CN110016755A - 一种防雷击安全网及其制作方法 - Google Patents
一种防雷击安全网及其制作方法 Download PDFInfo
- Publication number
- CN110016755A CN110016755A CN201910349030.6A CN201910349030A CN110016755A CN 110016755 A CN110016755 A CN 110016755A CN 201910349030 A CN201910349030 A CN 201910349030A CN 110016755 A CN110016755 A CN 110016755A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fiber
- compliant conductive
- flexible reinforced
- resistivity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种防雷击安全网机器制作方法,涉及安全防护网领域,采用线密度占比≥70%的柔性增强纤维(2)和线密度占比≤30%的柔性导电纤维(1)复合纱线经编成网,并且所述柔性导电纤维(1)包覆于柔性增强纤维(2)外层,其中所述柔性增强纤维(2)设置为电阻率R2≥1010Ω/m、强度F2≥18cN/dtex;所述柔性导电纤维(1)设置为电阻率R1≤106Ω/m、强度F1满足4cN/dtex≤F1≤7cN/dtex、伸长率E1≥20%。本发明对网体本身结构及材料使用进行改进,并设计了相对应的制作方法,防雷击效果好,安全性高,可根据被覆盖物形状不同进行拼接或搭接,便于携带和施工,可重复使用。
Description
技术领域
本发明涉及安全防护网领域,具体地说是一种防雷击安全网及其制作方法,主要用于多雷区的建筑施工场地、养殖基地、电路设施等民用设施的雷击防护。
背景技术
中国地处温带和亚热带地区,雷电灾害是中国最严重的自然灾害之一,具有发生频次高、突发性强、危害严重、范围广的特点。全国每年因雷电可以造成上千人的人身伤害以及巨大的经济损失,因此在多雷区及雷雨天做好防雷工作,是安全生产不可缺少的重要环节。现有防雷技术多采用避雷针引导雷电流泄放,避雷针的接地线为了可靠接地通常采用大量金属构件深埋地下,安装施工复杂,一次性投入成本较高,位置不可移动,不适用于很多领域。
例如:专利号2018204465567、名称为“一种防雷击通信光缆”,主要的保护措施是聚氯乙烯保护套,外表面通过高吸水性树脂与屏蔽层内壁固定连接,屏蔽层的外表面桃姐有阻燃聚氯乙烯;专利号2017214405479、名称为“一种建筑设备防雷击保护网”,主要设计了防雷击装置,保护防雷击装置的结构,保护网采用的是普通的防护网,在受到雷击时防雷击装置会将雷电通入地下将雷击效果消除;申请号号2018106923102、名称为“一种建筑设备防雷击保护网”,也是并未对保护网本体的结构进行改进,而是通过其他结构实现防护网的高度可调;专利号2015209378063、名称为“一种建筑设备防雷击保护网”,通过接闪器、避雷针、隔雷导线、避雷球等结构的组合实现更好的防雷击效果,同样未对防护网本身进行改进。
因此,行业内急需一种安装携带方便,成本低廉,可拆卸、折叠变形的防雷击安全防护网。
发明内容
为解决上述存在的技术问题,本发明提供了一种防雷击安全网及其制作方法,对网体本身结构及材料使用进行改进,并设计了相对应的制作方法,防雷击效果好,安全性高,可根据被覆盖物形状不同进行拼接或搭接,便于携带和施工,可重复使用。
本发明解决其技术问题采用的技术方案是:
