CN109928026A - A kind of corrosion-proof packing box and preparation method thereof - Google Patents
A kind of corrosion-proof packing box and preparation method thereof Download PDFInfo
- Publication number
- CN109928026A CN109928026A CN201910076951.XA CN201910076951A CN109928026A CN 109928026 A CN109928026 A CN 109928026A CN 201910076951 A CN201910076951 A CN 201910076951A CN 109928026 A CN109928026 A CN 109928026A
- Authority
- CN
- China
- Prior art keywords
- corrosion
- blender
- packing box
- wall
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of corrosion-proof packing box, the packing box includes box body and top cover, and the outer wall and inner wall of the box body and the top cover are equipped with corrosion-resistant coating, and the outer wall positioned at the outside of the packing box corrosion-resistant coating is equipped with the Zhuo Guang colored varnish；The present invention, pass through stock, oil liquid mixing, lipid is added, powder class is added, add anti-corrosion oxide-based, adding additives, defoaming cooling, purged and packed box, after anticorrosion with painting liquid and spary Zhuo Guang colored varnish sequence of operations, it can be made into corrosion-proof packing box best in quality, the anticorrosion fluid viscosity of preparation is moderate, it is not easy to be layered, convenient for spraying, bubble-free generates, each component sufficiently combines, comprehensive performance is preferable, so that anticorrosion liquid is capable of forming preferable film after spray coating, it is not likely to produce crackle, film-formation result is preferable, adhesion is preferable, it is not easily to fall off, substantially increase the antiseptic property of packing box.
Description
Technical field
The invention belongs to box technology fields, more specifically more particularly to a kind of corrosion-proof packing box.Meanwhile this hair
A kind of bright preparation method for further relating to corrosion-proof packing box.
Background technique
Packing box can classify such as the term suggests being exactly the box for being used to pack product by material: carton, can,
Wooden box, cloth box, skin box, acrylic box, corrugated package box, pvc box etc. can also classify such as: moon cake by the title of product
Box, tea caddy, fructus lycii box, bonbon box, exquisite gift box, local and special products box, wine box, chocolate box, food and medicine health care product box, food
Packing box, tea packaging box, writing case etc..It packs kit function: guaranteeing the safety of product in transport, promote the class etc. of product.
With the high speed development and continuous improvement of people's living standards of modern industry, people will constantly increase the demand of packing box
Add, and higher requirements are also raised to the quality of can.Short version living-article increases, improves processing quality, reduces production cost
It is equally the market pressure and problem that carton package enterprise is faced, this requires new skill is applied in iron box packing production process
Art is continuously improved the degree of automation of equipment, reduces the adjustment time of equipment and the auxiliary time of living-article.It is only constantly suitable
It answers the new change in market, meet the requirement of different user, the competitiveness of packing box wrapping enterprise could be improved.
Packing box is poor using very extensive but traditional packing box anticorrosion ability, and traditional use is in packaging outer box wall
Anticorrosion with painting loses liquid, and technique is unreasonable, and traditional anticorrosion liquid anticorrosion ability is poor, is not easy to spray, poor adhesion, is easy
Tomography haves the defects that certain, it is therefore desirable to design.
Summary of the invention
It is traditional the purpose of the present invention is to solve traditional packing box anticorrosion ability existing in the prior art is poor
Liquid is lost using in packaging outer box wall anticorrosion with painting, technique is unreasonable, and traditional anticorrosion liquid anticorrosion ability is poor, is not easy to spray
It applies, poor adhesion, easy tomography, and a kind of corrosion-proof packing box and preparation method thereof proposed.
To achieve the above object, the invention provides the following technical scheme: a kind of corrosion-proof packing box, the packing box include box
The outer wall and inner wall of body and top cover, the box body and the top cover are equipped with corrosion-resistant coating, positioned at the outside of packing box institute
The outer wall for stating corrosion-resistant coating is equipped with the Zhuo Guang colored varnish.
Preferably, the corrosion-resistant coating in parts by weight each group be grouped as it is as follows: anti-corrosion is 5-10 parts oxide-based, antiseptin
6-8 parts of class, 6-8 parts of polyacrylate emulsion, 3-7 parts of polystyrene acrylic acid lotion, 9-11 parts of dodecyl sodium sulfate lotion, silicon
7-9 parts of acrylic emulsion, 6-10 parts of epoxy resin, 15-20 parts of modified organic silicone resin, 9-13 parts of binder, defoaming agent 5-7, mineral
20-30 parts of base oil.
