CN109930062A - A method of improving special thick normalizing ship steel tensile property - Google Patents

A method of improving special thick normalizing ship steel tensile property Download PDF

Info

Publication number
CN109930062A
CN109930062A CN201811329586.0A CN201811329586A CN109930062A CN 109930062 A CN109930062 A CN 109930062A CN 201811329586 A CN201811329586 A CN 201811329586A CN 109930062 A CN109930062 A CN 109930062A
Authority
CN
China
Prior art keywords
normalizing
ship steel
ship
cold
steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811329586.0A
Other languages
Chinese (zh)
Inventor
张坤
王若钢
李新玲
于金洲
林亚桥
杨军
李黎明
刘立强
吴铎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Angang Steel Co Ltd
Original Assignee
Angang Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Angang Steel Co Ltd filed Critical Angang Steel Co Ltd
Priority to CN201811329586.0A priority Critical patent/CN109930062A/en
Publication of CN109930062A publication Critical patent/CN109930062A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of methods for improving special thick normalizing ship steel tensile property, the chemical composition comprises the following components in percentage by weight of the normalizing ship steel are as follows: C≤0.18%, Si≤0.50%, Mn:0.9~1.7%, P≤0.035%, S≤0.35%, ALS >=0.15%, Nb:0.02~0.050%, V:0.05~0.10%, Ti≤0.02%;Thickness >=60mm;Normalizing ship steel increases online ACC and controls cold technique after rolling, and optimizes the cold technological parameter of control.The average value surplus capacity of yield strength >=280Mpa of final normalizing ship steel, tensile strength >=450Mpa, yield strength and tensile strength reaches 40Mpa or more, and Measure of Process Capability Cpk reaches 1.0 or more.

