of well cutting is polished nine hours by dry powder, goes bamboo green, dyestuff is added in bruting process simultaneously；Bamboo chip after polishing is dried in drying bucket, until bamboo chip water content drops to 15% or less；Talcum powder is added on bamboo chip after the drying, keeps bamboo chip more smooth, then bamboo chip is put into retort and is carbonized, then measured again by colour photometer；After bamboo chip is carbonized, the lid of retort is opened, is sprayed water 5-6 minutes with giant, allows seed piece water tariff collection 12%；It rotates retort 20 minutes again.Using production technology of the invention, bamboo chip can be to avoid corruption by carbonization, because surface is handled by high temperature cabonization, and the color of every batch of is relatively unified, have the effect of it is antistatic, resist fracture, gas permeability is strong, water-resistance is good, the maintenance that is beneficial to human skin, flexibility are good.
Description
Technical field
The present invention relates to summer sleeping mat processing technique field, specifically a kind of carbonization summer sleeping bamboo mat production technology.
Background technique
Summer sleeping mat refers to that summer is nice and cool and the bamboo mat of place mat or straw mat.Belong to bedding.It is civil to be referred to as " flower seat ".With
In summer.Bamboo fibre summer sleeping mat is selected in clean pollution-free (Hainan remote mountains area) natural environment, and the newborn natural green bamboo of 3-4 are adopted
It is formed with the physical methods processing and fabricating such as boiling.There are straw plaited and two kinds of bamboo weaving.Decorations are knit out after thin bamboo strips used for weaving and grass blade are dyed colour
Figuratum summer sleeping mat.
The summer sleeping mat that is carbonized is very common summer sleeping mat.95% or more currently on the market is all carbonization summer sleeping mat, and carbonization is summer sleeping mat production
One of technique.As coffee-like, ecru, rufous these be all the effect of carbonization, existing carbonization summer sleeping mat, traditional handicraft every batch of
Secondary color all disunities.
Summary of the invention
It is mentioned above in the background art to solve the purpose of the present invention is to provide a kind of carbonization summer sleeping bamboo mat production technology
Problem.
To achieve the above object, the invention provides the following technical scheme:
A kind of carbonization summer sleeping bamboo mat production technology, steps are as follows: (1), the bamboo chip of well cutting by dry powder polish nine hours, go
Bamboo is green, and dyestuff is added in bruting process simultaneously；(2), the bamboo chip after polishing is dried in drying bucket, until bamboo chip
Until water content drops to 15% or less；(3), talcum powder is added on bamboo chip after the drying, then by bamboo chip be put into retort into
Row carbonization, is then measured by colour photometer again；(4) after bamboo chip is carbonized, the lid of retort is opened, giant is used
Water spray 5-6 minutes, allows seed piece water tariff collection 12%；(5) it rotates retort 20 minutes again, to reduce bamboo chip temperature and suction
Receive the moisture in retort；(6) bamboo chip is poured out, subsequently into subsequent polishing program.
As a further solution of the present invention: the color of pigment is resistance to tanned or sun-proof golden yellow in the step (1).
As a further solution of the present invention: the water content of bamboo chip is examined using moisture detector in the step (2)
It surveys.
As a further solution of the present invention: saying be the additional proportion of not talcum powder in step (3) to be one thousandth.
As a further solution of the present invention: the retort is burnt using the waste material bamboo scraps left after production bamboo chip
Heating.
As a further solution of the present invention: bamboo chip is put into after retort in the step (3), combustion heating three small
When, in-furnace temperature reaches 145-155 degree, is kept for half an hour, obtains dark bamboo chip.
As a further solution of the present invention: bamboo chip is put into after retort in the step (3), combustion heating three small
When, in-furnace temperature reaches 125-135 degree, is kept for half an hour, obtains light bamboo chip.
