CN109926757A - Corrosion resistant type flux-cored wire - Google Patents
Corrosion resistant type flux-cored wire Download PDFInfo
- Publication number
- CN109926757A CN109926757A CN201711355814.7A CN201711355814A CN109926757A CN 109926757 A CN109926757 A CN 109926757A CN 201711355814 A CN201711355814 A CN 201711355814A CN 109926757 A CN109926757 A CN 109926757A
- Authority
- CN
- China
- Prior art keywords
- powder
- cored wire
- flux
- corrosion resistant
- resistant type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to flux-cored wire fields, especially corrosion resistant type flux-cored wire.The flux-cored wire all the components mass percent is as follows: rutile 30 ~ 42%, quartz 4 ~ 7%, magnesia 2 ~ 5%, potassium fluoride 3 ~ 6%, nickel powder 11 ~ 14%, crome metal 5 ~ 8%, mid-carbon fe-mn 6 ~ 9%, niobium powder 8 ~ 11%, molybdenum powder 1 ~ 5%, iron powder 4 ~ 7%, and surplus is hafnium powder.The invention is more more corrosion-resistant than conventional flux-cored wire.
Description
Technical field
The present invention relates to flux-cored wire fields, especially corrosion resistant type flux-cored wire.
Background technique
Flux-cored wire is a kind of novel welding material, has the advantage of the various aspects such as high benefit, low cost, high quality,
It is adjustable that it inherits components of welding electrode, but overcome welding rod cannot continuous, automatic welding the shortcomings that, also have high-efficient, appearance of weld
The series of advantages such as fairing beauty.Flux-cored wire has following features: high production efficiency, constituent adjustment compared with solid core welding wire
Flexibly, energy saving low pollution.Such as in shipbuilding industry, flux-cored wire has replaced stick electrode and solid welding wire, and it is maximum to become consumption
Welding material, and by its welding have high intensity, high tenacity, cracking resistance, anti-stomata excellent properties, have become and make
Ship, large bridge, ocean platform etc. build most important wlding.But existing medicinal powder formulation ratio is undesirable, and flux-cored wire is not
It is corrosion-resistant.
Summary of the invention
In order to overcome not corrosion resistant enough the deficiency of existing flux-cored wire, the present invention provides corrosion resistant type flux-cored wires.
The technical solution adopted by the present invention to solve the technical problems is: a kind of corrosion resistant type flux-cored wire, all the components
Mass percent is as follows: rutile 30 ~ 42%, quartz 4 ~ 7%, magnesia 2 ~ 5%, potassium fluoride 3 ~ 6%, nickel powder 11 ~ 14%, and crome metal 5 ~
8%, mid-carbon fe-mn 6 ~ 9%, niobium powder 8 ~ 11%, molybdenum powder 1 ~ 5%, iron powder 4 ~ 7%, surplus is hafnium powder.
Specifically, the rutile 35 ~ 42%, quartz 4 ~ 6%, magnesia 2 ~ 4%, potassium fluoride 3 ~ 5%, nickel powder 11 ~ 13%, metal
Chromium 5 ~ 7%, mid-carbon fe-mn 6 ~ 8%, niobium powder 8 ~ 10%, molybdenum powder 1 ~ 4%, iron powder 4 ~ 6%, surplus are hafnium powder.
Specifically, the rutile 40%, quartz 5%, magnesia 3%, potassium fluoride 4%, nickel powder 12%, crome metal 6%, medium carbon manganese
Iron 7%, niobium powder 9%, molybdenum powder 3%, iron powder 5%, surplus are hafnium powder.
The invention has the advantages that the invention is more more corrosion-resistant than conventional flux-cored wire.
Specific embodiment
Embodiment one
A kind of corrosion resistant type flux-cored wire, all the components mass percent are as follows: rutile 30 ~ 42%, quartz 4 ~ 7%, and magnesia 2 ~
5%, potassium fluoride 3 ~ 6%, nickel powder 11 ~ 14%, crome metal 5 ~ 8%, mid-carbon fe-mn 6 ~ 9%, niobium powder 8 ~ 11%, molybdenum powder 1 ~ 5%, iron powder 4 ~
7%, surplus is hafnium powder.
Embodiment two
A kind of corrosion resistant type flux-cored wire, all the components mass percent are as follows: the rutile 35 ~ 42%, quartz 4 ~ 6%, magnesium
Sand 2 ~ 4%, potassium fluoride 3 ~ 5%, nickel powder 11 ~ 13%, crome metal 5 ~ 7%, mid-carbon fe-mn 6 ~ 8%, niobium powder 8 ~ 10%, molybdenum powder 1 ~ 4%, iron
Powder 4 ~ 6%, surplus are hafnium powder.
Embodiment three
A kind of corrosion resistant type flux-cored wire, all the components mass percent are as follows: the rutile 40%, quartz 5%, magnesia 3%,
Potassium fluoride 4%, nickel powder 12%, crome metal 6%, mid-carbon fe-mn 7%, niobium powder 9%, molybdenum powder 3%, iron powder 5%, surplus are hafnium powder.
Claims (3)
1. a kind of corrosion resistant type flux-cored wire, characterized in that all the components mass percent is as follows: rutile 30 ~ 42%, quartz
4 ~ 7%, magnesia 2 ~ 5%, potassium fluoride 3 ~ 6%, nickel powder 11 ~ 14%, crome metal 5 ~ 8%, mid-carbon fe-mn 6 ~ 9%, niobium powder 8 ~ 11%, molybdenum powder 1
~ 5%, iron powder 4 ~ 7%, surplus is hafnium powder.
2. corrosion resistant type flux-cored wire according to claim 1, it is characterised in that: the rutile 35 ~ 42%, quartz 4 ~
6%, magnesia 2 ~ 4%, potassium fluoride 3 ~ 5%, nickel powder 11 ~ 13%, crome metal 5 ~ 7%, mid-carbon fe-mn 6 ~ 8%, niobium powder 8 ~ 10%, molybdenum powder 1 ~
4%, iron powder 4 ~ 6%, surplus is hafnium powder.
3. corrosion resistant type flux-cored wire according to claim 1, it is characterised in that: the rutile 40%, quartz 5%, magnesium
Sand 3%, potassium fluoride 4%, nickel powder 12%, crome metal 6%, mid-carbon fe-mn 7%, niobium powder 9%, molybdenum powder 3%, iron powder 5%, surplus are hafnium powder.