CN109910491A - A kind of extension picture of releasable negative oxygen ion and preparation method thereof - Google Patents

A kind of extension picture of releasable negative oxygen ion and preparation method thereof Download PDF

Info

Publication number
CN109910491A
CN109910491A CN201910084759.5A CN201910084759A CN109910491A CN 109910491 A CN109910491 A CN 109910491A CN 201910084759 A CN201910084759 A CN 201910084759A CN 109910491 A CN109910491 A CN 109910491A
Authority
CN
China
Prior art keywords
negative oxygen
calligraphy
oxygen ion
parts
painting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910084759.5A
Other languages
Chinese (zh)
Inventor
王聚会
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhengzhou Gao Ju Powder Technology Co Ltd
Original Assignee
Zhengzhou Gao Ju Powder Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhengzhou Gao Ju Powder Technology Co Ltd filed Critical Zhengzhou Gao Ju Powder Technology Co Ltd
Priority to CN201910084759.5A priority Critical patent/CN109910491A/en
Publication of CN109910491A publication Critical patent/CN109910491A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of extension pictures of releasable negative oxygen ion, including bottom plate, the basal layer being coated on the bottom plate and the calligraphy and painting layer being produced on the basal layer, wherein, the material of the basal layer is inorganic coating, and the calligraphy and painting layer is drawn using the calligraphy and painting pigment of releasable negative oxygen ion.The pigment that calligraphy and painting layer in above-mentioned extension picture uses has the function of releasing negative oxygen ion, so that above-mentioned extension picture provided by the invention not only has artistic value, also has the effects that purify air, beautification indoor environment, health care.The present invention also provides a kind of production methods of above-mentioned extension picture.

Description

A kind of extension picture of releasable negative oxygen ion and preparation method thereof
Technical field
The present invention relates to interior decoration apparatus technical fields, and in particular to a kind of the extension picture and its system of releasable negative oxygen ion Make method.
Background technique
Picture is hung, it is a kind of room that one kind of decoration painting, which is constituted with multiple materials such as wooden, resin, plastics, hangs on interior, Indispensable ornament in interior trim is mainly used for modern house decoration.Hanging picture can be improved the aesthetics of interior decoration, increase Add indoor whole sentiment, embodies the artistic accomplishment and cultural taste of householder, relieving stress reduces fatigue etc..But existing extension picture Usually otherwise be made by the way of ink print or be that famous calligraphy and painting man writes.The extension that both modes make What picture generallyd use is all common ink, so that hanging the effect of picture only has value of art appreciation, do not have other.
Summary of the invention
In view of this, being drawn in it is necessory to the extension picture and preparation method thereof for providing a kind of releasable negative oxygen ion so that hanging While with artistic value, also has the function of environment-protecting health-care.
Therefore, the extension picture of a kind of releasable negative oxygen ion provided by the invention, including bottom plate, the base being coated on the bottom plate Plinth layer, and the calligraphy and painting layer being produced on the basal layer, wherein the material of the basal layer is inorganic coating, the calligraphy and painting layer It is drawn using the calligraphy and painting pigment of releasable negative oxygen ion.
Based on above-mentioned, the calligraphy and painting pigment includes the raw material of following mass parts: 5~10 parts of sierozem power, super finely ground slag 5~10 Part, 10~20 parts of white cement, 5~10 parts of latex powder, 25~40 parts of zeolite powder, 3~8 parts of tourmaline powder, Paris white 10~20 Part, 1~5 part of nano oxidized magnesium powder, 3~8 parts of diatomite, 2~8 parts of silica flour, 0.5~1.5 part of cellulose, defoaming agent 0.1~ 0.5 part and 5~10 parts of coloring earth, wherein the partial size of the sierozem power >=600 mesh, the zeolite powder and the tourmaline powder Partial size >=1000 mesh, 300 mesh of fineness > of the coloring earth.
