CN109994745A - A kind of fullerene grafting grapheme material loaded palladium catalyst and its preparation and application - Google Patents
A kind of fullerene grafting grapheme material loaded palladium catalyst and its preparation and application Download PDFInfo
- Publication number
- CN109994745A CN109994745A CN201910265553.2A CN201910265553A CN109994745A CN 109994745 A CN109994745 A CN 109994745A CN 201910265553 A CN201910265553 A CN 201910265553A CN 109994745 A CN109994745 A CN 109994745A
- Authority
- CN
- China
- Prior art keywords
- fullerene
- solvent
- grafting
- grapheme material
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of fullerene grafting grapheme material loaded palladium catalyst and its preparations and application.The catalyst is using the fulleropyrrolidine derivative of amino functional and graphene composite material as carrier.The preparation method includes: the fulleropyrrolidine derivative preparation of nitro functionalization, the fulleropyrrolidine derivative preparation of amino functional, fullerene grafting grapheme material preparation, fullerene grafting grapheme material loaded palladium catalyst preparation.The catalytic activity and stability that the catalyst has had have potential application foreground in a fuel cell.
Description
Technical field
The invention belongs to fuel-cell catalyst and its preparation and application field, in particular to a kind of fullerene grafts graphite
Alkene material load palladium catalyst and its preparation method and application.
Background technique
Fuel cell is one of the clean energy resource quickly grown in recent years.Due to being related to precious metal catalyst in fuel cell
Agent, therefore at high cost is always to restrict its a wide range of commercialized main bottleneck.In order to reduce cost and improve precious metal catalyst
The effective use of agent, currently used method are that noble metal catalyst is loaded to carbon material surface.In many carbon materials,
Emerging nano-carbon material such as carbon nanotube, graphene and fullerene-based material are in fuel-cell catalyst carrier application aspect
Huge potentiality are shown.Typically by single nano-carbon material be used as carrier come improve catalyst performance and reduce at
This, it is still less as the research of carrier using composite Nano carbon material.It discloses and passes through application No. is 201710409807.4 patents
Fullerene-graphene three-dimensional composite material loaded palladium catalyst that non-covalent bond self assembly obtains, shows than single carrier
The more superior catalytic performance of catalyst.It can be seen that developing composite Nano carbon carrier is one of the effective way for improving catalytic performance.
But the carrier material stability combined between fullerene and graphene by weak non-covalent bond effect is poor, it is difficult to effectively overcome
The stronger accumulation trend of graphene, therefore further exploring undoubtedly will be advantageous in graphene surface by covalent bond grafting fullerene
In the dispersion of graphene, and the catalytic performance of catalyst is improved in turn.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of fullerene grafting grapheme material loaded palladium catalyst and
Preparation method and application, to overcome the defect that palladium catalyst catalysis methanol oxidation activity is inadequate in the prior art.
The present invention provides a kind of fullerene grafting grapheme material loaded palladium catalyst, with the fullerene pyrrole of amino functional
It coughs up alkane derivatives and graphene composite material is carrier, the structural formula of the fulleropyrrolidine derivative of the amino functional
Are as follows:N=1~5 in formula.
The carrier is heated in a solvent instead by the fulleropyrrolidine derivative and graphene oxide of amino functional
Should after restore to obtain.