一种防雷击安全网,采用线密度占比≥70%的柔性增强纤维和线密度占比≤30%的柔性导电纤维复合纱线经编成网,并且所述柔性导电纤维包覆于柔性增强纤维外层,其中所述柔性增强纤维设置为电阻率R2≥1010Ω/m、强度F2≥18cN/dtex;所述柔性导电纤维设置为电阻率R1≤106Ω/m、强度F1满足4cN/dtex≤F1≤7cN/dtex、伸长率E1≥20%。
所述柔性增强纤维采用芳纶纤维,线密度Nd满足400D≤Nd≤1000D,所述柔性导电纤维采用尼龙复合石墨烯单丝,线密度Ny满足320D≤Ny≤2000D。
一种防雷击安全网的制作方法,通过如下步骤实现:
1)制备柔性增强纤维的纱线,将一定量的阻燃耐高温的柔性增强纤维复丝通过捻线机加捻,制成纱线,纱线捻度T2为80≤T2≤100捻/m,纱线捻向为Z向;
2)制备柔性导电纤维的纱线,将一定量的柔性导电纤维单丝通过并线机并线,并线后施加一定弱捻,弱捻捻度T1满足20≤T1≤30捻/m,捻向为Z向,束丝电阻率R与单丝根数n应满足下列关系:R=R1/n,R1为柔性导电纤维的电阻率,且R≤106;
3)制备复合纱线,将上述步骤1)和步骤2)制备的两种纱线按照S向进行复合,实现柔性导电纤维纱线对柔性增强纤维纱线的包缠,保证纱线的导电层位于外层,复合纱线捻度T0范围为40≤T0≤60捻/m;
4)制作盘头,将若干步骤3)制备的复合纱线安装在等张力纱架上,规则穿入整经板,平行的卷绕在整经机盘头上,保证张力均匀,纱线张力F控制在2N≤F≤15N,按照安全网的横向宽度,确定制作盘头的数量;
5)经编成网,将规定数量的盘头安装到经编网机上,卷曲密度为2-15横列/cm,针距为每英寸8-16针,丝线平行穿过送经、梳栉、针板,相互串套衬垫成网目内径2cm≤D≤5cm的网体。
本发明与传统的防雷击防护网相比,具有如下有益效果:
1)对网体本身进行改进,结构更加简单,使用更加方便、灵活性强,可根据使用工况,不同的被覆盖物形状进行网片的拼接与搭接,便于施工和拆除,一次性投入低,并可重复使用;
2)柔性增强纤维使得网的基体具有较高的强度和柔韧性,耐久性更强,柔性导电纤维和柔性增强纤维经编成网的特殊结构,使得导电材料在整张网上是并联结构,大大降低了导电材料的电阻与用量,提高了导电效率;
3)网的基体采用柔性增强材料,不会产生融化、燃烧的情况,安全性更高,防雷击效果更好;
4)制作方法上采用经编成圈的方式成网,无网结,网目直径大,在自然环境下的风阻力小,避免因大风产生倾倒或损坏现象,大大延长了安全网的使用寿命。
附图说明
图1为本发明结构示意图;
图2为柔性增强材料与柔性导电材料具体结构示意图。
具体实施方式
下面结合附图和具体实施例对本发明进行详细描述:
如图1-2所示,一种防雷击安全网,采用线密度占比≥70%的柔性增强纤维2和线密度占比≤30%的柔性导电纤维1复合纱线经编成网,,并且所述柔性导电纤维1包覆于柔性增强纤维2外层,其中所述柔性增强纤维2设置为电阻率R2≥1010Ω/m、强度F2≥18cN/dtex;所述柔性导电纤维1设置为电阻率R1≤106Ω/m、强度F1满足4cN/dtex≤F1≤7cN/dtex、伸长率E1≥20%。
所述柔性增强纤维2采用芳纶纤维,线密度Nd满足400D≤Nd≤1000D,所述柔性导电纤维1采用尼龙复合石墨烯单丝,线密度Ny满足320D≤Ny≤2000D。
一种防雷击安全网的制作方法,通过如下步骤实现:
1)制备柔性增强纤维2的纱线,将一定量的阻燃耐高温的柔性增强纤维2复丝通过捻线机加捻,制成纱线,纱线捻度T2为80≤T2≤100捻/m,纱线捻向为Z向;
2)制备柔性导电纤维1的纱线,将一定量的柔性导电纤维1单丝通过并线机并线,并线后施加一定弱捻,弱捻捻度T1满足20≤T1≤30捻/m,捻向为Z向,束丝电阻率R与单丝根数n应满足下列关系:R=R1/n,R1为柔性导电纤维1的电阻率,且R≤106;