Based on above-mentioned, the sierozem power, the super finely ground slag, the white cement and the latex powder mass ratio be 1:1: 2:1。
Based on above-mentioned, the basal layer is 1~3mm, and the material of the basal layer includes mixed uniformly dicalcium powder, zeolite Powder, tourmaline powder, white cement, barite, diatomite and cellulose.Preferably, in parts by mass, the material packet of the basal layer Include: 10~20 parts of dicalcium powder, 35~40 parts of zeolite powder, 6~8 parts of tourmaline powder, 10~15 parts of white cement, 5~15 parts of barite, 5~10 parts and 0.2~0.6 part of cellulose of diatomite, and 400~600 mesh of partial size of the zeolite powder and the tourmaline powder, It is more than 300 mesh of partial size of remaining raw material;The slurry that the material and water are mixed to prepare according to the ratio of 1:0.35 can be used to make base Plinth layer, the basal layer have many advantages, such as to dry in the shade it is fast, meet water and will not form water stain, environmental purification air.
Based on above-mentioned, negative oxygen ion function layer is provided between the basal layer and the calligraphy and painting layer.
Based on above-mentioned, the material of the negative oxygen ion function layer includes mixed uniformly sierozem power, super finely ground slag, plain boiled water Mud, latex powder, Paris white, zeolite powder, diatomite, silica flour, talcum powder, cellulose.Preferably, in parts by mass, described The material of negative oxygen ion function layer includes: 6~10 parts of sierozem power, 6~10 parts of super finely ground slag, 12~20 parts of white cement, latex powder 6 ~10 parts, 30~40 parts of zeolite powder, 4~6 parts of tourmaline powder, 12~18 parts of Paris white, 4~6 parts of diatomite, talcum powder 4~6 Part, 4~6 parts of silica flour, 0.5~1 part of cellulose, and 500~600 mesh of partial size of the zeolite powder and the tourmaline powder, institute State 300~400 mesh of partial size of sierozem power;The slurry that the material and water are mixed to prepare according to the ratio of 1:0.4 can be used to make The negative oxygen ion function layer, and there is the negative oxygen ion function layer releasing negative oxygen ion, fast, the chance water that dries in the shade will not be formed The advantages that water stain, environmental purification air.
Based on above-mentioned, the material of the bottom plate is timber or plastics.
When bottom plate is timber, timber is usually textured, and easy to form water stain, as background, influences calligraphy and painting effect;When When bottom plate is plastics, the calligraphy and painting of drafting is then not easy quickly to dry in the shade;The basal layer and negative oxygen ion layer, which have, to dry in the shade fastly, will not Form the advantages that water stain, so, can be coated on bottom plate according to actual needs, the background as calligraphy and painting, will not generate watermark or It is water stain, can also calligraphy and painting be made quickly to dry in the shade, the basal layer is equivalent to the paper in traditional calligraphy and painting.
The present invention also provides a kind of production methods of the extension picture of above-mentioned releasable negative oxygen ion, comprising the following steps:
The basal layer is coated on the bottom plate;By the calligraphy and painting pigment and water according to the ratio uniform of 1:0.6~0.8 Calligraphy and painting pigment mixture is made in mixing;Calligraphy and painting is made on the basal layer using the calligraphy and painting pigment mixture.
The production method of extension picture based on above-mentioned releasable negative oxygen ion, comprising: be coated in the material of the basal layer batch After on the floor, negative oxygen ion function material bullet is coated on the basal layer, forms negative oxygen ion function layer, then again The calligraphy and painting is made on the negative oxygen ion function layer.
Based on above-mentioned, the step of making the calligraphy and painting includes: to turn the calligraphy and painting pigment mixture in such a way that sun is carved It moves on on the negative oxygen ion function layer and makes the calligraphy and painting layer;Or by the calligraphy and painting pigment mixture as prepared Chinese ink directly in institute It states and draws calligraphy and painting on negative oxygen ion function layer to form the calligraphy and painting layer.
Compared with prior art, the basal layer is set in the extension picture of releasable negative oxygen ion provided by the invention, the base Plinth layer is equivalent to the paper in traditional calligraphy and painting, carrier and background as the calligraphy and painting layer;The pigment tool that the calligraphy and painting layer uses Have the function of releasing negative oxygen ion so that above-mentioned extension picture provided by the invention not only has an artistic value, also have purification air, The effects of beautifying indoor environment, health care.In addition, the present invention is by using the drawing pigment energy with releasing negative oxygen ion function So that hanging painter's paraphernalia has the functions such as environment purification, so that it is simple to hang picture structure.
