CN110003972A - A kind of easy cleaning stainless steel tapping oil - Google Patents
A kind of easy cleaning stainless steel tapping oil Download PDFInfo
- Publication number
- CN110003972A CN110003972A CN201910298853.0A CN201910298853A CN110003972A CN 110003972 A CN110003972 A CN 110003972A CN 201910298853 A CN201910298853 A CN 201910298853A CN 110003972 A CN110003972 A CN 110003972A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- emulsifier
- tapping
- stainless steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of easy cleaning stainless steel tapping oils, all raw materials and parts by weight are as follows: 10-15 parts of emulsifier, 5-10 parts of pentaerythritol oleate, 20-30 parts of chlorinated paraffin, 3-5 parts of olefine sulfide (Lu Borun 2540), 5-10 parts of sulfurized lard (light color), 3-5 parts of petroleum sodium sulfonate, 0.1-0.3 parts of defoaming agent and the nonstandard machinery oil of 32# or 24.9-53.9 parts of 32# base oil.The easy cleaning stainless steel tapping oil, due to the presence of emulsifier, so that tapping oil not only has the oily matter of good lubrication effect, and add wear-resistant substance and surfactant, layer protecting film can not only be formed in metal surface, and there is good cleaning, it is also easy to remove after processing, it ensure that the cleaning of operating environment, sulfurized lard and chlorinated paraffin etc. enhance wear-resistant, dispersion and lubricity, pentaerythritol oleate increases the film forming of tapping oil, petroleum sodium sulfonate and emulsifier contain antirust component, protect equipment, prolong the service life, it is watered use, enterprise is reduced with oily cost.
Description
Technical field
The present invention relates to tapping oils to produce correlative technology field, specially a kind of easy cleaning stainless steel tapping oil.
Background technique
Metal tapping, which refers to, is rotated into screw tap in the bottom outlet to be bored with certain torque, so that processing in bottom outlet
A kind of processing method of inside spin identical with screw tap surface, and when the surface of stainless steel carries out tapping, compared to more general
Logical steel, stainless steel often will appear that torque is excessive, and screw tap " being killed " is controlled in screw thread during carrying out tapping,
It collapses tooth or fractures, not only, rill dimension overproof, disorderly button and the phenomenon that screw tap serious wear occur thread surface, while tapping
Chip is acted on rake face with the pressure for being up to 2~3GPa, and is flowed out with higher speed along rake face, between cutter and workpiece
Friction generate heat tapping machining area temperature can be made to rise to 1000 DEG C or more, threading tool and surface irregularity place phase
The tapping cutting pressure of the contact point of contact can make surface loading at this reach 5000N/mm2, therefore, processed in metal tapping
It just needs to cause office when preventing tapping from cutting using the tapping liquid with excellent lubricity, cooling and rust-preventing characteristic in journey
The serious Welding Phenomena in portion, although however the type of the tapping oil on existing market with it is large number of, it is normally made
During or there is some problems；
1, the tapping oil on existing market cannot well protect metallic surface after the completion of carrying out use,
And after the completion of to tapping oil use, work cannot be removed to it well, so that whole operation environment is affected；
2, traditional tapping oil wear resistence, dispersibility and lubricity during carrying out use cannot all protect well
Card, and entire tapping oil cannot carry out protection work to equipment well, cause the top of equipment that can go out after the completion of use
The phenomenon for now getting rusty serious occurs；
Therefore, we just propose a kind of easy cleaned tapping oil conveniently to solve the above problems.
Summary of the invention
The purpose of the present invention is to provide a kind of easy cleaning stainless steel tapping oils, to solve to propose in above-mentioned background technique to attack
Silk oil cannot well protect metallic surface during carrying out use, can not easily be removed work,
And wear resistence, dispersibility and lubricity the problem of cannot all guaranteeing well.
To achieve the above object, the invention provides the following technical scheme: a kind of easy cleaning stainless steel tapping oil, described all
Raw material and parts by weight are as follows: 10-15 parts of emulsifier, 5-10 parts of pentaerythritol oleate, 20-30 parts of chlorinated paraffin, olefine sulfide
3-5 parts of (Lu Borun 2540), 5-10 parts of sulfurized lard (light color), 3-5 parts of petroleum sodium sulfonate, 0.1-0.3 parts of defoaming agent and 32# are non-
Mark machinery oil or 24.9-53.9 parts of 32# base oil.
Preferably, all raw materials and weight percent are as follows: emulsifier 13.3-32.5%, pentaerythritol oleate
6.7-21.7%, chlorinated paraffin 26.6-65.1%, olefine sulfide (Lu Borun 2540) 3.4-10.8%, sulfurized lard (light color)
6.7-21.7%, petroleum sodium sulfonate 3.4-10.8%, the nonstandard machinery oil of defoaming agent 1-2% and 32# or 32# base oil 33.1-
116.9%.
Preferably, the chlorinated paraffin is chlorinated paraffin 52.