Compared with prior art, the beneficial effects of the present invention are: using production technology of the invention, bamboo chip can by carbonization
To avoid corruption, because surface is handled by high temperature cabonization, and the color of every batch of is relatively more unified, puts bamboo chip into high pressure charcoal
Change furnace progress steam charing process makes surface form hard carbonization particulate layer by high temperature and pressure, meanwhile, bamboo itself also can
It is harder.It can achieve the effect that except acarid simultaneously！Meanwhile hard carbonization particle will form bacterium and be not easy living environment, by
Can be harder than common bamboo mat after carbonization, it prevents bamboo mat surface rapid wear and plays bamboo thorn problem.Summer sleeping mat after carbonization can adsorb
Thus a certain amount of impurity and pernicious gas are the summer sleeping mats that can be breathed, above high-quality old bamboo of life in selected 5 years is raw material,
In conjunction with advanced production technology, the difficulty that bamboo product is easily damaged by worms is overcome.With ventilative, nice and cool, not viscous sweat, not curled spy
Point.It is the indispensable good merchantable brand of summer and autumn high temperature season reducing temperature of heatstroke prevention.Be carbonized summer sleeping mat color is vivid, surface fiber it is fine and smooth it is smooth, density is high,
Be smooth to the touch, feel more comfortable, allow your refrigerant summer charing summer sleeping mat have it is antistatic, anti-fracture, gas permeability is strong, water-resistance is good, has
It is good beneficial to the maintenance of human skin, flexibility, it is suitble to be layered on simmons or cushion and uses, it has absorbing carbon dioxide, only
Change air, the effect to boost metabolism；Carbonizing summer sleeping mat has healthcare function, lies and tosses about to squeeze different portions by human body when sitting
Position, plays massage effect, and the bamboo chip adsorption capacity after carbonization is very strong, can inhale taste with absorbing sweat.
Specific embodiment
It should be noted that in the absence of conflict, the feature in embodiment and embodiment in the present invention can phase
Mutually combination.
Below in conjunction with embodiment, the present invention will be described in detail.
Embodiment one
A kind of carbonization summer sleeping bamboo mat production technology, steps are as follows: (1), the bamboo chip of well cutting by dry powder polish nine hours, go
Bamboo is green, and dyestuff is added simultaneously in bruting process, bamboo chip is allowed to have enough time uniform pickup dyestuff, allows and colours more uniform, color
It is more unified, it is bright-coloured；(2), by polishing after bamboo chip, drying bucket in dried, until bamboo chip water content drop to 15% with
Until lower；(3), talcum powder is added on bamboo chip after the drying, keeps bamboo chip more smooth, then by bamboo chip be put into retort into
Row carbonization, is then measured by colour photometer again；(4) after bamboo chip is carbonized, the lid of retort is opened, giant is used
Water spray 6 minutes allows bamboo chip water tariff collection 12%, and the effect of giant water spray exactly allows cooling more uniform.Moisture absorption is more
Add uniformly.Allow bamboo chip water tariff collection 12% or so, if water content is excessively high, bamboo chip is easy mouldy seed piece.If water content mistake
It is low, burning is easy to happen after bamboo chip contact oxygen；(5) it rotates retort 20 minutes again, to reduce bamboo chip temperature and suction
Receive the moisture in retort；(6) bamboo chip is poured out, subsequently into subsequent polishing program.
The color of pigment is resistance to tanned or sun-proof golden yellow in the step (1).
The water content of bamboo chip is detected using moisture detector in the step (2).
Say be the additional proportion of not talcum powder in step (3) to be one thousandth.
The retort carries out combustion heating, environmental protection and energy saving using the waste material bamboo scraps left after production bamboo chip.
Bamboo chip is put into after retort in the step (3), three hours of combustion heating, and in-furnace temperature reaches 135 degree, is protected
Half an hour is held, light bamboo chip is obtained.
Embodiment two
A kind of carbonization summer sleeping bamboo mat production technology, steps are as follows: (1), the bamboo chip of well cutting by dry powder polish nine hours, go
Bamboo is green, and dyestuff is added simultaneously in bruting process, bamboo chip is allowed to have enough time uniform pickup dyestuff, allows and colours more uniform, color
It is more unified, it is bright-coloured；(2), by polishing after bamboo chip, drying bucket in dried, until bamboo chip water content drop to 15% with
Until lower；(3), talcum powder is added on bamboo chip after the drying, keeps bamboo chip more smooth, then by bamboo chip be put into retort into
Row carbonization, is then measured by colour photometer again；(4) after bamboo chip is carbonized, the lid of retort is opened, giant is used
Water spray 5 minutes allows seed piece water tariff collection 12%, and the effect of giant water spray exactly allows cooling more uniform.Moisture absorption is more
Add uniformly.Allow bamboo chip water tariff collection 12% or so, if water content is excessively high, bamboo chip is easy mouldy seed piece.If water content mistake
It is low, burning is easy to happen after bamboo chip contact oxygen；(5) it rotates retort 20 minutes again, to reduce bamboo chip temperature and suction
Receive the moisture in retort；(6) bamboo chip is poured out, subsequently into subsequent polishing program.