Further, sierozem power, super finely ground slag, white cement and latex in the raw material for the drawing pigment that the present invention uses Powder mixes mixing, as the cementitious material in pigment, has the characteristics that intensity is high, durability is good and is firmly combined with substrate, especially It is when uniformly being mixed according to the mass ratio of sierozem power, super finely ground slag, white cement and latex powder for 1:1:2:1;The super finely ground slag Main component is silicon and aluminium element, and super finely ground slag activity with higher;The sierozem power be alkaline matter, mainly at It is divided into Ca (OH)2;The super finely ground slag and sierozem power can produce geopolymeric reaction, the drawing pigment add water and stir after Under room temperature, polymerization reaction occurs for the super finely ground slag and sierozem power, generates the drated calcium aluminate and aquation sial with gelling Melilite, reaction process are as follows:
Al2O3·2SiO2+M Ca(OH)2+n H2O→4CaO·3Al2O3·13H2O+X CaO·SiO2·YH2O。
The white cement and latex powder, which meet water, can also have gelling characteristic, so, the sierozem power, super finely ground slag, plain boiled water Mud and latex powder are used as cementitious material in the drawing pigment, mix with other component even adhesions, but also the drawing Pigment, for making calligraphy and painting, enables calligraphy and painting layer quickly to dry in the shade after water mixing.
Zeolite powder, tourmaline powder, nano magnesia and diatomite in the drawing pigment are filled out as functionality therein Material.The zeolite powder, tourmaline powder and diatomite are natural polar material, electrification, can hydrone in ionized air, by it It is ionized into hydrogen ion and hydroxide ion, hydroxide ion forms negative oxygen ion in conjunction with oxygen molecule, so zeolite powder, tourmaline Powder and diatomite all have the function of permanent releasing negative oxygen ion.Negative oxygen ion is electrically charged can to neutralize cation, have absorption The effect of PM2.5 and other air pellets and suspended matter in air, by its strong redox ability by formaldehyde, The pernicious gases such as TVOC resolve into harmless carbon dioxide and water, by sulfur dioxide, hydrogen sulfide, ammonia, the nitrogen oxides in air Equal gas purifications, but also the organism physiology activity of people can be generated beneficial to shadow by the nervous system and blood circulation of people Ring, therefore, the drawing pigment have the effects that environmental protection, purification air, health care, and these functions be implemented without additionally Energy auxiliary, such as electric energy, so that it may automatic to realize.
For the partial size of the zeolite powder and tourmaline powder more than 1000 mesh, particle is smaller so that its discharge negative oxygen from The function of son will improve tens times compared to the zeolite powder and tourmaline powder of 600 mesh of partial size, nano magnesia as anti-biotic material, There is stronger antibacterial activity than common magnesia, nano magnesia can not depend on illumination and just generate good antibacterial work Property, so, the functional filler in the drawing pigment is substantially superfine powder, substantially increases the property of functional filler Can, even if there is lesser area using the calligraphy and painting of drawing pigment production, it can also release a large amount of negative oxygen ion, it may have Preferable antibacterial action.The component of the drawing pigment is substantially all as inorganic material, so that the drawing pigment is environmentally friendly, is no different Taste.
Further, in the extension picture provided by the invention include negative oxygen ion function layer, can be further improved negative oxygen from The burst size of son.
The method that the present invention provides the releasable negative oxygen ion extension picture of production is fairly simple, easily operated.In addition, being applied using bullet Mode form negative oxygen ion function layer so that the specific surface area of the negative oxygen ion function layer is bigger, increase and air Contact area, to increase the burst size of negative oxygen ion.
Specific embodiment
Below by specific embodiment, technical scheme of the present invention will be described in further detail.
Embodiment 1
The present embodiment provides a kind of extension picture of releasable negative oxygen ion, size 0.8m × 1.2m of the extension picture, including plank, It is covered on the basal layer of the 2mm thickness on the plank, and the calligraphy and painting layer being produced on the basal layer, wherein the calligraphy and painting layer It is drawn using the calligraphy and painting pigment of releasable negative oxygen ion.Wherein, the calligraphy and painting pigment includes the raw material of following mass parts: ash 5 parts of calcium powder, 5 parts of super finely ground slag, 10 parts of white cement, 5 parts of latex powder, 25 parts of zeolite powder, 3 parts of tourmaline powder, 10 parts of Paris white, 1 part of nano oxidized magnesium powder, 3 parts of diatomite, 2 parts of silica flour, 0.5 part of cellulose, 0.1 part of defoaming agent and 5 parts of coloring earth, and institute State partial size >=600 mesh of sierozem power, the partial size of the zeolite powder and the tourmaline powder >=1000 mesh.The coloring earth Color needed for specific material has calligraphy and painting adjusts, and in the present embodiment, the coloring earth should select black inorganic pigment and red Color inorganic pigment.
