CN109928687A - Inorganic artificial stone formula - Google Patents
Inorganic artificial stone formula Download PDFInfo
- Publication number
- CN109928687A CN109928687A CN201910312346.8A CN201910312346A CN109928687A CN 109928687 A CN109928687 A CN 109928687A CN 201910312346 A CN201910312346 A CN 201910312346A CN 109928687 A CN109928687 A CN 109928687A
- Authority
- CN
- China
- Prior art keywords
- artificial stone
- model
- water
- agent
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses inorganic artificial stone formulas, are prepared from the following raw materials: including cement 10%-35%, aggregate composition 65%-90%, P29 model water-reducing agent 0.2%-.0.5%, P5044 model reinforcing agent 0.8%-1.0%, P031 model curing agent 0.02%, water purification 4%-8%；Aggregate composition is made by the materials stirring such as construction waste of sandstone, tailing slag, useless ceramic tile broken material, various low water absorptions；By using inorganic artificial stone formula of the invention, compare the artificial stone of conventional formulation manufacture, have the characteristics that hardness is big and intensity is high, and due to using inorganic pollution-free formula, it can guarantee that atelier is neatly hygienic in making artificial stone, and the artificial stone of production is using also having the characteristics that environmental protection, while this formula can be used the mode of assembly line and produce, and significantly increase production efficiency.
Description
Technical field
The invention belongs to artificial stone technical fields, and in particular to inorganic artificial stone formula.
Background technique 1
Artificial stone typically refers to artificial solid material, artificial stone quartz, artificial stone hilllock stone etc..Artificial stone type is not
Together, ingredient is also not quite similar.Ingredient is mainly resin, aluminium powder, pigment and curing agent.Using high molecular functional archiotecture material
Material, manufacturing process is a kind of chemical material reaction process, is generated and goes back with the progress of human society science and technology
It is that a kind of novel environment friendly is compound that the Practical science material artificial stone continuously improved, which is mainly used in architectural decoration it,
Material.
In the manufacturing process of existing artificial stone, since formula uses non-inorganic compounding, cause in process of production, production
The promotion of workshop condition is unable to improve, and the artificial stone manufactured out, because being caused using non-inorganic compounding using artificial
Shi Shihui generates pollution to environment and destroys, and artificial stone its own hardness and intensity it is lower, and existing artificial stone
Manufacturing process in can not use flow line production, the low problem of production efficiency, thus it is proposed that inorganic artificial stone formula.
Summary of the invention
The purpose of the present invention is to provide inorganic artificial stone formulas, mentioned above in the background art in the presence of pollution to solve
The lower problem with hardness and strength and production efficiency.
To achieve the above object, the invention provides the following technical scheme: the production method of inorganic artificial stone, uses three steps
Manufacturing process flow, first is that crushing and screening；Second is that proportion mixing；Third is that stirring compacting, concrete operation step are as follows:
(1) preparation of aggregate composition: the building of sandstone, tailing slag, useless ceramic tile broken material, various low water absorptions is given up
The materials such as material carry out crushing and screening.
(2) it adds cement: the cement of 10%-35% component is mixed with the aggregate composition of 65%-90% component.
(3) water-reducing agent is added: by mixture described in the P29 model water-reducing agent of 0.2%-.0.5% component and step (2)
Mixing.
(4) reinforcing agent is added: by mixture described in the P5044 model reinforcing agent of 0.8%-1.0% component and step (3)
Mixing.
(5) it adds curing agent: the P031 model curing agent of 0.02% component is mixed with mixture described in step (4).
(6) add and water purification and stir: by mixture described in step (5) and the water purification of 4%-8% component with mix.
(7) uniform stirring: and then at the uniform velocity and uniformly the stirring by mixing plant by mixture.
(8) compression moulding:, can be by inorganic artificial by the high pressure compression moulding of the mixture automatic hydraulic press stirred evenly
Stone completes.
Compared with prior art, the beneficial effects of the present invention are: being compared by using inorganic artificial stone formula of the invention
The artificial stone of conventional formulation manufacture has the characteristics that hardness is big and intensity is high, and due to using inorganic pollution-free formula, is making
It can guarantee that atelier is neatly hygienic when artificial stone, and the artificial stone made also has the characteristics that environmental protection in use, while originally matching
It can be produced by the way of assembly line, significantly increase production efficiency.