Preferably, the appearance of the emulsifier is brown viscous liquid, and its internal solid content is less than 99%, emulsifier
Density be 1.05g/ DEG C of m^3, and pH range of the emulsifier in 1% aqueous solution is 8-10, while the stabilization of emulsifier
Property the time be 2 years, emulsifier DX821.
Preferably, the procedure of processing of the tapping oil is as follows:
Step 1: it will be needed in entire modulated process using emulsifier, pentaerythritol oleate, chlorinated paraffin, the sulphur arrived
Change alkene (Lu Borun 2540), sulfurized lard (light color), petroleum sodium sulfonate, defoaming agent and the nonstandard machinery oil of 32# or 32# base oil
It matches and completes according to aforementioned proportion；
Step 2: by 5-10 parts of pentaerythritol oleate after the completion of modulation, 20-30 parts of chlorinated paraffin, olefine sulfide (road
2540) 3-5 parts of rich profit, 5-10 parts of sulfurized lard (light color) and 32# base oil or nonstandard machinery oil carry out hybrid working in proportion,
It controls the temperature inside entire mixed stirring device and is in 40-60 DEG C, above-mentioned principle is stirred 30 in 40-60 DEG C of device
After minute, stop stirring work；
Step 3: 0.1-0.3 parts of defoaming agent, petroleum after the completion of modulation are added in the mixed liquor after above-mentioned be stirred
3-5 parts of sodium sulfonate and compound emulsifying agent 10-15 part are added to the inside of entire agitating device, then proceed to entire mixing
Temperature inside device is controlled, so that the temperature inside device is controlled at 50-60 DEG C, starter continues to device
Inside is stirred work, and control mixing time is 1-2 hours；
Step 4: during raw material is added in step 3, can according to entire tapping oil later process cleaning,
10-15 times of clear water is added in the inside of whole device, and then, repeat the above steps the temperature and time control to processing, whole
The inside of a device is stirred work；
Step 5: after entire Beater operator is made, entire agitating device is closed, the tapping after being formed is stirred to device inside
Oil carries out cooling work, is carrying out tinning work to it after the completion of cooling, so that it may pack to tapping oil and sell and make
With.
Compared with prior art, the beneficial effects of the present invention are: the easy cleaning stainless steel tapping oil, due to depositing for emulsifier
So that tapping oil not only has the oily matter of good lubrication effect, but also wear-resistant substance and surfactant are being added, no
Only layer protecting film can be formed in metal surface, and there is good cleaning, be also easy to remove after processing, ensure that
The cleaning of operating environment, sulfurized lard and chlorinated paraffin etc. enhance wear-resistant, dispersion and lubricity, and pentaerythritol oleate increases
The film forming of tapping oil, petroleum sodium sulfonate and emulsifier contain antirust component, protect equipment, prolong the service life, be watered
It uses, reduces enterprise with oily cost.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The present invention provides a kind of technical solution: a kind of easy cleaning stainless steel tapping oil, all raw materials and parts by weight are as follows: cream
10-15 parts of agent, 5-10 parts of pentaerythritol oleate, 20-30 parts of chlorinated paraffin, 3-5 parts of olefine sulfide (Lu Borun 2540), sulphur
Change 5-10 parts of lard (light color), 3-5 parts of petroleum sodium sulfonate, 0.1-0.3 parts of defoaming agent and the nonstandard machinery oil of 32# or 32# base oil
24.9-53.9 parts.
All raw materials and weight percent are as follows: emulsifier 13.3-32.5%, pentaerythritol oleate 6.7-21.7%,
Chlorinated paraffin 26.6-65.1%, olefine sulfide (Lu Borun 2540) 3.4-10.8%, sulfurized lard (light color) 6.7-21.7%,
The nonstandard machinery oil of petroleum sodium sulfonate 3.4-10.8%, defoaming agent 1-2% and 32# or 32# base oil 33.1-116.9%.
Chlorinated paraffin is chlorinated paraffin 52, chlorinated paraffin.
The appearance of emulsifier is brown viscous liquid, and its internal solid content, less than 99%, the density of emulsifier is
1.05g/ DEG C of m^3, and pH range of the emulsifier in 1% aqueous solution is 8-10, while the stability time of emulsifier is
2 years, emulsifier DX821, the compound active agent on a variety of surfaces, dispersion performance was excellent, suitable for the cream under oil based system
Liquid is applicable in the emulsifier that mineral oil is made in the field of metal processing, can emulsify base oil well, emulsification, profit are played in system
Cunning, antirust, cleaning and the effect of thickening ensure that the cleaning of operating environment so that later process is readily cleaned.