The basal layer is inorganic coating, in parts by mass comprising: 15 parts of dicalcium powder, 35 parts of zeolite powder, tourmaline powder 7 parts, 15 parts of white cement, 10 parts of barite, 8 parts of diatomite and 0.5 part of cellulose, and the zeolite powder and the tourmaline powder 400~600 mesh of partial size, more than 300 mesh of partial size of remaining raw material.
The present embodiment also provides a kind of production method of the extension picture of above-mentioned releasable negative oxygen ion, comprising the following steps:
The material of the basal layer and water are mixed and made into slurry according to the ratio of 1:0.35, then the slurry batch is coated in pre- On the plank of scale cun, the basal layer of 2mm left and right thickness is formed;By the calligraphy and painting pigment and water according to the ratio uniform of 1:0.6 Calligraphy and painting pigment mixture is made in mixing;According to predetermined pattern, the calligraphy and painting pigment mixture is transferred in such a way that sun is carved On the basal layer, calligraphy and painting layer is formed.Specifically, the step of forming the calligraphy and painting layer includes: that predetermined pattern is soft using profession Part copy after is converted to polar plot, then using needle drawing machine engraving produce come;With Sticky Note imprinting at template, apply in the base On plinth layer;Then the calligraphy and painting pigment mixture batch is applied in the template applied, takes template off and cleans out calligraphy and painting completely Come;The template that will be completed, using solid wood frame mounting, the extension picture of the complete releasable negative oxygen ion of a width just calculates completion.
Embodiment 2
The present embodiment provides a kind of extension picture of releasable negative oxygen ion, size 0.6m × 1.5m of the extension picture, the extension picture Structure and the extension picture structure that embodiment 1 provides are essentially identical, the difference is that: in the present embodiment, the basal layer and described Negative oxygen ion function layer is provided between calligraphy and painting layer;In addition, the composition for the calligraphy and painting pigment that calligraphy and painting layer uses in the present embodiment is different. Specifically, in the present embodiment, the calligraphy and painting pigment includes the raw material of following mass parts: 6 parts of sierozem power, 6 parts of super finely ground slag, plain boiled water 12 parts of mud, 6 parts of latex powder, 30 parts of zeolite powder, 4 parts of tourmaline powder, 12 parts of Paris white, 3 parts of nano oxidized magnesium powder, diatomite 4 Part, 4 parts of silica flour, 1 part of cellulose, 0.2 part of defoaming agent and 6~8 parts of coloring earth, and the partial size of the sierozem power >=600 mesh, The partial size of the zeolite powder and the tourmaline powder >=1000 mesh.Moreover, the coloring earth should select black in the present embodiment Color inorganic pigment, Yellow organic dye and red inorganic pigment.
The negative oxygen ion function layer mainly include 6 parts of sierozem power, 6 parts of super finely ground slag, 12 parts of white cement, 6 parts of latex powder, 30 parts of zeolite powder, 4 parts of tourmaline powder, 12 parts of Paris white, 4 parts of diatomite, 4 parts of talcum powder, 4 parts of silica flour, cellulose 0.5 Part, and 300~400 mesh of partial size of the sierozem power, equal 500~600 mesh of the partial size of the zeolite powder and the tourmaline powder.
The present embodiment also provides a kind of production method of the extension picture of above-mentioned releasable negative oxygen ion, the production method and implementation The production method that example 1 provides is essentially identical, the difference is that: production method provided in this embodiment includes: described in the formation After basal layer, the material of negative oxygen ion function layer and water are mixed and made into slurry according to the ratio uniform of 1:0.4, then bullet again It is coated on the basal layer, forms negative oxygen ion function layer;Calligraphy and painting is made on the negative oxygen ion function layer again later, thus shape At the calligraphy and painting layer.