Preferably, oxide-based zirconium oxide, boron nitride, silicon nitride, titanium nitride and the magnesia by equal weight of the anti-corrosion mixes
It is combined into.
Preferably, the antiseptin class is made of equal weight amino resins powder, aluminium powder, the mixing of composite Nano titanium-iron powder.
The present invention also provides a kind of preparation methods of corrosion-proof packing box, include the following steps:
S1, stock: above-mentioned raw materials are first weighed；
S2, oil liquid mixing: first mineral base oil is added in blender, the temperature slowly increased in blender is Celsius to 50-60
Degree, then pours into stirring for polyacrylate emulsion, polystyrene acrylic acid lotion, dodecyl sodium sulfate lotion and silicone acrylic emulsion
In machine, controlling blender is 20-40r/min, is stirred 20 minutes；
S3, lipid is added: the revolving speed in blender is improved to 60-80r/min, the temperature in blender is increased to 70-80
Degree Celsius, then epoxy resin and modified organic silicone resin are added in blender, stirred 10 minutes；
S4, be added powder class: the revolving speed in blender is improved to 90-100r/min, be kept stirring it is temperature-resistant in machine, then
Antiseptin class is added in blender, is stirred 20 minutes；
S5 plus anti-corrosion are oxide-based: the revolving speed being kept stirring in machine is constant, the temperature in blender is improved Celsius to 80-90
Degree stirs 25 minutes；
S6, adding additives: being added binder, and stirring built-in temperature is then increased to 90-95 degrees Celsius, will improve blender
Revolving speed is increased to 120-160r/min, and blender stirs 5-15 minutes；
S7, defoaming cooling: and then defoaming agent is added, the temperature in blender is slowly reduced to room temperature, anticorrosion liquid is made.
S8, purged and packed box: box body and top cover outer wall and inner wall to packing box are cleaned comprehensively, and then flood is dry；
S9, anticorrosion with painting liquid: anticorrosion liquid made from step S7 is uniformly sprayed using high-pressure sprayer spray gun and is dried in cleaning
Box body and top cover outer wall and inner wall after dry, are then dried by drying box, i.e., anticorrosion are made on the surface of box body and top cover
Layer；
S10, the spary Zhuo Guang colored varnish: by the outer wall spary Zhuo Guang colored varnish of the packing box with corrosion-resistant coating, then pass through baking
Dry case is dried.
Preferably, the blender is DF-101S heat collecting type heated at constant temperature magnetic stirrer.
Preferably, in S2, S3, S5 and S6, temperature increase rate is 1 degrees celsius/minute.
Preferably, it in S4, before antiseptin class is added, needs to grind antiseptin class, then leads to 100 purposes again
After screen filtration, add in blender.
Preferably, in S9, after first being filtered with the mesh screen of 100 mesh to anticorrosion liquid, recycle high-pressure sprayer spray gun that will prevent
Corrosive liquid uniformly sprays the box body after cleaning, drying and top cover outer wall and inner wall.
Preferably, in S9 and S10, for drying box when being worked, controlling the temperature inside drying box is that 80-90 is Celsius
Degree, drying time period 20-30 minutes.
Technical effect and advantage of the invention: it is of the invention, by stock, oil liquid mixing, addition lipid, addition powder class, add
Anti-corrosion is oxide-based, adding additives, defoams cooling, purged and packed box, anticorrosion with painting liquid and a series of behaviour of the spary Zhuo Guang colored varnish
After work, corrosion-proof packing box best in quality can be made into, the anticorrosion fluid viscosity of preparation is moderate, is not easy to be layered, is convenient for spraying, without gas
Bubble generates, each component sufficiently combines, and comprehensive performance is preferable, so that anticorrosion liquid is capable of forming preferable film after spray coating, no
It is also easy to produce crackle, film-formation result is preferable, and adhesion is preferable, and it is not easily to fall off, substantially increase the antiseptic property of packing box.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.Based on the embodiments of the present invention, those of ordinary skill in the art are not before making creative work
Every other embodiment obtained is put, shall fall within the protection scope of the present invention.
Embodiment 1
A kind of corrosion-proof packing box, the packing box include box body and top cover, and the outer wall and inner wall of the box body and the top cover are equal
Equipped with corrosion-resistant coating, the outer wall positioned at the outside of the packing box corrosion-resistant coating is equipped with the Zhuo Guang colored varnish.