The present invention also provides a kind of preparation methods of fullerene grafting grapheme material loaded palladium catalyst, comprising:
(1) by fullerene C under condition of nitrogen gas60, paranitrobenzaldehyde and sarcosine with mass ratio be 0.8-1.2:1.8-
2.2:1.8-2.2 reacts in a solvent, cooling, and separating-purifying obtains the fulleropyrrolidine derivative of nitro functionalization, wherein
Fullerene C60Ratio with solvent is 60-80mg:40-50mL;
(2) fulleropyrrolidine derivative of nitro functionalization in step (1) is dissolved in solvent, it is anti-that reducing agent is added
It answers, lower layer's solution that liquid separation obtains adjusts pH to neutrality, filters, washs, drying obtains the fullerene chemistry of amino functional
Derivative, wherein the ratio of the fulleropyrrolidine derivative, reducing agent and solvent of nitro functionalization is 95-105mg:250-
300mg:95-105mL;
(3) by the fulleropyrrolidine derivative of amino functional in step (2) and graphene oxide with mass ratio for 1:
6-10 disperses in a solvent, and 80-100 DEG C of reaction 36-48h under condition of nitrogen gas is cooling, centrifuge separation, obtains fullerene grafting stone
Black alkene material, wherein the ratio of graphene oxide and solvent is 15-25mg:15-25mL;
(4) fullerene grafting grapheme material in step (3) is dispersed in water, palladium chloride aqueous solution, ultrasound vibration is added
It swings, reducing agent solution is added, is stirred to react, be centrifugated, washing obtains fullerene grafting grapheme material load palladium catalysis
Agent, wherein the mass ratio of carrier and palladium is 4-6:1 in catalyst, and it is 15- that fullerene, which grafts grapheme material and the ratio of water,
25mg:30mL。
Solvent is toluene in the step (1).
Reaction temperature is 100-120 DEG C in the step (1), reaction time 12-16h.
The fulleropyrrolidine derivative structural formula of nitro functionalization in the step (1) are as follows:
N is 1~5 in formula.
Separating-purifying uses silica gel column chromatography in the step (1), and wherein eluant, eluent is toluene/ethanol (5:1).
Solvent is the toluene and alcohol mixed solvent of volume ratio 1.8-2.2:1 in the step (2).
Reducing agent is stannous chloride in the step (2).
Reaction temperature is room temperature, reaction time 10-15h in the step (2).
Solvent is dimethyl sulfoxide in the step (3);Graphene oxide is prepared using Hummers method.
Reducing agent is sodium borohydride, while redox graphene and palladium ion in the step (4).
The sonic oscillation time is 25-35min in the step (4).
It is room temperature that temperature is stirred to react in the step (4), and being stirred to react the time is 10-15h.
The present invention also provides a kind of fullerenes to graft grapheme material loaded palladium catalyst answering in methanol fuel cell
With.
The electrochemical workstation that electrocatalysis characteristic test utilizes in the application is CHI 660D, and potential scanning speed is
50mV/s, electric potential scanning range are -1~0.2V;Working electrode is glass-carbon electrode, is platinum electrode to electrode, and reference electrode is
Saturated calomel electrode (SCE), electrolyte are 1.0M CH3OH+1.0M NaOH solution.
Beneficial effect
(1) compared with the patent application No. is 201710409807.4, the present invention is grafted rich by strong covalent bond effect
Alkene is strangled in graphene surface overcomes the poor dispersion of graphene in the former the shortcomings that, and is conducive to improve the catalysis of catalyst in turn
Performance;
(2) preparation method of the present invention is easy, and it is negative to be prepared for fullerene grafting grapheme material by room temperature chemical reduction method
Carry the new fuel cell catalyst of palladium;
(3) fullerene grafting grapheme material prepared by the present invention has compared with by the palladium catalyst of carrier of simple graphene
More superior catalytic performance has potential application foreground in a fuel cell.
Detailed description of the invention
Fig. 1 is the transmission electron microscope picture of fullerene grafting grapheme material loaded palladium catalyst in embodiment 4.
Fig. 2 is the palladium catalyst (Pd/RGO-NH that fullerene grafting grapheme material is carrier in embodiment 52-C60) and it is single
Pure graphene is the palladium catalyst (Pd/RGO) of carrier to anodic oxidation of methanol cyclic voltammetry curve.
Fig. 3 is chronoa mperometric plot of the palladium catalyst in embodiment 5 on different carriers to anodic oxidation of methanol.
Specific embodiment
Present invention will be further explained below with reference to specific examples.It should be understood that these embodiments are merely to illustrate the present invention
Rather than it limits the scope of the invention.In addition, it should also be understood that, after reading the content taught by the present invention, those skilled in the art
Member can make various changes or modifications the present invention, and such equivalent forms equally fall within the application the appended claims and limited
Range.
Embodiment 1
The synthesis of nitro Functional Fullerene pyrrolidin derivatives.