3)制备复合纱线,将上述步骤1)和步骤2)制备的两种纱线按照S向进行复合,实现柔性导电纤维1纱线对柔性增强纤维2纱线的包缠,保证纱线的导电层位于外层,复合纱线捻度T0范围为40≤T0≤60捻/m;
4)制作盘头,将若干步骤3)制备的复合纱线安装在等张力纱架上,规则穿入整经板,平行的卷绕在整经机盘头上,保证张力均匀,纱线张力F控制在2N≤F≤15N,按照安全网的横向宽度,确定制作盘头的数量;
5)经编成网,将规定数量的盘头安装到经编网机上,卷曲密度为2-15横列/cm,针距为每英寸8-16针,丝线平行穿过送经、梳栉、针板,相互串套衬垫成网目内径2cm≤D≤5cm的网体。
实施例1:
1)制备柔性增强纤维2的纱线:选取Nd=400D的芳纶纤维,强度F2=18cN/dtex,电阻率R2=1010Ω/m,将20根芳纶纤维复丝通过捻线机加捻,制成纱线,纱线捻度T2=100捻/m,纱线捻向为Z向,制成的纱线线密度为0.9g/m;
2)制备柔性导电纤维1的纱线,选取Ny=320D尼龙复合石墨烯单丝,强度F1=4cN/dtex,伸长率E1=20%,电阻率R1=106Ω/m,将3根尼龙复合石墨烯单丝通过并线机并线,并线后施加弱捻T1=20捻/m,捻向为Z向,制成的纱线线密度为0.12g/m,束丝电阻率R=3×105;
3)制备复合纱线,将上述步骤1)和步骤2)制备的两种纱线按照S向进行复合,使用分线盘穿线,将芳纶纤维纱线处于分线盘中心,尼龙复合石墨烯纤维纱线在分线盘中心外侧,实现尼龙复合石墨烯纤维纱线对芳纶维纱线的包缠,保证纱线的导电层位于外层,复合纱线捻度T0=60捻/m,柔性增强材料占比89%;
4)制作盘头,将100根步骤3)制备的复合纱线安装在等张力纱架上,规则穿入整经板,平行的卷绕在整经机盘头上,保证张力均匀,纱线张力F=2N,按照安全网的2米的横向宽度,制作16个盘头;
5)经编成网,将16个盘头安装到经编网机上,按照目脚长度1cm设置,卷曲密度为2横列/cm,针距为每英寸16针,丝线平行穿过送经、梳栉、针板,相互串套衬垫成网目内径D=2cm的网体,该网体的断裂强力4.8KN,电阻率为1.9×102Ω/m。
实施例2:
1)制备柔性增强纤维2的纱线:选取Nd=1000D的芳纶纤维,强度F2=20cN/dtex,电阻率R2=2×1010Ω/m,将20根芳纶纤维复丝通过捻线机加捻,制成纱线,纱线捻度为T2=80捻/m,纱线捻向为Z向,制成的纱线线密度为2.4g/m;
2)制备柔性导电纤维1的纱线,选取Ny=2000D尼龙复合石墨烯单丝,强度F1=7cN/dtex,伸长率E1=25%,电阻率R1=0.4×106Ω/m,将2根尼龙复合石墨烯单丝通过并线机并线,并线后施加弱捻T1=30捻/m的,捻向为Z向,制成的纱线线密度为0.44g/m,束丝电阻率R=0.2×106;
3)制备复合纱线,将上述步骤1)和步骤2)制备的两种纱线按照S向进行复合,使用分线盘穿线,将芳纶纤维纱线处于分线盘中心,尼龙复合石墨烯纤维纱线在分线盘中心外侧,实现尼龙复合石墨烯纤维纱线对芳纶维纱线的包缠,保证纱线的导电层位于外层,复合纱线捻度T0=40捻/m,柔性增强材料占比70%;
4)制作盘头,将80根步骤3)制备的复合纱线安装在等张力纱架上,规则穿入整经板,平行的卷绕在整经机盘头上,保证张力均匀,纱线F=15N,按照安全网的4米的横向宽度,制作8个盘头;
5)经编成网,将8个盘头安装到经编网机上,按照目脚长度2.5cm设置,卷曲密度为15横列/cm,针距为每英寸8针,丝线平行穿过送经、梳栉、针板,相互串套衬垫成网目内径D=5cm的网体,该网体的断裂强力13KN,电阻率为3.1×102Ω/m。