Description

A method of improving special thick normalizing ship steel tensile property
Technical field
The present invention relates to technical field of steel rolling more particularly to a kind of methods for improving special thick normalizing ship steel tensile property.
Background technique
When finished product thickness >=60mm spy's thickness normalizing deck of boat steel rolling, limited by sotck thinkness, compression ratio is generally less than 8, it causes degree of grain refinement insufficient, while normalized treatment has the function of reduction to steel plate stretching intensity, steel plate is easily caused to bend It is relatively low lower than standard value or tensile strength average performance value surplus capacity to take intensity and tensile strength, a performance of steel plate is closed Lattice rate is lower.
Summary of the invention
The present invention provides a kind of methods for improving special thick normalizing ship steel tensile property, by increasing after steel plate rolls Line ACC controls cold technique, and optimizes the cold technological parameter of control, is effectively improved the tensile property of normalizing ship steel, product qualified rate reaches 100%.
In order to achieve the above object, the present invention is implemented with the following technical solutions:
A method of improving special thick normalizing ship steel tensile property, the chemical component by weight hundred of the normalizing ship steel Ratio is divided to be calculated as: C≤0.18%, Si≤0.50%, Mn:0.9~1.7%, P≤0.035%, S≤0.35%, ALs >=0.15%, Nb:0.02~0.050%, V:0.05~0.10%, Ti≤0.02%;Thickness >=60mm;The normalizing ship steel increases after rolling Online ACC controls cold technique, and it is as follows to control cold technological parameter:
With a thickness of the steel plate of 60~80mm: opening 720~780 DEG C of cold temperature, upper 16~18m of water3/ min, lower water 32~ 36m3/ min, ACC 0.5~0.7m/s of roller table speed, 620~680 DEG C of final cooling temperature;
With a thickness of the steel plate of 81~100mm: opening 700~760 DEG C of cold temperature, upper 20~22m of water3/ min, lower water 40 ~44m3/ min, ACC 0.5~0.7m/s of roller table speed, 600~660 DEG C of final cooling temperature;
Yield strength >=280Mpa of the normalizing ship steel, tensile strength >=450Mpa, yield strength and tensile strength Average value surplus capacity reach 40Mpa or more.
Compared with prior art, the beneficial effects of the present invention are:
Cold technique is controlled by increasing online ACC after steel plate rolls, and optimizes the cold technological parameter of control, is effectively improved the normalizing deck of boat The tensile property of steel, product qualified rate reach 100%.
Specific embodiment
A method of improving special thick normalizing ship steel tensile property, the chemical component by weight hundred of the normalizing ship steel Ratio is divided to be calculated as: C≤0.18%, Si≤0.50%, Mn:0.9~1.7%, P≤0.035%, S≤0.35%, ALS >=0.15%, Nb:0.02~0.050%, V:0.05~0.10%, Ti≤0.02%;Thickness >=60mm;The normalizing ship steel increases after rolling Online ACC controls cold technique, and it is as follows to control cold technological parameter:
With a thickness of the steel plate of 60~80mm: opening 720~780 DEG C of cold temperature, upper 16~18m of water3/ min, lower water 32~ 36m3/ min, ACC 0.5~0.7m/s of roller table speed, 620~680 DEG C of final cooling temperature;
With a thickness of the steel plate of 81~100mm: opening 700~760 DEG C of cold temperature, upper 20~22m of water3/ min, lower water 40 ~44m3/ min, ACC 0.5~0.7m/s of roller table speed, 600~660 DEG C of final cooling temperature;
Yield strength >=280Mpa of the normalizing ship steel, tensile strength >=450Mpa, yield strength and tensile strength Average value surplus capacity reach 40Mpa or more.
Following embodiment is implemented under the premise of the technical scheme of the present invention, gives detailed embodiment and tool The operating process of body, but protection scope of the present invention is not limited to following embodiments.Method therefor is such as without spy in following embodiments Not mentionleting alone bright is conventional method.
[embodiment 1]
In the present embodiment, normalizing ship steel produced is D grades of ship steels, thickness 70mm, chemical component percentage by weight Than being calculated as: C:0.10%, Si:0.15%, Mn:1.5%, P:0.015%, S:0.015%, ALs:0.035%, Nb: 0.030%, V:0.07%, Ti:0.010%.
Normalizing ship steel increases online ACC and controls cold technique after rolling, it is as follows to control cold technological parameter:
Open 750 DEG C of cold temperature, 15 groups of water nozzle standard-sized sheets, upper water 16.8m3/ min, lower water 33m3/ min, ACC roller table speed 0.6m/s, 671 DEG C of final cooling temperature.
The service check result of normalizing ship steel: yield strength 283Mpa (yield strength standard value is >=235Mpa) resists Tensile strength 456Mpa (tensile strength standard value is 400~520Mpa).The average value surplus capacity of yield strength and tensile strength is equal Reach 40Mpa or more, Measure of Process Capability Cpk reaches 1.0 or more, and product qualified rate reaches 100%.
[embodiment 2]
In the present embodiment, normalizing ship steel produced is D grades of ship steels, thickness 85mm, chemical component percentage by weight Than being calculated as: C:0.09%, Si:0.14%, Mn:1.45%, P:0.013%, S:0.01%, ALs:0.038%, Nb: 0.031%, V:0.075%, Ti:0.010%.
Normalizing ship steel increases online ACC and controls cold technique after rolling, it is as follows to control cold technological parameter:
Open 740 DEG C of cold temperature, 15 groups of water nozzle standard-sized sheets, upper water 21.0m3/ min, lower water 42m3/ min, ACC roller table speed 0.6m/s, 644 DEG C of final cooling temperature.
The service check result of normalizing ship steel: yield strength 288Mpa, tensile strength 451Mpa.Yield strength and tension The average value surplus capacity of intensity reaches 40Mpa or more, and Measure of Process Capability Cpk reaches 1.0 or more, and product qualified rate reaches 100%.
[embodiment 3]
In the present embodiment, normalizing ship steel produced is D grades of ship steels, thickness 100mm, chemical component percentage by weight Than being calculated as: C:0.09%, Si:0.15%, Mn:1.48%, P:0.011%, S:0.010%, ALS:0.04%, Nb: 0.033%, V:0.072%, Ti:0.010%.
Normalizing ship steel increases online ACC and controls cold technique after rolling, it is as follows to control cold technological parameter:
Open 732 DEG C of cold temperature, 15 groups of water nozzle standard-sized sheets, upper water 22.0m3/ min, lower water 44m3/ min, ACC roller table speed 0.5m/s, 627 DEG C of final cooling temperature.
The service check result of normalizing ship steel: yield strength 280Mpa, tensile strength 452Mpa.Yield strength and tension The average value surplus capacity of intensity reaches 40Mpa or more, and Measure of Process Capability Cpk reaches 1.0 or more, and product qualified rate reaches 100%.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto, Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.

Claims (1)

1. a kind of method for improving special thick normalizing ship steel tensile property, which is characterized in that the chemistry of the normalizing ship steel at Divide by weight percentage are as follows: C≤0.18%, Si≤0.50%, Mn:0.9~1.7%, P≤0.035%, S≤0.35%, ALS >=0.15%, Nb:0.02~0.050%, V:0.05~0.10%, Ti≤0.02%;Thickness >=60mm;The normalizing ship Slab increases online ACC and controls cold technique after rolling, it is as follows to control cold technological parameter:
With a thickness of the steel plate of 60~80mm: opening 720~780 DEG C of cold temperature, upper 16~18m of water3/ min, 32~36m of lower water3/ Min, ACC 0.5~0.7m/s of roller table speed, 620~680 DEG C of final cooling temperature;
With a thickness of the steel plate of 81~100mm: opening 700~760 DEG C of cold temperature, upper 20~22m of water3/ min, lower water 40~ 44m3/ min, ACC 0.5~0.7m/s of roller table speed, 600~660 DEG C of final cooling temperature;
Yield strength >=280Mpa of the normalizing ship steel, tensile strength >=450Mpa, yield strength and tensile strength are put down Mean value surplus capacity reaches 40Mpa or more.
CN201811329586.0A 2018-11-09 2018-11-09 A method of improving special thick normalizing ship steel tensile property Pending CN109930062A (en)