Further, the corrosion-resistant coating in parts by weight each group be grouped as it is as follows: anti-corrosion is 5 parts oxide-based, antiseptin
6 parts of class, 6 parts of polyacrylate emulsion, 3 parts of polystyrene acrylic acid lotion, 9 parts of dodecyl sodium sulfate lotion, silicone acrylic emulsion 7
Part, 6 parts of epoxy resin, 15 parts of modified organic silicone resin, 9 parts of binder, defoaming agent 5,20 parts of mineral base oil.
Further, oxide-based zirconium oxide, boron nitride, silicon nitride, titanium nitride and the magnesia by equal weight of the anti-corrosion
Mixing composition.
Further, the antiseptin class is made of equal weight amino resins powder, aluminium powder, the mixing of composite Nano titanium-iron powder.
The present invention also provides a kind of preparation methods of corrosion-proof packing box, include the following steps:
S1, stock: above-mentioned raw materials are first weighed；
S2, oil liquid mixing: first will mineral base oil be added blender in, slowly increase blender in temperature to 50 degrees Celsius,
Then polyacrylate emulsion, polystyrene acrylic acid lotion, dodecyl sodium sulfate lotion and silicone acrylic emulsion are poured into blender
In, controlling blender is 20r/min, is stirred 20 minutes；
S3, lipid is added: the revolving speed in blender is improved to 60r/min, the temperature in blender is increased to 70 degrees Celsius,
Then epoxy resin and modified organic silicone resin are added in blender, are stirred 10 minutes；
S4, powder class is added: the revolving speed in blender is improved to 90r/min, be kept stirring temperature-resistant in machine, then will prevent
Rotten powder class is added in blender, stirs 20 minutes；
S5 plus anti-corrosion are oxide-based: the revolving speed being kept stirring in machine is constant, and the temperature in blender is improved to 80 degrees Celsius,
Stirring 25 minutes；
S6, adding additives: being added binder, and stirring built-in temperature is then increased to 90 degrees Celsius, will improve turning for blender
Speed is increased to 120r/min, and blender stirs 5 minutes；
S7, defoaming cooling: and then defoaming agent is added, the temperature in blender is slowly reduced to room temperature, anticorrosion liquid is made.
S8, purged and packed box: box body and top cover outer wall and inner wall to packing box are cleaned comprehensively, and then flood is dry；
S9, anticorrosion with painting liquid: anticorrosion liquid made from step S7 is uniformly sprayed using high-pressure sprayer spray gun and is dried in cleaning
Box body and top cover outer wall and inner wall after dry, are then dried by drying box, i.e., anticorrosion are made on the surface of box body and top cover
Layer；
S10, the spary Zhuo Guang colored varnish: by the outer wall spary Zhuo Guang colored varnish of the packing box with corrosion-resistant coating, then pass through baking
Dry case is dried.
Further, the blender is DF-101S heat collecting type heated at constant temperature magnetic stirrer.
Further, in S2, S3, S5 and S6, temperature increase rate is 1 degrees celsius/minute.
Further, it in S4, before antiseptin class is added, needs to grind antiseptin class, then leads to 100 mesh again
Screen filtration after, add in blender.
Further, in S9, after first being filtered with the mesh screen of 100 mesh to anticorrosion liquid, recycle high-pressure sprayer spray gun will
Anticorrosion liquid uniformly sprays the box body after cleaning, drying and top cover outer wall and inner wall.
Further, in S9 and S10, for drying box when being worked, controlling the temperature inside drying box is 80 degrees Celsius,
Drying time period 20 minutes.
Embodiment 2
A kind of corrosion-proof packing box, the packing box include box body and top cover, and the outer wall and inner wall of the box body and the top cover are equal
Equipped with corrosion-resistant coating, the outer wall positioned at the outside of the packing box corrosion-resistant coating is equipped with the Zhuo Guang colored varnish.
Further, the corrosion-resistant coating in parts by weight each group be grouped as it is as follows: anti-corrosion is 10 parts oxide-based, antiseptin
8 parts of class, 8 parts of polyacrylate emulsion, 7 parts of polystyrene acrylic acid lotion, 11 parts of dodecyl sodium sulfate lotion, silicone acrylic emulsion 9
Part, 10 parts of epoxy resin, 20 parts of modified organic silicone resin, 13 parts of binder, defoaming agent 7,30 parts of mineral base oil.