Embodiment 3
The present embodiment provides a kind of extension picture of releasable negative oxygen ion, the extension pictures of structure and embodiment 2 offer of the extension picture Structure is essentially identical, the difference is that: the material of calligraphy and painting layer uses in the present embodiment calligraphy and painting pigment and negative oxygen ion function layer Material composition is different from embodiment 2;Specifically, the calligraphy and painting pigment includes the raw material of following mass parts: 8 parts of sierozem power, ultra-fine mine 8 parts of powder, 16 parts of white cement, 8 parts of latex powder, 35 parts of zeolite powder, 5 parts of tourmaline powder, 15 parts of Paris white, nano oxidized magnesium powder 5 Part, 5 parts of diatomite, 5 parts of silica flour, 1 part of cellulose, 0.3 part of defoaming agent and 6~8 parts of coloring earth, and the grain of the sierozem power The partial size of diameter >=600 mesh, the zeolite powder and the tourmaline powder >=1000 mesh.
The negative oxygen ion function layer mainly include 8 parts of sierozem power, 8 parts of super finely ground slag, 16 parts of white cement, 8 parts of latex powder, 35 parts of zeolite powder, 5 parts of tourmaline powder, 15 parts of Paris white, 5 parts of diatomite, 5 parts of talcum powder, 5 parts of silica flour, 1 part of cellulose, And 300~400 mesh of partial size of the sierozem power, equal 500~600 mesh of the partial size of the zeolite powder and the tourmaline powder.
The present embodiment also provides a kind of production method of the extension picture of above-mentioned releasable negative oxygen ion, the production method and implementation The production method that example 2 provides is essentially identical.
Embodiment 4
The present embodiment provides a kind of extension picture of releasable negative oxygen ion, the extension pictures of structure and embodiment 2 offer of the extension picture Structure is essentially identical, the difference is that: the material of calligraphy and painting layer uses in the present embodiment calligraphy and painting pigment and negative oxygen ion function layer Material composition is different from embodiment 2;Specifically, the calligraphy and painting pigment includes the raw material of following mass parts: 10 parts of sierozem power, ultra-fine mine 10 parts of powder, 20 parts of white cement, 10 parts of latex powder, 40 parts of zeolite powder, 8 parts of tourmaline powder, 20 parts of Paris white, nano oxidized magnesium powder 5 parts, 8 parts of diatomite, 8 parts of silica flour, 1.5 parts of cellulose, 0.5 part of defoaming agent and 8~10 parts of coloring earth, and the sierozem power Partial size >=600 mesh, the partial size of the zeolite powder and the tourmaline powder >=1000 mesh.
The negative oxygen ion function layer mainly includes 10 parts of sierozem power, 10 parts of super finely ground slag, 20 parts of white cement, latex powder 10 Part, 40 parts of zeolite powder, 8 parts of tourmaline powder, 20 parts of Paris white, 8 parts of diatomite, 6 parts of talcum powder, 8 parts of silica flour, cellulose 1 Part, and 300~400 mesh of partial size of the sierozem power, equal 500~600 mesh of the partial size of the zeolite powder and the tourmaline powder.
The present embodiment also provides a kind of production method of the extension picture of above-mentioned releasable negative oxygen ion, the production method and implementation The production method that example 2 provides is essentially identical.
Performance test
Test condition: in 25 ± 2 DEG C of room temperature, the closed room of 50 ± 10%RH of humidity, using air ion detector, The extension picture that concentration of formaldehyde detector, PM2.5 granule density detector detect the offer of embodiment 1,2,3,4 respectively hangs over area about 16m2Room before and after space air in negative oxygen ion concentration, concentration of formaldehyde and PM2.5 granule content, testing result is such as Shown in Tables 1 and 2.
1 space air quality measurements table of table
2 room negative oxygen ion concentration testing result table of table
Sample Embodiment 1 Embodiment 2 Embodiment 3 Embodiment 4
It puts before hanging picture 200-300/s.cm2 350-400/s.cm2 280-330/s.cm2 310-420/s.cm2
It puts after hanging picture 600-700/s.cm2 800-900/s.cm2 750-860/s.cm2 670-890/s.cm2
From the data of Tables 1 and 2 it can be seen that can make within 8 hours after extension picture provided in an embodiment of the present invention is put into room The negative oxygen ion concentration for obtaining room at least doubles, and the removal rate that formaldehyde removal rate reaches 76.4% or more, PM2.5 particle reaches To 69% or more, so as to prove extension picture provided in an embodiment of the present invention can discharge a large amount of negative oxygen ion, decomposing formaldehyde, The content for reducing air PM2.5 particle has the effects that purify air, environmental protection, health care.
