CN109930394A - A kind of compound sun shading material of acrylic polyvinyl chloride high molecular material - Google Patents
A kind of compound sun shading material of acrylic polyvinyl chloride high molecular material Download PDFInfo
- Publication number
- CN109930394A CN109930394A CN201711372127.6A CN201711372127A CN109930394A CN 109930394 A CN109930394 A CN 109930394A CN 201711372127 A CN201711372127 A CN 201711372127A CN 109930394 A CN109930394 A CN 109930394A
- Authority
- CN
- China
- Prior art keywords
- acrylic
- polyvinyl chloride
- acrylic emulsion
- high molecular
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of compound sun shading material of acrylic polyvinyl chloride high molecular material, and primary raw material includes: sunlight cloth fabric and coating paste；Wherein, sunlight fabric be it is a kind of by polyvinyl chloride cladding yarn weaving form, have certain percent opening and translucency；Coating paste is made of acrylic emulsion, titanium dioxide filler, foam stabilizer and fire retardant；Main component acrylic emulsion of the present invention in the slurry, using the acrylic acid alkyl rouge of acrylic monomers and its C1~C8 after polymerization reaction after synthesis of acrylic ester slurry copolymer adhesive, high performance acrylate adhesive synthesis is added, the solidification point of the acrylic emulsion is at 150 degree or so；Fundamentally solve the problems, such as that coating fabric foaming face is tacky, the defect rate for reducing product improves the surface smoothness of product, tidiness increases product category, plays very big popularizing action for marketing and product sale and improves enterprise core competence.
Description
Technical field
The present invention relates to technical field of macromolecules, the compound sunshade of specifically a kind of acrylic polyvinyl chloride high molecular material
Material.
Background technique
Sunlight fabric be it is a kind of by polyvinyl chloride cladding yarn weaving made of, have certain percent opening and light transmission
Property be mainly used for making the roller shutter to keep the sun off daytime, hold court from behind a screen, seat cushion etc., and coating fabric is then on the basis of sunlight fabric
Made of being added to be further processed after acrylic acid slurry as main component by several techniques, mainly for the production of night use
Roller shutter is held court from behind a screen, seat cushion etc., and market demand is very big, there is very big promotion prospect.
But having some insoluble problems as follows in process of production:
On the one hand because of the property of the acrylic system in the polyvinyl chloride and coating paste in the compound sun shading material of macromolecule
Difference, the high temperature resistant degree of the two have very big difference, and the fusing point of polyvinyl chloride is probably in 140 degrees centigrades, and acrylic acid
Solidification temperature probably in 150 degrees centigrades, full shading sunlight cloth fabric, which needs to be carried on the back by acrylic acid foaming system, applies polychlorostyrene second
Alkene polymer composite and film-forming, acrylic acid synthesizing and polyvinyl chloride are undoubtedly contradictory in this case, often
Will appear the also uncured polyvinyl chloride of acrylic acid just melted, sudden and violent silk the phenomenon that, so that polymer composite is sticked together, table
Face is not smooth, and product quality is difficult to meet customer need.
Summary of the invention
The object of the present invention is to provide a kind of compound sun shading materials of acrylic polyvinyl chloride high molecular material, have quality
The polymer composite of the strong feature of softness, good heat insulating, light-proofness, to solve asking for above-mentioned technical background technology proposition
Topic.
To achieve the above object, the invention provides the following technical scheme:
A kind of compound sun shading material of acrylic polyvinyl chloride high molecular material, primary raw material include: sunlight cloth fabric and
Coating paste；Wherein, sunlight fabric be it is a kind of by polyvinyl chloride cladding yarn weaving made of, have certain percent opening
And translucency；Coating paste is made of acrylic emulsion, titanium dioxide filler, foam stabilizer and fire retardant.
Preferably, in a kind of compound sun shading material of above-mentioned acrylic polyvinyl chloride high molecular material, the coating slurry
Material is made of 55% acrylic emulsion, 30% titanium dioxide filler, 10% foam stabilizer and 5% fire retardant and other auxiliary agents.
Preferably, in a kind of compound sun shading material of above-mentioned acrylic polyvinyl chloride high molecular material, the acrylic acid
The synthesis of acrylic ester slurry after polymerization reaction is total using the acrylic acid alkyl rouge of acrylic monomers and its C1~C8 for lotion
High performance acrylate adhesive synthesis is added after polymers adhesive, the solidification point of the acrylic emulsion is at 150 degree or so.
