CN109913076A - A kind of synthetic paper is compound to use water quick-drying coating - Google Patents
A kind of synthetic paper is compound to use water quick-drying coating Download PDFInfo
- Publication number
- CN109913076A CN109913076A CN201910255335.0A CN201910255335A CN109913076A CN 109913076 A CN109913076 A CN 109913076A CN 201910255335 A CN201910255335 A CN 201910255335A CN 109913076 A CN109913076 A CN 109913076A
- Authority
- CN
- China
- Prior art keywords
- parts
- synthetic paper
- articulamentum
- coating
- silica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of compound water quick-drying coatings of synthetic paper, including terpene resin, titanium dioxide, polyamide alcohol-sol-resin, flatting silica, isopropanol, nitrocotton, aqueous acrylic emulsion, silica, ethyl ester, ink electrostatic agent, coating includes two layers, is respectively coated in the articulamentum on synthetic paper surface and coated in the surface layer on the articulamentum.The present invention adds silica in the coating, the production curing time of general synthetic paper is 3-4 days, it is added after silica, the dry solidification speed of coating foreshortens to 20-30 minutes, it substantially reduces synthetic paper and solidifies the required time, improve the efficiency of synthetic paper production, set coating to the combination of articulamentum and surface layer, articulamentum is for handling paper surface, and play the role of connecting surface layer and paper, so that coating bonding effect greatly promotes, surface layer modifies the surface of articulamentum, to provide the composed paper of surfacing.
Description
Technical field
The present invention relates to synthetic paper production coating technology fields, and in particular to a kind of synthetic paper is compound to be applied with water quick-drying
Layer.
Background technique
Synthetic paper (synthetic paper) be add the production of some additives using chemical raw material such as olefines and
At, with soft, stretching resistance is strong, water-resistance is high, fast light cold-hot and can resist chemical substance corrosion it is again dirty without environment
Dye, good permeability, the printing for being widely used for the advanced art work, map, picture album, high-grade books and periodicals etc. are divided by the difference of structure
Single layer synthetic paper, three layers of synthetic paper, five layers of synthetic paper.
Synthetic paper may require that carry out compound working procedure sometimes during production, and two or multiple synthetic papers are compounded in one
Rise, form new synthetic paper, generally understand applying coating on the surface of synthetic paper, the performance significant portion of coating determine it is compound after
The quality of synthetic paper, there is many problems for coating used at present, not environmentally such as coating, cause to pollute environment, the property of coating
Can be bad, there is the phenomenon that layering, fall off after fitting in synthetic paper, influences the quality of synthetic paper, and there are coating dryings
Time is too long, and the general synthetic paper dry solidification time is 3-4 days, and the efficiency of synthetic paper production is lower, and there are also coating surfaces to take
Static electrification is not handled electrostatic effectively, is caused paper when printing that cannot separate as early as possible, is existed to paper adsorption occur
Together the case where, causes printing machine to be shut down, and reduces the efficiency of synthetic paper printing.
Summary of the invention
Present invention aim to address above-mentioned deficiencies, provide a kind of synthetic paper compound water quick-drying coating.
To achieve the above object, technical solution provided by the invention is as follows: a kind of synthetic paper is compound to use water quick-drying coating,
Including terpene resin, titanium dioxide, polyamide alcohol-sol-resin, flatting silica, isopropanol, nitrocotton, aqueous acrylic emulsion, titanium dioxide
Silicon, ethyl ester, ink electrostatic agent, the coating include two layers, are respectively coated in the articulamentum on synthetic paper surface and are coated in
Surface layer on the articulamentum；
The articulamentum includes 30-35 parts of terpene resin, 50-60 parts of titanium dioxide, polyamide alcohol-sol-resin 15-25 by weight
Part, 4-8 parts of flatting silica, 15-25 parts of isopropanol；
The surface layer includes 48-58 parts of nitrocotton, 6-10 parts of flatting silica, 100-150 parts of aqueous acrylic emulsion, two by weight
8-12 parts of silica, 35-45 parts of ethyl ester, 20-30 parts of isopropanol, 0.5-1.5 parts of ink electrostatic agent.
Further, terpene resin used in the articulamentum is T-80 terpene resin.
Further, titanium dioxide used in the articulamentum is rutile type titanium white.
Further, the nitrocotton is 1/4 second nitrocotton.
Water quick-drying coating is used the invention discloses a kind of synthetic paper is compound, have it is following the utility model has the advantages that
1, the present invention can increase the adhesive force of coating using T-80 terpene resin；Rutile type titanium white is used to make coating
Performance increases and improves the weatherability of coating, and can be improved the duration of gloss and color after coating coating；
2, the present invention uses 1/4 second nitrocotton, for adjusting the consistency of coating；Using flatting silica, for the delustring of coating surface,
Disperse coating surface light, the coating of production department's matt effect；Use aqueous acrylic emulsion as the auxiliary agent in surface layer, improves
The coating performance of film surface；
3, the present invention adds silica in the coating, improves the dry solidification speed of coating, and the production of general synthetic paper is solid
Changing the time is 3-4 days, is added after silica, the dry solidification speed of coating foreshortens to 20-30 minutes, substantially reduces conjunction
Solidify the required time at paper, improves the efficiency of synthetic paper production；
4, the present invention adds ink electrostatic agent in the coating, and the electrostatic for going removing coating to carry is avoided because the presence of electrostatic causes
Paper adsorption together, the generation of situation is shut down so as to cause printing machine in printing process, so that the synthetic paper produced is printing
It can not shut down and be printed during brush, cost is greatly saved；
5, the combination of the invention by setting coating to articulamentum and surface layer, articulamentum are used to handle paper surface,
And play the role of connecting surface layer and paper, so that coating bonding effect greatly promotes, surface layer carries out the surface of articulamentum
Finishing, to provide the composed paper of surfacing.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiment is only a part of the embodiments of the present invention, instead of all the embodiments.It gives in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts,
Belong to the scope of protection of the invention.
