CN109987914A - A kind of ardealite insulation blocks and its preparation process - Google Patents
A kind of ardealite insulation blocks and its preparation process Download PDFInfo
- Publication number
- CN109987914A CN109987914A CN201910402130.0A CN201910402130A CN109987914A CN 109987914 A CN109987914 A CN 109987914A CN 201910402130 A CN201910402130 A CN 201910402130A CN 109987914 A CN109987914 A CN 109987914A
- Authority
- CN
- China
- Prior art keywords
- ardealite
- block body
- insulation blocks
- building
- decoration panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to building material technical fields, specially a kind of ardealite insulation blocks and its preparation process, including block body, decoration panel is provided at the top of block body, decoration panel is adapted with the top area size of block body, the side of block body offers connected slot, block body is provided with connection bump far from the side of connected slot, block body Material Percentage are as follows: building ardealite 40%-70%, flyash 20%-30%, cement 10%-20%, foaming agent 2%-3%, retarder 0.75%-1.5%, water-reducing agent 0.75%-1.5% and chopped strand 1.5%-3%.The present invention is using building ardealite as cementitious material, ardealite insulation blocks intensity is higher, it is excellent in terms of mechanical property and light thermal-insulation, thermal coefficient is 0.25~0.3W/mk, compression strength is up to 3.5-4.5MPa, insulation ability is strong, and light-weight anti-seismic performance is good, and the cream insulation blocks self weight of 120mm thickness is less than 90kg/m2,, foaming agent makes ardealite insulation blocks containing a large amount of said minuscule holes, there is thermal and insulating performance, the chopped strand of addition, and the problem of can effectively inhibiting crack.
Description
Technical field
The present invention relates to building material technical field, specially a kind of ardealite insulation blocks and its preparation process.
Background technique
Ardealite block is the green building productions of sustainable development, needs to accelerate to study the application skill of ardealite walling
Art widens its application form.Ardealite wall introduces China not as other cement class materials for walls one from the eighties in last century
Sample is widely used.There is a large amount of ardealite waste material to be not easy to handle every year, to turn waste into wealth as early as possible, with Chinese wall
The space that the novel wall that ardealite is raw material creates a development is given in the propulsion of reform.
Currently, the country has begun using building ardealite production construction material and applies in engineering；Building trade phosphorus
The building materials of gypsum block wall mainly use clay brick, solid block or building-block, these descriptions of materials are single, keep the temperature
Performance is poor, is ugly in appearance, and wastes resource, is inconvenient to be aligned when building a wall.In consideration of it, we provide a kind of ardealite
Insulation blocks and its preparation process.
Summary of the invention
The purpose of the present invention is to provide a kind of ardealite insulation blocks and its preparation processes, to solve above-mentioned background technique
Nowadays Ardealite block description of materials is single for middle proposition, poor thermal insulation property, and wastes resource, also affects the use in house
The problem of performance.
To achieve the above object, the invention provides the following technical scheme:
A kind of ardealite insulation blocks, including block body are provided with decoration panel at the top of the block body, described
Decoration panel is adapted with the top area size of the block body, and the side of the block body offers connected slot, institute
It states block body and the side of the connected slot is provided with connection bump, the section of the connected slot and connection bump is equal
For semicircle, and sectional dimension is adapted, and the end of the block body offers reinforced hole；
The top surface of the block body offers several uniformly equidistant decorative panel fixing grooves in rectangular arranged, described
Be equipped on the bottom surface of decoration panel it is several uniformly it is equidistant be in rectangular arranged decoration panel connecting columns, the decoration panel connecting column and
The position of decorative panel fixing groove is corresponding, size is adapted and decorates panel connecting column and decorative panel fixing groove is mating.
Preferably, the decoration panel use artificial plywood or sham wood dermatotome, and decoration panel with a thickness of
0.5-3.0mm。
Preferably, quantity setting 3-7 of the reinforced hole, the diameter of the reinforced hole are 1-3cm.