实施例3:
1)制备柔性增强纤维2的纱线:选取Nd=800D的芳纶纤维,强度F2=22cN/dtex,电阻率R2=1.5×1010Ω/m,将20根芳纶纤维复丝通过捻线机加捻,制成纱线,纱线捻度T2=90捻/m,纱线捻向为Z向,制成的纱线线密度为1.8g/m;
2)制备柔性导电纤维1的纱线,选取Ny=1200D尼龙复合石墨烯单丝,强度F1=5cN/dtex,伸长率E1=30%,电阻率R1=0.6×106Ω/m,将3根尼龙复合石墨烯单丝通过并线机并线,并线后施加弱捻T1=25捻/m的,捻向为Z向,制成的纱线线密度为0.4g/m,束丝电阻率R=106;
3)制备复合纱线,将上述步骤1)和步骤2)制备的两种纱线按照S向进行复合,使用分线盘穿线,将芳纶纤维纱线出国分线盘中心,尼龙复合石墨烯纤维纱线在分线盘中心外侧,实现尼龙复合石墨烯纤维纱线对芳纶维纱线的包缠,保证纱线的导电层位于外层,复合纱线捻度T0=50捻/m,柔性增强材料占比82%;
4)制作盘头,将120根步骤3)制备的复合纱线安装在等张力纱架上,规则穿入整经板,平行的卷绕在整经机盘头上,保证张力均匀,纱线张力F=10N之间,按照安全网的2米的横向宽度,制作8个盘头;
5)经编成网,将8个盘头安装到经编网机上,按照目脚长度1.5cm设置,卷曲密度为8横列/cm,针距为每英寸10针,丝线平行穿过送经、梳栉、针板,相互串套衬垫成D=3cm的网体,该网体的断裂强力11.6KN,电阻率为2.1×102Ω/m。
当然,上述说明并非是对本发明的限制,本发明也并不仅限于上述举例,本技术领域的技术人员在本发明的实质范围内所做出的变化、改型、添加或替换,也应属于本发明的保护范围。
Claims (3)
1.一种防雷击安全网,其特征在于,采用线密度占比≥70%的柔性增强纤维(2)和线密度占比≤30%的柔性导电纤维(1)复合纱线经编成网,并且所述柔性导电纤维(1)包覆于柔性增强纤维(2)外层,其中所述柔性增强纤维(2)设置为电阻率R2≥1010Ω/m、强度F2≥18cN/dtex;所述柔性导电纤维(1)设置为电阻率R1≤106Ω/m、强度F1满足4cN/dtex≤F1≤7cN/dtex、伸长率E1≥20%。
2.根据权利要求1所述的一种防雷击安全网,其特征在于,所述柔性增强纤维(2)采用芳纶纤维,线密度Nd满足400D≤Nd≤1000D,所述柔性导电纤维(1)采用尼龙复合石墨烯单丝,线密度Ny满足320D≤Ny≤2000D。
3.一种如权利要求1所述的防雷击安全网的制作方法,其特征在于,通过如下步骤实现:
1)制备柔性增强纤维(2)的纱线,将一定量的阻燃耐高温的柔性增强纤维复丝通过捻线机加捻,制成纱线,纱线捻度T2为80≤T2≤100捻/m,纱线捻向为Z向;
2)制备柔性导电纤维(1)的纱线,将一定量的柔性导电纤维单丝通过并线机并线,并线后施加一定弱捻,弱捻捻度T1满足20≤T1≤30捻/m,捻向为Z向,束丝电阻率R与单丝根数n应满足下列关系:R=R1/n,R1为柔性导电纤维(1)的电阻率,且R≤106;
3)制备复合纱线,将上述步骤1)和步骤2)制备的两种纱线按照S向进行复合,实现柔性导电纤维纱线对柔性增强纤维纱线的包缠,保证纱线的导电层位于外层,复合纱线捻度T0范围为40≤T0≤60捻/m;
4)制作盘头,将若干步骤3)制备的复合纱线安装在等张力纱架上,规则穿入整经板,平行的卷绕在整经机盘头上,保证张力均匀,纱线张力F控制在2N≤F≤15N,按照安全网的横向宽度,确定制作盘头的数量;
5)经编成网,将规定数量的盘头安装到经编网机上,卷曲密度为2-15横列/cm,针距为每英寸8-16针,丝线平行穿过送经、梳栉、针板,相互串套衬垫成网目内径2cm≤D≤5cm的网体。