Embodiment 1:
A kind of synthetic paper is compound to use water quick-drying coating, including terpene resin, titanium dioxide, polyamide alcohol-sol-resin, flatting silica, different
Propyl alcohol, nitrocotton, aqueous acrylic emulsion, silica, ethyl ester, ink electrostatic agent, the coating include two layers, are respectively applied
Overlay on the articulamentum on synthetic paper surface and coated in the surface layer on the articulamentum；
The articulamentum includes 30 parts of T-80 terpene resin, 50 parts of rutile type titanium white, polyamide alcohol-sol-resin by weight
15 parts, 4 parts of flatting silica, 15 parts of isopropanol；
The surface layer includes 1/4 second 48 parts of nitrocotton, 6 parts of flatting silica, 100 parts of aqueous acrylic emulsion, titanium dioxide by weight
8 parts of silicon, 35 parts of ethyl ester, 20 parts of isopropanol, 0.5 part of ink electrostatic agent.
Embodiment 2:
A kind of synthetic paper is compound to use water quick-drying coating, including terpene resin, titanium dioxide, polyamide alcohol-sol-resin, flatting silica, different
Propyl alcohol, nitrocotton, aqueous acrylic emulsion, silica, ethyl ester, ink electrostatic agent, the coating include two layers, are respectively applied
Overlay on the articulamentum on synthetic paper surface and coated in the surface layer on the articulamentum；
The articulamentum includes 30 parts of T-80 terpene resin, 55 parts of rutile type titanium white, polyamide alcohol-sol-resin by weight
18 parts, 5 parts of flatting silica, 20 parts of isopropanol；
The surface layer includes 1/4 second 50 parts of nitrocotton, 7 parts of flatting silica, 130 parts of aqueous acrylic emulsion, titanium dioxide by weight
10 parts of silicon, 40 parts of ethyl ester, 20 parts of isopropanol, 1 part of ink electrostatic agent.
Embodiment 3:
A kind of synthetic paper is compound to use water quick-drying coating, including terpene resin, titanium dioxide, polyamide alcohol-sol-resin, flatting silica, different
Propyl alcohol, nitrocotton, aqueous acrylic emulsion, silica, ethyl ester, ink electrostatic agent, the coating include two layers, are respectively applied
Overlay on the articulamentum on synthetic paper surface and coated in the surface layer on the articulamentum；
The articulamentum includes 35 parts of T-80 terpene resin, 60 parts of rutile type titanium white, polyamide alcohol-sol-resin by weight
25 parts, 8 parts of flatting silica, 25 parts of isopropanol；
The surface layer includes 1/4 second 58 parts of nitrocotton, 10 parts of flatting silica, 150 parts of aqueous acrylic emulsion, titanium dioxide by weight
12 parts of silicon, 45 parts of ethyl ester, 30 parts of isopropanol, 1.5 parts of ink electrostatic agent.
What has been described above is only an embodiment of the present invention, and well known characteristic common sense does not describe excessively herein in scheme.It answers
When pointing out, for those skilled in the art, under the premise of not departing from the present invention, several improvement are also made, these
Protection scope of the present invention should be shown in.
Claims (4)
1. a kind of synthetic paper is compound to use water quick-drying coating, it is characterised in that: molten including terpene resin, titanium dioxide, polyamides amine alcohol
Resin, flatting silica, isopropanol, nitrocotton, aqueous acrylic emulsion, silica, ethyl ester, ink electrostatic agent, the coating packet
It includes two layers, is respectively coated in the articulamentum on synthetic paper surface and coated in the surface layer on the articulamentum；
The articulamentum includes 30-35 parts of terpene resin, 50-60 parts of titanium dioxide, polyamide alcohol-sol-resin 15-25 by weight
Part, 4-8 parts of flatting silica, 15-25 parts of isopropanol；
The surface layer includes 48-58 parts of nitrocotton, 6-10 parts of flatting silica, 100-150 parts of aqueous acrylic emulsion, two by weight
8-12 parts of silica, 35-45 parts of ethyl ester, 20-30 parts of isopropanol, 0.5-1.5 parts of ink electrostatic agent.
2. a kind of synthetic paper as described in claim 1 is compound to use water quick-drying coating, it is characterised in that: make in the articulamentum
Terpene resin is T-80 terpene resin.
3. a kind of synthetic paper as described in claim 1 is compound to use water quick-drying coating, it is characterised in that: make in the articulamentum
Titanium dioxide is rutile type titanium white.
4. a kind of synthetic paper as described in claim 1 is compound to use water quick-drying coating, it is characterised in that: the nitrocotton is 1/
4 seconds nitrocottons.