Detailed description of the invention
Fig. 1 is the strength relationship figure of cement and aggregate proportion and artificial stone in this formula；
Fig. 2 is this additives in raw materials content and the intensity and water absorption rate of artificial stone with reference to figure；
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Embodiment one
As shown in Figure 1, the present invention provides a kind of technical solution: inorganic artificial stone formula, including following component: cement
15%, aggregate composition 79.98%, P29 model water-reducing agent 0.2%, P5044 model reinforcing agent 0.8%, the solidification of P031 model
Agent 0.02%, water purification 4%.
The present embodiment, it is preferred that water-reducing agent is a kind of water-reducing agent of P29 model.
A kind of the present embodiment, it is preferred that reinforcing agent of P5044 model when reinforcing agent.
The present embodiment, it is preferred that curing agent is a kind of curing agent of P031 model.
Inorganic artificial stone makes according to the following steps: the aggregate composition of 79.98% component of cement of 15% component is mixed
It closes, then adds water-reducing agent, the P29 model water-reducing agent of 0.2% component is mixed with said mixture, then adds reinforcing agent, it will
The P5044 model reinforcing agent of 0.8% component is mixed with said mixture, and adds curing agent, by the P031 type of 0.02% component
Number curing agent is mixed with said mixture, and addition water purification is simultaneously stirred, then by the water purification of mixture described above and 4% component and
Mixing, last uniform stirring and compression moulding will stir evenly mixture at the uniform velocity and uniformly stirring by mixing plant
Mixture by the high pressure compression moulding of automatic hydraulic press, inorganic artificial stone can be completed, use this formula producer
Make stone strength criterion >=7.0.
Embodiment two
As shown in Figure 1, the present invention provides a kind of technical solution: inorganic artificial stone formula, including following component: cement
20%, aggregate composition 74.98%, P29 model water-reducing agent 0.2%, P5044 model reinforcing agent 0.8%, the solidification of P031 model
Agent 0.02%, water purification 4%.
The present embodiment, it is preferred that water-reducing agent is a kind of water-reducing agent of P29 model.
A kind of the present embodiment, it is preferred that reinforcing agent of P5044 model when reinforcing agent.
The present embodiment, it is preferred that curing agent is a kind of curing agent of P031 model.
Inorganic artificial stone makes according to the following steps:, the aggregate composition of 74.98% component of cement of 20% component is mixed
It closes, then adds water-reducing agent, the P29 model water-reducing agent of 0.2% component is mixed with said mixture, then adds reinforcing agent, it will
The P5044 model reinforcing agent of 0.8% component is mixed with said mixture, and adds curing agent, by the P031 type of 0.02% component
Number curing agent is mixed with said mixture, and addition water purification is simultaneously stirred, then by the water purification of mixture described above and 4% component and
Mixing, last uniform stirring and compression moulding will stir evenly mixture at the uniform velocity and uniformly stirring by mixing plant
Mixture by the high pressure compression moulding of automatic hydraulic press, inorganic artificial stone can be completed, use this formula producer
Make stone strength criterion >=7.5.
Embodiment three
As shown in Figure 1, the present invention provides a kind of technical solution: inorganic artificial stone formula, including following component: cement
25%, aggregate composition 69.98%, P29 model water-reducing agent 0.2%, P5044 model reinforcing agent 0.8%, the solidification of P031 model
Agent 0.02%, water purification 4%.
The present embodiment, it is preferred that water-reducing agent is a kind of water-reducing agent of P29 model.
A kind of the present embodiment, it is preferred that reinforcing agent of P5044 model when reinforcing agent.
The present embodiment, it is preferred that curing agent is a kind of curing agent of P031 model.
Inorganic artificial stone makes according to the following steps: the aggregate composition of 69.98% component of cement of 25% component is mixed
It closes, then adds water-reducing agent, the P29 model water-reducing agent of 0.2% component is mixed with said mixture, then adds reinforcing agent, it will
The P5044 model reinforcing agent of 0.8% component is mixed with said mixture, and adds curing agent, by the P031 type of 0.02% component
Number curing agent is mixed with said mixture, and addition water purification is simultaneously stirred, then by the water purification of mixture described above and 4% component and
Mixing, last uniform stirring and compression moulding will stir evenly mixture at the uniform velocity and uniformly stirring by mixing plant
Mixture by the high pressure compression moulding of automatic hydraulic press, inorganic artificial stone can be completed, use this formula producer
Make stone strength criterion >=8.0.