Preferably, the diameter of section of the connected slot and connection bump is 2-5cm.
A kind of preparation method of ardealite insulation blocks, the block body are made of the raw material of following mass percent:
Build ardealite 40%-70%, flyash 20%-30%, cement 10%-20%, foaming agent 2%-3%, retarder 0.75%-
1.5%, the ratio of water-reducing agent 0.75%-1.5% and chopped strand 1.5%-3%, mixed raw material and water is 1:0.47-1:
0.5；
The ardealite insulation blocks preparation method includes the following steps:
S1: building ardealite 50%, flyash 25%, cement 15%, foaming agent 2%, retarder 0.75%, water-reducing agent are taken
0.75% and chopped strand 1.5%；
S2: water is added to be mixed evenly water-reducing agent, retarder in proportion raw material, then the addition building phosphorus into mixed solution
After stirring 15-20s with the revolving speed of 115-130r/min, then with the revolving speed stirring 1min of 200-250r/min, mixing is made in gypsum
Solution A；
S3: sequentially adding flyash, cement into mixed solution A obtained, stirs 20- with the revolving speed of 115-130r/min
After 30s, then with the revolving speed stirring 1min of 200-250r/min, mixed solution B is made；
S4: foaming agent 2% being added into mixed solution B obtained, stirs 20-30s, system with the revolving speed of 115-130r/min
Obtain mixed solution C；
S5: being added chopped strand into mixed solution C obtained, stirs 20-30s with the revolving speed of 115-130r/min, then
1.5min is stirred with the revolving speed of 200-250r/min, building block slurry is made after mixing evenly；
S6: building block slurry obtained is poured into building block mould, is spontaneously dried 3-5 hours, is demoulded, can be prepared by building
Block body；
S7: glue will be painted in the decorative panel fixing groove of the back side of the decoration panel after shearing and block body, by glue
Water is smeared uniformly, and the decoration panel connecting column grafting at decoration panel back is entered in decorative panel fixing groove, and by the decoration panel back side
It is closely bonded with the top surface of block body, natural air drying 30-60min can be prepared by ardealite insulation blocks.
Preferably, the building ardealite is phosphorus ardealite, flue gas desulfurization ardealite or both mixture.
Preferably, the foaming agent is that aluminium powder, zinc powder, magnesium powder, hydrogen peroxide, calcium carbide or sodium carbonate add hydrochloric acid.
Preferably, the retarder is phosphate, lignin, boric acid or citric acid.
Preferably, the chopped strand is polypropylene fibre or glass fibre.
Compared with prior art, the beneficial effects of the present invention are: what this ardealite insulation blocks and its preparation process produced
Ardealite insulation blocks are excellent in terms of mechanical property and light thermal-insulation, and thermal coefficient is 0.25~0.3W/mk, compression strength
Up to 8-10MPa, insulation ability is strong, and light-weight anti-seismic performance is good, and the cream insulation blocks self weight of 120mm thickness is less than 90kg/
m2,, the foaming agent of addition, so that ardealite insulation blocks contain a large amount of said minuscule holes, with excellent thermal and insulating performance；It can be with
Ardealite largely is built using phosphorus, and can be recycled, it is more environmentally-friendly；Aerating Ardealite block has good add
Work can be sawed, digs, bores, be followed closely, when in use can be as needed, carry out any processing, and binding material appropriate can be used to bond,
Advantageous condition is provided to construction, ardealite insulation blocks are good as ardealite interior wall soundproof effect, effectively reduce
Wall area occupied improves residential usage rate, mitigates structural load, improve shock resistance of the building and security performance, reduces comprehensive
Cost is closed, is the best substitute of tradition wall material.It effectively improves building from wet construction to dry construction
Transformation process realizes house component, technical equipment modernization, application legalization and construction equipment integration.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of ardealite insulation blocks of the present invention；
Fig. 2 is the structural schematic diagram of block body of the present invention；
Fig. 3 is the structural schematic diagram of decoration panel of the present invention.