Under a nitrogen atmosphere, the C of 70mg is added into 100ml round-bottomed flask60, 140mg paranitrobenzaldehyde, 140mg
Sarcosine and 45ml toluene, 115 DEG C of back flow reaction 12h, cold filtration is pure through silica gel column chromatography after filtrate is concentrated
Change, eluant, eluent is toluene/ethanol (5:1).Products therefrom by MALDI-TOF-MS characterize, molecular weight be 897,1077,
1255, serial mass spectra peak is observed at 1431 and 1610, correspond respectively to the nitro Functional Fullerene pyrroles of 1-5 substituent group
Alkane derivatives.
Embodiment 2
The synthesis of amino functional fulleropyrrolidine derivative.
Under nitrogen protection, the fulleropyrrolidine derivative (100mg) of above-mentioned nitro functionalization is dissolved in 100ml first
280mg stannous chloride is added in benzene-ethyl alcohol (2:1) in the mixed solvent, reacts 15h, stratification at room temperature, and lower layer's solution leads to
It crosses liquid separation to obtain and be separated by filtration the solid being precipitated to neutrality through sodium hydroxide adjusting pH, and is washed with deionized, 40
DEG C drying 24 hours to get arrive amino functional fulleropyrrolidine derivative;Products therefrom passes through MALDI-TOF-MS table
Sign is to observe serial mass spectra peak at 867,1015,1164,1312 and 1461 in molecular weight, corresponds respectively to 1-5 substituent group
Amino functional fulleropyrrolidine derivative.
Embodiment 3
The preparation of fullerene grafting grapheme material.
By the fulleropyrrolidine derivative (2.5mg) of above-mentioned amino functional and graphene oxide (20mg) ultrasonic disperse
In dimethyl sulfoxide (20ml), under nitrogen protection, temperature is heating reaction 48h at 90 DEG C, is cooled to room temperature, is centrifugated,
Ethanol washing, 40 DEG C are grafted grapheme material to get to fullerene in drying 24 hours.
Embodiment 4
The preparation of fullerene grafting grapheme material loaded palladium catalyst.
By the above-mentioned fullerene grafting grapheme material ultrasonic disperse of 20mg in 30ml deionized water, 2ml palladium chloride is added
Aqueous solution (2mg/ml), then ultrasound 30 minutes, the sodium borohydride aqueous solution (10mg/ml) that 10ml is newly configured is slowly added dropwise, in room
It is stirred to react under temperature 12 hours.After centrifuge separation, precipitating deionized water and dehydrated alcohol respectively wash three times, it is placed in vacuum drying
Grapheme material loaded palladium catalyst (Pd/RGO-NH is grafted to get fullerene within dry 24 hours at 40 DEG C in case2-C60).Pass through
TEM is characterized, it is seen that catalyst nano-particles are dispersed in fullerene grafting grapheme material material surface (Fig. 1).With
Simple grapheme material is that the palladium catalyst (Pd/RGO) of carrier is prepared using the above identical process, just with graphite oxide
Alkene replaces fullerene to graft grapheme material.
Embodiment 5
Electro-catalysis methanol oxidation performance test.
The made fullerene of embodiment 4 is grafted into grapheme material loaded palladium catalyst (Pd/RGO-NH2-C60) sonic oscillation
Dispersion in ethanol (2mg/ml), pipettes 5 μ l and is transferred to glassy carbon electrode surface, after infrared lamp drying, then 5 μ l Nafion are added dropwise
Working electrode is made in solution (0.5%).Working electrode obtained is put into 1.0M CH3In OH+1.0M NaOH mixed solution,
It is that with saturated calomel electrode (SCE) for reference electrode, the cyclic voltammetric of anodic oxidation of methanol is tested to electrode with platinum electrode
Curve and chronoa mperometric plot.It is carried out pair to using simple grapheme material as the test of the palladium catalyst (Pd/RGO) of carrier simultaneously
According to.It can be seen that grafting grapheme material loaded palladium catalyst (Pd/RGO-NH with fullerene2-C60) compared with simple graphene material
Material is that the palladium catalyst (Pd/RGO) of carrier has higher catalytic activity (Fig. 2) and stability (Fig. 3), and wherein the former electric current is strong
Degree improves about 2 times compared with the latter, and still keeps higher current strength after continuous discharge 2500 seconds.It can be seen that the present invention in
Fullerene grafting grapheme material is that the palladium catalyst of carrier can significantly improve the performance of catalysis methanol oxidation reaction, in fuel electricity
There is potential application foreground in pond.