Further, oxide-based zirconium oxide, boron nitride, silicon nitride, titanium nitride and the magnesia by equal weight of the anti-corrosion
Mixing composition.
Further, the antiseptin class is made of equal weight amino resins powder, aluminium powder, the mixing of composite Nano titanium-iron powder.
The present invention also provides a kind of preparation methods of corrosion-proof packing box, include the following steps:
S1, stock: above-mentioned raw materials are first weighed；
S2, oil liquid mixing: first will mineral base oil be added blender in, slowly increase blender in temperature to 60 degrees Celsius,
Then polyacrylate emulsion, polystyrene acrylic acid lotion, dodecyl sodium sulfate lotion and silicone acrylic emulsion are poured into blender
In, controlling blender is 40r/min, is stirred 20 minutes；
S3, lipid is added: the revolving speed in blender is improved to 80r/min, the temperature in blender is increased to 80 degrees Celsius,
Then epoxy resin and modified organic silicone resin are added in blender, are stirred 10 minutes；
S4, be added powder class: the revolving speed in blender is improved to 100r/min, be kept stirring it is temperature-resistant in machine, then will
Antiseptin class is added in blender, stirs 20 minutes；
S5 plus anti-corrosion are oxide-based: the revolving speed being kept stirring in machine is constant, and the temperature in blender is improved to 90 degrees Celsius,
Stirring 25 minutes；
S6, adding additives: being added binder, and stirring built-in temperature is then increased to 95 degrees Celsius, will improve turning for blender
Speed is increased to 160r/min, and blender stirs 15 minutes；
S7, defoaming cooling: and then defoaming agent is added, the temperature in blender is slowly reduced to room temperature, anticorrosion liquid is made.
S8, purged and packed box: box body and top cover outer wall and inner wall to packing box are cleaned comprehensively, and then flood is dry；
S9, anticorrosion with painting liquid: anticorrosion liquid made from step S7 is uniformly sprayed using high-pressure sprayer spray gun and is dried in cleaning
Box body and top cover outer wall and inner wall after dry, are then dried by drying box, i.e., anticorrosion are made on the surface of box body and top cover
Layer；
S10, the spary Zhuo Guang colored varnish: by the outer wall spary Zhuo Guang colored varnish of the packing box with corrosion-resistant coating, then pass through baking
Dry case is dried.
Further, the blender is DF-101S heat collecting type heated at constant temperature magnetic stirrer.
Further, in S2, S3, S5 and S6, temperature increase rate is 1 degrees celsius/minute.
Further, it in S4, before antiseptin class is added, needs to grind antiseptin class, then leads to 100 mesh again
Screen filtration after, add in blender.
Further, in S9, after first being filtered with the mesh screen of 100 mesh to anticorrosion liquid, recycle high-pressure sprayer spray gun will
Anticorrosion liquid uniformly sprays the box body after cleaning, drying and top cover outer wall and inner wall.
Further, in S9 and S10, for drying box when being worked, controlling the temperature inside drying box is 90 degrees Celsius,
Drying time period 30 minutes.
Embodiment 3
A kind of corrosion-proof packing box, the packing box include box body and top cover, and the outer wall and inner wall of the box body and the top cover are equal
Equipped with corrosion-resistant coating, the outer wall positioned at the outside of the packing box corrosion-resistant coating is equipped with the Zhuo Guang colored varnish.
Further, the corrosion-resistant coating in parts by weight each group be grouped as it is as follows: anti-corrosion is 8 parts oxide-based, antiseptin
7 parts of class, 7 parts of polyacrylate emulsion, 5 parts of polystyrene acrylic acid lotion, 10 parts of dodecyl sodium sulfate lotion, silicone acrylic emulsion 8
Part, 7 parts of epoxy resin, 16 parts of modified organic silicone resin, 11 parts of binder, defoaming agent 6,25 parts of mineral base oil.
Further, oxide-based zirconium oxide, boron nitride, silicon nitride, titanium nitride and the magnesia by equal weight of the anti-corrosion
Mixing composition.
Further, the antiseptin class is made of equal weight amino resins powder, aluminium powder, the mixing of composite Nano titanium-iron powder.