Preferably, in a kind of compound sun shading material of above-mentioned acrylic polyvinyl chloride high molecular material, process flow are as follows:
Coating paste is made by 55% acrylic emulsion, 30% titanium dioxide filler, 10% foam stabilizer and 5% fire retardant and other auxiliary agents,
The slurry is put into foaming machine, foaming system is formed and applies process through back and sunlight fabric is smeared, through certain temperature and
Speed control is finally as the main component with slipping agent together by addition by acrylic emulsion film-forming on sunlight fabric
Coating protection lacquer craftwork and form the strong compound sun shading material of soft, good heat insulating, light-proofness.
It can be seen via above technical scheme that compared with prior art, coating paste of the present invention by 55% acrylic emulsion,
30% titanium dioxide filler, 10% foam stabilizer and 5% fire retardant are constituted, wherein the coating manufactured with titanium dioxide, bright in luster, are covered
Power is high, and strong coloring force is low-consuming, wide in variety, can play a protective role to the physical stability of sunlight fabric, and can enhance coating
The adhesive force of film, prevents crackle, prevents ultraviolet light and moisture from penetrating, extends coating membrane lifetime.With acrylic emulsion be mainly at
Divide the slurry wearability mainly formed good, intensity is big, good toughness, and water-fast, adhesive force is strong.The addition of foam stabilizer is applied for foaming
Layer slurry provides convenience in the technologic foaming process of foaming machine, forms foaming system and applies through back painting process to sunlight fabric
It smears, through certain temperature and speed control by acrylic emulsion film-forming on sunlight fabric, finally together by addition
Lacquer craftwork is protected with slipping agent coating as the main component, and forms the strong foaming face of soft, good heat insulating, light-proofness
Material.Fundamentally solve the problems, such as that coating fabric foaming face is tacky, the defect rate for reducing product improves the surface of product
Flatness, tidiness increase product category, play very big popularizing action for marketing and product sale and improve enterprise
Industry core competitiveness.
Detailed description of the invention
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below
There is attached drawing needed in technical description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this
The embodiment of invention for those of ordinary skill in the art without creative efforts, can also basis
The attached drawing of offer obtains other attached drawings.
Fig. 1 attached drawing is process flow chart of the invention.
Specific embodiment
Implement the attached drawing in side below in conjunction with the present invention, technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Process flow are as follows:
1, it is made of 55% acrylic emulsion, 30% titanium dioxide filler, 10% foam stabilizer and 5% fire retardant and other auxiliary agents
Coating paste；
2, the slurry is put into foaming machine foaming processing；
3, it forms foaming system to smear sunlight fabric through back painting process, pass through through certain temperature and speed control
Acrylic emulsion film-forming on sunlight fabric；
4, finally, protecting lacquer craftwork together by addition with slipping agent coating as the main component.
Each embodiment in this specification is described in a progressive manner, the highlights of each of the examples are with other
The difference of embodiment, the same or similar parts in each embodiment may refer to each other.For device disclosed in embodiment
For, since it is corresponded to the methods disclosed in the examples, so being described relatively simple, related place is said referring to method part
It is bright.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention.
Various modifications to these embodiments will be readily apparent to those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one
The widest scope of cause.
Claims (4)
1. a kind of compound sun shading material of acrylic polyvinyl chloride high molecular material, primary raw material include: sunlight cloth fabric and painting
Layer slurry；Wherein, sunlight fabric is made of a kind of yarn weaving by polyvinyl chloride cladding, with certain percent opening and
Translucency；Coating paste is made of acrylic emulsion, titanium dioxide filler, foam stabilizer and fire retardant.
2. a kind of compound sun shading material of acrylic polyvinyl chloride high molecular material according to claim 1, feature exist
In the coating paste is by 55% acrylic emulsion, 30% titanium dioxide filler, 10% foam stabilizer, 5% fire retardant and other auxiliary agents
It constitutes.
3. a kind of compound sun shading material of acrylic polyvinyl chloride high molecular material according to claim 1, feature exist
In the acrylic emulsion synthesizes third using acrylic monomers and its acrylic acid alkyl rouge of C1~C8 after polymerization reaction
High performance acrylate adhesive synthesis, the solidification of the acrylic emulsion are added after olefin(e) acid esters slurry copolymer adhesive
O'clock at 150 degree or so.
4. a kind of compound sun shading material of acrylic polyvinyl chloride high molecular material according to claim 1, feature exist
In process flow are as follows: by 55% acrylic emulsion, 30% titanium dioxide filler, 10% foam stabilizer, 5% fire retardant and other auxiliary agents
Coating paste is made, the slurry is put into foaming machine, forms foaming system and is coated on sunlight fabric by back painting process, passed through
Certain temperature and speed control are by acrylic emulsion and the film-forming on sunlight fabric, finally by addition together with cunning
Refreshing agent coating as the main component protects lacquer craftwork and forms the strong compound sunshade material of soft, good heat insulating, light-proofness
Material.