By the catalyst performance of catalyst in the present invention in application No. is 201710409807.4 patents compared with catalyst,
It can be seen that the current density of catalyst methanol oxidation enhances more than 2 times in the present invention, the former has reached 730mA/mgPd(such as Fig. 2
It is shown), and the latter is only 350mA/mgPd, show to urge in the present invention with fullerene-graphene carrier material that covalent bond is grafted
Agent has the catalytic performance significantly improved.
Claims (9)
1. a kind of fullerene grafts grapheme material loaded palladium catalyst, which is characterized in that with the fullerene pyrrole of amino functional
It coughs up alkane derivatives and graphene composite material is carrier, the structural formula of the fulleropyrrolidine derivative of the amino functional
Are as follows:N=1~5 in formula.
2. a kind of preparation method of fullerene grafting grapheme material loaded palladium catalyst, comprising:
(1) by fullerene C under condition of nitrogen gas60, paranitrobenzaldehyde and sarcosine with mass ratio be 0.8-1.2:1.8-2.2:
1.8-2.2 reacts in a solvent, cooling, and separating-purifying obtains the fulleropyrrolidine derivative of nitro functionalization, wherein fowler
Alkene C60Ratio with solvent is 60-80mg:40-50mL;
(2) fulleropyrrolidine derivative of nitro functionalization in step (1) is dissolved in solvent, reducing agent reaction is added,
Lower layer's solution that liquid separation obtains adjusts pH to neutrality, filters, washs, drying, the fullerene chemistry for obtaining amino functional spreads out
Biology, wherein the ratio of the fulleropyrrolidine derivative, reducing agent and solvent of nitro functionalization is 95-105mg:250-
300mg:95-105mL;
It (3) is 1:6-10 with mass ratio by the fulleropyrrolidine derivative of amino functional in step (2) and graphene oxide
In a solvent, 80-100 DEG C of reaction 36-48h under condition of nitrogen gas is cooling, centrifuge separation for dispersion, obtains fullerene grafting graphene
Material, wherein the ratio of graphene oxide and solvent is 15-25mg:15-25mL;
(4) fullerene grafting grapheme material in step (3) is dispersed in water, palladium chloride aqueous solution is added, sonic oscillation adds
Entering reducing agent solution, be stirred to react, is centrifugated, washing obtains fullerene grafting grapheme material loaded palladium catalyst, wherein
The mass ratio of carrier and palladium is 4-6:1 in catalyst, and it is 15-25mg:30mL that fullerene, which grafts grapheme material and the ratio of water,.
3. method according to claim 2, which is characterized in that solvent is toluene in the step (1);Reaction temperature is 100-
120 DEG C, reaction time 12-16h.
4. method according to claim 2, which is characterized in that the fullerene chemistry of nitro functionalization in the step (1)
Derivant structure formula are as follows:N is 1~5 in formula.
5. method according to claim 2, which is characterized in that solvent is the first of volume ratio 1.8-2.2:1 in the step (2)
Benzene and alcohol mixed solvent;Reducing agent is stannous chloride.
6. method according to claim 2, which is characterized in that reaction temperature is room temperature in the step (2), and the reaction time is
10-15h。
7. method according to claim 2, which is characterized in that solvent is dimethyl sulfoxide in the step (3);Graphene oxide
It is to be prepared using Hummers method.
8. method according to claim 2, which is characterized in that reducing agent is sodium borohydride in the step (4);Sonic oscillation
Time is 25-35min;Being stirred to react temperature is room temperature, and being stirred to react the time is 10-15h.
9. a kind of application of catalyst as described in claim 1 in methanol fuel cell.