Finally it should be noted that: the above embodiments are merely illustrative of the technical scheme of the present invention and are not intended to be limiting thereof;To the greatest extent The present invention is described in detail with reference to preferred embodiments for pipe, it should be understood by those ordinary skilled in the art that: still It can modify to a specific embodiment of the invention or some technical features can be equivalently replaced;Without departing from this hair The spirit of bright technical solution should all cover within the scope of the technical scheme claimed by the invention.

Claims (10)

1. a kind of extension picture of releasable negative oxygen ion, which is characterized in that including bottom plate, the basal layer being coated on the bottom plate and system Make the calligraphy and painting layer on the basal layer, wherein the material of the basal layer is inorganic coating, and the calligraphy and painting layer is using releasable The calligraphy and painting pigment of negative oxygen ion is drawn.
2. the extension picture of releasable negative oxygen ion according to claim 1, which is characterized in that the calligraphy and painting pigment includes following The raw material of mass parts: 5~10 parts of sierozem power, 5~10 parts of super finely ground slag, 10~20 parts of white cement, 5~10 parts of latex powder, zeolite 25~40 parts of powder, 3~8 parts of tourmaline powder, 10~20 parts of Paris white, 1~5 part of nano oxidized magnesium powder, 3~8 parts of diatomite, stone 2~8 parts of English powder, 0.5~1.5 part of cellulose, 0.1~0.5 part of defoaming agent and 5~10 parts of coloring earth, wherein the sierozem power Partial size >=600 mesh, the partial size of the zeolite powder and the tourmaline powder >=1000 mesh, the fineness > of the coloring earth 300 mesh.
3. the extension picture of releasable negative oxygen ion according to claim 2, which is characterized in that the sierozem power, described ultra-fine The mass ratio of miberal powder, the white cement and the latex powder is 1:1:2:1.
4. the extension picture of releasable negative oxygen ion according to claim 1 or 2 or 3, which is characterized in that the basal layer is 1 ~3 mm, the material of the basal layer include mixed uniformly dicalcium powder, zeolite powder, tourmaline powder, white cement, barite, silicon Diatomaceous earth and cellulose.
5. the extension picture of releasable negative oxygen ion according to claim 4, which is characterized in that the basal layer and the calligraphy and painting Negative oxygen ion function layer is provided between layer.
6. the extension picture of releasable negative oxygen ion according to claim 5, which is characterized in that the negative oxygen ion function layer Material includes mixed uniformly sierozem power, super finely ground slag, white cement, latex powder, Paris white, zeolite powder, diatomite, quartz Powder, talcum powder and cellulose.
7. the extension picture of releasable negative oxygen ion according to claim 1, which is characterized in that the material of the bottom plate is timber Or plastics.
8. a kind of production method of the extension picture of releasable negative oxygen ions described in any item according to claim 1~7, including it is following Step:
The basal layer is coated on the bottom plate;The calligraphy and painting pigment and water are mixed according to the ratio uniform of 1:0.6~0.8 It closes, calligraphy and painting pigment mixture is made;Calligraphy and painting is made on the basal layer using the calligraphy and painting pigment mixture.
9. the production method of the extension picture of releasable negative oxygen ion according to claim 8, which is characterized in that further include step It is rapid: after the material of the basal layer batch is coated on the floor, negative oxygen ion function material bullet being coated onto the basal layer On, negative oxygen ion function layer is formed, then makes the calligraphy and painting on the negative oxygen ion function layer again.
10. the production method of the extension picture of releasable negative oxygen ion according to claim 9, which is characterized in that described in production The step of calligraphy and painting includes: that the calligraphy and painting pigment mixture is transferred on the negative oxygen ion function layer in such a way that sun is carved to make Make the calligraphy and painting layer;Or the calligraphy and painting pigment mixture is directly drawn into calligraphy and painting on the negative oxygen ion function layer as prepared Chinese ink To form the calligraphy and painting layer.
CN201910084759.5A 2019-01-29 2019-01-29 A kind of extension picture of releasable negative oxygen ion and preparation method thereof Pending CN109910491A (en)