CN109929458A - A kind of polishing slurries - Google Patents
A kind of polishing slurries Download PDFInfo
- Publication number
- CN109929458A CN109929458A CN201711355731.8A CN201711355731A CN109929458A CN 109929458 A CN109929458 A CN 109929458A CN 201711355731 A CN201711355731 A CN 201711355731A CN 109929458 A CN109929458 A CN 109929458A
- Authority
- CN
- China
- Prior art keywords
- parts
- polishing slurries
- tsl
- aluminum oxide
- potassium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to the technical field of slurry more particularly to a kind of polishing slurries.This polishing slurries are made of raw material from the following weight: 10-30 parts of aluminum oxide polishing powder, 3-5 parts of potassium hydroxide, 1~3 part of stearic acid, 1~5 part of 3- TSL 8330,15~40 parts of water.The raw material of this polishing slurries is common to be easy to get, and at low cost, and the slurry being finally made has excellent electric conductivity and adherence, and stream malleability is good, and has wide range of applications.
Description
Technical field
The present invention relates to a kind of slurry more particularly to a kind of polishing slurries.
Background technique
Existing slurry is mainly using resin as binder, and the physics sex differernce of metal and resin is big during preparing, system
Many at often leading to the problem of after formula, for example, processing procedure is poor, halftone blocking, easy cleaning need to often not eliminate replacement, and slurry is difficult
Stream or electric conductivity is bad and sticky bad problem.
Summary of the invention
Present invention seek to address that drawbacks described above, provides a kind of polishing slurries.
In order to overcome defect present in background technique, the technical solution adopted by the present invention to solve the technical problems is:
This polishing slurries are made of raw material from the following weight:
10-30 parts of aluminum oxide polishing powder, 3-5 parts of potassium hydroxide, 1~3 part of stearic acid, 3- TSL 8330 1~5
Part, 15~40 parts of water.
According to another embodiment of the invention, further comprise 30 parts of the aluminum oxide polishing powder, 5 parts of potassium hydroxide,
3 parts of stearic acid, 5 parts of 3- TSL 8330,40 parts of water.
According to another embodiment of the invention, further comprise 10 parts of the aluminum oxide polishing powder, 3 parts of potassium hydroxide,
1 part of stearic acid, 1 part of 3- TSL 8330,15 parts of water.
According to another embodiment of the invention, further comprise 15 parts of the aluminum oxide polishing powder, 4 parts of potassium hydroxide,
2 parts of stearic acid, 3 parts of 3- TSL 8330,25 parts of water.
It is easy to get the beneficial effects of the present invention are: the raw material of this polishing slurries is common, and at low cost, the slurry being finally made
Material has excellent electric conductivity and adherence, and has wide range of applications.
Specific embodiment
This polishing slurries are made of raw material from the following weight:
10-30 parts of aluminum oxide polishing powder, 3-5 parts of potassium hydroxide, 1~3 part of stearic acid, 3- TSL 8330 1~5
Part, 15~40 parts of water.
30 parts of aluminum oxide polishing powder, 5 parts of potassium hydroxide, 3 parts of stearic acid, 5 parts of 3- TSL 8330, water 40
Part.
10 parts of aluminum oxide polishing powder, 3 parts of potassium hydroxide, 1 part of stearic acid, 1 part of 3- TSL 8330, water 15
Part.
15 parts of aluminum oxide polishing powder, 4 parts of potassium hydroxide, 2 parts of stearic acid, 3 parts of 3- TSL 8330, water 25
Part.
It is easy to get the beneficial effects of the present invention are: the raw material of this polishing slurries is common, and at low cost, the slurry being finally made
Material has excellent electric conductivity and adherence, and has wide range of applications.
Claims (4)
1. a kind of polishing slurries, which is characterized in that be made of raw material from the following weight:
10-30 parts of aluminum oxide polishing powder, 3-5 parts of potassium hydroxide, 1~3 part of stearic acid, 3- TSL 8330 1~5
Part, 15~40 parts of water.
2. polishing slurries as described in claim 1, it is characterised in that: 30 parts of the aluminum oxide polishing powder, 5 parts of potassium hydroxide,
3 parts of stearic acid, 5 parts of 3- TSL 8330,40 parts of water.
3. polishing slurries as described in claim 1, it is characterised in that: 10 parts of the aluminum oxide polishing powder, 3 parts of potassium hydroxide,
1 part of stearic acid, 1 part of 3- TSL 8330,15 parts of water.
4. polishing slurries as described in claim 1, it is characterised in that: 15 parts of the aluminum oxide polishing powder, 4 parts of potassium hydroxide,
2 parts of stearic acid, 3 parts of 3- TSL 8330,25 parts of water.