The procedure of processing of tapping oil is as follows:
Step 1: it will be needed in entire modulated process using emulsifier, pentaerythritol oleate, chlorinated paraffin, the sulphur arrived
Change alkene (Lu Borun 2540), sulfurized lard (light color), petroleum sodium sulfonate, defoaming agent and the nonstandard machinery oil of 32# or 32# base oil
It matches and completes according to aforementioned proportion；
Step 2: by 5-10 parts of pentaerythritol oleate after the completion of modulation, 20-30 parts of chlorinated paraffin, olefine sulfide (road
2540) 3-5 parts of rich profit, 5-10 parts of sulfurized lard (light color) and 32# base oil or nonstandard machinery oil carry out hybrid working in proportion,
It controls the temperature inside entire mixed stirring device and is in 40-60 DEG C, above-mentioned principle is stirred 30 in 40-60 DEG C of device
After minute, stop stirring work；
Step 3: 0.1-0.3 parts of defoaming agent, petroleum after the completion of modulation are added in the mixed liquor after above-mentioned be stirred
3-5 parts of sodium sulfonate and compound emulsifying agent 10-15 part are added to the inside of entire agitating device, then proceed to entire mixing
Temperature inside device is controlled, so that the temperature inside device is controlled at 50-60 DEG C, starter continues to device
Inside is stirred work, and control mixing time is 1-2 hours；
Step 4: during raw material is added in step 3, can according to entire tapping oil later process cleaning,
10-15 times of clear water is added in the inside of whole device, and then, repeat the above steps the temperature and time control to processing, whole
The inside of a device is stirred work, is watered use, reduces the oily cost of enterprise, meets the requirement of environmental protection；
Step 5: after entire Beater operator is made, entire agitating device is closed, the tapping after being formed is stirred to device inside
Oil carries out cooling work, is carrying out tinning work to it after the completion of cooling, so that it may pack to tapping oil and sell and make
With.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (5)
1. a kind of easy cleaning stainless steel tapping oil, it is characterised in that: all raw materials and parts by weight are as follows: emulsifier 10-15
Part, 5-10 parts of pentaerythritol oleate, 20-30 parts of chlorinated paraffin, 3-5 parts of olefine sulfide (Lu Borun 2540), sulfurized lard are (shallow
Color) 5-10 parts, 3-5 parts of petroleum sodium sulfonate, 0.1-0.3 parts of defoaming agent and the nonstandard machinery oil of 32# or 32# base oil 24.9-53.9
Part.
2. a kind of easy cleaning stainless steel tapping oil according to claim 1, it is characterised in that: all raw materials and weight
Percentage is as follows: emulsifier 13.3-32.5%, pentaerythritol oleate 6.7-21.7%, chlorinated paraffin 26.6-65.1%, sulphur
Change alkene (Lu Borun 2540) 3.4-10.8%, sulfurized lard (light color) 6.7-21.7%, petroleum sodium sulfonate 3.4-10.8%, disappears
The nonstandard machinery oil of infusion 1-2% and 32# or 32# base oil 33.1-116.9%.
3. a kind of easy cleaning stainless steel tapping oil according to claim 1, it is characterised in that: the chlorinated paraffin is chlorination
Paraffin 52.
4. a kind of easy cleaning stainless steel tapping oil according to claim 1, it is characterised in that: the appearance of the emulsifier is
Brown viscous liquid, and its internal solid content, less than 99%, the density of emulsifier is 1.05g/ DEG C of m^3, and emulsifier exists
PH range in 1% aqueous solution is 8-10, while the stability time of emulsifier is 2 years, emulsifier DX821.
5. a kind of modulator approach of easy cleaning stainless steel tapping oil according to claim 1, it is characterised in that: the tapping
The procedure of processing of oil is as follows:
Step 1: it will be needed in entire modulated process using emulsifier, pentaerythritol oleate, chlorinated paraffin, the vulcanization alkene arrived
Hydrocarbon (Lu Borun 2540), sulfurized lard (light color), petroleum sodium sulfonate, defoaming agent and the nonstandard machinery oil of 32# or 32# base oil according to
Aforementioned proportion proportion is completed；
Step 2: by 5-10 parts of pentaerythritol oleate after the completion of modulation, 20-30 parts of chlorinated paraffin, olefine sulfide (Lu Borun
2540) 3-5 parts, 5-10 parts of sulfurized lard (light color) and 32# base oil or nonstandard machinery oil carry out hybrid working in proportion, control
Temperature inside entire mixed stirring device is in 40-60 DEG C, and above-mentioned principle is stirred 30 minutes in 40-60 DEG C of device
Afterwards, stop stirring work；
Step 3: 0.1-0.3 parts of defoaming agent, mahogany acid after the completion of modulation are added in the mixed liquor after above-mentioned be stirred
3-5 parts of sodium and compound emulsifying agent 10-15 parts are added to the inside of entire agitating device, then proceed to entire mixed stirring device
Internal temperature is controlled, so that the temperature inside device is controlled at 50-60 DEG C, starter continues the inside to device
It is stirred work, control mixing time is 1-2 hours；
Step 4:, can be according to entire tapping oil later process cleaning, entire during raw material is added in step 3
10-15 times of clear water is added in the inside of device, and then, repeat the above steps the temperature and time control to processing, is entirely filling
The inside set is stirred work；
Step 5: after entire Beater operator is made, closing entire agitating device, to device inside stir the tapping oil after being formed into
Row cooling work is carrying out tinning work to it after the completion of cooling, so that it may carry out packaging to tapping oil and sell and use.