Example IV
As depicted in figs. 1 and 2, the present invention provides a kind of technical solution: inorganic artificial stone formula, including following component: water
Mud 30%, aggregate composition 64.98%, P29 model water-reducing agent 0.2%, P5044 model reinforcing agent 0.8%, the solidification of P031 model
Agent 0.02%, water purification 4%.
The present embodiment, it is preferred that water-reducing agent is a kind of water-reducing agent of P29 model.
A kind of the present embodiment, it is preferred that reinforcing agent of P5044 model when reinforcing agent.
The present embodiment, it is preferred that curing agent is a kind of curing agent of P031 model.
Inorganic artificial stone makes according to the following steps: the aggregate composition of 64.98% component of cement of 30% component is mixed
It closes, then adds water-reducing agent, the P29 model water-reducing agent of 0.2% component is mixed with said mixture, then adds reinforcing agent, it will
The P5044 model reinforcing agent of 0.8% component is mixed with said mixture, and adds curing agent, by the P031 type of 0.02% component
Number curing agent is mixed with said mixture, and addition water purification is simultaneously stirred, then by the water purification of mixture described above and 4% component and
Mixing, last uniform stirring and compression moulding will stir evenly mixture at the uniform velocity and uniformly stirring by mixing plant
Mixture by the high pressure compression moulding of automatic hydraulic press, inorganic artificial stone can be completed, use this formula producer
Make stone strength criterion >=8.5.
It can be seen that, with the increase of cement content, the intensity of artificial stone increases therewith in the case where ceteris paribus
Add, but cost is also promoted therewith, at the same can also the raw material difference of aggregate adjust, aggregate adhesive property is good, and intensity is high, can
Suitably to reduce cement amount, final purpose is to ensure that product strength is up to standard, and as described in Figure 2, with water-reducing agent and reinforcing agent
Content increase, the intensity of the artificial stone of output increases therewith, but water absorption rate is then as the content of water-reducing agent and reinforcing agent increases
And reduce, in conclusion artificial stone formula can be adjusted according to the different demands and different use environments of user,
Production cost is reduced with this, by maximum revenue.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. inorganic artificial stone formula, which is characterized in that be prepared from the following raw materials: including cement 10%-35%, aggregate composition
65%-90%, P29 model water-reducing agent 0.2%-.0.5%, P5044 model reinforcing agent 0.8%-1.0%, P031 model curing agent
0.02%, water purification 4%-8%.
2. inorganic artificial stone formula according to claim 1, it is characterised in that: the aggregate composition is by sandstone, tailing
The materials stirring such as construction waste of slag, useless ceramic tile broken material, various low water absorptions is made into.
3. inorganic artificial stone formula according to claim 1, it is characterised in that: the water-reducing agent is a kind of P29 model
Water-reducing agent.
4. inorganic artificial stone formula according to claim 1, it is characterised in that: a kind of P5044 model when the reinforcing agent
Reinforcing agent.
5. inorganic artificial stone formula according to claim 1, it is characterised in that: the curing agent is a kind of P031 model
Curing agent.
6. the production method of inorganic artificial stone according to claim 1, includes the following steps.
(1) preparation of aggregate composition: by sandstone, tailing slag, useless ceramic tile broken material, construction waste of various low water absorptions etc.
Material carries out crushing and screening.
(2) it adds cement: the cement of 10%-35% component is mixed with the aggregate composition of 65%-90% component.
(3) it adds water-reducing agent: the P29 model water-reducing agent of 0.2%-0.5% component is mixed with mixture described in step (2).
(4) reinforcing agent is added: mixture described in the P5044 model reinforcing agent of 0.8%-1.0% component and step (3) is mixed
It closes.
(5) it adds curing agent: the P031 model curing agent of 0.02% component is mixed with mixture described in step (4).
(6) add and water purification and stir: by mixture described in step (5) and the water purification of 4%-8% component with mix.
(7) uniform stirring: and then at the uniform velocity and uniformly the stirring by mixing plant by mixture.
(8) compression moulding:, can be made of stones by inorganic artificial by the high pressure compression moulding of the mixture automatic hydraulic press stirred evenly
It completes.