In figure: 1, block body；2, decoration panel；3, connected slot；4, connection bump；5, decorative panel fixing groove；6, it fills
Plaque connecting column；7, reinforced hole.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
In the description of the present invention, it is to be understood that, term " center ", " longitudinal direction ", " transverse direction ", " length ", " width ",
" thickness ", "upper", "lower", "front", "rear", "left", "right", "vertical", "horizontal", "top", "bottom", "inner", "outside", " up time
The orientation or positional relationship of the instructions such as needle ", " counterclockwise " is to be based on the orientation or positional relationship shown in the drawings, and is merely for convenience of
The description present invention and simplified description, rather than the equipment of indication or suggestion meaning or element must have a particular orientation, with spy
Fixed orientation construction and operation, therefore be not considered as limiting the invention.
Embodiment 1
A kind of ardealite insulation blocks, as shown in Figure 1, including block body 1, the top of block body 1 is provided with decoration
Panel 2, decoration panel 2 are adapted with the top area size of block body 1, and decoration panel 2 uses artificial plywood or sham wood
Dermatotome, and decoration panel 2 with a thickness of 0.5-3.0mm, as the preferred of the present embodiment, decoration panel 2 uses artificial plywood,
With a thickness of 1.5mm, glued board be veneer is peeled by juggle or by flitch slicing at veneer, then with adhesive it is glued made of three
The board-like material of layer or multilayer usually uses odd-level veneer, and forms the orthogonal gluing of the machine direction of adjacent layer veneer,
Retain wood surface natural colored and texture, can choose panel material, decorative pattern and color, glued board natural simpleness, nature, beauty
See and it is noble, can build out elegance living environment.
Further, the side of block body 1 offers connected slot 3, side of the block body 1 far from connected slot 3
It is provided with connection bump 4, the section of connected slot 3 and connection bump 4 is semicircle, and sectional dimension is adapted, and connection is inserted
Slot 3 and the diameter of section of connection bump 4 are 2-5cm, as the preferred of the present embodiment, section of connected slot 3 and connection bump 4
Face diameter is 3cm, when building a wall, connected slot 3 and the connection bump 4 of adjacent ardealite insulation blocks can be matched
It closes, is disposably aligned and accurate.
In addition, the end of block body 1 offers reinforced hole 7, quantity setting 3-7 of reinforced hole 7, reinforced hole 7 it is straight
Diameter is 1-3cm, and as the preferred of the present embodiment, the quantity of reinforced hole 7 is arranged 5, and the diameter of reinforced hole 7 is 2cm, in reinforced hole
It is inserted into reinforcing bar in 7, increases the intensity of block body 1, in addition it is also possible to share one group of steel with adjacent ardealite insulation blocks
Muscle guarantees the stabilization of wall body structure.
Block body 1 is made of the raw material of following mass percent: building ardealite 40%-70%, flyash 20%-
30%, cement 10%-20%, foaming agent 2%-3%, retarder 0.75%-1.5%, water-reducing agent 0.75%-1.5% and short
Cut fiber 1.5%-3%, the ratio of mixed raw material and water is 1:0.47-1:0.5；
Specifically, ardealite insulation blocks preparation method includes the following steps:
S1: building ardealite 50%, flyash 25%, cement 15%, foaming agent 2%, retarder 0.75%, water-reducing agent are taken
0.75% and chopped strand 1.5%；
S2: water is added to be mixed evenly water-reducing agent, retarder in proportion raw material, then the addition building phosphorus into mixed solution
After stirring 15-20s with the revolving speed of 115-130r/min, then with the revolving speed stirring 1min of 200-250r/min, mixing is made in gypsum
Solution A；
S3: sequentially adding flyash, cement into mixed solution A obtained, stirs 20- with the revolving speed of 115-130r/min
After 30s, then with the revolving speed stirring 1min of 200-250r/min, mixed solution B is made；
S4: foaming agent 2% being added into mixed solution B obtained, stirs 20-30s, system with the revolving speed of 115-130r/min
Obtain mixed solution C；
S5: being added chopped strand into mixed solution C obtained, stirs 20-30s with the revolving speed of 115-130r/min, then
1.5min is stirred with the revolving speed of 200-250r/min, building block slurry is made after mixing evenly；
S6: building block slurry obtained is poured into building block mould, is spontaneously dried 3-5 hours, is demoulded, can be prepared by building
Block body 1；
S7: will paint glue in the decorative panel fixing groove 5 of the back side of the decoration panel 2 after shearing and block body 1, will
Glue is smeared uniformly, and 6 grafting of decoration panel connecting column at 2 back of decoration panel is entered in decorative panel fixing groove 5, and by decoration panel
2 back sides and the top surface of block body 1 closely bond, and natural air drying 30-60min can be prepared by ardealite insulation blocks.