The present invention also provides a kind of preparation methods of corrosion-proof packing box, include the following steps:
S1, stock: above-mentioned raw materials are first weighed；
S2, oil liquid mixing: first will mineral base oil be added blender in, slowly increase blender in temperature to 55 degrees Celsius,
Then polyacrylate emulsion, polystyrene acrylic acid lotion, dodecyl sodium sulfate lotion and silicone acrylic emulsion are poured into blender
In, controlling blender is 25r/min, is stirred 20 minutes；
S3, lipid is added: the revolving speed in blender is improved to 65r/min, the temperature in blender is increased to 75 degrees Celsius,
Then epoxy resin and modified organic silicone resin are added in blender, are stirred 10 minutes；
S4, powder class is added: the revolving speed in blender is improved to 95r/min, be kept stirring temperature-resistant in machine, then will prevent
Rotten powder class is added in blender, stirs 20 minutes；
S5 plus anti-corrosion are oxide-based: the revolving speed being kept stirring in machine is constant, and the temperature in blender is improved to 85 degrees Celsius,
Stirring 25 minutes；
S6, adding additives: being added binder, and stirring built-in temperature is then increased to 90 degrees Celsius, will improve turning for blender
Speed is increased to 140r/min, and blender stirs 10 minutes；
S7, defoaming cooling: and then defoaming agent is added, the temperature in blender is slowly reduced to room temperature, anticorrosion liquid is made.
S8, purged and packed box: box body and top cover outer wall and inner wall to packing box are cleaned comprehensively, and then flood is dry；
S9, anticorrosion with painting liquid: anticorrosion liquid made from step S7 is uniformly sprayed using high-pressure sprayer spray gun and is dried in cleaning
Box body and top cover outer wall and inner wall after dry, are then dried by drying box, i.e., anticorrosion are made on the surface of box body and top cover
Layer；
S10, the spary Zhuo Guang colored varnish: by the outer wall spary Zhuo Guang colored varnish of the packing box with corrosion-resistant coating, then pass through baking
Dry case is dried.
Further, the blender is DF-101S heat collecting type heated at constant temperature magnetic stirrer.
Further, in S2, S3, S5 and S6, temperature increase rate is 1 degrees celsius/minute.
Further, it in S4, before antiseptin class is added, needs to grind antiseptin class, then leads to 100 mesh again
Screen filtration after, add in blender.
Further, in S9, after first being filtered with the mesh screen of 100 mesh to anticorrosion liquid, recycle high-pressure sprayer spray gun will
Anticorrosion liquid uniformly sprays the box body after cleaning, drying and top cover outer wall and inner wall.
Further, in S9 and S10, for drying box when being worked, controlling the temperature inside drying box is 85 degrees Celsius,
Drying time period 25 minutes.
In summary: a kind of corrosion-proof packing box provided by the invention and preparation method thereof, by stock, oil liquid mixing plus
Enter lipid, powder class is added, adds oxide-based anti-corrosion, adding additives, defoaming cooling, purged and packed box, anticorrosion with painting liquid and spary
After Zhuo Guang colored varnish sequence of operations, corrosion-proof packing box best in quality can be made into；, antiseptin class oxide-based by anti-corrosion,
Polyacrylate emulsion, polystyrene acrylic acid lotion, dodecyl sodium sulfate cream, silicone acrylic emulsion, epoxy resin, modified organic silicon
The collective effect of resin, binder, defoaming agent, mineral base oil can be made the anticorrosion liquid of function admirable, be mentioned by binder
The high viscosity of anticorrosion liquid, the foam of anticorrosion liquid is eliminated by defoaming agent, recycles high-pressure sprayer spray gun by anti-corrosion
Erosion liquid uniformly sprays the box body after cleaning, drying and top cover outer wall and inner wall, is finally dried, substantially increases packaging
The Corrosion Protection of box, the processing step for preparing anticorrosion liquid is fairly simple, easy to accomplish, and the anticorrosion fluid viscosity of preparation is suitable
In, be not easy to be layered, convenient for spraying, bubble-free generate, each component sufficiently combines, comprehensive performance is preferable, so that anticorrosion liquid is spraying
It is capable of forming preferable film after painting, is not likely to produce crackle, film-formation result is preferable, and the anticorrosion liquid of preparation has preferable anti-corrosion
Corrosion energy, adhesion is preferable, not easily to fall off, substantially increases the antiseptic property of packing box.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (10)
1. a kind of corrosion-proof packing box, it is characterised in that: the packing box includes box body and top cover, the box body and the top cover
Outer wall and inner wall are equipped with corrosion-resistant coating, and it is transparent to be equipped with Zhuo Guang positioned at the outer wall of the outside of the packing box corrosion-resistant coating
Paint.