The color of pigment is resistance to tanned or sun-proof golden yellow in the step (1).
The water content of bamboo chip is detected using moisture detector in the step (2).
Say be the additional proportion of not talcum powder in step (3) to be one thousandth.
The retort carries out combustion heating, environmental protection and energy saving using the waste material bamboo scraps left after production bamboo chip.
Bamboo chip is put into after retort in the step (3), three hours of combustion heating, and in-furnace temperature reaches 125 degree, is protected
Half an hour is held, light bamboo chip is obtained.
Embodiment three
A kind of carbonization summer sleeping bamboo mat production technology, steps are as follows: (1), the bamboo chip of well cutting by dry powder polish nine hours, go
Bamboo is green, and dyestuff is added simultaneously in bruting process, bamboo chip is allowed to have enough time uniform pickup dyestuff, allows and colours more uniform, color
It is more unified, it is bright-coloured；(2), by polishing after bamboo chip, drying bucket in dried, until bamboo chip water content drop to 15% with
Until lower；(3), talcum powder is added on bamboo chip after the drying, keeps bamboo chip more smooth, then by bamboo chip be put into retort into
Row carbonization, is then measured by colour photometer again；(4) after bamboo chip is carbonized, the lid of retort is opened, giant is used
Water spray 6 minutes allows seed piece water tariff collection 12%, and the effect of giant water spray exactly allows cooling more uniform.Moisture absorption is more
Add uniformly.Allow bamboo chip water tariff collection 12% or so, if water content is excessively high, bamboo chip is easy mouldy seed piece.If water content mistake
It is low, burning is easy to happen after bamboo chip contact oxygen；(5) it rotates retort 20 minutes again, to reduce bamboo chip temperature and suction
Receive the moisture in retort；(6) bamboo chip is poured out, subsequently into subsequent polishing program.
The color of pigment is resistance to tanned or sun-proof golden yellow in the step (1).
The water content of bamboo chip is detected using moisture detector in the step (2).
Say be the additional proportion of not talcum powder in step (3) to be one thousandth.
The retort carries out combustion heating, environmental protection and energy saving using the waste material bamboo scraps left after production bamboo chip.
Bamboo chip is put into after retort in the step (3), three hours of combustion heating, and in-furnace temperature reaches 155 degree, is protected
Half an hour is held, dark bamboo chip is obtained.
Example IV
A kind of carbonization summer sleeping bamboo mat production technology, steps are as follows: (1), the bamboo chip of well cutting by dry powder polish nine hours, go
Bamboo is green, and dyestuff is added simultaneously in bruting process, bamboo chip is allowed to have enough time uniform pickup dyestuff, allows and colours more uniform, color
It is more unified, it is bright-coloured；(2), by polishing after bamboo chip, drying bucket in dried, until bamboo chip water content drop to 15% with
Until lower；(3), talcum powder is added on bamboo chip after the drying, keeps bamboo chip more smooth, then by bamboo chip be put into retort into
Row carbonization, is then measured by colour photometer again；(4) after bamboo chip is carbonized, the lid of retort is opened, giant is used
Water spray 5 minutes allows seed piece water tariff collection 12%, and the effect of giant water spray exactly allows cooling more uniform.Moisture absorption is more
Add uniformly.Allow bamboo chip water tariff collection 12% or so, if water content is excessively high, bamboo chip is easy mouldy seed piece.If water content mistake
It is low, burning is easy to happen after bamboo chip contact oxygen；(5) it rotates retort 20 minutes again, to reduce bamboo chip temperature and suction
Receive the moisture in retort；(6) bamboo chip is poured out, subsequently into subsequent polishing program.
The color of pigment is resistance to tanned or sun-proof golden yellow in the step (1).
The water content of bamboo chip is detected using moisture detector in the step (2).
Say be the additional proportion of not talcum powder in step (3) to be one thousandth.