It is worth noting that building ardealite is that phosphorus ardealite, flue gas desulfurization ardealite or both mixture, foaming agent are
Aluminium powder, zinc powder, magnesium powder, hydrogen peroxide, calcium carbide or sodium carbonate add hydrochloric acid, and retarder is phosphate, lignin, boric acid or lemon
Acid, chopped strand are polypropylene fibre or glass fibre.
The ardealite insulation blocks of the present embodiment are using building ardealite as cementitious material, ardealite insulation blocks intensity
It is higher, up to 8-10MPa, it can be used for filled wall material, excellent in terms of mechanical property and light thermal-insulation, thermal coefficient is
0.25~0.3W/mk, for compression strength up to 3.5-4.5MPa, insulation ability is strong, and light-weight anti-seismic performance is good, 120mm
Thick cream insulation blocks self weight is less than 90kg/m2,, the foaming agent of addition makes ardealite insulation blocks containing a large amount of said minuscule holes, tool
There is an excellent thermal and insulating performance, the chopped strand of addition, the problem of can effectively inhibiting crack；It can largely be built using phosphorus
Ardealite, and can be recycled, it is more environmentally-friendly；Aerating Ardealite block has good machinability, can saw, dig,
It bores, nail, when in use can be as needed, any processing is carried out, and binding material appropriate can be used to bond, is provided to construction
Advantageous condition, ardealite insulation blocks are good as ardealite interior wall soundproof effect, effectively reduce wall area occupied, mention
High residential usage rate mitigates structural load, improves shock resistance of the building and security performance, reduces comprehensive cost, is conventional wall
The best substitute of body material.It effectively improves transformation process of the building from wet construction to dry construction, realizes
House component, technical equipment modernization, application legalization and construction equipment integration.
Embodiment 2
As second of embodiment of the invention, as shown in Figures 2 and 3, the top surface of block body 1 offers several
Uniformly equidistantly it is in the decorative panel fixing groove 5 of rectangular arranged, is equipped on the bottom surface of decoration panel 2 several uniformly equidistantly in rectangle row
The decoration panel connecting column 6 of column, decoration panel connecting column 6 is corresponding with the position of decorative panel fixing groove 5, size is adapted and decorative panel
Connecting column 6 and decorative panel fixing groove 5 are mating, convenient for decoration panel 2 to be fixed.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
For personnel it should be appreciated that the present invention is not limited to the above embodiments, described in the above embodiment and specification is only the present invention
Preference, be not intended to limit the invention, without departing from the spirit and scope of the present invention, the present invention also has various
Changes and improvements, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by institute
Attached claims and its equivalent thereof.
Claims (9)
1. a kind of ardealite insulation blocks, it is characterised in that: including block body (1), the top of the block body (1) is arranged
Have decoration panel (2), the decoration panel (2) is adapted with the top area size of the block body (1), the block body
(1) side offers connected slot (3), and the block body (1) is provided with connection far from the side of the connected slot (3)
The section of raised (4), the connected slot (3) and connection bump (4) is semicircle, and sectional dimension is adapted, the block
The end of block body (1) offers reinforced hole (7)；
The top surface of the block body (1) offers several uniformly equidistant decorative panel fixing grooves (5) in rectangular arranged, institute
It states and several uniformly equidistant decoration panel connecting columns (6) in rectangular arranged, the decorative panel is installed on the bottom surface of decoration panel (2)
Connecting column (6) is corresponding with the position of decorative panel fixing groove (5), size is adapted and decorates panel connecting column (6) and decorative panel is solid
It is mating to determine slot (5).