2. a kind of corrosion-proof packing box according to claim 1, it is characterised in that: corrosion-resistant coating each group in parts by weight
Be grouped as follows: anti-corrosion is 5-10 parts oxide-based, 6-8 parts of antiseptin class, 6-8 parts of polyacrylate emulsion, polystyrene acrylic acid
3-7 parts of lotion, 9-11 parts of dodecyl sodium sulfate lotion, 7-9 parts of silicone acrylic emulsion, 6-10 parts of epoxy resin, modified organic silicon tree
15-20 parts of rouge, 9-13 parts of binder, defoaming agent 5-7,20-30 parts of mineral base oil.
3. a kind of corrosion-proof packing box according to claim 2, it is characterised in that: the oxide-based oxygen by equal weight of the anti-corrosion
Change zirconium, boron nitride, silicon nitride, titanium nitride and magnesia mixing composition.
4. a kind of corrosion-proof packing box according to claim 2, it is characterised in that: the antiseptin class is by equal weight amino resins
Powder, aluminium powder, composite Nano titanium-iron powder mixing composition.
5. a kind of preparation method of corrosion-proof packing box as claimed in claim 2, characterized by the following steps:
S1, stock: above-mentioned raw materials are first weighed；
S2, oil liquid mixing: first mineral base oil is added in blender, the temperature slowly increased in blender is Celsius to 50-60
Degree, then pours into stirring for polyacrylate emulsion, polystyrene acrylic acid lotion, dodecyl sodium sulfate lotion and silicone acrylic emulsion
In machine, controlling blender is 20-40r/min, is stirred 20 minutes；
S3, lipid is added: the revolving speed in blender is improved to 60-80r/min, the temperature in blender is increased to 70-80
Degree Celsius, then epoxy resin and modified organic silicone resin are added in blender, stirred 10 minutes；
S4, be added powder class: the revolving speed in blender is improved to 90-100r/min, be kept stirring it is temperature-resistant in machine, then
Antiseptin class is added in blender, is stirred 20 minutes；
S5 plus anti-corrosion are oxide-based: the revolving speed being kept stirring in machine is constant, the temperature in blender is improved Celsius to 80-90
Degree stirs 25 minutes；
S6, adding additives: being added binder, and stirring built-in temperature is then increased to 90-95 degrees Celsius, will improve blender
Revolving speed is increased to 120-160r/min, and blender stirs 5-15 minutes；
S7, defoaming cooling: and then defoaming agent is added, the temperature in blender is slowly reduced to room temperature, anticorrosion liquid is made;
S8, purged and packed box: box body and top cover outer wall and inner wall to packing box are cleaned comprehensively, and then flood is dry；
S9, anticorrosion with painting liquid: anticorrosion liquid made from step S7 is uniformly sprayed using high-pressure sprayer spray gun and is dried in cleaning
Box body and top cover outer wall and inner wall after dry, are then dried by drying box, i.e., anticorrosion are made on the surface of box body and top cover
Layer；
S10, the spary Zhuo Guang colored varnish: by the outer wall spary Zhuo Guang colored varnish of the packing box with corrosion-resistant coating, then pass through baking
Dry case is dried.
6. a kind of preparation method of corrosion-proof packing box according to claim 5, it is characterised in that: the blender is DF-
101S heat collecting type heated at constant temperature magnetic stirrer.
7. a kind of preparation method of corrosion-proof packing box according to claim 5, it is characterised in that: in S2, S3, S5 and S6
In, temperature increase rate is 1 degrees celsius/minute.
8. a kind of preparation method of corrosion-proof packing box according to claim 5, it is characterised in that: anti-being added in S4
It before rotten powder class, needs to grind antiseptin class, after then leading to the screen filtration of 100 mesh again, add in blender.
9. a kind of preparation method of corrosion-proof packing box according to claim 5, it is characterised in that: in S9, first with 100 purposes
After mesh screen filters anticorrosion liquid, recycle high-pressure sprayer spray gun that anticorrosion liquid is uniformly sprayed to the box after cleaning, drying
Body and top cover outer wall and inner wall.
10. a kind of preparation method of corrosion-proof packing box according to claim 5, it is characterised in that: in S9 and S10, drying
For case when being worked, controlling the temperature inside drying box is 80-90 degrees Celsius, drying time period 20-30 minutes.