The retort carries out combustion heating, environmental protection and energy saving using the waste material bamboo scraps left after production bamboo chip.
Bamboo chip is put into after retort in the step (3), three hours of combustion heating, and in-furnace temperature reaches 145 degree, is protected
Half an hour is held, dark bamboo chip is obtained.
Using production technology of the invention, bamboo chip can be to avoid corruption, because surface is by high temperature cabonization by carbonization
Reason, and the color of every batch of is relatively more unified, puts bamboo chip into high-pressure retort and carries out steam charing process, by high temperature height
Pressure, makes surface form hard carbonization particulate layer, meanwhile, bamboo itself also can be harder.It can achieve the effect that except acarid simultaneously！
Meanwhile hard carbonization particle will form bacterium and be not easy living environment, since meeting is harder than common bamboo mat after carbonization, prevent
Bamboo mat surface rapid wear and bamboo pierce problem.Summer sleeping mat after carbonization can adsorb a certain amount of impurity and pernicious gas, thus be meeting
It is easy to overcome bamboo product in conjunction with advanced production technology for raw material for the summer sleeping mat of breathing, above high-quality old bamboo of life in selected 5 years
The difficulty damaged by worms.Has the characteristics that ventilative, nice and cool, not viscous sweat, not curled.It is the indispensable good of summer and autumn high temperature season reducing temperature of heatstroke prevention
Product.Be carbonized summer sleeping mat color is vivid, surface fiber it is fine and smooth it is smooth, density is high, is smooth to the touch, feels more comfortable, allow your refrigerant summer charcoal
Change summer sleeping mat have it is antistatic, anti-fracture, gas permeability is strong, water-resistance is good, the maintenance that is beneficial to human skin, flexibility are good, be suitble to
It is layered on simmons or cushion and uses, it has absorbing carbon dioxide, purifies air, the effect to boost metabolism；It carbonizes cool
Seat has healthcare function, lies and tosses about to squeeze different parts by human body when sitting, plays massage effect, the bamboo chip adsorption capacity after carbonization
It is very strong, taste can be inhaled with absorbing sweat.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (7)
1. a kind of carbonization summer sleeping bamboo mat production technology, which is characterized in that steps are as follows: (1), the bamboo chip of well cutting beats by dry powder
Nine hours are ground, goes bamboo green, dyestuff is added in bruting process simultaneously；(2), the bamboo chip after polishing carries out in drying bucket
Drying, until bamboo chip water content drops to 15% or less；(3), talcum powder is added on bamboo chip after the drying, then by bamboo chip
It is put into retort and is carbonized, then measured again by colour photometer；(4) after bamboo chip is carbonized, retort is opened
Lid is sprayed water 5-6 minutes with giant, allows seed piece water tariff collection 12%；(5) it rotates retort 20 minutes again, to drop
Low bamboo chip temperature and the moisture being absorbed into retort；(6) bamboo chip is poured out, subsequently into subsequent polishing program.
2. a kind of carbonization summer sleeping bamboo mat production technology according to claim 1, which is characterized in that pigment in the step (1)
Color be it is resistance to tanned or sun-proof golden yellow.
3. a kind of carbonization summer sleeping bamboo mat production technology according to claim 2, which is characterized in that bamboo chip in the step (2)
Water content detected using moisture detector.
4. a kind of carbonization summer sleeping bamboo mat production technology according to claim 1, which is characterized in that say it is not sliding in step (3)
The additional proportion of mountain flour is one thousandth.
5. a kind of carbonization summer sleeping bamboo mat production technology according to claim 1, which is characterized in that the retort utilizes production
The waste material bamboo scraps left after bamboo chip carry out combustion heating.
6. a kind of carbonization summer sleeping bamboo mat production technology according to claim 1-5, which is characterized in that the step
(3) bamboo chip is put into after retort in, three hours of combustion heating, and in-furnace temperature reaches 145-155 degree, is kept for half an hour,
Obtain dark bamboo chip.
7. a kind of carbonization summer sleeping bamboo mat production technology according to claim 1-5, which is characterized in that the step
(3) bamboo chip is put into after retort in, three hours of combustion heating, and in-furnace temperature reaches 125-135 degree, is kept for half an hour,
Obtain light bamboo chip.