2. ardealite insulation blocks according to claim 1, it is characterised in that: the decoration panel (2) uses artificial rubber
Plywood or sham wood dermatotome, and decoration panel (2) with a thickness of 0.5-3.0mm.
3. ardealite insulation blocks according to claim 1, it is characterised in that: 3-7 is arranged in the quantity of the reinforced hole (7)
A, the diameter of the reinforced hole (7) is 1-3cm.
4. ardealite insulation blocks according to claim 1, it is characterised in that: the connected slot (3) and connection bump
(4) diameter of section is 2-5cm.
5. a kind of preparation method of ardealite insulation blocks keeps the temperature including ardealite described in claim 1-4 any one and builds
Block, it is characterised in that: the block body (1) is made of the raw material of following mass percent: building ardealite 40%-70%,
Flyash 20%-30%, cement 10%-20%, foaming agent 2%-3%, retarder 0.75%-1.5%, water-reducing agent 0.75%-
The ratio of 1.5% and chopped strand 1.5%-3%, mixed raw material and water is 1:0.47-1:0.5；
The ardealite insulation blocks preparation method includes the following steps:
S1: building ardealite 50%, flyash 25%, cement 15%, foaming agent 2%, retarder 0.75%, water-reducing agent are taken
0.75% and chopped strand 1.5%；
S2: water is added to be mixed evenly water-reducing agent, retarder in proportion raw material, then the addition building phosphorus stone into mixed solution
After stirring 15-20s with the revolving speed of 115-130r/min, then with the revolving speed stirring 1min of 200-250r/min, it is molten that mixing is made in cream
Liquid A；
S3: sequentially adding flyash, cement into mixed solution A obtained, stirs 20-30s with the revolving speed of 115-130r/min
Afterwards, then with the revolving speed of 200-250r/min 1min is stirred, mixed solution B is made；
S4: foaming agent 2% being added into mixed solution B obtained, stirs 20-30s with the revolving speed of 115-130r/min, is made mixed
Close solution C；
S5: being added chopped strand into mixed solution C obtained, with the revolving speed stirring 20-30s of 115-130r/min, then with
The revolving speed of 200-250r/min stirs 1.5min, and building block slurry is made after mixing evenly；
S6: building block slurry obtained is poured into building block mould, is spontaneously dried 3-5 hours, is demoulded, can be prepared by building block sheet
Body (1)；
S7: will paint glue in the decorative panel fixing groove (5) of the back side of the decoration panel (2) after shearing and block body (1),
Glue is smeared uniformly, decoration panel connecting column (6) grafting at decoration panel (2) back is entered in decorative panel fixing groove (5), and will
Decoration panel (2) back side and the top surface of block body (1) closely bond, natural air drying 30-60min, can be prepared by ardealite guarantor
Warm building block.
6. the preparation process of ardealite insulation blocks according to claim 5, it is characterised in that: the building ardealite is
Phosphorus ardealite, flue gas desulfurization ardealite or both mixture.
7. the preparation process of ardealite insulation blocks according to claim 5, it is characterised in that: the foaming agent is aluminium
Powder, zinc powder, magnesium powder, hydrogen peroxide, calcium carbide or sodium carbonate add hydrochloric acid.
8. the preparation process of ardealite insulation blocks according to claim 5, it is characterised in that: the retarder is phosphoric acid
Salt, lignin, boric acid or citric acid.
9. the preparation process of ardealite insulation blocks according to claim 5, it is characterised in that: the chopped strand is poly-
Tacryl or glass fibre.